CN100430328C - 颜色玻璃粉色着色剂及制备工艺 - Google Patents

颜色玻璃粉色着色剂及制备工艺 Download PDF

Info

Publication number
CN100430328C
CN100430328C CNB2004100235408A CN200410023540A CN100430328C CN 100430328 C CN100430328 C CN 100430328C CN B2004100235408 A CNB2004100235408 A CN B2004100235408A CN 200410023540 A CN200410023540 A CN 200410023540A CN 100430328 C CN100430328 C CN 100430328C
Authority
CN
China
Prior art keywords
coloring agent
pigment
fusing assistant
preparing
coloring
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2004100235408A
Other languages
English (en)
Other versions
CN1640836A (zh
Inventor
孙国庆
吴向松
苏文海
江小林
刘景柱
王国才
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dezhou Zhenhua Decoration Glass Co Ltd
Original Assignee
Dezhou Zhenhua Decoration Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dezhou Zhenhua Decoration Glass Co Ltd filed Critical Dezhou Zhenhua Decoration Glass Co Ltd
Priority to CNB2004100235408A priority Critical patent/CN100430328C/zh
Publication of CN1640836A publication Critical patent/CN1640836A/zh
Application granted granted Critical
Publication of CN100430328C publication Critical patent/CN100430328C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种颜色玻璃粉色着色剂及制备工艺。它采用铅硼配方，硒、镉着色且在配方中添加锌、铬、锂成分铬、铜着色，通过助熔剂配制，熔釉粉制备，色素配制，着色剂制备等工艺流程，获得颗粒状颜色玻璃粉色着色剂，采用该新型着色剂，产品质量稳定，克服了同类产品易出现色道、气泡的不足，使用方便，效果优于同类着色剂，生产成本大大降低，能替代进口产品。

Description

颜色玻璃粉色着色剂及制备工艺
技术领域
本发明涉及一种玻璃着色剂化合物及制备方法。
背景技术
20世纪60年代末，颜色玻璃开始在国外出现，我国于70年代开始研究，起初是在道中加入粉末状色素，色素熔化后经搅拌作用，使其与基础玻璃混合成均一的物质，经均化后成形，然而这种颜色玻璃只得到有限的推广。第一，在向玻璃液中加入着色剂时会产生许多困难，第二，对玻璃液进行二次加热有不良影响，主要问题是出现二次气泡。后使用美国进口颗粒状着色剂，该着色剂国外产品一般采用铬着色，虽有改进，但仍存在产品质量不稳定，极易出现色道、气泡、色块等缺陷，且产品进口，价格昂贵，急需替代产品。
发明内容
为了克服现有技术价格昂贵，产品质量不稳定，应用效果不理想，极易出现色道、气泡、色块等缺陷，本发明提供一种新的颜色玻璃着色剂及生产工艺。
本发明所提供的新的颜色玻璃粉色着色剂，采用铅硼配方，硒、镉着色，且在配方中添加锌、锂成分，其化学成分如下：SiO225-30％；AI2O34-6％；PbO30-40％；B2O35-8％；R2O15-25％；Se3-5％；CdS2-4％；ZnO8-12％。
上述的化合物可以通过如下的方法来制备。
(a)助熔剂的配制：助熔剂原料配比为：SiO230-35％；AI2O36-10％；CaO0.5-2％；MgO0.2-1％；PbO45-50％；B2O34-8％；K2O+Na2O10-15％。
(b)熔釉粉的制备：助熔剂按上述化学组成配料后在坩埚中加温1100-1200℃熔制，高温保温40-60min，经水淬，球磨、干燥、过筛得到熔釉粉。
(c)色素的配制，粉色剂采用硒、镉着色，其原料配方：亚硒酸钠30-40％；MnO10-15％；CdS15-20％；ZnO15-20％，Li2CO310-15％，B2O33-5％。将硼砂先溶于水中，其余原料混匀后粉料加入，拌匀烘干，球磨，过筛，得到色素
(d)着色剂的制备：将助熔剂与色素按2∶1比例混合后在坩埚中熔融，然后注入冷水中淬裂，干燥后破碎过筛，得粉色颗粒剂。
具体实施方式
下面结合实施例对本发明作进一步说明
本发明所指的颜色玻璃粉色着色剂的制备通过以下工艺方法实现。
一、助熔剂的配制
为了适应料道的作业温度及玻璃基础料的化学组成及化学性质。减少PbO，B2O3等原料的挥发量，助熔剂选用下列原料配比：SiO230-35％；AI2O36-10％；CaO0.5-2％；MgO0.2-1％；PbO45-50％；B2O34-8％；K2O+Na2O10-15％。
二、熔釉粉的制备
助熔剂按其上述配比组成配料后在坩埚中熔制成玻璃体，熔制温度为1180℃左右，最高温度保持50min，然后倒入水中进行水淬，水淬后的溶釉球磨28小时。干燥后过80日筛，得到釉粉。
三、色素的配制
粉色着色剂采用镍、硒系色剂，其色素原料配比：亚硒酸钠30-40％；MnO10-15％；CdS15-20％；ZnO15-20％，Li2CO310-15％，B2O33-5％。色素所用原料均采用化学纯原料，要求质量稳定，硼砂先溶于水中，将其余原料混匀后粉料加入、拌匀烘干，球磨25小时左右，过280目筛，得到色素。
四、着色剂的制备
将助熔剂与色素按2∶1比例混合后在坩埚内熔融，然后注入冷水中淬裂，干燥后破碎过4目，10目筛，中间颗粒即为颗粒状粉色着色剂，其主要化学成分：SiO225-30％；AI2O34-6％；PbO30-40％；B2O35-8％；R2O15-25％；Se3-5％；CdS2-4％；ZnO8-12％。

Claims (1)

1、一种颜色玻璃粉色着色剂的制备工艺，其特征在于这种制备工艺的步骤如下：
(a)助熔剂原料配比以百分重量计为SiO2 30-35％、Al2O3 6-10％、CaO0.5-2％、MgO 0.2-1％、PbO 45-50％、B2O3 4-8％、K2O+Na2O 10-15％；
(b)助熔剂的制备：将上述的助熔剂原料置于坩埚中，在1100-1200℃下加热40-60分钟，再经水淬、球磨、干燥、过筛得到所述的助熔剂；
(c)色素配制，色素原料配比以百分重量计为亚硒酸钠30-40％、MnO10-15％、CdS 15-20％、ZnO 15-20％、Li2CO3 10-15％、B2O3 3-5％；先将硼砂溶于水中，再加入混匀后的其余原料，拌匀烘干，球磨，过筛得到所述的色素；
(d)将上述的助熔剂与上述的色素按照重量比2∶1混合，再在坩埚中熔融，然后注入冷水中淬裂，干燥后破碎过筛得到所述的玻璃颜色粉色着色剂。
CNB2004100235408A 2004-01-17 2004-01-17 颜色玻璃粉色着色剂及制备工艺 Expired - Fee Related CN100430328C (zh)