CN100554201C - A kind of rhodo glass producing process - Google Patents
A kind of rhodo glass producing process Download PDFInfo
- Publication number
- CN100554201C CN100554201C CNB2006100538611A CN200610053861A CN100554201C CN 100554201 C CN100554201 C CN 100554201C CN B2006100538611 A CNB2006100538611 A CN B2006100538611A CN 200610053861 A CN200610053861 A CN 200610053861A CN 100554201 C CN100554201 C CN 100554201C
- Authority
- CN
- China
- Prior art keywords
- blank
- glass
- rhodo
- producing process
- degree centigrade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of rhodo glass producing process, key step is as follows: 1.1) raw material is by following weight proportion: SiO
240-60 part; Al
2O
30.5-1.5 part; PbO 6-35 part; K
2O 2-16 part or Na
2O 3-15 part; ZnO0.5-3 part; B
2O
30.5-3 part; Au 0.3-0.15 part; 1.2) various raw materials are required to be uniformly mixed to form compound input vitrified pot in proportion, and seal in the stove of sealing and fire; 1.3) form the blank of required handicraft through selected mould, again blank is broken burr, shaping, sizing screening; 1.4) blank that will select drops into coloring furnace and heating, and strict controlled temperature is at 450-650 degree centigrade, 5-15 minute heat-up time, when making the blank temperature reach the softening zone of glass at last to be the rhodo colour developing till.The effect that the present invention is useful: the production technique working specification is grasped easily, and glass can not produce magnetization in process of production, avoids taking place variegated and the aberration phenomenon, constant product quality, and starting material loss less wastage reduces production costs.
Description
Technical field
The present invention relates to the process of glass field, mainly is a kind of rhodo glass producing process.
Background technology
The rose red glass is the making material of artistic glassware and glass.What sold existing domestic market is Korea-invested enterprise produced or adopted spray colouration with Korea S's technology handicraft product.The former rose red glass of producing as developing technology of tinting material with gold is difficult to standard because of technological operation, and it is many artificially to reach environmental impact factor, and glass reason such as very easily be magnetized causes the glass color difference phenomenon serious, unstable product quality in the art production process.Waste material is overstocked many simultaneously, and raw materials consumption is big, especially precious metal--and the consumption of-Jin increases, and causes the production cost height, is not suitable for industrialization dirt and produces.
Xian Se production technique (technical process is illustrated as Fig. 1) once: be various raw materials to be uniformly mixed to form compound by the formulation ratio requirement drop into vitrified pot and seal, in the stove of sealing, fire, heating and temperature control is at 1450-1520 degree centigrade, fire after 7 hours stove and stop heating, then open fire door and crucible seals, glass solution in the crucible is manually stirred material, and discharge surface material slag.When treating that the feed liquid naturally cooling shows rose in the crucible, feed liquid is chosen the shape embryo (work in-process) of making required handicraft through selected mould by modes such as roll extrusion or crowded tension and compression.
Summary of the invention
The objective of the invention is in order to overcome above-mentioned deficiency, and a kind of steady quality and the low rhodo glass producing process of production cost are provided.
The present invention realizes the technical scheme that above-mentioned purpose adopts.This rhodo glass producing process, key step is as follows:
1.1), raw material is by following weight proportion: SiO
240-60 part; Al
2O3 0.5-1.5 part; PbO 6-35 part; K
2O 2-16 part or Na
2O 3-15 part; ZnO 0.5-3 part; B
2O
30.5-3 part; Au 0.3-0.15 part;
1.2), various raw materials required to be uniformly mixed to form compound in proportion drop into vitrified pot, and seal in the stove of sealing and fire, heating and temperature control is at 1480-1520 degree centigrade, fires after 7 hours stove and stops heating and open fire door and crucible seals, and manually stirs material and deslagging;
1.3), when treating in the crucible feed liquid and so being cooled between 1050--1150 degree centigrade, feed liquid is chosen, form the blank of required handicraft through selected mould, in natural cooling process, again blank is broken burr, shaping, sizing screening;
1.4), the blank that will select drops into coloring furnace and heating, and strict controlled temperature is at 450-650 degree centigrade, 5-15 minute heat-up time, when making the blank temperature reach the softening zone of glass at last to be the rhodo colour developing till.
The effect that the present invention is useful: the production technique working specification is grasped easily, glass can not produce magnetization in process of production, avoid taking place variegated and the aberration phenomenon, constant product quality, starting material loss less wastage, especially the usage quantity of gold can reduce 30-35%, reduces production costs, and more adapts to industrialization production.
Description of drawings:
Fig. 1 is the process flow diagram of prior art;
Fig. 2 is a process flow diagram of the present invention;
Embodiment:
Below in conjunction with embodiment the present invention is further described, embodiment will help to understand the present invention better, but the present invention is not limited only to following embodiment.
Embodiment 1: this rhodo glass producing process, and key step is as follows:
1.1), raw material is by following weight proportion: SiO
240 parts; Al
20.5 part of O3; 6 parts of PbO; K
22 parts of O; 0.5 part of ZnO; B
2O
30.5 part; 0.15 part of Au;
1.2), various raw materials required to be uniformly mixed to form compound in proportion drop into vitrified pot, and seal in the stove of sealing and fire, heating and temperature control is at 1480-1520 degree centigrade, fires after 7 hours stove and stops heating and open fire door and crucible seals, and manually stirs material and deslagging;
1.3), when treating that feed liquid naturally cools between 1050--1150 degree centigrade in the crucible, feed liquid is chosen, form the blank of required handicraft through selected mould by modes such as roll extrusion or crowded tension and compression, in natural cooling process, again blank is broken burr, shaping, sizing screening;
1.4), the blank that will select drops into heating in the coloring furnace (typing electric furnace), and strict controlled temperature is at 450-650 degree centigrade, 5-15 minute heat-up time, when making the blank temperature reach the softening zone of glass at last to be bright red colour developing till.
Embodiment 2; Difference from Example 1 is: raw material is by following weight proportion: SiO
260 parts; Al
21.5 parts of O3; 35 parts of PbO; K
216 parts of O; 3 parts of ZnO; B
2O
33 parts; 0.3 part of Au.
Embodiment 3; Difference from Example 1 is: raw material is by following weight proportion: SiO
240 parts; Al
20.5 part of O3; 6 parts of PbO; Na
23 parts of O; 0.5 part of ZnO; B
2O
30.5 part; 0.15 part of Au.
Embodiment 4; Difference from Example 1 is: raw material is by following weight proportion: SiO
260 parts; Al
21.5 parts of O3; 35 parts of PbO; Na
2O15 part; 3 parts of ZnO; B
2O
33 parts; 0.3 part of Au.
Embodiment 5: difference from Example 1 is: raw material is by following weight proportion: SiO
250 parts; Al
21 part of O3; 20 parts of PbO; K
29 parts of O; 2 parts of ZnO; B
2O
32 parts; 0.2 part of Au.
Embodiment 6; Difference from Example 1 is: raw material is by following weight proportion: SiO
250 parts; Al
21 part of O3; 20 parts of PbO; Na
29 parts of O; 2 parts of ZnO; B
2O
32 parts; 0.2 part of Au.
Claims (3)
1, a kind of rhodo glass producing process, it is characterized in that: key step is as follows:
1.1), raw material is by following weight proportion: SiO
240-60 part; Al
2O
30.5-1.5 part; PbO 6-35 part; K
2O 2-16 part or Na
2O 3-15 part; ZnO 0.5-3 part; B
2O
30.5-3 part; Au 0.3-0.15 part;
1.2), various raw materials required to be uniformly mixed to form compound in proportion drop into vitrified pot, and seal in the stove of sealing and fire, heating and temperature control is at 1480-1520 degree centigrade, fires after 7 hours stove and stops heating and open fire door and crucible seals, and manually stirs material and deslagging;
1.3), when treating that feed liquid naturally cools between 1050--1150 degree centigrade in the crucible, feed liquid is chosen, form the blank of required handicraft through selected mould, in natural cooling process, again blank is broken burr, shaping, sizing screening;
1.4), the blank that will select drops into coloring furnace and heating, and strict controlled temperature is at 450-650 degree centigrade, 5-15 minute heat-up time, when making the blank temperature reach the softening zone of glass at last to be bright red colour developing till.
2, rhodo glass producing process according to claim 1 is characterized in that: the blank that forms required handicraft through selected mould by the roll extrusion mode.
3, rhodo glass producing process according to claim 1 is characterized in that: the blank that forms required handicraft through selected mould by crowded tension and compression mode.