CN100448792C - 建筑防冻早强剂 - Google Patents
建筑防冻早强剂 Download PDFInfo
- Publication number
- CN100448792C CN100448792C CNB2007100048922A CN200710004892A CN100448792C CN 100448792 C CN100448792 C CN 100448792C CN B2007100048922 A CNB2007100048922 A CN B2007100048922A CN 200710004892 A CN200710004892 A CN 200710004892A CN 100448792 C CN100448792 C CN 100448792C
- Authority
- CN
- China
- Prior art keywords
- building anti
- concrete
- accelerator
- freezing
- freezing accelerator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种建筑用混凝土中使用的防冻早强剂，包括有重量份的如下组份：无水氯化钙，粉煤灰，肌醇六磷酸酯，三乙醇胺，苯甲酸钠，苯骈三氨唑，加入一乙醇胺调节上述组合物的pH值为9-9.5，即制得建筑防冻早强剂。优点在于：(1)低成本、原材料易得、无毒无害，对使用的环境无污染。(2)明显提高混凝土的各龄期的抗压强度及抗渗、抗炭化、防冻等各项性能。(3)使混凝土提高1/2、3/4时间达到设计强度，从而缩短工期。(4)本产品对混凝土收缩，徐变均无不良影响，可改善混凝土的抗渗、防冻、抗炭化等性能，减水泌水性，改善施工和易性，在保证强度与坍落度的同时还能节约水泥用量。
Description
技术领域
本发明涉及一种建筑用混凝土中使用的防冻早强剂。
背景技术
目前我国建筑行业中使用的防冻剂和早强剂，由于使用复合材料，故而成本较高，材料来源少，而且没有一种能够同时起到防冻功能和早强功能为一体的添加剂。
发明内容
本发明的目的在于提供一种用于建筑混凝土的高效低成本的防冻早强剂，可有效提高混凝土在冬季施工时的防冻，也可用于施工单位为缩短工期在混凝土中用作早强剂使用，在同等条件下可节省水泥3-4％。
本发明的目的由如下技术方案实施：建筑防冻早强剂，其包括有重量份的如下组份：无水氯化钙600-800份，粉煤灰200-400份，肌醇六磷酸酯5-15份，三乙醇胺10-30份，苯甲酸钠2-10份，苯骈三氮唑0.5-5份，加入一乙醇胺调节上述组合物的PH值为9-9.5，即制得建筑防冻早强剂。
一种建筑防冻早强剂的生产方法，将重量份为600-800份无水氯化钙，200-400份的粉煤灰，5-15份的肌醇六磷酸酯，10-30份的三乙醇胺，2-10份的苯甲酸钠，0.5-5份的苯骈三氮唑的上述组合物经混合搅拌均匀后，经破碎后，过60目～120目筛子筛分后，加入一乙醇胺，调节上述组合物的PH值为9-9.5，即制得建筑防冻早强剂。
本发明的优点在于：(1)、低成本、原材料易得、无毒无害，对使用的环境无污染。本发明产品可有效阻止氯离子对钢筋的腐蚀作用，从实验数据推算，钢筋混凝土可在80年内无损坏性的影响，本产品具有混凝土中防冻和早强的复合功能，可在零下25度气温下施工。可广泛用于建筑混凝土的防冻早强剂使用。解决了氯盐中氯离子对混凝土中钢筋的腐蚀难题，防冻早强剂的水溶液对碳钢的腐蚀率相当于普通自来水对碳素钢的腐蚀率，并且将防冻与早强功能集于一体，可节约水泥3-4％。(2)、在混凝土拌和物中掺加适量本产品与水泥发生各种物理化学反应，加快水泥的水化反应，从而明显提高混凝土的各龄期的抗压强度及抗渗，抗炭化、防冻等各项性能，(3)、在-5℃一-25℃平均气温下掺加2.5％的早强减水剂，可使混凝土R1-R7天抗压强度提高20-100％，抗折强度提高20-80％。使混凝土提高1/2、3/4时间达到设计强度，从而缩短工期。(4)、本产品对混凝土收缩，徐变均无不良影响，可改善混凝土的抗渗、防冻、抗炭化等性能，减水泌水性，改善施工和易性，在保证强度与坍落度的同时还能节约水泥用量。
具体实施方式
实施例1：建筑防冻早强剂包括无水氯化钙6000克，粉煤灰2000克，肌醇六磷酸酯50克，三乙醇胺100克，苯甲酸钠20克，苯骈三氮唑5克，上述组合物经混合搅拌均匀后，经破碎后，过60目筛子筛分后，加入一乙醇胺，调节上述组合物的PH值为9，即制得建筑防冻早强剂。
实施例2：建筑防冻早强剂包括无水氯化钙8000克，粉煤灰4000克，肌醇六磷酸酯150克，三乙醇胺300克，苯甲酸钠100克，苯骈三氮唑50克，上述组合物经混合搅拌均匀后，经破碎后，过120目筛子筛分后，加入一乙醇胺，调节上述组合物的PH值为9.5，即制得建筑防冻早强剂。
实施例3：建筑防冻早强剂包括无水氯化钙7000克，粉煤灰3000克，肌醇六磷酸酯100克，三乙醇胺200克，苯甲酸钠60克，苯骈三氮唑28克，上述组合物经混合搅拌均匀后，经破碎后，过90目筛子筛分后，加入一乙醇胺，调节上述组合物的PH值为9.2，即制得建筑防冻早强剂。
实施例4：使用方法
1、适用于日最低气温-5℃度以上需要早强、节约水泥的普通混凝土、钢筋混凝土及预应力蒸养混凝土等，对常用的硅酸盐水泥、普通水泥的掺量范围2-3％，减水率3-5％，节灰率2-4％。
2.常温下早强减水剂掺量范围2.0-3.0％，减水率8-12％，节灰率6-10％。早强、节约水泥，适用于10-20度需要早强现浇混凝土和预制构件。
3.缓凝早强减水剂--推荐掺量2.5％，掺量范围2.0-3.0％，减水率10-14％，节灰率8-12％。早强、缓凝、节约水泥，适用于20度以上高温，需要早强现浇混凝土和预制构件。
Claims (2)
1、建筑防冻早强剂，其特征在于：其包括有重量份的如下组份：
无水氯化钙 600-800份，
粉煤灰 200-400份，
肌醇六磷酸酯 5-15份，
三乙醇胺 10-30份，
苯甲酸钠 2-10份，
苯骈三氮唑 0.5-5份，
加入一乙醇胺调节上述组合物的PH值为9-9.5，即制得建筑防冻早强剂。
2、如权利要求1所述的一种建筑防冻早强剂的生产方法，其特征在于，将重量份为600-800份无水氯化钙，200-400份的粉煤灰，5-15份的肌醇六磷酸酯，10-30份的三乙醇胺，2-10份的苯甲酸钠，0.5-5份的苯骈三氮唑的上述组合物经混合搅拌均匀后，经破碎后，经过60目～120目筛子筛分后，加入一乙醇胺调节上述组合物的PH值为9-9.5，即制得建筑防冻早强剂。