CN100475995C - 一种天然斑铜产品的生产方法 - Google Patents
一种天然斑铜产品的生产方法 Download PDFInfo
- Publication number
- CN100475995C CN100475995C CNB200710066029XA CN200710066029A CN100475995C CN 100475995 C CN100475995 C CN 100475995C CN B200710066029X A CNB200710066029X A CN B200710066029XA CN 200710066029 A CN200710066029 A CN 200710066029A CN 100475995 C CN100475995 C CN 100475995C
- Authority
- CN
- China
- Prior art keywords
- natural
- production method
- bornite
- smelting
- zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种天然斑铜产品的生产方法，属金属材料加工技术领域。本发明的生产方法包括雕塑造型—制造模型—复制熔模—制作型模—脱离熔模—冶炼—浇铸—二次结晶-—锻打成型—打磨抛光—烧结—煮斑及染色—检验—包装等工序；其中：a.冶炼工序为：当天然斑铜冶炼温度达到1100-1280℃时，直接向天然斑铜熔液中添加入硅、铝、铅、锑、硫、钠、钡、银、镁、锌、磷、硼合金元素，合金元素的添加量为：锌1-10%、其余均为0.5-5‰；b.浇铸工序后增加二次结晶及锻打人工成型工序。本发明的生产方法的其余工序及操作条件均与常规斑铜产品生产方法相同。本发明与现有技术相比，具有天然斑铜产品外观精致、其晶型为多质结晶、晶型大小均匀、立体感较强、天然斑铜产品的质量明显提高等优点。
Description
技术领域：
本发明涉及一种天然斑铜产品的生产方法，属金属材料加工技术领域。
背景技术：
众所周知，天然斑铜产品及其制备方法已历史悠久。但其生产工艺仍然存在一定的问题，如浇铸工序后的初级产品不能再进行锻打、天然斑铜产品的原料仅为一种或二种等。由于上述问题，导致生产出的天然斑铜产品外观欠精致、其晶型为单质结晶、晶型大小不均匀、无立体效果。
经文献检索，未见与本发明相同的公开报道。
发明内容：
本发明的目的在于通过对传统的天然斑铜产品的生产方法进行改进，提供一种可提高产品质量、易操作的天然斑铜产品的生产方法。
本发明的生产方法包括雕塑造型-制造模型-复制熔模-制作型模-脱离熔模-冶炼-浇铸-二次结晶-锻打成型-打磨抛光-烧结-煮斑及染色-检验-包装等工序；其中：
a.冶炼工序为：当天然斑铜冶炼温度达到1100-1280℃时，直接向天然斑铜熔液中添加入炭、铁、钙、硅、锂、锡、碲、铋、砷、铝、铅、锑、硫、钠、钡、银、镁、锌、磷、硼合金元素，合金元素的添加量为：锌1-10％、其余均为0.5-5‰；所添加的元素均为高纯度。
b.浇铸工序后增加锻打人工成型工序及二次结晶工序，其操作条件与常规方法相同。
本发明的生产方法的其余工序及操作条件均与常规斑铜产品生产方法相同。
本发明与现有技术相比，具有天然斑铜产品外观精致、其晶型为多质结晶、晶型大小均匀、立体感较强、天然斑铜产品的质量明显提高等优点。
具体实施方式：
实施例1：
本发明的生产方法包括雕塑造型-制造模型-复制熔模-制作型模-脱离熔模-冶炼-浇铸-二次结晶-锻打成型-打磨抛光-烧结-煮斑及染色-检验-包装等工序；其中：
a.冶炼工序为：当天然斑铜冶炼温度达到1100℃时，直接向天然斑铜熔液中添加入炭、铁、钙、硅、锂、锡、碲、铋、砷、铝、铅、锑、硫、钠、钡、银、镁、锌、磷、硼合金元素，合金元素的添加量为：锌1％、其余均为5‰；
b.浇铸工序后增加二次结晶及锻打人工成型工序，其操作条件与常规方法相同。
本发明的生产方法的其余工序及操作条件均与常规斑铜产品生产方法相同。
实施例2：
基本同实施例1。不同之处为：冶炼工序中，当天然斑铜冶炼温度达到1200℃时，直接向天然斑铜熔液中添加入硅、铝、铅、锑、硫、钠、钡、银、镁、锌、磷、硼合金元素，合金元素的添加量为：锌5％、其余均为2‰。
实施例3：
基本同实施例1。不同之处为：冶炼工序中，当天然斑铜冶炼温度达到1280℃时，直接向天然斑铜熔液中添加入硅、铝、铅、锑、硫、钠、钡、银、镁、锌、磷、硼合金元素，合金元素的添加量为：锌10％、其余均为0.5‰。
Claims (1)
1、一种天然斑铜产品的生产方法，其特征在于该方法在传统天然斑铜产品生产方法的基础上改进而成；改进部分为：
a.冶炼工序为：当天然斑铜冶炼温度达到1100-1280℃时，直接向天然斑铜熔液中添加入碳、铁、钙、硅、锂、锡、碲、铋、砷、铝、铅、锑、硫、钠、钡、银、镁、锌、磷、硼合金元素，合金元素的添加量为：锌1-10％、其余均为0.5-5‰；
b.浇铸工序后增加二次结晶及锻打成型工序。