CN103215713A - Production method of bastose wet spinning yarn - Google Patents
Production method of bastose wet spinning yarn Download PDFInfo
- Publication number
- CN103215713A CN103215713A CN2013101415939A CN201310141593A CN103215713A CN 103215713 A CN103215713 A CN 103215713A CN 2013101415939 A CN2013101415939 A CN 2013101415939A CN 201310141593 A CN201310141593 A CN 201310141593A CN 103215713 A CN103215713 A CN 103215713A
- Authority
- CN
- China
- Prior art keywords
- wet spinning
- production method
- minutes
- ball
- ramie stripes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a production method of a bastose wet spinning yarn. The production method of the bastose wet spinning yarn comprises the steps of heckling, degumming, scouring and bleaching, dyeing, drying and softening, then color mixture is carried out on two kinds or more than two kinds of ramie strips of different colors according to different color ratios, the ramie strips are mixed and drafted after 4-6 drawing working procedures, roving and wet spinning thinning working procedures are carried out on the ramie strips, and finally the ramie strips are dried, spooled and packaged to form a finished product. The production method of the bastose wet spinning yarn is characterized in that the heckling working procedure comprises a process of strip manufacturing and a process of ball formation, the process of strip manufacturing means that short fibers are removed and then long bastose fibers are manufactured into the ramie strips; and the process of ball formation means that the continuous ramie strips are wound layer by layer from inside to outside to form a hollow cylindrical bastose ball. The produced bastose wet spinning yarn is uniform in dyeing, bright in color, rich in level, and good in color fastness.
Description
Technical field
The present invention relates to a kind of ramee spinning technical field, the production method of the flax fibre wet spinning dyed yarn line of especially a kind of clothes that are used for knitting or woven processing and tame textile fabric.
Background technology
Present domestic bast fibre spinning corporate boss will produce the ramie yarn kind of monochrome (white and primary colors), and will dye, usually through following several method: the one, the dimity of white is dyed different colors one by one, and then as required the dimity of different colours is carried out look and knit; The 2nd, the cloth that the dimity is woven dyes as required.
More than two kinds of methods have the following disadvantages: 1, dye not thoroughly, because tube yarn parcel is closely, remaining pectin stops dyestuff to be penetrated into a yarn center fully and " the white heart " phenomenon occurs on the yarn simultaneously; 2, uneven dyeing, piece dyeing finishing because the cylinder that technology and environmental error bring is poor, end to end aberration and while arriving aberration; 3, dyeing cost height, big for environment pollution; 4, color is single, lacks the bulky color effect, and the finished product outward appearance is stiff.
The patent No. is 200710066825.3, patent name is for disclosing a kind of technology in the Chinese patent of " manufacture craft of flax color spinning ": will dye after the bleaching of breakings material, after the oven dry successively through connection comb, grilling, single smart, multiple essence, three road grillings, last pin operation, in three road grilling processes, sneak into the linen fibre drawing-off of different colours and add and be twisted into rove, with reeling roving on flyer bobbin, put into to boil and float container and boil and float, make spun yarn through spinning then, at last oven dry, winder aftershaping.Technique scheme adopts flax weak point to spin route, and its shortcoming and defect is: (1) through single smart, multiple Seiko preface, the combing noil is very high, and row yielding is low, the cost height; (2) can not spin the above high grade yarn of 30Nm, should; (3) spinning yarn quality is poor, weaving performance is poor.
The patent No. is 201010570251.5, and patent name is for disclosing a kind of technological process in the Chinese patent of " a kind of linen is spun line yarn and preparation technology's flow process thereof ": (1) raw material choice; (2) beam splitting; (3) hackling; (4) raw material slivering; (5) dyeing; (6) zero also; (7) in the lump; (8) two also; (9) three also; (10) end also; (11) rove; (12) boil and float; (13) spun yarn; (14) radio-frequency seasoning; (15) choose yarn; (16) winder; (17) finished product, packing.Technique scheme has only been enumerated the title of each operation, and concrete operation process discloses, so those skilled in the art can't implement.And above-mentioned technological process is spun and indifference with conventional flax is long except that dyeing process, and its shortcoming and defect is: (1) can't satisfy the package requirement of dyeing to ramie stripes, and it is low to produce efficient in batches; (2) sticking after the ramie stripes dyeing oven dry also phenomenon is serious, and the later process difficulty of processing is big; (3) spinnability is poor, and spinning yarn quality is poor, and weaving performance is poor.
The patent No. is 201210314826.6, and patent name discloses a kind of method in the Chinese patent of " a kind of producer of flax fibre fiber dyed yarn ": the 1) preliminary treatment of flax fibre: flax fibre is respectively through concise and penetrant treating; With scouring agent 3-4%owf temperature 56-62 ℃ under neutrallty condition refining time be 45-60min; (2) reeling of flax fibre: the weight of reeling is 500-700g; (3) dyeing of flax fibre: flax fibre is dyed required color; But used dyestuff is a discharge material or can not the discharge material; (4) fixation of flax fibre: fixation is 0.5 hour-1 hour under temperature 90-110 degree; (5) spinning of flax fibre: the flax fibre of different colours is woven into fiber dyed yarn.The shortcoming and defect of technique scheme is: (1) can not realize the mixing of arbitrary proportion, and color is single; (2) finished product is that two kinds of dyed yarns are handed over the effect of twisting with the fingers, and can not produce the bulky color effect; (3) operation is long, efficient is low, cost is high; (4) flax fibre all dyes, and the spinning of checking colors is mutually polluted big, not environmental protection.
Summary of the invention
Technical problem to be solved by this invention be overcome deficiency of the prior art and provide that a kind of dyeing is full and uniform, bright-colored, levels are rich, COLOR FASTNESS be good, with the production method of the diverse flax fibre wet spinning of normal dyeing product effect dyed yarn line.
The technical scheme that the present invention solves the problems of the technologies described above employing is: the production method of flax fibre wet spinning dyed yarn line, comprise hackling, come unstuck, boil float, dyeing, oven dry and soft treatment, then the ramie stripes of different colours more than 2 kinds or 2 kinds is pressed different color ratio colour mixtures,, drawing-off mixed also through 4-6 road mixing in doubling step, pass through rove, wet spinning spinning process again, oven dry at last, winder, finished product packing, it is characterized in that: described hackling operation comprises system bar and two processes of balling-up, system bar process is that staple fibre is removed, and longer flax fibre is made ramie stripes; The balling-up process is the uniform hollow cylindrical fiber crops of outer density ball in continuous ramie stripes is successively reeled from the inside to the outside.The present invention makes ramie stripes special numb ball shape in the hackling process, such purpose is to be convenient to carrying and even dyeing, and back road adds the man-hour ramie stripes and is easy to unwinding, makes things convenient for drafting production.
Balling-up process of the present invention successively is wound on the take up roll continuous ramie stripes by the feeding unit that traverses on numb ball up-coiler from the inside to the outside, the uniform hollow cylindrical fiber crops of outer density ball in forming, fiber crops ball internal diameter 5-10cm, external diameter 35-45cm, balling-up height 30-40cm, be convenient to dyeing dress cage, unwinding also is convenient in road, back processing simultaneously.
The process of floating of boiling of the present invention comprises that the Asia is floated with cryogenic oxygen and floats two processes that process is floated for numb ball is put into water in the Asia, adds the NaClO of 1-2g/L
2, pH value 2.5-3.5, initial temperature is 25 ℃, is warming up to 50 ℃ with 30 minutes, is incubated 30 minutes after washings, finishes the Asia and floats; The described cryogenic oxygen process of floating is to add the H of 5-15g/L
2O
2, pH value 10-11, initial temperature is 25 ℃, is warming up to 60 ℃ with 30 minutes, is incubated 50 minutes after washings, finishes oxygen and floats.Above-mentioned technical process and select concrete technological parameter, conventional hemp spinning process effect relaxes, and has alleviated and has boiled the damage of the process of floating to fiber, is beneficial to later process processing.
Dyeing course of the present invention places 25 ℃-30 ℃ water for the numb ball after will bleaching, requirement according to dying color adds REACTIVE DYES, be warming up to 60 ℃-80 ℃ and kept 50-60 minute, add washing agent 1g/L after the discharge opeing, under 80 ℃-90 ℃ temperature, carry out the washing first time, add clear water washing for the second time under 80 ℃-90 ℃ temperature after the discharge opeing again, discharge opeing is afterwards under 40 ℃-50 ℃ temperature, adding softener 1-2g/L soaked 20-30 minute, dewatered 20-40 minute after the discharge opeing, keep moisture content, dry after the dehydration at 50%-70%, numb ball after the oven dry is carried out soft treatment again, reach machine production requirement on the drafting.
Dyeing course of the present invention places 25 ℃-30 ℃ water for the ramie stripes after will bleaching, and adds REACTIVE DYES, adds Na after 10 minutes
2SO
410g/L-70g/L kept 15-20 minute, was warming up to 60 ℃-80 ℃ with 1 ℃/minute speed then, added the Na of 10g/L-20g/L
2CO
3, keep adding again after 20 minutes the Na of 10g/L-30g/L
2CO
3, keep after 40-50 minute that discharge opeing is washed successively again, oven dry and soft treatment.
Washing agent of the present invention is a soaping agent, and described softener is ester based quaternary ammonium salt softener QL, has good degradability, and environmental protection can not have any impact to environment.
Soft treatment of the present invention be will oven dry numb ball unwinding, and by having the stripping-cutting machine of two serpentine bending parts, make ramie stripes through alternating bending and the drawing-off effect loose softness that becomes.Adopt special stripping-cutting machine to make the loose softness of ramie stripes, be easy to processing, solved the problem that conventional ramie stripes can't shredding after bleachinging and dyeing be produced.
Mixing in doubling step of the present invention its 0 and process in the ramie stripes of different colours more than 2 kinds or 2 kinds mix also, drawing-off, make the colour mixture ramie stripes that polychrome mixes the assembly effect.Color is natural and implicit, and dim sense is strong, contains the fiber of part no dyeing in the dyed yarn, compares the traditional handicraft of spinning after stain earlier, and the dyeing amount is few, energy-conserving and environment-protective relatively.
The present invention compared with prior art has the following advantages: the dyeing ramie stripes fiber after the soft treatment has excellent advantages such as pliability, slippery and elasticity, and the numb dyed yarn color that processes is enriched beautiful, can adapt to knitting or woven processing, it is fluffy, soft to knit the fabric of making, the finished product COLOR FASTNESS is good, has greatly satisfied soft feel and the color demand of people on dress ornament.
Description of drawings
Fig. 1 is a process chart of the present invention.
Fig. 2 is a dyeing course process chart of the present invention.
Fig. 3 is the two serpentine workspaces of stripping-cutting machine of the present invention schematic diagrames.
The specific embodiment
Embodiment one
Referring to Fig. 1, Fig. 2, with the raw ramie hackling, hackling comprises system bar and two processes of balling-up, the staple fibre that the system bar is about in the raw ramie is removed, and longer flax fibre is made ramie stripes, successively is wound on the take up roll continuous ramie stripes from the inside to the outside by the feeding unit that traverses on numb ball up-coiler then, the uniform hollow cylindrical fiber crops of outer density ball in forming, fiber crops ball internal diameter 5-10cm, external diameter 35-45cm, balling-up height 30-40cm.The fiber crops ball is bleached after coming unstuck, and described bleaching comprises that the Asia is floated with cryogenic oxygen and floats two steps: the sodium chlorite NaClO that adds 1.5g/L earlier in water
2, pH value 2.5-3.5, initial temperature is 30 ℃, is warming up to 50 ℃ with 30 minutes, is incubated 20 minutes after washings, finishes the Asia and floats.Carry out cryogenic oxygen then and float, add the H of 15g/L
2O
2, pH value 10-11, initial temperature is 25 ℃, is warming up to 60 ℃ with 30 minutes, is incubated 50 minutes after washings, finishes cryogenic oxygen and floats.Numb ball after the bleaching is placed 30 ℃ water, add the light yellow B-EXF REACTIVE DYES of Megafix of 3.2g/L, be incubated 10 minutes and add Na afterwards
2SO
4(glauber salt) 70g/L is incubated the speed that begins with 1 ℃/minute after 20 minutes and is warming up to 60 ℃, adds the Na of 10g/L
2CO
3, keep adding again after 20 minutes the Na of 10g/L
2CO
3, keep discharge opeing after 45 minutes, add soaping agent 1g/L, under 80 ℃-90 ℃ temperature, carried out washing the first time 20 minutes, add clear water again after the discharge opeing and under 80 ℃-90 ℃ temperature, washed once more 10 minutes.Under 40 ℃-50 ℃ temperature, add ester based quaternary ammonium salt softener QL1.5g/L and soaked 20-30 minute after the discharge opeing, dewatered 20-40 minute after the discharge opeing, keep moisture content at 50%-70%.Numb ball after dehydration speed with 4m/h in radio frequency dryer is dried.Referring to Fig. 3,, and by having the stripping-cutting machine of two serpentine bending parts 1, make ramie stripes through alternating bending and the drawing-off effect loose softness that becomes with the numb ball unwinding after the oven dry.After the processing ramie stripes of different colours more than 2 kinds or 2 kinds is proportionally carried out colour mixture on 0 road drawing frame and closes, make the colour mixture ramie stripes of 25g/m, then through 1 also, 2 also, 3 also, end and multiple tracks drafting grilling carry out repeatedly and close and drawing-off.End and ramie stripes are made rove through drawing-off, and rove is added the twist of 32T/m, are wound on the flyer bobbin.Flyer bobbin put into to boil float container and soak into, after draw twisting, making spun yarn on the fine spining machine then with normal-temperature water.Spun yarn is placed the speed oven dry of radio frequency dryer with 6m/h, last winder moulding.
Embodiment two
Referring to Fig. 1, Fig. 2, with the raw ramie hackling, hackling comprises system bar and two processes of balling-up, the staple fibre that the system bar is about in the raw ramie is removed, and longer flax fibre is made ramie stripes, successively is wound on the take up roll continuous ramie stripes from the inside to the outside by the feeding unit that traverses on numb ball up-coiler then, the uniform hollow cylindrical fiber crops of outer density ball in forming, fiber crops ball internal diameter 5-10cm, external diameter 35-45cm, balling-up height 30-40cm.The fiber crops ball is bleached after coming unstuck, and described bleaching comprises that the Asia is floated with cryogenic oxygen and floats two steps: the sodium chlorite NaClO that adds 1g/L now in the water
2, pH value 2.5-3.5, initial temperature is 30 ℃, is warming up to 50 ℃ with 30 minutes, is incubated 20 minutes after washings, finishes the Asia and floats.Carry out cryogenic oxygen then and float, add the H of 5g/L
2O
2, pH value 10-11, initial temperature is 25 ℃, is warming up to 60 ℃ with 30 minutes, is incubated 50 minutes after washings, finishes cryogenic oxygen and floats.Numb ball after the bleaching is placed 25 ℃ water, add the Megafix orange B-2RN REACTIVE DYES of bright red B-EXF of Megafix and the 1.2g/L of 0.8g/L, be incubated 10 minutes and add Na afterwards
2SO
4(glauber salt) 40g/L is incubated the speed that begins with 1 ℃/minute after 15 minutes and is warming up to 70 ℃, adds the Na of 15g/L
2CO
3, keep adding again after 20 minutes the Na of 20g/L
2CO
3, keep discharge opeing after 40 minutes, add soaping agent 1g/L, under 80 ℃-90 ℃ temperature, washed 20 minutes, add clear water again after the discharge opeing and under 80 ℃-90 ℃ temperature, washed once more 10 minutes.Under 40 ℃-50 ℃ temperature, add ester based quaternary ammonium salt softener QL1g/L and soaked 20-30 minute after the discharge opeing, dewatered 20-40 minute after the discharge opeing, keep moisture content at 50%-70%.Numb ball after dehydration speed with 4m/h in radio frequency dryer is dried.Referring to Fig. 3,, and by having the stripping-cutting machine of two serpentine bending parts 1, make ramie stripes through alternating bending and the drawing-off effect loose softness that becomes with the numb ball unwinding after the oven dry.After the processing ramie stripes of different colours more than 2 kinds or 2 kinds is proportionally carried out colour mixture on 0 road drawing frame and closes, make the colour mixture ramie stripes of 25g/m, then through 1 also, 2 also, 3 also, end and multiple tracks drafting grilling carry out repeatedly and close and drawing-off.End and ramie stripes are made rove through drawing-off, and rove is added the twist of 32T/m, are wound on the flyer bobbin.Flyer bobbin put into to boil float container and soak into, after draw twisting, making spun yarn on the fine spining machine then with normal-temperature water.Spun yarn is placed the speed oven dry of radio frequency dryer with 6m/h, last winder moulding.
Embodiment three
Referring to Fig. 1, Fig. 2, with the raw ramie hackling, hackling comprises system bar and two processes of balling-up, the staple fibre that the system bar is about in the raw ramie is removed, and longer flax fibre is made ramie stripes, successively is wound on the take up roll continuous ramie stripes from the inside to the outside by the feeding unit that traverses on numb ball up-coiler then, the uniform hollow cylindrical fiber crops of outer density ball in forming, fiber crops ball internal diameter 5-10cm, external diameter 35-45cm, balling-up height 30-40cm.The fiber crops ball is bleached after coming unstuck, and described bleaching comprises that the Asia is floated with cryogenic oxygen and floats two steps: the sodium chlorite NaClO that adds 2g/L now in the water
2, pH value 2.5-3.5, initial temperature is 30 ℃, is warming up to 50 ℃ with 30 minutes, is incubated 20 minutes after washings, finishes the Asia and floats.Carry out cryogenic oxygen then and float, add the H of 10g/L
2O
2, pH value 10-11, initial temperature is 25 ℃, is warming up to 60 ℃ with 30 minutes, is incubated 50 minutes after washings, finishes cryogenic oxygen and floats.Numb ball after the bleaching is placed 30 ℃ water, add the gorgeous blue B-EXF of Megafix of 1.7g/L and the red B-EXF REACTIVE DYES of Megafix of 0.01g/L, be incubated 10 minutes and add Na afterwards
2SO
4(glauber salt) 10g/L is incubated the speed that begins with 1 ℃/minute after 20 minutes and is warming up to 80 ℃, adds the Na of 20g/L
2CO
3, keep adding again after 20 minutes the Na of 30g/L
2CO
3, keep discharge opeing after 50 minutes, add soaping agent 1g/L, under 80 ℃-90 ℃ temperature, washed 20 minutes, add clear water again after the discharge opeing and under 80 ℃-90 ℃ temperature, washed once more 10 minutes.Under 40 ℃-50 ℃ temperature, add ester based quaternary ammonium salt softener QL2g/L after the discharge opeing, soaked 20-30 minute, dewatered 20-40 minute after the discharge opeing, keep moisture content at 50%-70%.Numb ball after dehydration speed with 4m/h in radio frequency dryer is dried.Referring to Fig. 3,, and by having the stripping-cutting machine of two serpentine bending parts 1, make ramie stripes through alternating bending and the drawing-off effect loose softness that becomes with the numb ball unwinding after the oven dry.After the processing ramie stripes of different colours more than 2 kinds or 2 kinds is proportionally carried out colour mixture on 0 road drawing frame and closes, make the colour mixture ramie stripes of 25g/m, then through 1 also, 2 also, 3 also, end and multiple tracks drafting grilling carry out repeatedly and close and drawing-off.End and ramie stripes are made rove through drawing-off, and rove is added the twist of 32T/m, are wound on the flyer bobbin.Flyer bobbin put into to boil float container and soak into, after draw twisting, making spun yarn on the fine spining machine then with normal-temperature water.Spun yarn is placed the speed oven dry of radio frequency dryer with 6m/h, last winder moulding.
Embodiment four
Referring to Fig. 1, Fig. 2, with the raw ramie hackling, hackling comprises system bar and two processes of balling-up, the staple fibre that the system bar is about in the raw ramie is removed, and longer flax fibre is made ramie stripes, successively is wound on the take up roll continuous ramie stripes from the inside to the outside by the feeding unit that traverses on numb ball up-coiler then, the uniform hollow cylindrical fiber crops of outer density ball in forming, fiber crops ball internal diameter 5-10cm, external diameter 35-45cm, balling-up height 30-40cm.The fiber crops ball is bleached after coming unstuck, and described bleaching comprises that the Asia is floated with cryogenic oxygen and floats two steps: the sodium chlorite NaClO that adds 2g/L now in the water
2, pH value 2.5-3.5, initial temperature is 30 ℃, is warming up to 50 ℃ with 30 minutes, is incubated 20 minutes after washings, finishes the Asia and floats.Carry out cryogenic oxygen then and float, add the H of 10g/L
2O
2, pH value 10-11, initial temperature is 25 ℃, is warming up to 60 ℃ with 30 minutes, is incubated 50 minutes after washings, finishes cryogenic oxygen and floats.Numb ball after the bleaching is placed 30 ℃ water, add the gorgeous blue B-EXF of Megafix of 1.7g/L and the red B-EXF REACTIVE DYES of Megafix of 0.01g/L, be warming up to 60 ℃-80 ℃ and kept 50-60 minute, add washing agent 1g/L after the discharge opeing, under 80 ℃-90 ℃ temperature, carry out the washing first time, add clear water washing for the second time under 80 ℃-90 ℃ temperature after the discharge opeing again, discharge opeing is afterwards under 40 ℃-50 ℃ temperature, adding ester based quaternary ammonium salt softener 1.5g/L soaked 20-30 minute, dewatered 20-40 minute after the discharge opeing, keep moisture content at 50%-70%, the speed with 4m/h in radio frequency dryer of the numb ball after the dehydration is dried.Referring to Fig. 3,, and by having the stripping-cutting machine of two serpentine bending parts 1, make ramie stripes through alternating bending and the drawing-off effect loose softness that becomes with the numb ball unwinding after the oven dry.After the processing ramie stripes of different colours more than 2 kinds or 2 kinds is proportionally carried out colour mixture on 0 road drawing frame and closes, make the colour mixture ramie stripes of 25g/m, then through 1 also, 2 also, 3 also, end and multiple tracks drafting grilling carry out repeatedly and close and drawing-off.End and ramie stripes are made rove through drawing-off, and rove is added the twist of 32T/m, are wound on the flyer bobbin.Flyer bobbin put into to boil float container and soak into, after draw twisting, making spun yarn on the fine spining machine then with normal-temperature water.Spun yarn is placed the speed oven dry of radio frequency dryer with 6m/h, last winder moulding.
Though the present invention with embodiment openly as above; but it is not in order to limit protection scope of the present invention; any technical staff who is familiar with this technology, change and the retouching done in not breaking away from design of the present invention and scope all should belong to protection scope of the present invention.
Claims (8)
1. the production method of a flax fibre wet spinning dyed yarn line, comprise hackling, come unstuck, boil float, dyeing, oven dry and soft treatment, then the ramie stripes of different colours more than 2 kinds or 2 kinds is pressed different color ratio colour mixtures,, drawing-off mixed also through 4-6 road mixing in doubling step, pass through rove, wet spinning spinning process again, oven dry at last, winder, finished product packing is characterized in that: described hackling operation comprises system bar and two processes of balling-up, system bar process is that staple fibre is removed, and longer flax fibre is made ramie stripes; The balling-up process is the uniform hollow cylindrical fiber crops of outer density ball in continuous ramie stripes is successively reeled from the inside to the outside.
2. the production method of flax fibre wet spinning dyed yarn line according to claim 1, it is characterized in that: described balling-up process successively is wound on the take up roll continuous ramie stripes by the feeding unit that traverses on numb ball up-coiler from the inside to the outside, the uniform hollow cylindrical fiber crops of outer density ball in forming, fiber crops ball internal diameter 5-10cm, external diameter 35-45cm, balling-up height 30-40cm.
3. the production method of flax fibre wet spinning dyed yarn line according to claim 1 is characterized in that: the described process of floating of boiling comprises that the Asia is floated with cryogenic oxygen and floats two processes that process is floated for numb ball is put into water in the Asia, adds the NaClO of 1-2g/L
2, pH value 2.5-3.5, initial temperature is 30 ℃, is warming up to 50 ℃ with 30 minutes, is incubated 20 minutes after washings, finishes the Asia and floats; The described cryogenic oxygen process of floating is to add the H of 5-15g/L
2O
2, pH value 10-11, initial temperature is 25 ℃, is warming up to 60 ℃ with 30 minutes, is incubated 50 minutes after washings, finishes oxygen and floats.
4. the production method of flax fibre wet spinning dyed yarn line according to claim 1, it is characterized in that: described dyeing course places 25 ℃-30 ℃ water for the numb ball after will bleaching, requirement according to dying color adds REACTIVE DYES, be warming up to 60 ℃-80 ℃ and kept 50-60 minute, add washing agent 1g/L after the discharge opeing, under 80 ℃-90 ℃ temperature, carry out the washing first time, add clear water washing for the second time under 80 ℃-90 ℃ temperature after the discharge opeing again, discharge opeing is afterwards under 40 ℃-50 ℃ temperature, adding softener 1-2g/L soaked 20-30 minute, dewatered 20-40 minute after the discharge opeing, keep moisture content at 50%-70%, dry after the dehydration, the numb ball after the oven dry is carried out soft treatment again.
5. flax fibre wet spinning dyed yarn line according to claim 4 and production method thereof is characterized in that: described dyeing course places 25 ℃-30 ℃ water for the ramie stripes after will bleaching, and adds REACTIVE DYES, adds Na after 10 minutes
2SO
410g/L-70g/L kept 15-20 minute, was warming up to 60 ℃-80 ℃ with 1 ℃/minute speed then, added the Na of 10g/L-20g/L
2CO
3, keep adding again after 20 minutes the Na of 10g/L-30g/L
2CO
3, keep after 40-50 minute that discharge opeing is washed successively again, oven dry and soft treatment.
6. the production method of flax fibre wet spinning dyed yarn line according to claim 4, it is characterized in that: described washing agent is a soaping agent, described softener is ester based quaternary ammonium salt softener QL.
7. according to the production method of claim 1,4 or 5 described flax fibre wet spinning dyed yarn lines, it is characterized in that: described soft treatment is the numb ball unwinding with oven dry, and, make ramie stripes through alternating bending and the drawing-off effect loose softness that becomes by having the stripping-cutting machine of two serpentine bending parts.
8. flax fibre wet spinning dyed yarn line according to claim 1 and production method thereof, it is characterized in that: described mixing in doubling step its 0 and process in the ramie stripes of different colours more than 2 kinds or 2 kinds mix also, drawing-off, make the colour mixture ramie stripes that polychrome mixes the assembly effect.