CN100556947C - A kind of low-smoke bittern-free highly fire-proof elastic polyolefin electric cable material - Google Patents
A kind of low-smoke bittern-free highly fire-proof elastic polyolefin electric cable material Download PDFInfo
- Publication number
- CN100556947C CN100556947C CNB2007100219339A CN200710021933A CN100556947C CN 100556947 C CN100556947 C CN 100556947C CN B2007100219339 A CNB2007100219339 A CN B2007100219339A CN 200710021933 A CN200710021933 A CN 200710021933A CN 100556947 C CN100556947 C CN 100556947C
- Authority
- CN
- China
- Prior art keywords
- weight
- content
- parts
- elastomerics
- magnesium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Component | Parts by weight |
The EVA elastomerics, melting index≤5g/10min, vinyl acetate content 40% weight in the multipolymer | 50 |
The POE elastomerics, melting index≤3g/10min, hardness≤75 Shao Shi A | 36 |
The EMA elastomerics, melting index≤5g/10min, methyl acrylate content 30% weight in the multipolymer | 14 |
The surface treatment magnesium hydroxide | 60 |
The surface treating nano magnesium hydroxide, median size 40nm | 25 |
Peroxide cross-linking agent (or claiming vulcanizing agent)-DCP | 0.3 |
Phenolic antioxidant (or claiming anti-aging agent)-1010 oxidation inhibitor | 2 |
Silane coupling agent-A-172 | 3 |
Lubricant-PE wax | 3 |
Amount to: | 193.3 |
Component | Parts by weight |
The EVA elastomerics, melting index≤5g/10min, vinyl acetate content 40% weight in the multipolymer | 70 |
The POE elastomerics, melting index≤3g/10min, hardness≤75 Shao Shi A | 25 |
The EMA elastomerics, melting index≤5g/10min, methyl acrylate content 30% weight in the multipolymer | 5 |
The surface treatment magnesium hydroxide | 50 |
The surface treating nano magnesium hydroxide, median size 40nm | 30 |
Peroxide cross-linking agent (or claiming vulcanizing agent)-DCP | 0.3 |
Phenolic antioxidant (or claiming anti-aging agent)-1010 oxidation inhibitor | 1 |
Silane coupling agent-A-172 | 2 |
Lubricant-PE wax | 2 |
Amount to: | 185.3 |
Component | Parts by weight |
The EVA elastomerics, melting index≤5g/10min, vinyl acetate content 40% weight in the multipolymer | 60 |
The POE elastomerics, melting index≤3g/10min, hardness≤75 Shao Shi A | 30 |
The EMA elastomerics, melting index≤5g/10min, methyl acrylate content 30% weight in the multipolymer | 10 |
The surface treatment magnesium hydroxide | 55 |
The surface treating nano magnesium hydroxide, median size 40nm | 30 |
Peroxide cross-linking agent (or claiming vulcanizing agent)-DCP | 0.3 |
Phenolic antioxidant (or claiming anti-aging agent)-1010 oxidation inhibitor | 1.5 |
Silane coupling agent-A-172 | 2.5 |
Lubricant-PE wax | 2.5 |
Amount to: | 191.8 |
Component | Parts by weight |
The EVA elastomerics, melting index≤5g/10min, vinyl acetate content 40% weight in the multipolymer | 75 |
The POE elastomerics, melting index≤3g/10min, hardness≤75 Shao Shi A | 20 |
The EMA elastomerics, melting index≤5g/10min, methyl acrylate content 30% weight in the multipolymer | 5 |
The surface treatment magnesium hydroxide | 65 |
The surface treating nano magnesium hydroxide, median size 40nm | 25 |
Peroxide cross-linking agent (or claiming vulcanizing agent)-DCP | 0.3 |
Phenolic antioxidant (or claiming anti-aging agent)-1010 oxidation inhibitor | 1 |
Silane coupling agent-A-172 | 2.5 |
Lubricant-PE wax | 3 |
Amount to: | 196.8 |
Claims (4)