CN100418714C - Fabricating method of decorative board and decorative board made by the same - Google Patents
Fabricating method of decorative board and decorative board made by the same Download PDFInfo
- Publication number
- CN100418714C CN100418714C CNB2004100710774A CN200410071077A CN100418714C CN 100418714 C CN100418714 C CN 100418714C CN B2004100710774 A CNB2004100710774 A CN B2004100710774A CN 200410071077 A CN200410071077 A CN 200410071077A CN 100418714 C CN100418714 C CN 100418714C
- Authority
- CN
- China
- Prior art keywords
- cardboard
- coating
- decorative panel
- resin
- furniture material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a method for manufacturing a decorative plate for a furniture material and a manufactured decorative plate used for the furniture material, wherein the decorative plate has the advantages of drug resistance, scrape resistance, wear resistance of a surface layer, and has the function of generating anion has affinity to the environment. A melamine series resin which is enforcedly soaked on the facade of a very thin paper plate, is used as thermosetting resin, and is used as a main agent. Then, the main agent is mixed with resin which is formed by mixing a silicon series demoulding agent and fluorine carbide series resin, and the mixture is dried for some time. Thus, coating layer resin solution which is mixed by titanium containing microparticles and tourmalinite according to the proportion of six to four is enforcedly soaked on the back side of the paper plate, and coating is carried out. Thus, the paper plate which is integral with the coating layer resin solution is obtained. Then, an adhesive layer is formed on the single side or both sides of the decorative plate. After the paper plate is adhered, the decorative plate used for the furniture material is obtained through hot pressing, punching and processing.
Description
Technical field
The present invention relates to have the furniture material that improves the surface physical property function manufacture method of decorative panel and the furniture material decorative panel of making according to the method, in more detail, the present invention relates to have resistance to chemical reagents, chemical resistance, scratch resistance, superficial layer abrasion performance, can produce with the furniture material of the affine ultrared function of anion of environment with the manufacture method of decorative panel and the furniture material decorative panel according to said method made, it is realized by following method: with steel rider resin forcibly is impregnated into quite light cardboard (35g/m for example
2～80g/m
2High light weight cardboard) the front, the front is coated with, described resin is to be host with a kind of thermosetting resin melamine series plastics, and be mixed with silicon series releasing agent, fluorine carbonization system resin forms; Make its accurate dry certain hour subsequently, to contain the titanium of particulate (for example 10000 orders) and supply to the another one steel rider with the coating resin liquid that the tourmaline that embodies the far infrared irradiation effect by the ejaculation anion mixes with 6: 4 ratio, the back side that makes above-mentioned cardboard is by this steel rider, forcibly the back side to above-mentioned cardboard is coated with, and obtains forming with described coating fluid the cardboard of an integral body; Form adhesive layer at the single or double of decorative panel thereafter, glue together above-mentioned cardboard after, carry out the hot pressing punch process, obtain the furniture material decorative panel.
Background technology
Fancy plywood (also claiming decorative panel) is meant that to increase decorative effect be purpose, surface at normal plywood, be pasted with thin multi-layer sheet, mainly be the normal plywood that is pasted with smooth lamina, also comprise the surface in recent years in its notion and be pasted with melmac or diaryl ester of phthalic acid resinous coat and cover paper, decorate or be printed on the glued board of decorating with the vinyl chloride resin film of pattern etc. with bristol paper.
Usually decorative panel known to or decoration are with enumerating the following thermoplastic resin decorative panel that obtains in the rubber cover plywood and decorating and use the rubber cover plywood, promptly printed patterns and painted on polyvinyl chloride resin film or polyester film is bonded in this film on glued board and the hardboard then.
Decorative panel uses under the situation of the ethene thin plate be printed on various patterns or decorative pattern and painted unlike material film etc., with the EVA thermoplastic adhesive rete and ply of paper is glued together, and in this coating carbamate coatings etc. above film, thereby obtains decorative panel.The advantage of the decorative panel that obtains like this is to have flexibility, processing freedom, but its problem is to lack case hardness, hear resistance and chemical proofing, it is problematic in that simultaneously: formed dope layer after bristol paper that will approach owing to colding pressing and membrane coat are joined together, to the water saturates phenomenon very a little less than, even soaking into of small amount of moisture just can make adhesive layer come off, and has the shortcoming that daylight etc. is easy to variable color.
In addition, except that described decorative panel, also can enumerate and utilize melmac, benzoguanamine resin, phenolic resins or unsaturated polyester resin etc. painted or be printed on the stencil paper of decorative pattern or fabric panel applies for several times, perhaps apply for several times with the copolymerization condensation product of these resins simultaneously, clad plate is solidified, by the thermosetting resin decorative sheet of this method manufacturing; After perhaps making the clad plate of equal therewith paper or fabric, this thin plate and base material are solidified into an integral body, the thermosetting resin decorative sheet that obtains by this method, cover decorative panel etc.
In above-mentioned thermosetting resin decorative sheet, use maximum and representational decorative panel is with melamine plate hot pressing, make its bonding LPM that obtains (low pressure melamine (Low PressureMelamine)).Describe the manufacturing process of described LPM simply, in the urea resin groove, the dapple paper of printing or the fabric panel of batching on roller applied exactly, in the melmac groove, apply again and make its drying, with 180 ℃ temperature and 20kg/cm
2Pressure, resulting product was promptly formed LPM in 40 seconds in the one side hot pressing of glued board.
Such LPM resembles and melamine plate etc. is carried out heat cure above-mentioned and handle and obtain, so the decorative panel that obtains thus can be brought into play the effect of hear resistance and chemical proofing aspect excellence, and the effect of aspect excellences such as mechanical-physical character such as case hardness, but goods price height, and there is the problem that lacks flexibility.
On the other hand, though the decorative panel made by melmac etc. is arranged, in its foaming process, when under optimum condition, solidifying, gloss, resistance to water, chemical proofing can make moderate progress, but further are cured, and can find the shortcoming that crack resistance reduces.
In addition, the problem as a class material of vinyl plate of producing as cheap material is, when decorative panel is bonded with described vinyl plate, has an awful dread of water, even a spot of water saturates just can make adhesive layer come off, and the phenomenon that vinyl plate breaks away from from decorative panel takes place.
So, in order to address the above problem, the application's applicant is according to the korean patent application of having filed an application in Korean Patent Room 10-2002-35355 number (furniture material is used with the manufacture method that covers decorative panel and according to the furniture material that the method is made and covered decorative panel), it is low but suitable case hardness and intensity are arranged to have proposed price comparison, prevented from the impact of outside or contacted easily scraping phenomenon of caused decorative panel surface, furniture is prolonged service life, at gloss, flexibility, light resistance, chemical proofing, the furniture material of crack resistance aspect excellence is with covering decorative panel.
But, to former decorative panel was self-evident, even described the application's decorative panel in first to file, because as thin as a wafer, gummed to each other is difficulty very, even if may glue together, the decorative panel that scribbles coating on the presspaper to the tolerance of water very a little less than, can not solve because of problems such as variable color such as daylight.
And, when on cardboard as thin as a wafer, carrying out the coating processing of resin of series such as melamine, the words that coating layer thickness is thin, coating result is not good, therefore have the surface strength of paper superficial layer, performances such as abrasion performance, scratch resistance, resistance to chemical reagents are low, can not be as the problem of goods use.
That is to say, for according to the cardboard of prior art at the one or both sides of decorative panel gummed, in order to reach described effect by coating processing, only make the thickness of cardboard reach certain value and can obtain such effect, because of buying cardboard expense rising etc., so the problem that has occurred making the production cost of goods to improve.
Summary of the invention
Carry out the present invention in order to solve aforesaid existing issue, its purpose is following content.Forcibly make resin impregnated, be coated to the quite thin 35g/m that is printed on multiple pattern or decorative pattern
2～80g/m
2Cardboard inside, described resin be with a kind of thermosetting resin melamine series plastics as host, and the releasing agent, the fluorine carbonization system resin that mix silicon series make.Then, the light and shade of plate surface shows on the described cardboard during because of gummed presspaper on high density compressed reinforcement wood etc., in order to prevent that cardboard from this variable color taking place, to contain titanium and tourmaline forcibly is soaked on the described cardboard with the mixed mixed resin liquid of certain charge ratio, even obtain will thin cardboard being glued at the surface of high density compressed reinforcement wood etc. whereby, also can obtain the effect of desired diamond plate.
Another object of the present invention be improve the surface strength of described cardboard, to mar proof, resistance to chemical reagents, the chemical resistance of scraping and prevent to soak into separating between the base plate that causes and cardboard because of moisture.
A further object of the invention provides and is produced by cardboard and have the anion of affinity naturally, and antibiotic, bacteria-eliminating efficacy is provided, and has the caused foreign flavor indoors of formaldehyde that contains in the raw material now, brings out harmful effects such as nauseating thereby remove.
To achieve the above object, the invention provides the furniture material manufacture method of decorative panel and the furniture material decorative panel of making by this method, described furniture material has following operation with being characterized as of manufacture method of decorative panel: the 1st coating treatment process (S1), be formed with on a plurality of the 1st concavo-convex steel riders to superficial layer and supply with thermosetting resin, make the cardboard that is printed on decorative pattern etc. by described the 1st steel rider, soak into described thermosetting resin with this front, form face-coating at described cardboard; The 1st drying process (S2) will pass through drying oven by the cardboard that described the 1st coating treatment process (S1) obtains, and make it accurate dry; The 2nd coating treatment process (S3), be formed with the coating resin liquid of supplying with the mixture that contains titanium and tourmaline on a plurality of concavo-convex the 2nd steel riders to the surface, and make cardboard pass through described the 2nd steel rider through described the 1st coating treatment process (S1) and described the 1st drying process (S2), form back coating at the back side of cardboard thus; The 2nd drying process (S4) makes the described cardboard through the 2nd coating treatment process (S3) pass through drying oven, makes it accurate dry; Accurate bonding process (S5) between base plate and the cardboard, contour at the such base plate of normal plywood or PB, MDF, HDF, in, the low-density compression one side or the two sides of strengthening the base plate that wood makes form adhesive layer, behind the stacked described cardboard, make it pass through roller thereon, carry out the standard gummed; Hot pressing punch process operation (S6) is carried out the hot pressing punch process with the hot pressing stamping machine to described base plate and cardboard through described accurate bonding process.
According to the present invention described above, front at as thin as a wafer cardboard, forcibly carrying out a kind of thermosetting resin melamine is the 1st coating processing of resin, carry out accurate drying then the 1st time, described melamine is releasing agent and fluorine carbonization system resin and the tourmaline that has mixed silicon series in the resin with certain mixing ratio; At the back side of described cardboard, forcibly carry out the 2nd coating of the coating resin liquid formed by titanium and tourmaline and handle, carry out then the 2nd time accurate dry; The described cardboard of accurate bonding on the single or double of strengthening the wooden base plate that forms by normal plywood or high compression; Then,, the decorative panel of quite thin cardboard can be obtained being bonded with,, the effect of producing cost can be sought to reduce on the whole so can considerably reduce the supply price of the high cardboard of the price that is printed on flower-pattern layer through the hot pressing punch process.
In addition, for the existing decorative panel that uses millboard, overcome separating and the frequent generation of the phenomenon such as come off of the flower-pattern layer of cardboard of cardboard and base plate, by front at as thin as a wafer cardboard, the back side applies-drying-coating-flow charts such as drying, resin liquid is soaked into fully and overlayed on the cardboard is conspicuous, when between cardboard and base plate, gluing together, by high pressure-temperature etc., prevented the phenomenon of peeling off that produces between flower-pattern layer and the cardboard fully, the furniture made from this decorative panel, even long-time the use also can prevent between cardboard and base plate to soak into the segregation phenomenon that causes and the metachromatism of cardboard etc. because of moisture fully.
In addition, handle by containing the high and coating that have an affine naturally tourmaline of far infrared irradiation effect of a certain amount of anion emission efficiency, anion that radiates with decorative panel from furniture and far-infrared engergy promote the harmful toxins substance decomposition in the human body, enhanced metabolism, the effect of fatigue recovery, indoor antibiotic, degerming, and the harmful formaldehyde that produced from timber in the past is by being removed fully with the chemical reaction of described tourmaline, thereby fundamentally cured the side effect of formaldehyde to producing in the human body.
Description of drawings
Fig. 1 is the flow chart of expression process sequence of the present invention.
Fig. 2 is the sectional view that the front that is illustrated in cardboard as thin as a wafer is formed with the state of flower-pattern layer.
To be expression carry out that the 1st coating handled and the simple sectional view that forms the 1st coating treatment process of face-coating to the front of described cardboard to Fig. 3.
Fig. 4 is the 1st time dry drying process of drying oven standard passed through in expression through the cardboard of described the 1st coating processing a simple sectional view.
Fig. 5 is that the back side that is illustrated in the cardboard 10 of the described drying oven of process applies the coating resin liquid that is mixed with certain proportion by titanium and tourmaline, forms the simple sectional view of the 2nd coating treatment process of back coating.
Fig. 6 is that the cardboard that described the 2nd coating of expression process handled passes through the further simple sectional view of the 2nd drying process of accurate drying of drying oven.
To be expression be glued at operation on the sheet material, the i.e. simple sectional drawing of base plate and the accurate bonding process of cardboard through the cardboard of described the 2nd drying process by the adhesive layer standard to Fig. 7.
Fig. 8 is illustrated in through carrying out the sketch of the operation of hot pressing punch process on the base plate of described accurate bonding process.
Fig. 9 is that expression is through described hot pressing punch process operation and the sectional view of the decorative panel that obtains.
Symbol description
10 cardboards
11 flower-pattern layers
12 face-coatings
13 back coatings
20 the 1st steel riders
21 is concavo-convex
30 drying ovens
40 the 2nd steel riders
41 is concavo-convex
50 base plates
51 adhesive layers
60 rollers
70 hot pressing stamping machines
The specific embodiment
Below, describe the preferred embodiment of the invention in detail based on accompanying drawing.
Among the present invention, the cardboard as thin as a wafer that makes one side be printed on multiple decorative pattern or pattern etc. is formed with a plurality of the 1st, the 2nd concavo-convex steel riders by the surface, make the resin liquid of supplying with from steel rider respectively forcibly soak into, be coated on the described cardboard, stick with glue then agent etc. with its be glued at normal plywood base plate, PB, MDF, HDF contour, in, the low-density compression single face or the two sides of strengthening the base plate that wood forms, carry out the hot pressing punch process, obtain decorative panel.
Fig. 1 is an expression process flow chart of the present invention.Below, based on Fig. 1 operation of the present invention is described.
(the 1st operation-the 1st time coating treatment process: S1)
At first, to strengthen attachment glue on the base plate 50 that wood makes and play the effect of decorative panel in order to finish in the compression of base plate such as normal plywood or described such high, medium and low density, is 30～80g/m of 30～80g every square metre of suitable weight of area
2The flower-pattern layer 11 (with reference to Fig. 2) that is used for showing various decorative patterns or pattern is printed in the front of cardboard 10 as thin as a wafer.
In the one side of the presspaper 10 that forms flower-pattern layer 11 as described like that, promptly form the one side of described flower-pattern layer 11, apply a kind of thermosetting resin melamine series plastics.At this moment, to sneak into the melamine series plastics that 2 weight %～3 weight % obtain as the tourmaline powder of hexagonal crystal system mineral as the silicon of the polymer of silicon organic derivative series releasing agent, 5 weight %～6 weight % fluorine carbide series plastics, 8 weight %～10 weight % for described melamine series plastics, be coated in the front of described cardboard 10, just be printed on the front of flower-pattern layer 11.
Sneaking into described silicon series releasing agent is in order to add man-hour good stripping result to be arranged; Sneak into described fluorine carbide series plastics and be in order to improve surface strength, suppressing printed layers is coming off of flower-pattern layer 11; Sneak into described tourmaline and be for produce the anion affine with environment facies, because of the far infrared irradiation effect to playing of human body enhance metabolism, fatigue recovery, improvement circulation etc.
In order to make cardboard successfully soak into described melamine series plastics and the surface to be applied, as shown in Figure 3, supply with the melamine series plastics of described mixing constantly to the 1st steel rider 20 that has formed a plurality of concavo-convex or protruding 21 through the processing of net pressure and on the surface, make described cardboard 10 by described the 1st steel rider 20, thereby make the front of described cardboard 10 soak into melamine series plastics (with reference to Fig. 3) fully.
At this moment, apply the effect maximization, preferably make cardboard 10 by described the 1st steel rider 20 twice in order to make.
Make cardboard 10 twice the 1st steel rider 20 like this, can guarantee that the coating rate that concavo-convex or protruding 21 pairs of cardboards 10 apply reaches 60%～70% by pressing processing to form through net.
On the other hand, in order to improve the coating rate of resin, described the 1st steel rider 20 concavo-convex or protruding 21 between the narrow more coating effect in interval good more.So, in operating process, be necessary to adjust under the situation of coating rate, as previously mentioned, prepare in advance to form concavo-convex or protruding 21 multiple the 1st steel rider 20 with various different interval, adjust coating rate by changing the 1st steel rider.
(the 2nd operation-the 1st time drying process; S2)
This operation is that the cardboard of handling through described the 1st coating treatment process (S1) 10 is carried out accurate dry operation the 1st time, wherein, making described cardboard 10 is 80～100 ℃ drying oven 30 by internal temperature, makes cardboard 10 dryings of handling through described the 1st coating treatment process 80%～85% (with reference to Fig. 4) with this.
Carrying out accurate dry reason like this is, in the 2nd processing of back processing cardboard 10 in addition when Gao Re and high pressure, has been suppressed to produce bubble because of the resin boiling, can not completely crued problem when being used for remedying super-dry.
(the 3rd operation-the 2nd time coating treatment process; S3)
This operation is that the cardboard 10 through the accurate drying regime of described the 1st drying process (S2) is carried out the operation that the 2nd coating handled, wherein, handle by coating, make the back side of cardboard 10 forcibly soak into the coating resin liquid of the mixture that contains titanium and tourmaline, conscientiously prevent variable color of cardboard 10 etc. with this, described variable color is meant when extremely thin cardboard 10 is glued together with the one side of compressing sheet materials such as strengthening wood or base plate 50, the surperficial intrinsic decorative patterns of base plate 50 etc. see through cardboard 10 and manifest, and produce the variable color of cardboard 10.
In order to make the resin that obtains be used for cardboard 10 is carried out giving cardboard these characteristics when the 2nd coating handled, combined silver white metal titanium of the present invention and on the effect that produces anion, emitting far infrared ray excellent and mineral matter tourmaline that belong to hexagonal crystal system obtain coating resin liquid, wherein, pure titanium is used as the material of corrosion resistance container because of having the ductility, heating can forging, intensity and corrosion resistance is strong and the structure materials such as aircraft, boats and ships that are used as in light weight in the chemical industry.That is to say, the titanium of particulate (for example 10000 orders) and tourmaline are sneaked into 6: 4 ratio and obtain coating resin liquid.
To the 2nd steel rider 40 of same structure being arranged with described the 1st steel rider 20, supply with the coated with resins liquid that as above obtains like that constantly, make described cardboard 10 by described the 2nd steel rider 40, carry out coating whereby and handle, so that the described coating resin liquid of the mixture that contains titanium and tourmaline is forcibly soaked at the back side of described cardboard 10.
At this moment, identical in order to improve coating effect with described the 1st coating treatment process (S1) to cardboard 10 back sides, make cardboard 10 twice by described the 2nd steel rider 40 (with reference to Fig. 5).
(the 4th operation-the 2nd time drying process; S4)
This operation is to make the cardboard 10 that mechanically soaks into and be coated with the coating resin liquid of the mixture that contains titanium and tourmaline through described the 2nd coating treatment process (S3), by the internal temperature with condition identical with described the 1st drying process (S2) is 80～100 ℃ drying oven 30, and accurate dry operation.
At this moment, identical with described the 1st drying process (S2), in accurate bonding process described later (S5) and hot pressing punch process operation (S6), in order to prevent that high thermal high from making the resin boiling produce bubble, or can not completely crued phenomenon because of super-dry, the index of aridity of preferred cardboard is 80%～85% (with reference to Fig. 6).
(the bonding process of the 5th operation-base plate and cardboard; S5)
(S1～S4) is the manufacture process that is illustrated in the cardboard 10 that the high density compressed one side of strengthening base plate 50 wood or normal plywood adheres to described operation, and this operation is to be used for and will to be glued on the single or double of described base plate 50 through cardboard 10 standards that above-mentioned operation is produced, and makes the adhesive layer 51 that forms by adhesive coating between its middle operation.
In view of the characteristic of furniture material, even the preferred long-time use of used adhesive still keeps good gummed power, resistance to water, hear resistance, cold resistance etc. in this operation.In order to have above such characteristic, preferably use urea resin series adhesive as thermosetting resin series.
Except that described adhesive, using and being mixed with titanium is that the adhesive of filler also can glue together at base plate 50 and 10 of cardboards.In this case, when described adhesive glue was bonded on the cardboard 10, adhesive soaked into when imbedding the micropore of tissue of cardboard 10, so can show the good texture of decorative panel at the superficial layer of cardboard 10.
So, at first block PB, the HDF, the MDF that become certain-length or width state with severing contour, in, low-density compression strengthens the single or double of timber apron or normal plywood base plate 50, applying implenent has the adhesive of described characteristic, form adhesive layer 51, at the cardboard 10 that upper layer prestack one operation of this adhesive layer 51 obtains, carry out the standard gummed.
Thereafter, make described base plate 50 by having proper temperature and pressure, promptly temperature is that 80～100 ℃, pressure are 20～25kg/cm
2Roller 60, finish the accurate bonding process (with reference to Fig. 7) between base plate 50 and the cardboard 10.
(the 6th operation-hot pressing stamping procedure; S6)
This operation is by the base plate 50 behind the accurate bonding process (S5) between described base plate and the described cardboard is carried out the hot pressing punch process, thereby obtains the operation of the decorative panel of completion status, wherein, described base plate 50 is dropped into maintain 10～13kg/cm
2Pressure and the hot pressing stamping machine of 170～200 ℃ temperature in, approximately carry out 50～85 seconds hot pressing punch process (with reference to Fig. 8).
Through such hot pressing punch process, finished the gummed between adhesive and the cardboard 10, good resistance to water and gummed power have been given, the adhesive of adhesive layer 51 solidifies when soaking between the micro organization of cardboard 10, through described 2 accurate drying processes, even also prevented the coming off of flower-pattern layer 11 of cardboard 10 fully in the hot pressing punching course, perhaps the resin bed of handling through coating is the phenomenon that starting appears in the coating 12,13 of front and back.
Further dry by 80%～85% standard, even in having the hot pressing punching course of quite high pressure and temperature, prevented fully that also the resin boiling from producing bubble or super-dry causes the incomplete phenomenon of curing, eliminated fully that the cardboard 10 that occurs separates, surface strength is low in existing goods, water saturates causes the situation such as separate between base plate 50 and the cardboard 10, obtained the decorative panel of that glue together fully and beauty that formed by coating between base plate 50 and the cardboard 10.
Claims (7)
1. furniture material is characterized in that it has following operation with the manufacture method of decorative panel:
The 1st coating treatment process (S1), be formed with on a plurality of the 1st concavo-convex steel riders to superficial layer and supply with thermosetting resin, make the cardboard that is printed on decorative pattern by described the 1st steel rider, soak into described thermosetting resin with this front at described cardboard, form face-coating, in the described thermosetting resin, the releasing agent of silicon series accounts for 2 weight %～3 weight %, the resin of fluorine carbide series accounts for 5 weight %～6 weight %, and tourmaline accounts for 8 weight %～10 weight %;
The 1st drying process (S2) will pass through drying oven by the cardboard that described the 1st coating treatment process (S1) obtains, and make it accurate dry;
The 2nd coating treatment process (S3), be formed with the coating resin liquid of supplying with the mixture that contains titanium and tourmaline on a plurality of concavo-convex the 2nd steel riders to the surface, and make cardboard pass through described the 2nd steel rider through described the 1st coating treatment process (S1) and the 1st drying process (S2), form back coating at the back side of cardboard thus, described coating resin liquid contains the titanium and the tourmaline of the 10000 order particles that mix with 6: 4 ratio;
The 2nd drying process (S4) makes the described cardboard through the 2nd coating treatment process (S3) pass through drying oven, makes it accurate dry;
Accurate bonding process (S5) between base plate and the cardboard forms adhesive layer on the one side or the two sides of normal plywood base plate or the wooden base plate of making of high, medium and low density compression reinforcement, behind the stacked in the above described cardboard, makes it pass through roller, carries out the standard gummed;
Hot pressing punching press processing operation (S6) is carried out the hot pressing punch process with the hot pressing stamping machine to described base plate and cardboard through described accurate bonding process, and wherein the temperature of hot pressing stamping machine is 170～200 ℃, and pressure is 10～13kg/cm
2, processed 50～85 seconds.
2. furniture material as claimed in claim 1 is characterized in that with the manufacture method of decorative panel described thermosetting resin is the resin of melamine series.
3. furniture material as claimed in claim 1 is characterized in that with the manufacture method of decorative panel described cardboard is 30～80g/m
2Cardboard.
4. furniture material as claimed in claim 1 is characterized in that with the manufacture method of decorative panel described drying oven maintains 80～100 ℃.
5. furniture material as claimed in claim 1 is characterized in that with the manufacture method of decorative panel in the accurate bonding process (S5) of described base plate and cardboard, the temperature of roller is 80～100 ℃, and pressure is 20～25kg/cm
2
6. furniture material as claimed in claim 1 is characterized in that with the manufacture method of decorative panel the superficial layer of described the 1st, the 2nd steel rider is applied by the grid roller.
7. the furniture material as claimed in claim 1 manufacture method of decorative panel, it is characterized in that, in described the 1st coating treatment process and described the 2nd the coating treatment process, the cardboard after last processing passes through described the 1st steel rider and the 2nd steel rider each 2 times respectively, carries out coating and handles.