CN100486756C - 一种高强度铜合金防爆工具模锻生产工艺 - Google Patents
一种高强度铜合金防爆工具模锻生产工艺 Download PDFInfo
- Publication number
- CN100486756C CN100486756C CNB2004100645489A CN200410064548A CN100486756C CN 100486756 C CN100486756 C CN 100486756C CN B2004100645489 A CNB2004100645489 A CN B2004100645489A CN 200410064548 A CN200410064548 A CN 200410064548A CN 100486756 C CN100486756 C CN 100486756C
- Authority
- CN
- China
- Prior art keywords
- blank
- mould
- die
- production technology
- calendering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种铍青铜、铝青铜合金防爆工具模锻生产工艺，其按着铍青铜、铝青铜防爆工具合金材料的配比成分，适应制造工具材料的百分比成份，将此原料按着生产工艺加入冶炼炉进行合金熔炼。熔炼温度达1100℃±20℃开始砂型铸造。将熔炼温度合格的铜液搅拌均匀浇入砂型或钢胎浇口内形成铸件毛坯。上述的铸件合格毛坯再经过二次加热至780℃±10℃时取出坯件，将坯件延时5-10秒钟，使其温度降至700℃±10℃时，此时将模具预热到300℃±20℃，放入锻压设备模具内用压延备压延，采用本发明工艺生产的模锻产品不弯曲、不变形、密度高、使用寿命长。
Description
技术领域
本发明涉及一种铍青铜、铝青铜合金防爆工具模锻生产工艺。
技术背景
目前普通的防爆工具是由铍青铜、铝青铜合金材料组成，生产工艺按着铍青铜、铝青铜防爆工具合金材料的配比成分，适应制造工具材料的百分比成份，将此原料按着生产工艺加入冶炼炉进行合金熔炼。熔炼，温度达1100℃±20℃开始砂型铸造，将熔炼温度合格的铜液搅拌均匀浇入砂型或钢胎浇口内形成铸件毛坏，再经机械加工关键部位，其表面抛光打磨为合格品。采用此工艺生产的防爆工具强度低、品质差、使用寿命短。
发明内容
本发明所要解决的技术问题是提供一种产品性能好使用寿命长的高强度铍青铜、铝青铜合金防爆工具模锻生产工艺。
本发明采用如下技术方案：
本发明按着铍青铜、铝青铜防爆工具合金材料的配比成分，适应制造工具材料的百分比成份，将此原料按着生产工艺加入冶炼炉进行合金熔炼。熔炼温度达1100C±20℃开始砂型铸造。将熔炼温度合格的铜液搅拌均匀浇入砂型或钢胎浇口内形成铸件毛坏。上述的铸件合格毛坯再经过二次加热至780℃±10℃时取出坯件，将坯件延时5-10秒钟，使其温度降至700C±10℃时，此时将模具预热到300℃±20℃，放入锻压设备模具内用压延备压延。
本发明开机前必须将压延装备的上下模具校正，然后把加热好的坯件放进模具内，再进行开机压延，双开模具，合成一体，开机前将模具预热到300℃±20℃，然后把压好的坯件取出放入冲床落边模内，最后把压延出来的毛边、毛刺冲掉为合格锻坯件。
本发明的压延设备为160T—2500T大型摩擦压力机。
本发明积极效果如下：采用本发明工艺生产的模锻产品不弯曲、不变形、密度高、使用寿命长。
采用本发明工艺和传统工艺两种工艺生产的工具数据对比：
| 产品分类 | 材质 | 硬度 | 延伸率δ | 抗拉强度δb |
| 传统铸胎工具 | 铍青铜 | HRC≥35 | δ8％ | 105-120kgf/mm2 |
| 传统铸胎工具 | 铝青铜 | HRC≥25 | δ5％ | 75-85kgff/mm2 |
| 本发明模锻工具 | 铍青铜 | HRC≥42 | δ11％ | 110-125kgf/mm2 |
| 本发明模锻工具 | 铝青铜 | HRC≥30 | δ9％ | 90-100kgf/mm2 |
具体实施方式
本发明实施例如下：
实施例1：
本发明按着铍青铜、铝青铜防爆工具合金材料的配比成分，适应制造工具材料的百分比成份，将此原料按着生产工艺加入冶炼炉进行合金熔炼。熔炼温度达1100℃开始砂型铸造。将熔炼温度合格的铜液搅拌均匀浇入砂型或钢胎浇口内形成铸件毛坏。上述的铸件合格毛坯再经过二次加热至780℃时取出坯件，将坯件延时5秒钟，使其温度降至700℃时，此时将模具预热到300℃，放入锻压设备模具内用压延备压延；开机前必须将压延装备的上下模具校正，然后把加热好的坯件放进模具内，再进行开机压延，双开模具，合成一体，开机前将模具预热到300℃，然后把压好的坯件取出放入冲床落边模内，最后把压延出来的毛边、毛刺冲掉为合格锻坯件；压延设备为160T或400T大型摩擦压力机。
实施例2：
本发明按着铍青铜、铝青铜防爆工具合金材料的配比成分，适应制造工具材料的百分比成份，将此原料按着生产工艺加入冶炼炉进行合金熔炼。熔炼温度达1080℃开始砂型铸造。将熔炼温度合格的铜液搅拌均匀浇入砂型或钢胎浇口内形成铸件毛坏。上述的铸件合格毛坯再经过二次加热至770℃时取出坯件，将坯件延时7秒钟，使其温度降至690℃时，此时将模具预热到280℃，放入锻压设备模具内用压延备压延；开机前必须将压延装备的上下模具校正，然后把加热好的坯件放进模具内，再进行开机压延，双开模具，合成一体，开机前将模具预热到280℃，然后把压好的坯件取出放入冲床落边模内，最后把压延出来的毛边、毛刺冲掉为合格锻坯件，压延设备为630T或1000T大型摩擦压力机。
实施例3：
本发明按着铍青铜、铝青铜防爆工具合金材料的配比成分，适应制造工具材料的百分比成份，将此原料按着生产工艺加入冶炼炉进行合金熔炼。熔炼温度达1120℃开始砂型铸造。将熔炼温度合格的铜液搅拌均匀浇入砂型或钢胎浇口内形成铸件毛坏。上述的铸件合格毛坯再经过二次加热至790℃时取出坯件，将坯件延时10秒钟，使其温度降至710℃时，此时将模具预热到320℃，放入锻压设备模具内用压延备压延；开机前必须将压延装备的上下模具校正，然后把加热好的坯件放进模具内，再进行开机压延，双开模具，合成一体，开机前将模具预热到320℃，然后把压好的坯件取出放入冲床落边模内，最后把压延出来的毛边、毛刺冲掉为合格锻坯件；本发明的压延设备为2500T大型摩擦压力机。
Claims (2)
1、一种高强度铜合金防爆工具模锻生产工艺，其特征在于按着铍青铜或铝青铜防爆工具合金材料的配比成分，适应制造工具材料的百分比成份，将此原料按着生产工艺加入冶炼炉进行合金熔炼，熔炼温度达1100℃±20℃开始砂型铸造，将熔炼温度合格的合金溶液搅拌均匀浇入砂型或钢胎浇口内形成铸件毛坯，合格的上述铸件毛坯再经过二次加热至780℃±10℃时取出坯件，将坯件延时5-10秒钟，使其温度降至700℃±10℃时，放入锻压设备模具内用压延设备压延，此时将模具预热到300℃±20℃，所述的压延设备为160T—2500T大型摩擦压力机。
2、根据权利要求1所述的一种高强度铜合金防爆工具模锻生产工艺，其特征在于开机压延前，将模具预热到300℃±20℃，必须将压延设备的上、下模具校正，然后把加热好的坯件放进模具内，再进行开机压延，双开模具，合成一体，然后把压好的坯件取出放入冲床落边模内，最后把压延出来的毛边、毛刺冲掉，成为合格锻坯件。