CN100415843C - 一种纸板淀粉胶活性剂及纸板淀粉胶 - Google Patents
一种纸板淀粉胶活性剂及纸板淀粉胶 Download PDFInfo
- Publication number
- CN100415843C CN100415843C CNB2007101107877A CN200710110787A CN100415843C CN 100415843 C CN100415843 C CN 100415843C CN B2007101107877 A CNB2007101107877 A CN B2007101107877A CN 200710110787 A CN200710110787 A CN 200710110787A CN 100415843 C CN100415843 C CN 100415843C
- Authority
- CN
- China
- Prior art keywords
- cardboard
- starch gum
- promoting agent
- cardboard starch
- activating agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种纸板淀粉胶活性剂及纸板淀粉胶，其特征在于，所述的活性剂包括以下重量百分比的物质：海泡石粉65-75%、轻钙粉10-20%、砂浆增塑剂1-5%、羧甲基纤维素纳3-6%、白砂糖1-5%。所述的淀粉胶中该活性剂的含量为1-6%。采用本发明活性剂制得的淀粉胶无毒无害，不易出现水胶分离的现象，且该淀粉胶粘合能力强，制造工艺简单，产品品质稳定，污染小，粘合得到的纸板抗压力大，车速快，耐戳穿力强。
Description
技术领域
本发明涉及一种粘合剂的活性剂及采用该活性剂的粘合剂，具体的说，本发明涉及一种纸板淀粉胶活性剂及纸板淀粉胶。
背景技术
当前，对于纸板的粘合多采用淀粉胶，如瓦楞纸板、蜂窝纸板的生产中均大多使用的淀粉粘接胶。但由于此种粘合剂粘结力弱，抗压性、防潮能力差，因此生产出的产品质量得不到保证。于是现有技术中出现了向该淀粉胶中添加其他成分来改善其性能的方法。
然而，此类添加成分中往往含有对人体有刺激性的成分，容易出现水胶分离沉淀的现象，既造成浪费，又严重影响了粘接力。有的则需要机械粉碎或二次制胶，既复杂，又增加了工时、污染，产品也难以稳定。
发明内容
因此，本发明的目的在于提供一种纸板淀粉胶活性剂及纸板淀粉胶，该活性剂无毒无害，制得的纸板淀粉胶粘合性能强、不易出现水胶分离，且制作简单。
为了实现本发明的目的，提供一种纸板淀粉胶活性剂，其特征在于，所述的活性剂包括以下重量百分比的物质：
海泡石粉65-75％、轻钙粉10-20％、砂浆增塑剂1-5％、羧甲基纤维素钠3-6％、白砂糖1-5％。其中砂浆增塑剂为市面上可以购买到的任何砂浆增塑剂，如梨树园新型建筑材料厂生产的″固创″牌WF型砂浆剂。
更优选的，所述的活性剂包括以下重量百分比的物质：
海泡石粉68-72％、轻钙粉15-20％、砂浆增塑剂2-4％、羧甲基纤维素钠4-5％、白砂糖1.5-4％。
本发明使用市面上出售的海泡石粉末，其中海泡石成分一般占40-85％，优选海泡石成分的重量大于80％的海泡石粉末。
本发明的海泡石粉与所述的轻钙粉的粒度可使用常见的200目以上的粉末，优选均为800-1200目。
本发明所述的砂浆增塑剂更优选为其成分中包含萘磺酸盐甲醛缩合物或蜜胺树脂或脂肪族磺酸盐中的一种砂浆增塑剂，能达到更高效的减水效果。
为了实现本发明的目的，提供一种纸板淀粉胶，其特征在于，所述的纸板淀粉胶加入本发明所述的纸板淀粉胶活性剂后搅拌均匀，该活性剂的加入量为该纸板淀粉胶重量的1-6％
本发明的有益效果在于：采用本发明的成分以及配比的纸板淀粉胶活性剂制得的淀粉胶无毒无害，不易出现水胶分离的现象，而且该淀粉胶的粘合能力强，制造工艺简单，产品品质稳定，车速快，粘合得到的纸板抗压力大，耐戳穿力强。
具体实施方式
实施例1
本实施例的活性剂是将以下重量百分比的物质均匀混合而成：
海泡石粉70％，其中海泡石含量为85％，粒度为800目；
轻钙粉20％，粒度为1200目；
砂浆增塑剂2.5％，梨树园新型建筑材料厂生产的″固创″牌WF型砂浆剂；
羧甲基纤维素钠5％，工业级；
白砂糖2.5％，民用级；
将上述成分均匀混合后即得到本实施例的活性剂。再将其加入到市售的普通纸板淀粉胶中搅拌均匀即可，活性剂的加入量为淀粉胶重量的1％。
实施例2
本实施例的活性剂是将以下重量百分比的物质均匀混合而成：
海泡石粉75％，其中海泡石含量为70％，粒度为1200目；
轻钙粉10％，粒度为1000目；
砂浆增塑剂5％，为含萘磺酸钠甲醛缩合物的砂浆增塑剂；
羧甲基纤维素钠6％，工业级；
白砂糖1％，民用级；
粉煤灰3％；
将上述成分均匀混合后即得到本实施例的活性剂。再将其加入到市售的普通纸板淀粉胶中搅拌均匀即可，活性剂的加入量为淀粉胶重量的3％。
实施例3
本实施例的活性剂是将以下重量百分比的物质均匀混合而成：
海泡石粉65％，其中海泡石含量为78％，粒度为1000目；
轻钙粉15％，粒度为800目；
砂浆增塑剂1％，为含十二烷基磺酸钠的砂浆增塑剂；
羧甲基纤维素钠3％，工业级；
白砂糖5％，民用级；
膨润土11％；
将上述成分均匀混合后即得到本实施例的活性剂。再将其加入到市售的普通纸板淀粉胶中搅拌均匀即可，活性剂的加入量为淀粉胶重量的6％。
Claims (6)
1. 一种纸板淀粉胶活性剂，其特征在于，所述的活性剂包括以下重量百分比的物质：
海泡石粉65-75％、轻钙粉10-20％、砂浆增塑剂1-5％、羧甲基纤维素钠3-6％、白砂糖1-5％。
2. 根据权利要求1所述的纸板淀粉胶活性剂，其特征在于，所述的活性剂包括以下重量百分比的物质：
海泡石粉68-72％、轻钙粉15-20％、砂浆增塑剂2-4％、羧甲基纤维素钠4-5％、白砂糖1.5-4％。
3. 根据权利要求1或2所述的纸板淀粉胶活性剂，其特征在于，所述的海泡石粉中海泡石成分的重量大于80％。
4. 根据权利要求1或2所述的纸板淀粉胶活性剂，其特征在于，所述的海泡石粉与所述的轻钙粉的粒度均为800-1200目。
5. 根据权利要求1或2所述的纸板淀粉胶活性剂，其特征在于，所述的砂浆增塑剂的成分中包含萘磺酸盐甲醛缩合物或蜜胺树脂或脂肪族磺酸盐中的一种。
6. 一种纸板淀粉胶，其特征在于，所述的纸板淀粉胶加入如权利要求1或2所述的纸板淀粉胶活性剂后搅拌均匀，该活性剂的加入量为该纸板淀粉胶重量的1-6％。