CN100424308C - Ceramic plastic composite decorative material and making technique thereof - Google Patents
Ceramic plastic composite decorative material and making technique thereof Download PDFInfo
- Publication number
- CN100424308C CN100424308C CNB2005100183145A CN200510018314A CN100424308C CN 100424308 C CN100424308 C CN 100424308C CN B2005100183145 A CNB2005100183145 A CN B2005100183145A CN 200510018314 A CN200510018314 A CN 200510018314A CN 100424308 C CN100424308 C CN 100424308C
- Authority
- CN
- China
- Prior art keywords
- ceramic
- plastic
- ceramic panel
- strip
- panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a ceramoplastic compound decorative material which is characterized in that plastic framing strips are compounded and fixed at the near edges of the two symmetrical sides of the back of a rectangle ceramic panel; the plastic framing strips are formed into convex tenon sides towards one side of the edge of the rectangle ceramic panel; slot edges corresponding to the convex tenon sides for matching pressing strips are arranged on at least one side; ceramoplastic compounding is that the turnover back of the rectangle ceramic panel faces upward when the rectangle ceramic panel is removed out of a kiln after glost firing; panel temperature is dropped within 180 DEG C to 220 DEG C, and then, the plastic framing strips are placed on the rectangle ceramic panel to be lightly pressurized for 6 to 8 seconds, so the plastic framing strips and the back of the rectangle ceramic panel are hot fused. The present invention has the advantages of reasonable compound structure, novel method and no need of chemical mediators, such as binding agents, etc. The ceramic plastic compound decorative material is fundamentally physical distortion composition, so the ceramic plastic compound decorative material is reliable and is not easy to fall off. When in construction, the pressing strips are previously and horizontally fixed on a wall, and then, the rectangle ceramic panel is embedded between the two pressing strips to be fixed on the wall. When in construction, cement, etc. do not need to be used as pasting media, so the present invention has the characteristics of dry construction and rapid construction progress.
Description
Technical field:
The invention belongs to the architectural pottery field, particularly a kind of ceramic plastic composite decorative material.
Background technology:
Pottery is in the long history in existing several thousand of China, it has made very important contribution to human culture on the technological development history, ceramic process is as an applied science, knowhow and science and technology theory have extensively been compiled, various types of ceramic technologies constantly occur, its character, manufacturing process and purposes have nothing in common with each other, and roughly can divide: domestic ceramics, architectural pottery, sanitary ceramics, art ceramics and industrial ceramics etc.
The modern architecture pottery is developed under the promotion of the scientific and technological progress of making rapid progress rapidly, modern advanced industrial technology and technical equipment, realized the bright and colourful of architectural pottery product, stable quality and speed of production fast, architectural pottery is extended to outside the room within doors, as interior wall nogging, wood floor bolck etc., for the interior trim of building construction provides requisite material, it has clean, elegant in appearance, the easy cleaning of light, is difficult for adsorbing booty, high strength, corrosion-resistant, the good characteristic that quality is stable is subjected to people's favor deeply.As: be widely used in used by hotels and restaurants by, commerce and trade place, health care place, the humanity contacts place of public activity, the interior trim in entertainment leisure place; Be widely used in enterprise's factory building, the interior trim of work office service location building ... or the like.
Because the relation of visual effect, ceramic inner wall brick is generally rectangle structure, and the ceramic floor brick is generally square structure, and ceramic veneer has muffle painting on the surface, and the back side is pressed into has scrobicula burr reason.Must adopt cement slurry that it is pasted and fixed on metope or the ground during construction.This unalterable form of construction work in all age has no idea to change both at home and abroad.For example, the interior trim of house wall surface needs exper ienced technician's operation; During construction, need earlier bright and clean metope hacking, the fine adsorbed water material-mud of ability, and metope level and vertical plane drawn a design with fine rule, for last walltile is prepared, then that humidity is moderate cement slurry is uniformly coated on the ceramic veneer back side, then it is pasted on the wall, and beat with rubber and constantly to beat the brick face, make it meet setting-out plane and vertical standard.Because ceramic veneer starching amount is wanted manual operations, the Grace Person grasps by rule of thumb, need open heavily starching less so occur slurry often; Slurry then overflows for a long time all around, the brick face that pollution is completed and will cleaning again, utilize the absorption solidification adhesive material of cement as ceramic veneer, its construction is also influenced by ambient temperature, the north in winter is not suitable for construction, and not only freezing and can't constructing appears in cement paste easily, even walltile sticks, and be difficult for solidifying and parching, influenced the progress of construction.Therefore, traditional decoration process makes architectural pottery all multifactor incompatible with the socio-economic development situation, certainly will innovate on inheriting tradition, to adapt to the Times'Demand of new situations.
One of factor, modern architecture house property industry is risen rapidly, and people had pursued to have enough to eat and wear from the past and transformed pursuing the material amenities of life till now, pursued the level of comfort of doing of work living environment, because the emergence of architectural decoration has promoted the development in ornament materials market.And in all age extremely the architectural pottery of people favor become first-selected ornament materials naturally, building ceramic decoration technology just should be by inheriting and innovate the growth requirement that cater to market.
Two of factor, the development of modern architecture indoor decorative art has promoted the continuous appearance of various ornament materials, as the stainless steel ornament materials, wooden decorative material, decorative plastic material, organic chemistry ornament materials and various compound decorating material inlet chamber interior trims field.These ornament materials are with elegant in appearance, and decoration process is convenient, flexible, and efficient is characteristics efficiently, developed rapidly at decoration market, the influence of producing certain restriction for the development in architectural pottery market, thereby the innovation of building ceramic decoration technology on inheriting is imperative.
Three of factor, modern architecture artistic development, steel-wood structure house that novel building occurred and lightweight body of wall thereof, for with cement slurry as absorption, the ceramic veneer of settable cementitious material more can't relate to its application, and this also needs to seek new technology and solves.
Four of factor; modern health industry is risen, because the raising of people's living standard and the enhancing of health care consciousness, people's an urgent demand improvement work and home environment sanitary condition; improve the life health quality; various ceramic veneers antibiotic, that sterilize, preserve the ecological environment arise at the historic moment, and it can suppress the breeding of bacterium effectively, prevents various microbial growths; eliminate dirt; purifying the air of a room, be of value to and promote health, is a kind of green material.Speed develops and benefits the society but its application market is desired to seek quickness, still need to seek the decoration technique field that ceramic veneer is widened on a road that changes the new technology of complicated and loaded down with trivial details traditional decoration technology, thereby reach the purpose of widening domestic and international market application and development space, this just need be in the scientific and technical innovation on tradition is inherited.
Generally speaking, because social progress and economic development, make the traditional interior trim process efficiency of architectural pottery more and more incompatible with the development of modern production power, this just need rely on the new science and technology innovation, the road of development new technologies in inheriting tradition technology, enlarge the decoration process technical field, allow traditional architectural pottery grow with each passing hour, achieve more glorious results, this also is to give a duty-bound historical mission being engaged in architectural pottery industry people both at home and abroad.
Nowadays, in the epoch that science and technology is developed by leaps and bounds, ceramic materials, metal material and plastic material have constituted three big pillars of modern new material revolution.My invention thinking is the complex technique of research and development ceramic materials and plastic material, creates novel porous materials, makes ceramic veneer both have the good characteristics of ceramics, has plastics organic macromolecule premium properties again.Thereby realize breaking through traditional decoration process technology general layout, innovation and creation go out the decoration process new technology, walk out a new road, realize that inheriting tradition technology and technological innovation develop simultaneously, and widen building ceramic decoration technology field.For time-honored Chinese pottery wins honour for, new contribution is made in progressive and social development for nationality.
Summary of the invention:
The objective of the invention is to design a kind of new ceramics plastics composite material for decoration and manufacture craft thereof that need not cement as cementing agent.
Technical solution of the present invention is achieved in that a kind of ceramic plastic composite decorative material, at least proximal edge place, rectangular ceramic back side of panel symmetry both sides is compositely fixed with plastic framing strip respectively, it is characterized in that plastic framing strip becomes convex tenon limit towards ceramic panel edge one side, cooperate at least one side of press strip to be provided with the trough rim corresponding with the tenon limit.During construction, be horizontally fixed on press strip on the body of wall in advance, and it is in the same plane to adjust press strip, form a young interior big guide groove between the trough rim of two press strips, and the plastic framing strip tenon limit on the symmetry limit, the ceramic panel back side constitutes the mouth imperial palace little tenon corresponding with the press strip guide groove, the tenon that ceramic panel utilizes compound fixing plastic framing strip to form is embedded at and is fixed between two press strips on body of wall or the decoration frame, need not cement etc. during construction as paste medium.
The manufacture craft of described ceramic plastic composite decorative material, comprise that press strip moulding, plastic framing strip moulding, ceramic panel moulding and ceramoplastic are compound, it is characterized in that ceramoplastic is compound is meant the ceramic panel moulding and behind biscuiting, glaze firing kiln discharge ceramic panel is overturn the back side up, panel temperature is reduced between 180 ℃ to 220 ℃, plastic framing strip is placed on the ceramic panel back side, and slightly pressurizeed 6 to 8 seconds, make plastic framing strip and ceramic panel back side hot melt compound, after cooling off case after the finished product quality inspection.This hot melt composite construction is a preferred plan, need not chemical mediators such as cementing agent, is that physical deformation is structural compound substantially, the sound construction difficult drop-off.
It is unique that the present invention has design, reasonable in design, and the surplus temperature of the ceramic panel that makes full use of kiln discharge to carry out heat compound, need not to increase additional energy source and Chemical Felter, plastic framing strip and ceramic panel are compound firmly, utilize press strip that ceramic panel is fixed on body of wall or the ornament framework during construction, need not auxiliary material media such as cement, realize dry construction, and can be on the framework body of wall decoration construction, the limitation that breakthrough is constructed on traditional brick wall, and construction cost is low, the characteristics that programming is fast, break through the traditional job practices of domestic and international ceramic building material, can adapt on the framework of various bodies of wall or decoration and construct, decorate as external and internal wall according to the design needs, ground decoration and artistic decoration material all can, enlarge the applications in ceramics face.
Description of drawings:
The present invention will be further described below in conjunction with concrete legend:
Fig. 1 ceramic plastic composite decorative material one sectional view
Fig. 2 ceramic plastic composite decorative material two sectional views
Structure chart before Fig. 3 ceramic panel and plastic framing strip are compound
The structural representation at Fig. 4 ceramic panel back side and the press strip back side
Fig. 5 ceramic panel structure two schematic diagrames
Fig. 6 horizontal type construction and installation schematic diagram
Fig. 7 indulges formula construction and installation schematic diagram
The vertical formula steel wood of Fig. 8 construction and installation schematic diagram
Fig. 9 ground construction scheme of installation
Wherein
1-ceramic panel 11-holds recessed 2-plastic framing strip 21-tenon limit
22-inclined plane 23-projection 3-press strip 31-trough rim
32-inclined-plane 33-concave groove 34-hole for nailing 35-breach
The pre-buried timber 7-of 4-body of wall 5-setting-out line of ink marker 6-channel-section steel
8-lumps of wood bar
The specific embodiment:
With reference to Fig. 1, a kind of ceramic plastic composite decorative material, wherein proximal edge place, symmetry both sides, rectangular ceramic panel 1 back side is compositely fixed with plastic framing strip 2 respectively at least, plastic framing strip 2 becomes convex tenon limit 21 towards ceramic panel edge one side, cooperates press strip 3 at least one sides to be provided with the trough rim 31 corresponding with tenon limit 21.Plastic framing strip 2 tenon limits 21 and press strip 3 trough rims 31 are square shape among the figure.
With reference to Fig. 2, described plastic framing strip tenon limit 21 forms the inclined plane 22 that an angle is an acute angle with ceramic plate 1 back side, and press strip trough rim 31 is made the inclined-plane 32 corresponding with plastic framing strip inclined plane 22.Utilize two inclined-planes to cooperate and can play reliable location, the inclined-plane of plastic framing strip tenon limit 21 and press strip trough rim 31 cooperates processing to be more suitable for using on slim press strip and the plastic framing strip, is this programme optimal selection.
As Fig. 1 and Fig. 2, wherein said press strip 3 width are at least the twice of ceramic panel 1 edge to plastic framing strip 2 phase contact spacings, and dual-side forms the trough rim 31 of symmetry.Such press strip 3 can about or limit ceramic panel 1 up and down respectively, when press strip 3 width when being ceramic panel 1 edge to the twice of plastic framing strip 2 phase contact spacings, 1 one-tenth seamless laying of ceramic panel.
In addition, place, axis, press strip 3 bottom offers a concave groove 33, and hole for nailing 34 has been laid staggeredly in concave groove 33 both sides.The default of concave groove 33 can make press strip 3 be divided into two equally from the concave groove easily, in order to edge single face location ceramic panel, do not expose redundance, also can save some press strip materials certainly; Hole for nailing 34 is convenient to adopt nail that press strip is fixed on body of wall or is set on the ornament framework, and the hole for nailing 34 that is laid staggeredly can effectively avoid hole for nailing to exist and the intensity of reduction press strip.Nail is preferably selected wood screw for use, also can adopt iron nail, during ailhead can submerge press strip after squeezing into, does not expose the press strip plane, is beneficial to the installation ceramic panel.
With reference to Fig. 3, ceramic panel 1 back side is big in place, four angles of proximal edge offers at least young holds recessedly 11, convexes with and hold the suitable projection 23 of recessed 11 bores on the plastic framing strip 2, and projection 23 embeds and holds that hot melts are compound in recessed 11 fixes.Be interior big young structure owing to hold recessed 11, in case projection 23 hot melts are deformed into and hold concavity, promptly being held recessed 11 is limited in wherein difficult drop-off in the cooling back.
With reference to Fig. 4, plastic framing strip 2 can be compound in edge, ceramic panel 1 back side, is connected into a sealing framework, and finished product rectangular ceramic panel 1 can horizontal type or vertical random construction.Ceramic panel 1 holds recessed 11 except that four jiaos of proximal edge place is provided with among the figure, also can add at proximal edge place anyhow a plurality ofly to hold recessedly 11, increases spot, also avoids the defective of the no spot in ceramic panel 1 cutting back.Offer breach 35 on the press strip 3 both sides trough rims 31, the incision at any time of ceramic panel 1 when being convenient to construct need not only to save time from the incision of press strip end, does not also influence the reliability of chimeric location, and also can save the material of press strip.
With reference to Fig. 5, plastic framing strip 2 also can only be compounded on the both sides, ceramic panel 1 back side symmetry limit, has the effect of more saving plastic framing strip 2 materials, can reach the purpose same with last example again, but has limited horizontal type or vertical laying requirement when dispatching from the factory.
The manufacture craft of described ceramic plastic composite decorative material, comprise the press strip moulding, the plastic framing strip moulding, ceramic panel moulding and ceramoplastic are compound, wherein ceramoplastic is compound is meant the ceramic panel moulding and through biscuiting, behind the glaze firing kiln discharge ceramic panel is overturn the back side up, panel temperature is reduced between 180 ℃ to 220 ℃, reach the best melt temperature of plastics, plastic framing strip is placed the ceramic panel back side, recessed being pressed into of holding that makes the projection on the plastic framing strip aim at the ceramic panel back side, and slightly pressurizeed 6 to 8 seconds, make projection be heat-fused in the ceramic panel back side and hold recessed interior Cheng Chengzhuan, realize that plastic framing strip and ceramic panel back side hot melt are compound, after cooling off finished product, case after the quality inspection.Because surplus warm molten compound when utilizing ceramic panel glaze firing kiln discharge need not to increase energy consumption, is preferred plan of the present invention.
Press strip and plastic framing strip moulding are one-shot forming, for default hole for nailing and breach on press strip, need carry out opening to press strip, utilize tapping machine that the press strip section bar is carried out the opening of equidistant hole for nailing and breach, form standard product, are convenient to direct construction.Press strip can adopt metal or plastic material to make.
The above-mentioned rectangular ceramic panel that relates to does not singly refer to OBL ceramic panel, should comprise foursquare ceramic panel yet; Press strip can be the above strip of 3cm of drawing and forming, also can be injection molded into the billet shape isometric with ceramic panel; Plastic framing strip is good with list structure, is convenient to injection mo(u)lding, but also do not get rid of plastic framing strip directly is not connected into rectangular box-like one-shot forming, then it is compounded in mode and structure on the ceramic panel again; Ceramic panel and plastic framing strip compound, compound with hot melt is good, does not also get rid of complex forms such as adopting the colloid adhesion.Above non-creativeness distortion also should belong to the present invention and protect content.
Below the exhaustive division narration is done in product construction and installation of the present invention, further highlighted characteristics of the present invention.
The construction of metope horizontal type:
With reference to Fig. 6, the construction and installation schematic diagram, 2 need of this legend plastic framing strip are fixed with one at ceramic panel respectively about in the of 1 on the symmetrical limit, and press strip 3 adopts strip.Work progress: one, setting-out on metope 4 or decoration frame in advance, press strip 3 equidistantly is fixed on the same horizontal plane, can adopt wood screw to fix; Two, 3 of adjacent two press strips ceramic panel 1 is embedded, can ceramic panel be put into from the press strip two ends, trough rim breach 35 places that also the tenon limit of ceramic panel rear plastic moulding 2 can be aimed at press strip insert, and adjust it and get final product to the appropriate location; Three, ceramic panel can be slit into narrowlyer by tradition cutting way, fill a vacancy, need this moment it is bonded on the press strip by cementing agents such as glass cements in order to the edge; Four, in some ditch seams agent on by traditional form of construction work between the ceramic panel slit of completing, solidify the back complete, a seamless ceramic decoration metope.The traditional ceramics face brick can not be decorated as smallpox, and promptly there is not this defective in the present invention, gets final product according to same method construction.
This job practices is also not exclusive, if press strip also adopts plastics to make, during installation panel, can directly the tenon limit of ceramic panel one side be inserted in the press strip groove in advance, and opposite side firmly is pressed into, and utilizes both elastic deformations, also ceramic panel can be embedded.The characteristics that horizontal type is installed are the weight that each bar press strip supports row's ceramic panel, are distributed on the whole metope.
The construction and installation method is a fixedly press strip of elder generation, and ceramic panel is installed in the back.
The vertical formula construction of metope:
With reference to Fig. 7, rectangle ceramic veneer wall decoration construction and installation schematic diagram, this legend is combined into a sealing framework about ceramic panel 1 rear portion, be fixed with plastic framing strip 2 respectively on the bilateral symmetry limit after the linking, press strip 3 adopts the short press strip suitable with rectangular ceramic face brick length.
Work progress: one, setting-out in advance, according to the ceramic panel dimensions, draw a design on metope 4 with the line of ink marker 5, determine the horizon and the vertical line of institute's decorated wall surface part, hole for nailing according to vertical installation press strip 3 is in pre-buried timber 6 or directly that batten is fixing on the wall on the metope, convenient overwood screw press strip securely then; Two, vertically fix a press strip 3 in advance, the plastic framing strip 2 of ceramic panel one side is inserted, adjust the position and again another press strip 3 is fixed on ceramic panel opposite side plastic framing strip 2 it is fixedly clamped, and then continue to install ceramic panel more successively; Three, the ceramic panel cutting is filled a vacancy, and need insert fixing the getting final product of horizontal up and down press strip this moment by the tenon limit of the plastic framing strip on the symmetrical limit about the ceramic panel; Four, ditch meet the back complete, a seamless ceramic veneer decorated wall surface.
The construction and installation method is that a press strip, a ceramic veneer are installed one by one successively.This method also is fit to the horizontal type construction.
The steel-wood structure construction:
With reference to Fig. 8, metope is a carrier with the wooden frame, or is the ceramic veneer construction and installation schematic diagram of body of wall with the steel-wood structure, is applicable to the decoration of the building internal and external ornament of steel-wood structure or inner partition wall, half wall.The ceramic panel rear portion is fixed with a plastic framing strip respectively on the symmetrical up and down limit, is combined into a sealing framework after the linking, and wood materials adopts 3cm * 3cm lumps of wood bar 8, and steel material adopts angle steel or the channel-section steel 7 that is complementary with lumps of wood bar specification.
Work progress, one, on the steel body of wall by the equidistant fixing lumps of wood bar 8 or fixingly make framework of ceramic panel width or length by lumps of wood bar, and peace horizontal type or vertical formula construction requirement, laterally or vertically fixing ceiling molding 3; Two, according to installation panel mode after custom one press strip, one ceramic panel being installed or press strip being installed earlier, horizontal type or vertical formula are installed ceramic panel; Three, the ceramic panel cutting is filled a vacancy; Four, ditch seam back complete, a seamless ceramic veneer decorating wall.
This job practices also is applicable to the light material body of wall, as foamed concrete wall, light weight concrete construction wall, fiber water mud wall etc.
Ground construction:
With reference to Fig. 9, ground is to be the ceramic veneer construction and installation schematic diagram of carrier with the steel-wood structure framework, and steel framework can make ceramic veneer ground decoration effect solid, smooth, firm, and wood frame helps the construction and installation of ceramic veneer.This legend ceramic veneer is square specification, and the place is fixed with 1 plastic framing strip respectively in surrounding, ceramic panel rear portion, is combined into a sealing framework after the linking.
Work progress, one, adopt lumps of wood bar 8 and the angle steel bar that is complementary with it or 7 specifications of channel-section steel to make the steel-wood structure frameworks by ceramic veneer, and adjust it and be on the same horizontal plane; Two, center that can the ground framework is a starting point, the beginning construction and installation, then to around extend and install.On the batten axis, fix earlier a press strip, the trough rim of the plastic framing strip tenon limit of ceramic panel one side being aimed at press strip inserts then, adjust it after adapt to the position, another press strip trough rim being aimed at the plastic framing strip tenon limit on ceramic panel symmetry limit inserts, and overwood screw press strip, then respectively with the fixing plastic framing strip on another symmetrical limit, ceramic panel rear portion of 2 press strips, continue framework construction and installation all around earthward more successively, fixing and supporting role around each ceramic veneer all forms, it can bear bigger pressure; Three, the ceramic panel cutting is filled a vacancy; Four, ditch seam back complete, a seamless ceramic veneer decorative ground.
This method is equally applicable to the construction of cement floor, can directly fix pre-buried timber on cement floor or be fixed on the construction and installation carrier of rough ground as ceramic veneer.
Claims (7)
1. ceramic plastic composite decorative material, at least proximal edge place, rectangular ceramic back side of panel symmetry both sides is compositely fixed with plastic framing strip respectively, it is characterized in that plastic framing strip becomes convex tenon limit towards ceramic panel edge one side, cooperate at least one side of press strip to be provided with the trough rim corresponding with the tenon limit.
2. ceramic plastic composite decorative material according to claim 1 is characterized in that the plastic framing strip tenon limit and the ceramic plate back side form the inclined plane that an angle is an acute angle, and the press strip trough rim is made the inclined-plane corresponding with the plastic framing strip inclined plane.
3. ceramic plastic composite decorative material according to claim 1 is characterized in that place, axis, press strip bottom offers a concave groove, and hole for nailing has been laid staggeredly in concave groove both sides.
4. according to claim 1 or 3 described ceramic plastic composite decorative materials, it is characterized in that offering breach on the trough rim of press strip both sides.
5. according to the manufacture craft of the described ceramic plastic composite decorative material of claim 1, comprise that press strip moulding, plastic framing strip moulding, ceramic panel moulding and ceramoplastic are compound, it is characterized in that ceramoplastic is compound is meant the ceramic panel moulding and behind biscuiting, glaze firing kiln discharge ceramic panel is overturn the back side up, panel temperature is reduced between 180 ℃ to 220 ℃, plastic framing strip is placed on the ceramic panel back side, and pressurizeed 6 to 8 seconds, make plastic framing strip and ceramic panel back side hot melt compound, but after cooling off case after the finished product quality inspection.
6. the manufacture craft of ceramic plastic composite decorative material according to claim 5 is characterized in that compound recessed being pressed into of holding that is meant the aligning of the projection on the plastic framing strip ceramic panel back side of hot melt, and projection is heat-fused in the ceramic panel back side and holds recessed interior Cheng Chengzhuan.
7. the manufacture craft of ceramic plastic composite decorative material according to claim 5 is characterized in that press strip is carried out opening, utilizes tapping machine the press strip section bar to be carried out the opening of equidistant hole for nailing and breach.