CN100458439C - 一种有效的评价树脂防污性能的室内挂板法 - Google Patents
一种有效的评价树脂防污性能的室内挂板法 Download PDFInfo
- Publication number
- CN100458439C CN100458439C CNB2005101047576A CN200510104757A CN100458439C CN 100458439 C CN100458439 C CN 100458439C CN B2005101047576 A CNB2005101047576 A CN B2005101047576A CN 200510104757 A CN200510104757 A CN 200510104757A CN 100458439 C CN100458439 C CN 100458439C
- Authority
- CN
- China
- Prior art keywords
- algae
- plate
- resin
- model
- algae liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种有效的评价树脂防污性能的室内挂板法,其特征是在室内将待评价的树脂均匀地涂布于宽为2.5~5cm、长为7.5~15cm、高为0.25~0.5cm的空白板上,实干后,将该涂层样板放入已到指数生长期的人工培养藻液中,再每隔6~12小时将该涂层样板取出,从显微镜下观察藻在不同树脂上的附着数量或用洗脱液冲洗样板,以空白板为阴性对照,通过分光光度计测定吸光值或用血球计数板计数,根据藻液中藻细胞浓度的变化率评价树脂的防污特性。本发明的藻类可以在短期内对树脂的防污性能进行简单的表征,以达到对其进行初步筛选的目的,与传统的实海挂板法相比具有易操作、实验周期短、可定量的优点。
Description
技术领域
本发明涉及一种树脂防污性能的室内挂板评价方法。
背景技术
目前,防污涂料主要由树脂、防污剂、辅助材料、填充料和溶剂5种组份组成,其中树脂和防污剂是防污涂料的关键组份。从本质上讲,防污涂料的发展依赖于新型树脂的开发和新型防污剂的开发两条主线。而具有良好性能的树脂是开发高性能防污涂料的前提条件之一。目前对于新开发的树脂,通常采用实海挂板的方法对其性能进行评价,而这种传统的评价方法受到很多限制,不仅周期长,难以定量,而且受环境影响较大,这就难以在短期内达到树脂筛选的目的。因此需要建立一个易操作、实验周期短、可定量的室内挂板评价方法。
发明内容
本发明的目的是提供一种有效的评价树脂防污性能的室内挂板法,以满足现有技术的上述需求。
一种有效的评价树脂防污性能的室内挂板法,其特征是在室内将待评价的树脂均匀地涂布于宽为2.5~5cm、长为7.5~15cm、高为0.25~0.5cm的空白板上,实干后,将该涂层样板放入已到指数生长期的人工培养藻液中,再每隔6~12小时将该涂层样板取出,从显微镜下观察藻在不同树脂上的附着数量或用洗脱液冲洗样板,将样板上的藻尽可能全部冲下,以空白板为阴性对照,通过分光光度计测定吸光值或用血球计数板计数,根据藻液中藻细胞浓度的变化率评价树脂的防污特性。
本发明的方法所选用的藻类为海上最典型的附着性藻类如硅藻、金藻或绿藻,可以在短期内对树脂的防污性能进行简单的表征,以达到对其进行初步筛选的目的,与传统的实海挂板法相比具有易操作、实验周期短、可定量的优点。
具体实施方式
1、实验用的新月菱形藻藻液的培养
将海水经玻璃砂芯漏斗过滤后煮沸消毒,冷却后用于配制培养液,该培养液含有营养盐的浓度(重量百分浓度)分别为:硝酸铵4%、磷酸二氢钾0.4%、尿素1.8%、柠檬酸铁0.045%、硅酸钠2%。所用的新月菱形藻藻液在人工气候箱内培养。把盛有新月菱形藻藻液的样品瓶轻轻地前后左右振荡,使藻细胞分散均匀。用不同数量的上述营养液稀释后用血球计数板计数得到分别各稀释液的藻细胞的浓度,并在最大吸收波长处测量各稀释液藻细胞的吸光值,从而得到一组藻液浓度-吸光值数据。并根据这组数据,将培养到指数生长期的藻液用营养液稀释成一定的浓度,摇匀待用。
2、制板
将以N-(4-羟基-3-甲氧基苄基)丙烯酰胺(HMBA)为共聚单体制得的树脂、N-(6-(丙烯酰胺甲基)-1,3-苯并二氧杂戊环-5-甲基)丙烯酰胺(AMBMA)为单体制得的树脂和以丙烯酰胺单体制得的树脂分别均匀地涂刷在25mm×75mm×5mm的玻璃样板上,涂布面积约为15cm2,在空气中自然晾干,备用。
3、在新月菱形藻藻液中进行挂板实验
将晾好的样板载放在样板架上,把该样板架放入盛有上述人工培养的藻液的玻璃缸(长×宽×高:30cm×25cm×15cm)中,在20℃下,光照强度为3000Lx的条件下培养。缸中液体总体积为5L,投放两块气石,藻液的初始浓度为3.88×105个/ml,挂板时间13天,检测时缸中藻液浓度为1.745×106个/ml。光照周期为12∶12,培养液仍为上述培养液。
将实验样板取出,首先从显微镜下观察藻类在不同树脂上的附着数量,从表观上可以看出新月菱形藻在三种不同树脂上的附着情况是不同的。或者用20ml洗脱液反复冲洗样片,将样片上的藻尽可能全部冲下,以空白板为阴性对照,将冲下的藻液用血球计数板计数,藻液浓度太稀时,可直接用分光光度计测定吸光值。从试验可以看出不同的树脂得到不同的试验结果,具体的结果见下表。
藻在挂板上的附着情况
从上表可以看出,不含功能性单体的树脂较含有功能单体HMBA或AMBMA的树脂附着的藻细胞多,而含HMBA或AMBMA的功能性树脂随着HMBA和AMBMA含量的增加,其附着的藻细胞数量减少。而玻璃空白上附着的藻细胞比较少,这可能是因为玻璃表面能比较低,不易于藻类附着。
若将实验用藻新月菱形藻替换为硅藻、金藻或绿藻同样可以得到类似的效果;将空白样板改为聚四氟乙烯平板、PE板、PP板、ABS板或PVC平板同样可以得到类似的效果。
本发明的室内检测树脂防污性能的方法与传统的实海挂板相比大大的缩减了树脂筛选的周期。本发明所选用的藻类为海上最典型的附着性藻类如硅藻、金藻或绿藻,可以在短期内对树脂的防污性能进行简单的表征,达到对其进行初步筛选的目的,能得到良好的应用效果。
Claims (2)
1、一种有效的评价树脂防污性能的室内挂板法,其特征是在室内将待评价的树脂均匀地涂布于宽为2.5~5cm、长为7.5~15cm、高为0.25~0.5cm的空白板上,实干后,将该涂层样板放入已到指数生长期的人工培养藻液中,再每隔6~12小时将该涂层样板取出,从显微镜下观察藻在不同树脂上的附着数量或用洗脱液冲洗样板,将样板上的藻尽可能全部冲下,以空白板为阴性对照,通过分光光度计测定吸光值或用血球计数板计数,根据藻液中藻细胞浓度的变化率评价树脂的防污特性;所述的空白板为玻璃平板、聚四氟乙烯平板、PE板、PP板、ABS板或PVC平板。
2、如权利要求1所述的方法,其特性是所述的藻液中的藻为硅藻、金藻或绿藻。