CN100404519C - Process for preparation of alicyclic diepoxy compounds, curable epoxy resin compositions, epoxy resin compositions for the encapsulation of electronic components, stabilizers for electrical insulating - Google Patents

Process for preparation of alicyclic diepoxy compounds, curable epoxy resin compositions, epoxy resin compositions for the encapsulation of electronic components, stabilizers for electrical insulating Download PDF

Info

Publication number
CN100404519C
CN100404519C CNB038189496A CN03818949A CN100404519C CN 100404519 C CN100404519 C CN 100404519C CN B038189496 A CNB038189496 A CN B038189496A CN 03818949 A CN03818949 A CN 03818949A CN 100404519 C CN100404519 C CN 100404519C
Authority
CN
China
Prior art keywords
composition
epoxy
weight
epoxy resin
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CNB038189496A
Other languages
Chinese (zh)
Other versions
CN1688561A (en
Inventor
前嵨尚
高井英行
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Daicel Corp
Original Assignee
Daicel Chemical Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Daicel Chemical Industries Ltd filed Critical Daicel Chemical Industries Ltd
Publication of CN1688561A publication Critical patent/CN1688561A/en
Application granted granted Critical
Publication of CN100404519C publication Critical patent/CN100404519C/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Epoxy resin compositions represented by the general formula (I) or (II), products of curing of the compositions, and a process for the preparation of the epoxy compounds through epoxidation with an organic percarboxylic acid: (I) (II) wherein R<1> to R<18> are each independently hydrogen, halogeno, a hydrocarbon group which may contain oxygen or halogen, or optionally substituted alkoxy.

Description

The manufacture method of alicyclic diepoxy compound, curable epoxy resin composition, electronic part encapsulation composition epoxy resin, electrical isolation stabilizers and electrical isolation casting composition epoxy resin
Technical field
The present invention relates to a kind of manufacture method of alicyclic diepoxy compound, its be by have the dicyclohexyl of containing-3,3 '-compound and the organic percarboxylic acids reaction of the unsaturated group of diene skeleton make.And the present invention also relates to curable resin composition and the cured article thereof of this di-epoxy compounds as neccessary composition.This resin combination uses in each side purposes such as coating, printing ink, tackiness agent, seal gum, sealing material.And, the present invention relates to the excellent moisture resistance of this alicyclic diepoxy compound, and have the composition epoxy resin that the electronic part encapsulations such as semi-conductor of high workability are used as neccessary composition.And the present invention also relates to electrical isolation stabilizers and electric insulation oil.In more detail, the long-time stability that constitutes by this alicyclic diepoxy compound electrical isolation stabilizers and the electric insulation oil that obtain improveing.Moreover, the present invention also relate to the composition epoxy resin that contains this alicyclic diepoxy compound and inanimate matter packing material etc. as the good electrical isolation of low viscosity, the operation of neccessary composition with casting composition epoxy resin and cured article thereof.
Background technology
Contain the multi-functional epoxy compound (below be called Resins, epoxy) of 2 above alicyclic ring skeletons at intramolecularly, existing now extensive stock is in market sale.For example, 3,4-cyclohexyl methyl-3 ', 4 '-epoxy hexamethylene carboxylicesters is (for example, the ERL4221 that セ ロ キ サ イ De 2021 that ダ イ セ Le chemical industry is made and associating carbide of calcium company make etc.), 1,2,8,9-diepoxy limonene (for example, ダ イ セ Le chemical industry system セ ロ キ サ イ De 3000), Te Kaiping 4-36263 communique and special opening on the two ends of disclosed 6-caprolactone oligopolymer in the flat 4-170411 communique have 3 respectively, 4-epoxycyclohexyl methyl alcohol and 3, the ester bond product of 4-epoxy cyclohexane carboxylic (for example, ダ イ セ Le chemical industry system セ ロ キ サ イ De 2081) or two (3,4-epoxycyclohexyl methyl) adipic acid ester (for example, associating carbide of calcium corporate system ERL4299 etc.) etc.And, Te Kaiping 4-69360 communique and spy open the disclosed epoxidation 3-of flat 4-170411 communique tetrahydrobenzene-1, two 3-cyclohexenyl methyl esters of 2-dicarboxylic acid and 6-caprolactone affixture (ダ イ セ Le chemical industry system GT300 series such as " エ Port リ one De GT301 ") thereof, and the existing commodity of the solidified nature epoxy compounds of epoxidation BTCA four-3-cyclohexenyl methyl esters and a plurality of alicyclic epoxy bases of 6-caprolactone affixture (ダ イ セ Le chemical industry system エ Port リ one De GT400 series such as " GT401 ") thereof.This polyfunctional epoxy compounds can be by obtaining cured article with various solidifying agent and curing catalysts reaction.This epoxy resin cured product has as the thermotolerance, the transparency of the resin feature of the compound that contains the alicyclic ring skeleton, good dielectric characteristics, this epoxy compounds can be used as the composition of various coating, tackiness agent, printing ink, seal gum, and the composition of the intermediate product of the end-use of conduct manufacturing medicine and medical treatment product.
Contain methyl because セ ロ キ サ イ De 3000 constitutes on the carbon atom of its epoxy group(ing), so, because of its steric barrier reactive low.And, セ ロ キ サ イ De 2021, セ ロ キ サ イ De 2081, ERL4299, owing to intramolecularly have ester group have water-disintegrable, so, use down or producing when using under the condition of strong acid in hot and humid, the rerum natura of cured article can reduce.
Therefore, intramolecularly does not have ester group and multi-functional epoxy compound with alicyclic ring skeleton is desirable.
In Russian document (Neftekhimiya, 1972,12,353), as the representative of following alicyclic diepoxy compound with general formula (I) expression, disclose dicyclohexyl-3,3 '-diepoxide.In the document, use the molybdenum chloride (V) of peroxidation hydrogenation thing (still, peroxidation hydrogenation thing is a tert-butyl hydroperoxide) and catalytic amount, as being used for the synthetic epoxidizing agent.In the document, peroxidation hydrogenation thing is to use in the high temperature more than 80 ℃, because peroxidation hydrogenation thing has the danger of the explosive decomposition followed, so from the consideration of security aspect problem is arranged.In addition, the molybdenum chloride (V) that uses as catalyzer costs an arm and a leg, strong toxicity, so, should consider to seek manufacture method from economy, environment aspect.
On the other hand, epoxy resin cured product, owing to generally have performances such as excellent in mechanical properties, water tolerance, erosion resistance, binding property, chemical proofing, thermotolerance, electrology characteristic, so in wide spectrums such as tackiness agent, coating, veneer sheet, IC sealing material, formed material, use.
Wherein, for example bisphenol-type epoxy resin, phenol novolak type epoxy resin etc. are the widespread use type aromatic epoxy resin of the Racemic glycidol ether type epoxy of representative, by adding solidifying agent, and according to circumstances add curing catalyst, also can further add weighting agents such as talcum powder, titanium, silica as required, under various conditions of cure, make curing, use as cured article.
Yet the cured article that is made of the widespread use type aromatic epoxy resin of above-mentioned Racemic glycidol ether type epoxy is because contain the aromatic series structure, so the weathering resistance variation outside the room.And, the viscosity of above-mentioned Racemic glycidol ether type epoxy (for example is to use E type rotational viscosimeter, Tokyo gauge system), measure down in 25 ℃, because bisphenol A-type is that 4000~20000mPas, Bisphenol F type are 1500~4500mPas etc., so the Resins, epoxy of general glycidyl ether type mobile low is mostly at toluene, dimethylbenzene, methylethylketone, vinyl acetic monomer etc. use for dissolving back in the solvent of representative, have the problem of operation, environmental safety.
Although do not use thinner, as the very low Resins, epoxy of viscosity, known its has cyclohexene oxide skeleton (alicyclic ring skeleton).The epoxy compounds that contains the alicyclic ring skeleton has the reactive characteristics with glycidyl ether type epoxy compounds same degree, and existing now extensive stock is sold.For example, have the monofunctional epoxy compound of alicyclic ring bone lattice, can enumerate monocycle oxidation 4 vinyl cyclohexene,, can enumerate 4 vinyl cyclohexene diepoxide or limonene diepoxide etc. as two sense epoxy compoundss at intramolecularly.
The compound that contains this alicyclic ring skeleton in manufacturing engineering, does not produce and results from halid halogen, the electrology characteristic excellence.And the compound that contains the alicyclic ring skeleton has thermotolerance, the transparency of the resin feature of using.
Contain the epoxy compounds of this alicyclic ring skeleton or contain its resin combination, can be used as composition or the stablizer of various thermoplastic resins or the various end-uses of medicine and medical treatment product of coating, tackiness agent, printing ink, seal gum.Moreover, known when making other useful compounds, also can be used as intermediate product.
The epoxy compounds that contains this alicyclic ring skeleton when using, has very good performance but reactivity is lower, and causes rerum natura and reactive reduction of cured article in such use.Therefore, wish that reactive high alicyclic epoxide compound occurs.Moreover above-mentioned monocycle oxidation 4 vinyl cyclohexene and limonene diepoxide have the problem on the operating environment owing at room temperature volatilizing.
In addition, alicyclic diepoxy compound and similar alicyclic diepoxy compound as the following general formula that the present invention relates to (I) expression, (for example can enumerate the alicyclic diepoxy compound of 2 alicyclic structures by bonds such as methylene radical, the spy opens clear 58-172387 communique, special public clear 50-10636 communique).
Moreover, the someone proposed in recent years, oxetane compound and cationic polymerization initiators, cooperate with alicyclic diepoxy compound or (for example through the curable resin composition of upgrading, the spy opens the 2002-53659 communique and the spy opens 2002-82527 communique etc.), the curable resin composition that contains this alicyclic diepoxy compound can't be brought into play satisfactory performance.
The inventor finds, the alicyclic diepoxy compound of following general formula (I) expression contains the curable epoxy resin composition of hot positively charged ion or light cationic polymerization initiators or acid anhydrides and makes its solidified cured article have excellent characteristic.
In the past, electronic units such as diode, triode, unicircuit adopt thermosetting resin to seal, unicircuit particularly, the system of using the o-cresols phenolic varnish type epoxy of thermotolerance, excellent moisture resistance or biphenyl type epoxy resin, phenolic varnish type phenolic resin to constitute mostly.
In recent years, in the trend of the miniaturization of e-machine, lightweight, high performance, follow semi-conductive integratedly, be inserted in insertion mounting means the substrate aperture, change to the surface mounting mode of substrate surface welding assembly from the past lead pin.The surface mounting mode is different with the insertion mounting means, when adopting scolding tin to install in the installation work, heats under 210~270 ℃ high temperature with sealing resin packages sealed integral body.The result is that the crack divide to take place resin portion, produces the crack or peels off at the periphery of contact, and reliability reduces, and produces the out of use problem of goods.
Generally, as fissured genesis mechanism, existing multiple hypothesis.In installation work, the sealing resin of packing can moisture absorption.On the other hand, during the surface mounting operation, under the whole high temperature that is exposed to more than 200 ℃ of packing, slim packing is through the short period of time, and package interior also reaches more than 200 ℃.When the packing of moisture absorption is heated to more than 200 ℃ sharp,, and when the interior pressure of packing is elevated to the rupture strength of sealing material, then produce the crack because of interior pressure takes place for the gasification of moisture.
Moreover interface peel results from the volumetric shrinkage that produces when curable resin such as Resins, epoxy solidifies, or the coefficient of linear expansion difference of metal and epoxy resin molding material and the thermal stresses of the package interior that takes place.
For overcoming above-mentioned shortcoming, adopted the method that makes sealing resin snappiness rateization or reduce line exapnsion rate.For example, the height fillingization of filler also is one of them.Yet the height of filler is filled and is turned to effective means, but gauge is arranged, and can cause the viscosity of sealing resin to rise or the mobile problem that reduces.The rising of resin viscosity causes lead distortion or fracture, and mobile decline can cause the low of fillibility, the possibility that has reliability to reduce.
As the electronic part encapsulation resin, known have various all multi-functional epoxy compounds that have the alicyclic ring skeleton at intramolecularly.
Yet above-mentioned 1,2,8,9-diepoxy limonene has methyl owing to constitute on the carbon of epoxy group(ing), and the person compares with there not being the methyl, epoxy group(ing) reactive low.And, because 3,4-epoxycyclohexyl methyl 3 ', 4 '-epoxycyclohexane carboxylate or two (3,4-epoxycyclohexyl methyl) adipic acid ester and lactone affixture thereof, epoxidation butanetetra-carboxylic acid four-3-cyclohexenyl methyl esters and 6-caprolactone affixture thereof are because intramolecularly has ester group and hydrolysis takes place sometimes.
Therefore, as mentioned above, because hot and humid the use down or hydrolysis reduced the rerum natura of cured article.
Moreover, as mentioned above, alicyclic epoxide compound (a) the similar alicyclic epoxide compound represented with following formula (I), the known alicyclic epoxide compound (for example, the spy opens the 2002-275169 communique, the spy opens clear 58-172387 communique, special public clear 50-10636 communique) that 2 alicyclic ring structures are arranged through bonds such as methylene radical.Yet the epoxidation rate is low slightly in this epoxy compounds.
And the spy opens the 2001-181481 communique and discloses the composition epoxy resin that a kind of encapsulating semiconductor that uses biphenyl type epoxy resin is used, and it has excellent water-absorbent, but mobile or solidify moment of torsion, that is to say that problem is still arranged aspect formability.
Here, wish a kind of intramolecularly of exploitation not have ester group and contain other alicyclic ring skeleton, and mobile excellent epoxy compounds, the inventor finds to contain the composition epoxy resin of represented alicyclic epoxide compound of following general formula (I) (a) and solidifying agent, has excellent characteristic as resin composition for sealing electronic component.
And in the purposes of electric insulation oil, the electric insulation oil that the transformer of charge of oil, particularly open type transformer are used requires the oxidative stability excellence because transformer oil contacts with air.Therefore, to oxidation inhibitor, particularly be oxidation inhibitor the person has carried out examining (spy opens flat 9-272891 communique) containing phenol.Yet, for example, add 0.3 weight %DBPC (2, the 6-ditertbutylparacresol) electric insulation oil (spy opens the 2002-260445 communique), aspect the oxidation stability test of JIS C 2101-1993, under 120 ℃ * 75 hours, observe because of existing oxidative phenomena and make total acid value rise (0.02~0.03mgKOH/ gram).That is to say, be when finishing already oxidised inductive phase in 75 hours, and the rising of total acid value is thereafter sharply carried out.
On the other hand, epoxy compounds as the technology that captures the impurity in the transformer oil composition or disperse the insulation stabilizers of discharge energy, is opened flat 3-171510 communique and spy the spy and opened in the flat 7-226332 communique and disclose the electrical condenser transformer oil.Yet employed epoxy compounds is mainly alicyclic diepoxy compound and aromatic series di-epoxy compounds that intramolecularly contains ester bond or ehter bond, and hydrolysis or pyrolysis take place for their in through use between long-term, thereby does not show the function of anti-oxidation.Moreover, in electrical condenser, in sealed structure, enclose transformer oil usually, make distortion because of decompose producing gas etc., or disintegration voltage reduces, electrostatic capacity reduces and can not use.
On the other hand, in the insulation division of electronic machine and the connection section of power cable etc., the composition epoxy resin casting product imbed metal electrode are set, support conductor through above-mentioned metal electrode portion.Generally speaking these composition epoxy resin casting product, are to use the composition epoxy resin that is made of polyfunctional epoxy resin, acid anhydrides and packing material etc. to make.Wherein, use bisphenol-type epoxy resin as the inanimate matter packing material, can make good upwards the promoting of fracture-resistant and physical strength or electrology characteristic balance as inanimate matter powder such as acid anhydrides, use aluminum oxide, silicas as Resins, epoxy, use anhydride phthalic acid.
In recent years, high-voltage is stronger with the tendency of the miniaturization of instrument, extra-high pressureization, also require the performance of composition epoxy resin casting product to improve more, and composition epoxy resin casting product in the past, there is the potential destructive boundary that reaches aspect electrology characteristic, the mechanical characteristics.That is to say, follow extra-high pressureization, require it that high electric field that meets with is had higher proof voltage intensity isolator (using electrical isolation casting composition epoxy resin).Moreover dielectric damage (ε tan δ E2) also is accompanied by extra-high pressureization and increases, and worries to be caused by the heat of its generation the thermal damage of isolator.Particularly, rise and rise if ε tan δ is accompanied by temperature, also being difficult to negates to have thermal runaway to destroy.And also there is the requirement that further improves the binding property of the metal electrode of imbedding with isolator and fracture-resistant aspect.
For example, the spy opens in the flat 9-77847 communique, uses bisphenol A type epoxy resin and novolac epoxy as Resins, epoxy, and the acid anhydrides that mixes more than 2 kinds is used resin as insulating; Again, the spy opens in the flat 11-60908 communique, and in bisphenol type epoxy and crystallinity epoxy as Resins, epoxy, the acid anhydrides of mixing more than 2 kinds is as the insulation resin.
Under these situations, because composition is solid, so, be not suitable for the purposes of casting or dipping.
Summary of the invention
Purpose of the present invention (1) provides the environment of a kind of security improvement, consideration economy, does not contain the manufacture method of the alicyclic diepoxy compound of ester group, low viscosity processing ease at intramolecularly.
Again, purpose of the present invention (2) provides the curable resin composition of making neccessary composition with this alicyclic diepoxy compound, hot positively charged ion or light cationic polymerization initiators or acid anhydrides, said composition is solidified, with comparison under epoxy compounds (resin) situation of using in the past, except that solidification reactivity, can obtain the cured article of excellent properties such as the transparency, thermotolerance, processibility, operational security.
And, it is a kind of by cooperating the alicyclic diepoxy compound with following general formula (I) expression that purpose of the present invention (3) provides, to solve electronic part encapsulation the problems referred to above with resin, and when electronic circuit components such as sealed semiconductor device, lead distortion or broken string, mobile height do not take place and fillibility is good and excellence such as wet fastness, the electronic part encapsulation composition epoxy resin.
Moreover purpose of the present invention (4) provides a kind of and uses the back than the oxidative stability excellent electric insulation stabilizers of the past product and stabilized electric insulation oil between long-term.
In addition, purpose of the present invention (5) provides a kind of composition epoxy resin of the alicyclic diepoxy compound by will containing following general formula (I) expression, the cooperation ratio of acid anhydrides, curing catalyst and inorganic filling material is set in specific scope, can obtain a kind of electrical isolation casting composition epoxy resin casting operation, cured article of not damaging with excellent heat resistance, electrology characteristic and mechanical characteristics.
According to the present invention (5), particularly use when dissolving aluminum oxide as above-mentioned inanimate matter packing material, promote 30~50% in the time of can obtaining electrology characteristic and mechanical characteristics all excellent electrical isolation casting composition epoxy resin, especially voltage-resistent characteristic than use electrofusion aluminum oxide.
The inventor etc., be to achieve the above object found that of concentrated self-criticism by using organic percarboxylic acids, can obtain economy, yield is good and purity is high di-epoxy compounds, and, the resin combination viscosity that contains this di-epoxy compounds is low, and operation is good, and has excellent solidified nature, the thermotolerance of resulting cured article and electrology characteristic excellence, moreover the stablizer that this di-epoxy compounds is used as electric insulation oil is effective, finishes, reaches the present invention (1)~(5).
That is to say, the of the present invention the 1st relates to a kind of manufacture method of alicyclic diepoxy compound, it is characterized in that, the represented alicyclic diolefin compound of following general formula (II) is carried out epoxidation through organic percarboxylic acids obtain alicyclic diepoxy compound with general formula (I) expression:
Figure C0381894900091
(in the formula, R 1~R 18Both can distinguish identical also can be different, it is that hydrogen atom, halogen atom maybe can contain the alkyl of Sauerstoffatom or halogen atom or can contain substituent alkoxyl group).
The of the present invention the 2nd provides the manufacture method of the alicyclic diepoxy compound of the 1st of a kind of foregoing invention, wherein, by with oxygen the aldehyde corresponding to organic percarboxylic acids being carried out oxidation, obtains moisture free in fact organic percarboxylic acids.
The of the present invention the 3rd provides the manufacture method of a kind of foregoing invention the 1st or 2 s' alicyclic diepoxy compound, and wherein, the moisture in the organic percarboxylic acids is below 0.8 weight %.
The of the present invention the 4th provides the manufacture method of the alicyclic diepoxy compound of the 4th of a kind of foregoing invention, and wherein, organic percarboxylic acids is a peroxyacetic acid.
The of the present invention the 5th provides the manufacture method of the alicyclic diepoxy compound of the 4th of a kind of foregoing invention, and wherein, peroxyacetic acid is a vinyl acetic monomer solution.
Again, the of the present invention the 6th provides a kind of curable epoxy resin composition, it is characterized in that, its be by the polymerization starter (B) of the represented alicyclic diepoxy compound (A) of formula (I), hot positively charged ion (b1) or light positively charged ion (b2) or acid anhydrides (C), and (D) other Resins, epoxy that optionally add constitute, wherein, formula (I) is as shown in the formula shown in (I):
Figure C0381894900101
(in the formula, R 1~R 18Both can distinguish identical also can be different, it is hydrogen atom, halogen atom, can contains the alkyl of Sauerstoffatom or halogen atom or can contain substituent alkoxyl group).
The of the present invention the 7th provides the curable epoxy resin composition of the 6th of a kind of foregoing invention, wherein, the represented alicyclic diepoxy compound of formula (I) be dicyclohexyl-3,3 '-diepoxide.
The of the present invention the 8th provides a kind of foregoing invention the 6th or 7 s' curable epoxy resin composition, and wherein, the light cationic polymerization initiators is that sulfonium salt is the light cationic polymerization initiators.
The of the present invention the 9th provides a kind of foregoing invention the 6th or 7 s' curable epoxy resin composition, and wherein, acid anhydrides is methyl six hydrogen anhydride phthalic acids.
The of the present invention the 10th provides a kind of cured article, and it is solidified each curable epoxy resin composition in the 6th~9 of the foregoing invention to form.
Moreover, the of the present invention the 11st provides a kind of electronic part encapsulation composition epoxy resin, comprising the represented alicyclic diepoxy composition (a) of formula (I), solidifying agent (b) is neccessary composition, the optionally curing catalyst of Pei Heing (c), inorganic filler (d) and other Resins, epoxy and make, (I) is as follows for its formula of:
Figure C0381894900102
(in the formula, R 1~R 18Both can distinguish identical also can be different, it is that hydrogen atom, halogen atom maybe can contain the alkyl of Sauerstoffatom or halogen atom or can contain substituent alkoxyl group).
The of the present invention the 12nd provides the electronic part encapsulation composition epoxy resin of the 11st of a kind of foregoing invention, wherein, described alicyclic diepoxy compound (a) be dicyclohexyl-3,3 '-diepoxide.
The of the present invention the 13rd provides a kind of foregoing invention the 11st or 12 s' electronic part encapsulation composition epoxy resin, and wherein solidifying agent (b) is that to be selected from amine be that solidifying agent, acid anhydrides are that solidifying agent or phenolic aldehyde are at least a of resin.
The of the present invention the 14th provides the electronic part encapsulation composition epoxy resin of the 11st of a kind of foregoing invention, and wherein (e) other Resins, epoxy are the cresols phenolic resin varnish type epoxy resin.
The of the present invention the 15th provides a kind of cured article, and it is solidified each electronic part encapsulation in the 11st~14 of the foregoing invention and makes with composition epoxy resin.
And the of the present invention the 16th provides a kind of electrical isolation stabilizers, and its alicyclic diepoxy compound by general formula (I) expression is made, and (I) is as follows for its Chinese style:
Figure C0381894900111
(in the formula, R 1~R 18Both can be identical or different respectively, it can be hydrogen atom, halogen atom and maybe can contain the alkyl of Sauerstoffatom or halogen atom or can contain substituent alkoxyl group).
The of the present invention the 17th provides the electrical isolation stabilizers of the 16th of a kind of foregoing invention, wherein, in the represented alicyclic diepoxy compound of general formula (I), R 1~R 18It all is hydrogen atom.
The of the present invention the 18th provides a kind of foregoing invention the 16th or 17 s' electrical isolation stabilizers, wherein, the represented alicyclic diepoxy compound of general formula (I) obtains pairing diolefin compound epoxidation by the organic percarboxylic acids that does not contain moisture in fact.
The of the present invention the 19th provides the electrical isolation stabilizers of the 18th of a kind of foregoing invention, and wherein, the moisture content in the organic percarboxylic acids is below the 0.8 weight %.
The of the present invention the 20th provides a kind of foregoing invention the 18th or 19 s' electrical isolation stabilizers, and wherein, organic percarboxylic acids is an organic solvent solution.
The of the present invention the 21st provides in the 16th~20 of a kind of foregoing invention each electrical isolation stabilizers, the insulation stabilizers that it is used for electrical condenser.
The of the present invention the 22nd provides a kind of electric insulation oil, it is characterized in that, comprising each electrical isolation stabilizers in the 16th~21 of the foregoing invention, it cooperates 0.05~15 weight part with respect to the transformer oil composition of 100 weight parts.
And the of the present invention the 23rd provides a kind of electrical isolation casting composition epoxy resin, and comprising heat-curing resin and inanimate matter packing material, this heat reactive resin comprises following (A)~(C) composition:
(A) composition epoxy resin
Comprising: the alicyclic diepoxy compound (a-1) that the general formula of 5~80 weight % (I) is represented:
Figure C0381894900121
(in the formula, R 1~R 18Both can distinguish identical also can be different, it can be hydrogen atom, halogen atom, can contain the alkyl of Sauerstoffatom or halogen atom or can contain substituent alkoxyl group), alicyclic diepoxy compound (a-1) alicyclic diepoxy compound (a-2) [wherein, alicyclic diepoxy compound (a-1) is 100 weight % with epoxy compounds (a-2) sum] in addition that the general formula of 95~20 weight % (I) is represented;
(B) acid anhydrides;
(C) curing catalyst;
Also further comprise,
(D) inanimate matter packing material;
Wherein, cooperation ratio that should (B) composition is 0.6~1.0 equivalent with respect to (A) composition 1 equivalent, (C) composition with respect to (A) and (B) 100 weight parts of total amount be 0.5~10 weight part, (D) composition is 30~80 weight % of (A)~(D) total amount.
The present invention the 24th provides the electrical isolation casting composition epoxy resin of the 23rd of a kind of foregoing invention, wherein, the represented alicyclic diepoxy compound (a-1) of general formula (I) be dicyclohexyl-3,3 '-di-epoxy compounds.
The present invention the 25th provides the electrical isolation casting composition epoxy resin of the 23rd of a kind of foregoing invention, and wherein, acid anhydrides is methyl six hydrogen anhydride phthalic acids or methyl norbornene dicarboxylic acids acid anhydride.
The present invention the 26th provides the electrical isolation casting composition epoxy resin of the 23rd of a kind of foregoing invention, and wherein, curing catalyst is ethylene glycol or diazabicylo hendecene.
The present invention the 27th provides the electrical isolation casting composition epoxy resin of the 23rd of a kind of foregoing invention, and wherein, the inanimate matter packing material is globular fused silica or fused aluminum oxide.
The present invention the 28th provides the electrical isolation casting composition epoxy resin of the 23rd of a kind of foregoing invention, wherein, epoxy compounds (a-2) is selected from 3 at least a, 4-epoxy group(ing) cyclohexyl methyl-3,4-epoxy-cyclohexane carboxylicesters, bisphenol-type epoxy resin or phenolic varnish phenol type Resins, epoxy.
The present invention the 29th provides a kind of cured article, and it is solidified through composition with casting epoxy tree by each electrical isolation in the 23rd~28 of the foregoing invention forms.
Description of drawings
Fig. 1 represents the NMR figure of the alicyclic diepoxide that obtains among the embodiment.
Specific embodiments
Below, the present invention (1) is described in detail.
The present invention (1) relate to the represented alicyclic diepoxy compound of general formula (I), be have dicyclohexyl-3,3 '-the diene skeleton with the represented unsaturated compound of general formula (II), make by the organic percarboxylic acids oxidation.
Figure C0381894900131
In general formula (I) and the general formula (II), R 1~R 18Both can be identical also can be different, it is hydrogen atom, halogen atom, maybe can contains the alkyl of Sauerstoffatom or halogen atom or can contain substituent alkoxyl group.
Have above-mentioned dicyclohexyl-3,3 '-unsaturated compound of diene skeleton, generally synthetic by the dehydration reaction of hydroxy-containing compounds.Manufacture method can adopt the 114th~127 page of new experimental chemistry lecture 14 " the kind limited-liability company of ball publishes; the synthetic and reaction (I) of organic compound ", spy to open clear 58-172387 communique, the spy opens the method for being put down in writing in the 2000-169399 communique etc., and is synthetic by the compound with hexalin structure.
According to the present invention (1), alicyclic epoxide compound be by have dicyclohexyl-3,3 '-unsaturated compound of diene skeleton and organic percarboxylic acids reaction and make.
In the present invention's (1) the manufacture method, epoxidizing agent uses organic percarboxylic acids (organic percarboxylic acids means peroxyformic acid, peroxyacetic acid, peroxybenzoic acid, crosses isopropylformic acid, trifluoro peroxyacetic acid etc.).Peroxyacetic acid particularly in the organic percarboxylic acids has necessary reactive and high stability simultaneously when alicyclic epoxide compound of the present invention is made, be preferred epoxidizing agent.
Wherein, use not moisturely in fact, particularly, use below the moisture content 0.8 weight %, the organic percarboxylic acids that preferred 0.6 weight % is following, the compound that can obtain having the epipodium oxidation ratio is preferred.The water-free in fact organic percarboxylic acids of what is called among the present invention (1) is by aldehydes, for example, the atmospheric oxidation of acetaldehyde and making, for example peroxyacetic acid can openly be speciallyyed permit communique No. 1418465 and specially opens the method for being put down in writing among the clear 54-3006 and make by Germany.If according to this method, synthesize organic percarboxylic acids from hydrogen peroxide, when comparing with the organic percarboxylic acids of making by solvent extraction, owing to can a large amount of continuously high densitys synthesize organic percarboxylic acids, so come down to cheap.
The qualification that the amount of epoxidizing agent is not strict especially is by variable factor decisions such as the reactivity of various epoxidizing agents of the optimal dose of using under each situation or alicyclic olefin compound, purpose epoxidation ratios.
Whether epoxidation reaction can be according to device or raw material rerum natura, to using solvent or temperature of reaction to regulate.As solvent, the purposes such as stabilization of can reduce according to material viscosity, epoxidizing agent diluting are used, and under the situation of using peroxyacetic acid, use ester class, aromatics, ethers etc.Particularly preferred solvent is vinyl acetic monomer, hexane, hexanaphthene, toluene, benzene etc., and especially preferred is vinyl acetic monomer.Temperature of reaction is decided according to used epoxidizing agent and the reactivity that contains the compound of unsaturated group.
For example, when using preferred epoxidizing agent peroxyacetic acid, temperature of reaction is 20~70 ℃.Reaction is slack-off during 20 ℃ of less thaies, and when surpassing 70 ℃ of temperature, peroxyacetic acid is followed heating and decomposed, and is unfavorable.
With respect to unsaturated link(age), the epoxidizing agent mol ratio of packing into, can according to unsaturated link(age) remaining what etc. purpose and changing.When the compound that the epoxidation rate is high was purpose, epoxidizing agent wished to add 1.0~3.0 moles with respect to 1 mole of unsaturated group, more wishes to add 1.05~1.5 moles.Consider from economy and side effect, unfavorable usually when surpassing 3.0 times of moles.If adopt the present invention's (1) manufacture method, then do not need to use expensive epoxidizing agent and catalyzer.
Thick liquid to the reaction gained does not need special operation, and for example, thick liquid stirred slaking through 1~5 hour preferable.By the appropriate method of the thick liquid separating ring of gained oxygen compound, for example can adopt the intermediate processing of poor solvent; The epoxide stirring is dropped in the hot water down, distills except that the method for desolvating; Direct desolventizing method etc.
Alicyclic diepoxy compound by the present invention's (1) manufacture method manufacturing with above-mentioned general formula (I) expression, can or further react by homopolymerization, copolymerization with other compounds, generate various coating, printing ink, tackiness agent, seal gum, moulded products, perhaps use the intermediate product of their other purposes.As the end-use of the represented alicyclic diepoxy compound of above-mentioned general formula (I), for example: acid scavenger, coatings for furniture, decorative paint, beverages can and other tin paint, tackiness agent, vehicle paint base, the sealing material, processing coating, the printing ink of Word message or graphic information, the seal gum of electronic component-use, be suitable for the photoresist of press plate or printed circuit board exploitation, printing casting roller, with unsaturated polyester and vinylbenzene is that main body is passed through glass, carbon, title complex that graphite or other fiber strengthened moulding are used or sheet material form with the made moulded products of title complex; Intermediate of other compounds that solvent, fire retardant, the various end-uses etc. that comprise medicine and medical treatment product are useful etc.
Moreover above-mentioned alicyclic diepoxy compound with general formula (I) expression has the resin feature that adopts the alicyclic ring framework compound and is thermotolerance, the transparency, good dielectric characteristics.
Secondly, the present invention (2) is described in detail.
The present invention (2) relates to and has curable epoxy resin composition and the cured article thereof that the di-epoxy compounds with alicyclic ring skeleton that does not contain ester bond is a neccessary composition.
Contain in the present invention's (2) the curable epoxy resin composition with following formula (I) is the alicyclic diepoxy compound (A) of the resinous principle of necessity:
Figure C0381894900151
(in the formula, R 1~R 18Both can be the same or different.It is hydrogen atom, halogen atom, can contains the alkyl of Sauerstoffatom or halogen atom or can contain substituent alkoxyl group), it is well-known, for example, can adopt the manufacture method of the present invention (1), special hope 2002-260490 specification sheets and Russian document (Neftekhimiya, 1972,12,353) method of being put down in writing in is made.Particularly, as described in the manufacture method of the present invention (1), use moisture to contain the low organic percarboxylic acids of rate, when making by the epoxidation of corresponding diolefin compound, the high person of the containing ratio of di-epoxy compounds is preferred.The object lesson of the alicyclic diepoxy compound (A) that above-mentioned general formula (I) is represented uses R 1~R 18Be the dicyclohexyl-3,3 of hydrogen atom '-diepoxide is preferred.
The present invention's (2) curable epoxy resin composition, except containing the represented alicyclic diepoxy compound (A) of above-mentioned general formula (I), also contain solidifying agent (B) as neccessary composition, further contain other Resins, epoxy (D), can also contain curing catalyst and other weighting agents or additive.
Solidifying agent (B) must use cationic polymerization initiators or acid anhydrides (C) by light or thermogenesis positively charged ion kind.The neccessary composition solidifying agent (B) of the present invention's (2) curable epoxy resin composition is because contain light cationic polymerization initiators (b1) or hot cationic polymerization initiators (b2) or acid anhydrides (C), so be cured polymerization by light or heat.
Light cationic polymerization initiators (b1) can use sulfonium salt Xi, Iodonium salt system, diazonium salt system, propadiene-compounds such as ion coordination series of compounds.For example UVACURE1590, the UVACURE1591 of sulfonium salt system (more than be ダ イ セ Le UCB. S.A. (BE) Bruxelles Belgium system), DAICAT11 (ダ イ セ Le chemical company system), CD-1011 (サ one ト マ corporate system), SI-60L, SI-80L, SI-100L (more than be three new chemical company systems) etc.; DAICAT12 (ダ イ セ Le chemical company system), the CD-1012 (サ one ト マ corporate system) of Iodonium salt system; SP-150, the SP-170 (Asahi Electro-Chemical Co. Ltd's system) etc. of diazonium salt system.In the light cationic polymerization initiators, also can produce positively charged ion by heating above-mentioned SI-60L, SI-80L, SI-100L.
Moreover hot cationic polymerization initiators (b2) also can use silanol such as tri-phenyl-silane alcohol system sun from aluminum chelating agent series catalysts such as catalyzer or aluminium tris(acetylacetonate)s.
In the present invention (2), above-mentioned cationic polymerization initiators is to the represented alicyclic diepoxy compound of general formula (I) and total amount 100 weight parts of following other Resins, epoxy that optionally added, cooperate 0.01~20 weight part, preferred 0.1~5 weight part more preferably cooperates about 0.1~3 weight part.When less than 0.01 weight part, Thermocurable obviously reduces, and when cooperate surpassing 20 weight parts, does not find that effect increases and be uneconomic that the rerum natura that produces cured article simultaneously reduces, so be unfavorable.
And the solidifying agent among the present invention (2) also can use acid anhydrides (C).As acid anhydrides, can adopt anhydride phthalic acid, maleic anhydride, trimellitic acid 1,2-anhydride, the tetrahydrochysene anhydride phthalic acid, methyl tetrahydrochysene anhydride phthalic acid, methyl norbornene dicarboxylic acids acid anhydride, methyl six hydrogen anhydride phthalic acids, six hydrogen anhydride phthalic acids, methyl humic acid anhydrides, pyromellitic acid anhydride, benzophenone tetracarboxylic dianhydride, 3,3 ', 4,4 '-biphenyl tetracarboxylic dianhydride, two (3,4-two carboxyphenyls) ether dianhydride, two (3,4-two carboxyphenyls) methane dianhydride, 2,2-two (3,4-two carboxyphenyls) propane dianhydride etc., preferably have 1 or 2 aliphatics ring or aromatic ring in the molecule, have 1 or 2 anhydride group simultaneously, 4~25 of carbonatomss, preferred about 8~20 acid anhydrides.
This acid anhydrides can also be used separately or more than 2 kinds.Wherein, the viewpoint that improves more from excellent heat resistance, electrology characteristic and physical strength particularly, it is preferred using methyl six hydrogen anhydride phthalic acids, tetrahydrochysene anhydride phthalic acid etc.
In this case, as acid anhydrides, the preferred compounds content 0.5 weight % following (that is, 0~0.5 weight %) with carboxyl (COOH yl), the acid anhydrides of preferred especially 0.4 weight % following (that is 0~0.4 weight %) of using.When carboxyl-content during more than 0.5 weight %, probably there is crystallization to take place, be unfavorable.At this moment, the content of carboxyl (COOH yl) is (that is, 0~0.3 weight %), particularly 0.25 weight % below the 0.3 weight % following (that is, 0~0.25 weight %) with respect to anhydride curing agent, because same reason is preferred.
Again, the use level of acid anhydrides with respect to 1 mole of the epoxy group(ing) total amount of the represented alicyclic diepoxy compound of general formula (I) and following other Resins, epoxy that optionally add, wishes that anhydride group is than the scope that reaches 0.3~0.7 mole.When below 0.3 mole the time, solidified nature is insufficient, and when surpassing 0.7 mole, acid anhydrides that can remained unreacted probably has second-order transition temperature and reduces.More wish scope at 0.4~0.6 mole.
And when being cured, curing catalyst can use 1,8-diazabicylo (5,4,0) hendecene amidine compounds such as (DBU); Or organo phosphorous compounds such as triphenylphosphine, tetraphenylphosphoniphenolate, tetraphenyl boric acid ester; Imidazolium compoundss such as glyoxal ethyline etc. are not particularly limited them.This curing catalyst can be used alone or as a mixture.Alicyclic diepoxy compound and following total amount 100 weight parts of the polymerization starter of other Resins, epoxy of interpolation optionally that use level is represented with respect to above-mentioned general formula (I), the scope of preferred 0.4~20 weight part.When use level less than 0.4 weight part, probably can't obtain sufficient solidified nature during hot briquetting, on the other hand, when surpassing 20 weight parts, solidify too soon, that filling probably takes place is bad because of the reduction of flowability when moulding, is unfavorable.
Other Resins, epoxy that in the alicyclic diepoxy compound that the present invention (2) represents with general formula (I), optionally add, be not particularly limited, for example being selected from bisphenol A type epoxy resin, bisphenol f type epoxy resin, bisphenol-s epoxy resin, dihydroxyphenyl propane D type Resins, epoxy, naphthalene type Resins, epoxy, biphenyl type epoxy resin and halid 2 officials thereof can Resins, epoxy.
Outside above-mentioned, can enumerate phenolic resin varnish such as phenol novolak type epoxy resin, bromination phenol novolak type epoxy resin, o-cresol phenolic epoxy varnish, bisphenol-A phenolic varnish type Resins, epoxy, dihydroxyphenyl propane D phenolic resin varnish type epoxy resin; The Resins, epoxy that contains the oxidation tricyclic decenyl; The ring type aliphatic epoxy resins such as epoxide of dicyclopentadiene-type resol; The aromatic epoxy resins such as epoxide of naphthalene type resol; Glycidyl group amine type Resins, epoxy such as glycidyl ester type epoxy resins such as dimeracid glycidyl ester, three-glycidyl ester, four Racemic glycidol amido biphenyl methane, triglycidyl group mutual-amino phenol, triglycidyl group mutual-amino phenol, four glycidyl group MXDP, the two amino methyl hexanaphthenes of four glycidyl group; Hetero ring type Resins, epoxy such as triglycidyl group isocyanuric acid ester; Fluorine glycinol triglycidyl ether, trihydroxy-xenyl triglycidyl ether, trihydroxybenzene methylmethane triglycidyl ether, T 55,2-[4-(2, the 3-glycidoxy) phenyl]-2-[4-[1,1-is two, and [4-(2, the 3-glycidoxy) phenyl] ethyl] phenyl] propane, 1,3-is two, and [4-[1-[4-(2, the 3-glycidoxy) phenyl]-1-[4-[1-[4-(2, the 3-glycidoxy) phenyl]-the 1-methylethyl] phenyl] ethyl] phenoxy group]-3 functional-type Resins, epoxy such as 2-propyl alcohol; 4 functional-type Resins, epoxy such as tetrahydroxy phenyl ethane four glycidyl ethers, four glycidyl group benzophenone, two Resorcinol four glycidyl ethers, Fourth Ring oxygen propoxy-biphenyl; 3,4-oxirane ring hexenyl methyl-3 ', 4 '-oxirane ring hexenyl carboxylicesters (ダ イ セ Le chemical industry system セ ロ キ サ イ De 2021), diepoxy limonene (ダ イ セ Le chemical industry system セ ロ キ サ イ De 3000), 3 of 6-caprolactone upgrading, 4-oxirane ring hexenyl methyl-3 ', 4 '-oxirane ring hexene carboxylicesters (ダ イ セ Le chemical industry system セ ロ キ サ イ De 2081), two (3,4-epoxycyclohexyl methyl) adipic acid ester (for example, ユ ニ オ Application カ one バ イ De system ERL4299 etc.), epoxidation 3-tetrahydrobenzene-1, two 3-cyclohexenyl methyl esters of 2-dicarboxylic acid and 6-caprolactone affixture (ダ イ セ Le chemical industry system GT300 series such as " エ Port リ one De GT301 ") thereof, and epoxidation butanetetra-carboxylic acid four-3-cyclohexenyl methyl esters and 6-caprolactone affixture cycloaliphatic epoxy resins such as (ダ イ セ Le chemical industry system エ Port リ one De GT400 such as " GT401 " series) thereof.The addition of other Resins, epoxy that this is optionally added, alicyclic diepoxy compound 100 weight parts of representing with respect to general formula (I) reach 1~10000 weight part, preferred 100~8000 weight parts, more preferably 1000~5000 weight parts.As if when than 1 weight part after a little while, these other Resins, epoxy that optionally added do not need to add, otherwise when than 10000 weight parts for a long time, the cured article that the alicyclic diepoxy compound of being represented by general formula (I) constitutes does not have excellent characteristic.
Moreover the present invention's (2) curable epoxy resin composition can optionally use thermoplastic resins such as polyethylene, polypropylene, polystyrene, polyethylene terephthalate, polycaprolactone, polycarbonate, polyarylester.
The present invention's (2) curable epoxy resin composition also can use synthetic rubber, elastomericss such as polyhutadiene, polyhutadiene polystyrene copolymer polymkeric substance.Nitrogenous compounds such as polyamide resins such as the present invention's (2) curable epoxy resin composition can use 6,6-nylon or polyimide resin.
The present invention's (2) curable epoxy resin composition also contains resol.For example, phenolic varnish resol, Dicyclopentadiene (DCPD) copolymerization mould assembly phenol phenolic resin varnish, naphthalene copolymerization mould assembly phenol phenolic resin varnish, biphenyl copolymerization mould assembly phenol phenolic resin varnish, dimethylbenzene copolymerization mould assembly phenol phenolic resin varnish, the cresols phenol phenolic resin varnish, Dicyclopentadiene (DCPD) copolymerization mould assembly cresols phenol phenolic resin varnish, naphthalene copolymerization mould assembly cresols phenol phenolic resin varnish, xenyl copolymerization mould assembly cresols phenol phenolic resin varnish, naphthalene copolymerization mould assembly cresols phenol phenolic resin varnish, solvable type resol, Dicyclopentadiene (DCPD) copolymerization mould assembly soluble phenolic resin, naphthalene copolymerization mould assembly soluble phenolic resin, biphenyl copolymerization mould assembly soluble phenolic resin, dimethylbenzene copolymerization mould assembly soluble phenolic resin etc.
The addition of polyethylene of Tian Jiaing etc. and resol optionally, alicyclic diepoxy compound 100 weight parts represented with respect to general formula (I) are 1~10000 weight part, more preferably 100~8000 weight parts especially are preferably 1000~5000 weight parts.When after a little while than 1 weight part, can not need to add polyethylene etc., on the contrary, when than 10000 weight parts for a long time, then the excellent characteristics that formed by the represented alicyclic diepoxy compound of general formula (I) do not appear in cured article.
In the curable epoxy resin composition of the present invention (2), also can optionally use weighting agent.All can use as the organic filler of weighting agent, any one of inorganic filler, if when considering hot exapnsion rate, inorganic filler is preferred.
As organic filler, for example, can enumerate the thermoplastic resin of nitrogen atoms such as acrylic resin; Thermoplastic resins such as polystyrene resin, polyvinyl resin, Resins, epoxy, polyorganosiloxane resin; Thermoplastic elastomer etc.As the example of inorganic filler, can enumerate aluminum oxide, talcum powder, glass powder, ceramic powder, crystallinity silica, fused silica etc.In addition, the content of weighting agent except that the effect of restriction to the present invention (2) do not cause the bad influence, there is no especially to limit.
Moreover the additive that the present invention (2) uses can be enumerated the wax classes such as low-stress agent, carnauba wax, higher fatty acid, synthetic wax such as thermosetting resin, organic synthesis rubber of nitrogen atom; Tinting materials such as carbon black; Halogen trapping agent, leveling agent, curing catalyst etc.
For mixing the common employed device of above-mentioned each composition, for example, after carrying out thorough mixing, re-use hot-rolling, kneader etc. and carry out melt kneading via mixing tanks such as blending machines, pulverize the cooling back, makes formed material.In addition,, can seal when making semiconductor device at electronic units such as sealing semiconductor original papers by transmitting the methods of forming such as modulus method, compression modulus method, injection modulus method.
The present invention's (2) curable epoxy resin composition is 30~240 ℃ of temperature, be preferably 35~180 ℃, more preferably under 35~60 ℃, 30~300 minutes set times, be preferably 45~240 minutes, be cured in more preferably 60~120 minutes.
When solidification value and set time are lower than the lower value of above-mentioned scope, solidifies insufficient, otherwise, when higher, because resinous principle decomposes, also for not good than the higher limit of above-mentioned scope.Condition of cure depends on various conditions, and when solidification value was high, shortened set time, and when solidification value was hanged down, set time was elongated, can do suitable adjustment.Usually, (solidification value is 30~240 ℃, is preferably 35~180 ℃ to carry out one-step solidification, more preferably 35~60 ℃, be 30~300 minutes set time, is preferably 45~240 minutes, more preferably 60~120 minutes) after, then (solidification value is 60~240 ℃ to regelate, is preferably 90~200 ℃, more preferably 120~200 ℃, be 30~180 minutes set time, be preferably 45~150 minutes, more preferably 60~120 minutes), can not produce and solidify deficiency.
Curable epoxy resin composition also can solidify as the light of ultraviolet ray and electron beam isoreactivity energy line by irradiation.
For example, the light source when carrying out uviolizing can use high pressure mercury vapour lamp, extra-high-pressure mercury vapour lamp, carbon arc lamp, xenon lamp, metal halide lamp etc.Irradiation time according to the distance of kind, light source and the coated face of light source, and other condition and different, can grow to tens of seconds, be generally the several seconds.After the uviolizing, optionally be heating and curing and also can seek completion of cure.Under the electron beam radiation situation, use to have 50~1, the electron beam of 000keV scope energy is preferably the irradiation dose of 2~5Mrad.Usually, the irradiating source about employing electric light output rating 80~300W/cm.
In the present invention's (2) the curable epoxy resin composition, as necessary resinous principle with the represented alicyclic diepoxy compound of general formula (I), because low viscosity, so its solidification compound also is low viscosity and has the feature of excellent in workability.In addition, since non-volatile in less than 100 ℃ temperature province, so operating environment is not had influence yet.
By the way, the represented alicyclic diepoxy compound of above-mentioned general formula (I) of the necessary resinous principle in the present invention's (2) the curable epoxy resin composition, react via homopolymerization, copolymerization or with other compound, make various coating, printing ink, tackiness agent, seal gum, moulding or moulded products, or be used for the intermediate product of other purposes.And, use the end-use of the present invention's (2) curable epoxy resin composition as the represented alicyclic diepoxy compound of the above-mentioned general formula (I) of necessary resinous principle, for example, acid scavenger, coatings for furniture, decorative paint, vehicle paint base, the sealing material, processing coating, beverages can and other jar coating, the printing ink of Word message or graphic information, the seal gum of electronic component-use, be suitable for the photosensitive resin film of press plate or printed circuit board exploitation, printing casting roller, with unsaturated polyester and vinylbenzene is that main body is passed through glass, carbon, graphite or with other fiber strengthened moulding title complexs or form the made moulded products of title complex of sheet material, solvent, fire retardant etc.
Below, the present invention (3) is described in detail.
As the represented alicyclic diepoxy compound (a) of above-mentioned general formula (I) of the necessary resinous principle in the present invention's (3) the electronic part encapsulation usefulness composition epoxy resin, with identical among the present invention (2) with the represented alicyclic diepoxy compound (A) of general formula (I).
Other Resins, epoxy (e) that optionally add in the employed alicyclic diepoxy compound (a) among the present invention (3), as long as contain the epoxy group(ing) more than 2 in its molecule at least, and molecular configuration, molecular weight etc. is not made special qualification, can directly use the employed Resins, epoxy of common encapsulating semiconductor.Particularly, with the invention described above (2) in enumerate in other Resins, epoxy of optionally adding identical.Other Resins, epoxy can mix use more than a kind or 2 kinds.
Optionally the content of other Resins, epoxy (e) of Tian Jiaing is 10~90 weight parts in total amount 100 weight parts of the represented alicyclic diepoxy compound (a) of above-mentioned general formula (I), is preferably 15~35 weight parts, more preferably 20~80 weight parts.
Below 10 weight parts, then unfavorable from cost consideration as the content of other Resins, epoxy (e) of optionally adding, as surpassing 90 weight parts, then the effect that causes of alicyclic diepoxy compound (a) diminishes.
As employed another neccessary composition solidifying agent (b) among the present invention (3), be that solidifying agent, phenol resin etc. can react with Resins, epoxy and its curing person is got final product so long as amine is solidifying agent, acid anhydrides, be not particularly limited.Particularly, for example, amine is aromatic diamines such as solidifying agent such as mphenylenediamine, diaminodiphenyl-methane, diamino diphenyl sulfone etc., acid anhydrides is solidifying agent such as maleic anhydride, anhydride phthalic acid, pyromellitic dianhydride etc., in addition, as phenolic resin curative, for example, can enumerate aralkyl resin, terpenes upgrading resol, Dicyclopentadiene (DCPD) upgrading resol, trisphenol propane etc. such as phenolic varnish type phenolic resin, cresols phenolic varnish type resin, p-Xylol upgrading resol, p-Xylol m-xylene upgrading resol, unqualified to them.Yet, consider rerum naturas such as water-intake rate, resol is that solidifying agent is preferred, wherein, phenol aralkyl resin is particularly preferred.
The proportioning of the alicyclic diepoxy compound (a) that above-mentioned formula (I) is represented and other Resins, epoxy (e) that optionally add and solidifying agent (b), functional group's equivalence ratio (epoxy group(ing)/functional group) is preferably 0.6~1.2 in its epoxy group(ing) and the solidifying agent in 0.5 to 2 scope.As equivalence ratio is below 0.5 or 2 when above, solidified cured article wet fastness, formability and electrology characteristic variation are unfavorable.
In addition, curing catalyst (c), so long as can promote the compound of the curing reaction of Resins, epoxy and solidifying agent to get final product, and be not particularly limited.For example, 1,8-diazabicylo (5,4,0) hendecene-7 amidine compounds such as (also representing sometimes) with DBU, organo phosphorous compoundss such as triphenylphosphine (also representing sometimes), tetraphenyl phosphine tetraphenyl boric acid ester with TPP, imidazolium compoundss such as glyoxal ethyline etc. limit especially to them.This curing catalyst can be used alone or as a mixture.Use level, the represented alicyclic diepoxy resin (a) of general formula (I) reaches other Resins, epoxy (e) of interpolation optionally and per 100 weight parts of total amount of solidifying agent (b), is preferably the scope of 0.4~20 weight part.When use level is 0.4 weight part when following, probably be difficult to obtain sufficient solidified nature during hot briquetting, on the other hand, when surpassing 20 weight parts, solidify too fast, because mobile reduction during moulding, it is bad probably can to produce filling, so be unfavorable.
In addition, as curing catalyst (c) composition in addition, can use the used inorganic filler of general sealing material (d).Particularly, for example broken silica powder of fusion, the spherical silica powder of fusion, crystalline silica powder, secondary aggegation silica powder, aluminum oxide, aluminium hydroxide, glass fibre etc., particularly the spherical silica of fusion is preferred.The shape of spherical silica is considered from the purpose that improves liquidity, and it is preferred limiting the use of spheroidal, and the wide person of particle size distribution is preferred.
The use level of inorganic filler (d), per 100 weight parts of total amount of the alicyclic diepoxy compound (a) that general formula (I) is represented and other Resins, epoxy (e) that optionally add and solidifying agent (b) are preferred in the scope of 200~2400 weight parts.When less than 200 weight parts, inorganic filler is difficult to fully present the effect of reinforcement, and as surpassing 2400 weight parts, the flowability of resin combination reduces and fills during moulding badly, and probably can produce lead distortion or broken string, is unfavorable.
The present invention's (3) electronic part encapsulation composition epoxy resin, except that (a)~(e) composition, can optionally suitably cooperate low-stress material such as tinting materials such as couplers such as inorganic ion exchanger, γ-glycidoxypropyltrime,hoxysilane, carbon black, red iron oxide, silicone oil, silicon rubber such as fire retardants such as brominated epoxy resin, weisspiessglanz, phosphorus series compound, bismuth oxide hydrate, various additives such as the sodium salt of releasing agents such as natural wax, synthetic wax, higher fatty acid and metal-salt or paraffin, oxidation inhibitor, phosphoric acid and Tripyrophosphoric acid or sylvite again.
When manufacturing the present invention's (3) electronic part encapsulation is used composition epoxy resin, the alicyclic diepoxy compound (a) that general formula (I) is represented and other Resins, epoxy (e), solidifying agent, curing catalyst, lamellar compound, other inorganic filler and other the additive that optionally add, behind thorough mixing such as mixing tank, further carry out melt kneading, pulverize after the cooling with hot-rolling, kneader etc.In addition, at the electronic unit of sealing semiconductor original paper etc., when making semiconductor device, can seal by transmitting the methods of forming such as modulus method, compression modulus method, injection modulus method.
The present invention's (3) electronic part encapsulation composition epoxy resin, 65~200 ℃ of temperature, be preferably 75~190 ℃, more preferably under 80~180 ℃, be 30~600 minutes set time, be preferably 45~540 minutes, more preferably be cured in 60~480 minutes.
When solidification value and set time are lower than above-mentioned scope lower value, solidify insufficient, otherwise, if when higher, can produce the situation that resinous principle decomposes than above-mentioned range limit value, be not good.Condition of cure can be done suitable adjustment according to various conditions, and lacked set time when solidification value was high, and set time was long when solidification value was low.
Below, the present invention (4) is elaborated.
Employed epoxy compounds among the present invention (4) is as the represented alicyclic diepoxy compound of general formula (I), identical with general formula (I) alicyclic diepoxy compound used in the present invention (2) or (3).
Wherein, R in the general formula (I) particularly 1~R 18Be the alicyclic diepoxy compound of hydrogen atom, industrial can the manufacturing is preferred.
<proportioning 〉
The addition of the alicyclic diepoxy compound that the general formula (I) that uses among the present invention (4) is represented in the scope of 0.05~15 weight part, is preferably 0.5~10 weight part with respect to transformer oil composition 100 weight parts, more preferably 0.5~5 weight part.When after a little while than 0.05 weight part, do not catch the effect of impurity in the transformer oil composition or the dispersion effect of discharge energy, there is not the value of adding.Otherwise when surpassing 10 weight parts, the electrology characteristic of transformer oil reduces, and particularly electrical condenser etc. is unfavorable because of the dissipation loss of inside generates heat, the function of electrical condenser etc. reduces.
<the transformer oil composition that uses is illustrated
For example, polyoxyalkylene glycol and upgrading thing thereof, neopentyl polyol ester, dihydroxyl acid esters, polyester, fluoridize wet goods and be suitable for, use as the mixture more than a kind or a kind wherein.
This transformer oil composition is described particularly,, for example can enumerate polypropylene glycol, polyoxyethylene glycol, polyoxyethylene polypropylene glycol etc. as polyoxyalkylene glycol, wherein, preferred molecular weight 200~3000.Again, oxyethylene group in the polyoxyethylene polypropylene glycol and oxypropylene group both can be random shape and also can be block-wise.
Upgrading thing as polyoxyalkylene glycol, can use the polyoxyalkylene glycol monoalky lether, the polyoxyalkylene glycol dialkyl ether, the poly suboxygen alkyl diol monoester, the polyoxyalkylene glycol diester, the epoxide affixture of Alkylenediamine etc., particularly, the ether of the straight or branched alkyl of above-mentioned polyoxyalkylene glycol and carbonatoms 1~18, the ester of the aliphatic carboxylic acid of carbonatoms 2~18 or quadrol, diethyl triamine, the propylene oxide adduct of triethyl tetramine, ethylene oxide adduct, the random affixture of oxyethane propylene oxide, oxyethane propylene oxide block affixture etc., in addition, can also enumerate polyoxyalkylene glycol glycerine three ethers, polyoxyalkylene glycol halogenide (particularly muriate) is as the modifier of above-mentioned polyoxyalkylene glycol.
As neopentyl polyol ester, can enumerate carbonatoms 2~18, be preferably the ester of the ester of the aliphatic carboxylic acid of carbonatoms 2~9 and amyl-based polyol or this aliphatic carboxylic acid and TriMethylolPropane(TMP), tetramethylolmethane, Dipentaerythritol, tripentaerythritol.
The dihydroxyl acid esters is preferably the ester of 1 grade or 2 grades alcohol of the dibasic carboxylic acid of carbonatoms 4~12 and carbonatoms 4~18, and concrete can enumerate, for example butyl phthalate, dihexyl phthalate etc.
As polyester, can enumerate that the spy opens flat 3-128991 communique, the spy opens the compound that flat 3-128992 communique etc. is put down in writing, for example by the divalent alcohol and/or the multivalence alcohol such as 3 valencys above multivalence alcohol of carbonatoms below 15 of 5~12 of carbonatomss, with the polyhydroxy-acid of 4~14 of 1 valency lipid acid of 2~18 of carbonatomss and/or carbonatomss and the polyester that constitutes.
As fluorinated oil, can enumerate the spy and open perfluor ether that flat 3-7798 communique puts down in writing etc.
In addition, in the present invention's (4) electrical isolation stabilizers, except that other represented alicyclic diepoxy compounds of above-mentioned general formula (I), in the present invention's (4) purpose scope, can add extreme-pressure additive according to hope, for example, oxidation inhibitor such as Tritolyl Phosphate or α-naphthalene benzylamine, thiodiphenylamine, BHT use in the scope of common addition.
Secondly, the present invention (5) is elaborated.
The present invention's (5) electrical isolation comprises the heat-curing resin that uses composition epoxy resin (A composition), acid anhydrides (B composition), the curing catalyst (C composition) contain specific epoxy compounds to be constituted with casting composition epoxy resin (hereinafter referred to as " casting composition epoxy resin "); And inanimate matter packing material (D composition) and constituting.
The above-mentioned composition epoxy resin (A composition) that contains specific epoxy compounds is by the represented alicyclic diepoxy compound (a-1) of general formula (I) and epoxy compounds in addition (a-2) thereof and constitute.
Above-mentioned alicyclic diepoxy compound (a-1), with used in the present invention (2)~(4) with represented identical of above-mentioned general formula (I), wherein, R especially 1~R 18For the hydrogen atom person, that is to say, employing dicyclohexyl-3,3 '-diepoxide is suitable.
The alicyclic diepoxy compound (a-1) that above-mentioned general formula (I) is represented and the cooperation ratio of epoxy compounds in addition (a-2) thereof, must be set at respectively: (a-1) be 5~80 weight % of whole composition epoxy resins (A composition) (following slightly be called " % "), be preferably 8~75 weight %, and be 95~20% (a-2), be preferably 92~25 weight %.
As the object lesson of (a-2), identical with other Resins, epoxy that optionally add in the invention described above (2)~(3).
Among the present invention (5), use 2 kinds of epoxy compoundss to constitute composition epoxy resin (A composition), therewith use acid anhydrides, curing catalyst, inanimate matter packing material, can not damage casting operation whereby, give cured article, thereby obtain electrical isolation casting composition epoxy resin with excellent electrology characteristic and mechanical characteristics as purpose.
The acid anhydrides (B composition) that uses simultaneously with above-mentioned composition epoxy resin (A composition), solidifying agent effect as above-mentioned composition epoxy resin (A composition), it is not particularly limited, can use above-mentioned known, i.e. cited acid anhydrides in the invention described above (2).
This acid anhydrides can also be used separately or more than 2 kinds.Wherein, consider that from excellent heat resistance, electrology characteristic and physical strength are high it is preferred using methyl six hydrogen anhydride phthalic acids, tetrahydrochysene anhydride phthalic acid, methyl norbornene dicarboxylic acids acid anhydride etc.
The cooperation ratio of above-mentioned acid anhydrides (B composition), with respect to containing the represented alicyclic diepoxy compound (a-1) of above-mentioned general formula (I) and (a-1) in addition composition epoxy resin (A composition) 1 equivalent of epoxy compounds (a-2), must be set in 0.6~1.0 normal scope.Be preferably 0.7~0.9 equivalent especially.That is, when the cooperation ratio of acid anhydrides surpassed 1.0 equivalents, electrology characteristic reduced, otherwise when less than 0.6 equivalent, thermotolerance reduces.Again, the equivalent (anhydride equivalent) of above-mentioned acid anhydrides (B composition) is set as follows.That is, be 1 equivalent during 1 of the anhydride group in the acid anhydrides, with respect to 1 epoxy group(ing) in the A composition.Therefore, above-mentioned cooperation ratio is 0.6~1.0 equivalent, above-mentioned with respect to containing (a-1) and (a-2) 1 epoxy group(ing) in the composition epoxy resin of 2 kinds of epoxy compoundss (A composition), and the acid anhydrides radix in the acid anhydrides is 0.6~1.0.
As the curing catalyst (C composition) that uses simultaneously with above-mentioned A composition and B composition, can enumerate tertiary amines such as benzyldimethylamine, three (dimethylamino) methylphenol, Triethylene Diamine; The alkoxide or the organometallic compounds such as methyl ethyl diketone, acetoacetate class of organic acid salt, triphenylphosphine, phosphoric acid ester, boric acid ester, Lewis acid, titanium or the aluminium of the bromine salt of quaternary amines such as four butyl bromation amine, diazabicylo hendecene (DBU) or DBU, imidazoles etc.They can also be used separately or more than 2 kinds.Particularly consider that from the excellent heat resistance of resulting cured article the bromine salt that uses above-mentioned tertiary amines and quaternary amine is preferred.
These commodity are called SA-102 (the diazabicylo hendecene is a curing catalyst), SA-506 (the diazabicylo hendecene is a curing catalyst), U-CAT5003 (phosphonium salt is a curing catalyst) [more than be サ Application ア プ ロ corporate system].
The use level of above-mentioned curing catalyst (C composition) adds up to 100 weight parts with respect to the composition epoxy resin (A composition) that is made of above-mentioned 2 kinds of epoxy compoundss, is set in the scope of 0.5~10 weight part.That is to say that when the use level of C composition was less than 0.5 weight part, curing reaction was slack-off, have the operation problem and produce, when surpassing 10 weight parts, the reaction times obviously accelerates, cause mobile reduction, and, the reduction of volume resistivity on electricity, probably also can be caused.
As with above-mentioned A~C composition simultaneously as (D) composition of neccessary composition, promptly the inanimate matter packing material can be enumerated silica, aluminum oxide, talcum powder, silica sand, lime carbonate, barium sulfate etc.It can also be used separately or more than 2 kinds.Consider that from tan δ and excellent this point of voltage-resistent characteristic use the spheroidal fused silica powder in the silica, the fused alumina in the aluminum oxide is preferred.That is to say,,, and get rid of the electric stress effect of concentrating and consider, can obtain the further effect that improves of dielectric loss tangent (tan δ) and voltage-resistent characteristic from inhibition interface split pole by adopting the spheroidal fused silica powder in the silica.When particularly using above-mentioned spheroidal fused silica, use the following particle of particle diameter 50 μ m to account for 99 all weight % above [essential condition (X)], and median size is the silica of 35 μ m following [essential condition (Y)], makes from preventing because viscosity rises all excellent casting composition epoxy resin of effect, electrology characteristic and physical strength of casting operation reduction considers it is preferred.In addition, fused alumina, generally speaking, with Bayer process (バ イ ヤ-) aluminum oxide or alumina as main raw material, the fusion of electricity consumption steam stove, through separating out, calcine, a succession of operation such as pulverizing, deferrization, washing, drying and obtaining, by using this fused alumina, same during with the above-mentioned fused silica of use, electrology characteristic and mechanical characteristics are all excellent, compare the effect that can be largely increased when particularly voltage-resistent characteristic is with the use fused alumina.
The use level of above-mentioned inanimate matter packing material (D), it is necessary that the electrical isolation that is set in the present invention (5) becomes the scope of 30~80 weight % of subtotaling amount with casting composition epoxy resin (A)~(D).That is to say that the use level of inanimate matter packing material (D) is 30% of not enough all compositions, electrical isolation of the present invention significantly reduces with the melt viscosity of casting composition epoxy resin, and sedimentation takes place inanimate matter packing material (D).And physical strength also can reduce.Otherwise,,, thereby probably can cause the reduction of operation because high viscosity can make Combination and flowability reduce as surpassing 80%.
Again, the present invention (5) electrical isolation is with in the casting composition epoxy resin, except above-mentioned A~C composition and (D) the inanimate matter packing material of composition, can optionally suitably cooperate and add other additive such as thinner, softening agent, pigment, releasing agent, fire retardant.
Therefore, be preparation the present invention's (5) electrical isolation casting composition epoxy resin, above-mentioned each raw material all with fixed ratio cooperation.Cooperation can be used known mixing machines such as dry type blending machine, banded blending machine, Henschel (Henschel) mixing tank, generally cooperates at normal temperature.
The title complex of above-mentioned each composition can be under heating under vacuum, continues behind the eliminating bubble to stir, mix, with preparation electrical isolation cast resin composition.Stirring, the temperature when mixing generally are set in 40~100 ℃.
As 40 ℃ of design temperature less thaies when preparing, because of high viscosity can't evenly stir, mixture operation is had any problem, otherwise, as the temperature when preparing surpasses 100 ℃ words, then producing curing reaction, can't obtain normal electrical isolation cast resin composition, is unfavorable.Stirring, when mixing, can use 1 or the machine of widespread uses such as multishaft extruder, kneader of band reliever.
So, with the electrical isolation of this preparation casting composition epoxy resin, inject in the fixed forming mould, be heating and curing under the fixed condition, be shaped to the present invention (5) cured article with anticipated shape.
The present invention's (5) electrical isolation casting composition epoxy resin can be preferably 100~190 ℃ 100~200 ℃ of temperature, and more preferably 100~180 ℃, be 30~600 minutes set time, is preferably 45~540 minutes, more preferably was cured in 60~480 minutes.
When solidification value and set time are lower than above-mentioned scope lower value, solidify insufficient, otherwise when higher than above-mentioned range limit value, resinous principle produces and decomposes, so, all undesirable.Condition of cure depends on various conditions, when solidification value is high set time short, when solidification value is low set time long, can do suitable adjustment.
Embodiment
The embodiment and the comparative example of<invention (1) 〉
Following embodiment is used to illustrate the present invention, and its scope does not have specific restriction.
Embodiment 1
The dicyclohexyl-3 of the alicyclic olefin compound that above-mentioned general formula (II) is represented, 3 '-diene 406 restrains, vinyl acetic monomer 1217 restrains in the reactor of packing into, nitrogen is sucked gas phase portion, and the temperature in the reaction system is controlled at 37.5 ℃, with about 3 hours, drip vinyl acetic monomer solution (moisture rate is 0.41 weight %) 457 grams of 30 weight % peroxyacetic acid.Peracetic acid solution makes reaction terminating in 40 ℃ of slakings in 1 hour after dripping and stopping.Wash at 30 ℃ of thick liquid during reaction terminating again, under 70 ℃/20mmHg, remove low-boiling compound, obtain epoxy compounds 415 grams.The rate of recovery is 85%.
The oxygen concn of the oxyethane of resulting epoxy compounds is 14.7 weight % (theoretical values: 16.5 weight %).
And, use 1HNMR measures, and can confirm that near the peak from internal double bonds δ 4.5~5ppm disappears, and near the proton peak from epoxy group(ing) δ 3.1ppm produces, and has confirmed that it is the represented alicyclic diepoxy compound of above-mentioned general formula (I).The NMR figure of resulting alicyclic epoxide compound as shown in Figure 1.
Embodiment 2
The dicyclohexyl-3 of the alicyclic olefin compound that above-mentioned general formula (II) is represented, 3 '-diene 243 restrains, vinyl acetic monomer 730 grams are packed into, nitrogen is blown into gas phase portion, and the temperature in the reaction system is controlled at 37.5 ℃, with about 3 hours, drip vinyl acetic monomer solution (moisture rate 0.41 weight %) 274 grams of 30 weight % peroxyacetic acid.After peracetic acid solution drips and stops, in 1 hour reaction terminating of 40 ℃ of slakings.Thick liquid when 30 ℃ of following washed reactions stop is removed low-boiling compound under 70 ℃/20mmHg again, obtains 270 gram epoxy compoundss.Its rate of recovery is 93%.
The oxyethane oxygen concn of resulting epoxy compounds is 15.3 weight %.
And, use 1HNMR measures, and can confirm that near the peak from internal double bonds δ 4.5~5ppm disappears, and near the proton peak from epoxy group(ing) δ 3.1ppm produces, and has confirmed as the represented alicyclic diepoxy compound of above-mentioned general formula (I).
Comparative example 1
The alicyclic olefin compound dicyclohexyl-3 that above-mentioned general formula (II) is represented, 3 '-diene 25 restrains, vinyl acetic monomer 20 grams are packed into, nitrogen is blown into gas phase portion, and the temperature in the reaction system is controlled under 60 ℃, dripped 30 weight % aqueous hydrogen peroxide solutions 36 with about 1 hour and restrain.After aqueous hydrogen peroxide solution drips and stops, stop at 12 hours afterreactions of 60 ℃ of slakings.
React thick liquid 1HNMR measures, and can confirm that the peak from internal double bonds does not disappear near δ 4.5~5ppm, does not observe the proton peak from epoxy group(ing) near δ 3.1ppm, and the represented alicyclic diepoxy compound of above-mentioned general formula (I) fails to synthesize.
Comparative example 2
The alicyclic olefin compound dicyclohexyl-3 that above-mentioned general formula (II) is represented, 3 '-diene 25 gram, benzene 135 grams, pack into as molybdenum pentachloride 0.07 gram of catalyzer, nitrogen is blown into gas phase portion, and the temperature in the reaction system is controlled under 80 ℃, with about 1 hour, drip benzole soln 120 grams of 30 weight % tert-butyl hydroperoxides.After the benzole soln of tert-butyl hydroperoxide drips and stops, at 80 ℃ of slakings 3 hours, reaction terminating.Thick liquid when 30 ℃ of following washed reactions stop is removed low-boiling compound under 70 ℃/20mmHg again, obtains epoxy compounds 25.3 grams.Its rate of recovery is 84.6%.
The oxyethane oxygen concn of resulting epoxy compounds is 12.6 weight %.
React thick liquid 1HNMR measures, and can confirm that the peak from internal double bonds disappears near δ 4.5~5ppm, also observes the proton peak from epoxy group(ing) near δ 3.1ppm, can confirm that it is the represented alicyclic diepoxy compound of above-mentioned general formula (I).But compare with 2 with embodiment 1, the rate of recovery of resulting alicyclic diepoxy compound is low, and has confirmed that the oxyethane oxygen concn is also low.
According to the present invention (1), with the represented alicyclic olefin compound of above-mentioned general formula (II), can be cheaply, the represented alicyclic diepoxy compound of good, the highly purified manufacturing general formula of the rate of recovery (I).
The embodiment and the comparative example of<invention (2) 〉
Embodiment 3
To make the composition viscosity that " サ Application エ イ De SI-60L " (light cationic polymerization initiators of sulfonium salt system) 0.6 weight part is fitted in as embodiment 1 resulting alicyclic diepoxy compound 100 weight parts of (A) composition, three new chemistry of conduct (B) composition, the E type rotational viscosimeter that uses Tokyo gauge company to make is determined as 50mPas under 25 ℃.
Above-mentioned resin combination, use TG/DTA device (the EXSTAR6000 TG/DTA 6200 that セ イ コ one イ Application ス Star Le メ Application Star company makes, down together) under the air ambient of per minute 200 ml, speed from 40 ℃ to 200 ℃ with 10 ℃ of per minutes heats up, and measures the temperature when heating makes resin combination volatilization or resin cured matter decomposition show that weight reduces.100 ℃ of weight that reduced is less than 0.5%, compares with starting weight, shows that the temperature that reduces by 5 weight % is 150.0 ℃.
Comparative example 3
With 100 weight parts 3,4-oxirane ring hexenyl methyl-3 ', 4 '-viscosity of the composition that oxirane ring hexenyl carboxylicesters [ダ イ セ Le chemical industry make " セ ロ キ サ イ De 2021P " (representing with CEL 202 1P in the table)] and 0.6 weight part " サ Application エ イ De SI-60L " are cooperated, use Tokyo gauge corporate system E type rotational viscosimeter is determined as 240mPas under 25 ℃.
Above-mentioned resin combination uses the TG/DTA device under the air ambient of per minute 200ml, is heated up by 40 ℃ to the 250 ℃ speed with 10 ℃ of per minutes, measures through heating to make the resin combination volatilization or resin cured matter is decomposed, the temperature when showing weight saving.100 ℃ of weight that reduced is less than 0.5%, compares with starting weight, and the temperature that demonstration weight reduces 5 weight % is 210.8 ℃.
Comparative example 4
With 3 of 100 weight part 6-caprolactone modifications, 4-oxirane ring hexenyl methyl-3, ' 4 '-viscosity of the composition that oxirane ring hexenyl carboxylic acid vinegar [ダ イ セ Le chemical industry system " セ ロ キ サ イ De 2081 " (representing with CEL 2081 in the table)] and 0.6 weight part " サ Application エ イ De SI-60L " are cooperated, use Tokyo gauge corporate system E type rotational viscosimeter under 45 ℃, to be determined as 90mPas.
Above-mentioned resin combination uses the TG/DTA device under the air ambient of per minute 200ml, is heated up by 40 ℃ to the 250 ℃ speed with 10 ℃ of per minutes, measures the temperature when heating makes the resin combination volatilization or make the resin cured matter decomposition show weight saving.100 ℃ of weight that reduced is less than 0.5%, compares with starting weight, and the temperature that demonstration weight reduces 5 weight % is 233.4 ℃.
Comparative example 5
Cooperate 0.6 weight part, three new chemistry to make the composition viscosity of " サ Application エ イ De SI-60L " 100 weight part limonene diepoxides [ダ イ セ Le chemical industry system " セ ロ キ サ イ De 3000 " (representing with CEL 3000 in the table)], use Tokyo gauge corporate system E type rotational viscosimeter under 25 ℃, to be determined as 20mPas.
Above-mentioned resin combination uses the TG/DTA device under the air ambient of per minute 200ml, is heated up by 40 ℃ to the 120 ℃ speed with 10 ℃ of per minutes, measures through heating resin combination volatilization or resin cured matter are decomposed, and shows the temperature of weight saving.100 ℃ of weight that reduced is below 8.3%, compares with starting weight, and the temperature that demonstration weight reduces 5 weight % is 96.2 ℃.
Comparative example 6
Epoxidation 3-tetrahydrobenzene-1 with 100 weight part 6-caprolactone modifications, the two 3-cyclohexenyl methyl esters (ダ イ セ Le chemical industry system " エ Port リ one De GT301 ") of 2-dicarboxylic acid cooperate the viscosity of the composition of 0.6 weight part, three new chemistry systems " サ Application エ イ De SI-60L ", use Tokyo gauge corporate system E type rotational viscosimeter to be determined as 300mPas under 75 ℃.
Above-mentioned resin combination uses the TG/DTA device under the air ambient of per minute 200ml, is heated up by 40 ℃ to the 280 ℃ speed with 10 ℃ of per minutes, measures through heating to make resin combination volatilization or resin cured matter decompose the temperature when showing weight saving.100 ℃ of weight that reduced is less than 0.5%, compares with starting weight, and the temperature that demonstration weight reduces 5 weight % is 247.9 ℃.
Comparative example 7
Cooperate 0.6 weight part, three new chemistry to make the viscosity of the composition of サ Application エ イ De SI-60L epoxidation butanetetra-carboxylic acid four-3-cyclohexenyl methyl esters (ダ イ セ Le chemical industry system " エ Port リ one De GT403 ") of 100 weight part 6-caprolactone modifications, use Tokyo gauge corporate system E type rotational viscosimeter under 75 ℃, to be determined as 800mPas.
Above-mentioned resin combination uses the TG/DTA device under the air ambient of per minute 200ml, and the speed from 40 ℃ to 280 ℃ with 10 ℃ of per minutes heats up, and measures through heating resin combination volatilization or resin cured matter are decomposed, and shows the temperature of weight saving.100 ℃ of weight that alleviated is less than 0.5%, compares with starting weight, and the temperature that demonstration weight reduces by 5 weight % is 253.7 ℃.
Table 1
Embodiment 3 Comparative example 3 Comparative example 4 Comparative example 5 Comparative example 6 Comparative example 7
Dicyclohexyl-3,3 '-epoxide 100 parts
CEL 2021P 100 parts
CEL 2081 100 parts
CEL 3000 100 parts
エ Port リ one De GT301 100 parts
エ Port リ one De GT403 100 parts
サンエイドSI-60L 0.6 part 0.6 part 0.6 part 0.6 part 0.6 part 0.6 part
Viscosity (mPas, 25 ℃) 50 240 20
Viscosity (mPas, 45 ℃) 90
Viscosity (mPas, 75 ℃) 300 800
Weight saving ratio at 100 ℃ Less than 0.5 % Less than 0.5 % Less than 0.5 % 8.30% Less than 0.5 % Less than 0.5%
5% heat decomposition temperature (℃) 150.0 210.8 233.4 96.2 247.9 253.7
Operation in room temperature × ×
Operational security, formability ×
Table 1 on the cooperation of each composition composition and resulting the results are shown in embodiment 3 and comparative example 3~7.
Expressed by last table 1, the viscosity of resin combination is low among the embodiment 3, and is very excellent aspect operation.The viscosity of the resin combination of comparative example 5 is also low, and so the weight when heating reduces greatlyyer, and heat decomposition temperature is low to moderate 96.2 ℃, and thermotolerance is insufficient.In addition, the heat decomposition temperature height of comparative example 6 and 7 resin combination, excellent heat resistance, too high at 75 ℃ down during heating because of viscosity, consider from formability, be inadequate.
Embodiment 4
Making resin combination as the 0.3 weight part サ Application エ イ De SI-60L that cooperates conduct (B) composition in embodiment 1 resulting alicyclic diepoxy compound 100 weight parts of (A) composition (three new chemistry systems).For measuring the reactivity of resin combination, use RAPRA corporate system sweep type vibration pin type solidity test machine SVNC (scanning VNC) to measure.Main condition determination is that the initial setting of equipment therefor is that (Dwell=250ms, Frequency Filter=50Hz, Amplitude Pilter=250 StopTime=1:0hrs:mins), measure down in 80 ℃.Heat up 3 minutes approximately to measuring temperature, begin to measure when reaching 80 ℃.The resonant frequency that begins to measure is during for about 66Hz, and the curing of resin combination is along with the variation of resonant frequency number, record in addition when reaching about 100Hz.Its result is 22 minutes and 51 seconds.
Comparative example 8
To 100 weight part ダ イ セ Le chemistry system セ ロ キ サ イ De 2021P (representing with CEL 2021P in the table), cooperate 0.3 weight part SI-100L (the sulfonium salt cation polymerization starters of three new chemistry systems), constitute resin combination.For measuring the reactivity of resin combination, use RAPRA corporate system sweep type vibration pin type solidity test machine SVNC (scanning VNC) to measure.Main condition determination is that the initial setting of equipment therefor is (Dwell=250ms, Frequency Filter=50Hz, AmplitudeFilter=250, Stop Time=1:0 hrs:mins), measures down in 80 ℃.Heated up about 3 minutes, and reached when measuring 80 ℃ of temperature and begin to measure.The resonant frequency number that begins to measure is about 66Hz, is accompanied by the curing of resin combination, and the resonant frequency number changes, and record reaches the time of about 100Hz.Its result is 50 minutes 49 seconds.
The cooperation of each composition composition and resulting result are as shown in table 2 below in embodiment 4 and the comparative example 8.
Table 2
Embodiment 4 Comparative example 8
Dicyclohexyl-3,3 '-epoxide 100 parts
CEL 2021P 100 parts
サンエイド 60L 0.3 part 0.3 part
Reach the time of SVNC100Hz 22 minutes 51 seconds 50 minutes 49 seconds
Reactivity to cationic catalyst
Can know significantly that by above-mentioned table 2 reactivity of resin combination is excellent more than 2 times than the resin combination in the comparative example 8 among the embodiment 4.
Embodiment 5
With respect to embodiment 1 resulting alicyclic diepoxy compound 100 weight parts as (A) composition, cooperate 0.6 weight part サ Application エ イ De SI-60L (three new chemistry systems) as (B) composition, make resin combination.The viscosity of composition uses Tokyo gauge corporate system E type rotational viscosimeter to be determined as 50mPas under 25 ℃.About 10 gram resin combinations are injected the aluminium vessel of diameter 54mm, dark 15mm, behind one-step solidification (35 ℃ of solidification values, 5 hours set times), then regelate (150 ℃ of solidification values, 1 hour set time) can obtain water white resin cured matter.
The line exapnsion rate of resin cured matter is measured according to JIS K 7197, and the extrapolation point that line exapnsion rate is changed is as second-order transition temperature.Cut out 2 samples from identical casting thing, by measuring glass transition point under 40 ℃ to 400 ℃ the scope, the variation of line exapnsion rate can't confirm that second-order transition temperature is very high, can't confirm.
Resin combination is to use the TG/DTA device under the air ambient of per minute 200ml, speed from 40 ℃ to 400 ℃ with 10 ℃ of per minutes heats up, mensuration makes the resin combination volatilization show the temperature that weight reduces through heating, compare with starting weight, show that temperature was 272.6 ℃ when weight reduced by 3 weight %, show that the temperature when reducing by 5 weight % is 288.1 ℃.
Embodiment 6
With respect to embodiment 1 resulting alicyclic diepoxy compound 100 weight parts as (A) composition, cooperate methyl six hydrogen anhydride phthalic acids (new Japanese physics and chemistry system as (C) composition, リ カ シ Star De MH-700) 139.1 weight parts and as ethylene glycol 1 weight part of initiator, as the DBU (1 of curing catalyst, 8-diazabicylo (5,4,0) 0.5 weight part hendecene) constitutes resin combination.The viscosity of said composition uses Tokyo gauge corporate system E type rotational viscosimeter to be determined as 60mPas at 25 ℃.With the aluminium vessel of 10 gram resin combinations injection diameter 54mm, dark 15mm, behind the one-step solidification (110 ℃ of solidification values, 2 hours set times), then regelate (150 ℃ of solidification values, 1 hour set time) obtains water white resin cured matter.
The line exapnsion rate of resin cured matter is measured according to JIS K 7197, and the extrapolation point that line exapnsion rate is changed is as second-order transition temperature.Cutting out 2 samples from identical casting thing, measure glass transition point under 40 ℃ to 400 ℃ scope, is 120.4 ℃.
Resin cured matter is to use the TG/DTA device under the air ambient of per minute 200ml, and the speed from 40 ℃ to 400 ℃ with 10 ℃ of per minutes heats up, and measures through the heating resin cured matter and decomposes, and shows the temperature that weight reduces.
With original comparing, the temperature that demonstration weight reduces by 3 weight % is 197.9 ℃, shows that the temperature that 5 weight % reduce is 231.7 ℃.
Embodiment 7
With respect to embodiment 1 resulting alicyclic diepoxy compound 100 weight parts as (A) composition, cooperate the リ カ シ Star De MH-700139.1 weight part made as the new Japanese physics and chemistry of (C) composition and as ethylene glycol 1 weight part of initiator, as the DBU (1 of curing catalyst, 8-diazabicylo (5,4,0) hendecene) 0.5 weight part is made resin combination.The viscosity of composition uses Tokyo gauge corporate system E type rotational viscosimeter to be determined as 60mPas under 25 ℃.10 gram resin combinations are injected the aluminium vessel of diameter 54mm, dark 15mm, behind the one-step solidification (110 ℃ of solidification values, 2 hours set times), then regelate (180 ℃ of solidification values, 1 hour set time) can get water white resin cured matter.
The line exapnsion rate of resin cured matter is measured according to JIS K 7197, and the extrapolation point that line exapnsion rate is changed is as second-order transition temperature.Cutting out 2 samples from identical casting thing, measure glass transition point from 40 ℃ to 400 ℃ scopes, is 121.0 ℃.
Resin cured matter is to use the TG/DTA device under the air ambient of per minute 200ml, and the speed from 40 ℃ to 400 ℃ with 10 ℃ of per minutes heats up, and measures through heating resin cured matter is decomposed, and shows the temperature that weight reduces.
With original comparing, the temperature that demonstration weight reduces by 3 weight % is 223.0 ℃, shows that the temperature that 5 weight % reduce is 253.9 ℃.
Embodiment 8
With respect to embodiment 1 resulting alicyclic diepoxy compound 100 weight parts as (A) composition, cooperate as the new Japanese physics and chemistry system リ カ シ Star De MH-700 of 139.1 weight parts of (C) composition and as ethylene glycol 1 weight part, the DBU (1 of initiator, 8-diazabicylo (5,4,0) hendecene) 0.5 weight part is made resin combination.The viscosity of composition uses Tokyo gauge corporate system E type rotational viscosimeter to be determined as 60mPas under 25 ℃.10 gram resin combinations are injected the aluminium vessel of diameter 54mm, dark 15mm, behind one-step solidification (120 ℃ of solidification values, 1 hour set time), then regelate (180 ℃ of solidification values, 2 hours set times) obtains water white resin cured matter.
The line exapnsion rate of resin cured matter is measured according to JIS K 7197, and the extrapolation point that line exapnsion rate is changed is as second-order transition temperature.Cutting out 2 samples from identical casting thing, measure glass transition point under 40 ℃ to 400 ℃ scope, is 205.4 ℃.
Resin cured matter uses the TG/DTA device under the air ambient of per minute 200ml, and the speed from 40 ℃ to 400 ℃ with 10 ℃ of per minutes heats up, and measures through heating resin cured matter is decomposed, and shows the temperature when weight reduces.
With original comparing, the temperature that demonstration weight reduces by 3 weight % is 223.6 ℃, shows that the temperature that 5 weight % reduce is 270.8 ℃.
Comparative example 9
100 weight part ダ イ セ Le chemistry system セ ロ キ サ イ De 2021P (representing with CEL 2021P in the table) are cooperated 0.6 weight part SI-100L (three new chemistry systems), make resin combination.The viscosity of composition uses Tokyo gauge corporate system E type rotational viscosimeter to be determined as 240mPas under 25 ℃.10 gram resin combinations are injected the aluminium vessel of diameter 54mm, dark 15mm, through one-step solidification (because temperature can't solidify below 60 ℃ the time, so solidification value is 65 ℃.2 hours set times) after, then regelate (150 ℃ of solidification values, 1 hour set time) obtains transparent resin cured matter.
The line exapnsion rate of resin cured matter is measured according to JIS K 7197, and the extrapolation point that line exapnsion rate is changed is as second-order transition temperature.Cut out 2 samples from identical casting thing, measuring glass transition point under 40 ℃ to 400 ℃ the scope is 159.8 ℃.
Resin cured matter is to use the TG/DTA device under the air ambient of per minute 200ml, and the speed from 40 ℃ to 400 ℃ with 10 ℃ of per minutes heats up, and measures through heating resin cured matter is decomposed, and weight shows the temperature when reducing.
Compare with starting weight, weight shows that the temperature that reduces by 3 weight % is 217.5 ℃, shows that the temperature that 5 weight % reduce is 257.5 ℃.
Comparative example 10
To 100 weight part ダ イ セ Le chemistry system セ ロ キ サ イ De 2021P (representing with CEL 2021P in the table), cooperate new Japanese physics and chemistry system リ カ シ Star De MH-700 139.1 weight parts and ethylene glycol 1 weight part, DBU (1,8-diazabicylo (5,4,0) hendecene) 0.5 weight part is made resin combination.The viscosity of composition uses Tokyo gauge corporate system E type rotational viscosimeter to be determined as 110mPas under 25 ℃.
10 gram resin combinations are injected diameter 54mm, dark 15mm aluminium vessel, behind one-step solidification (120 ℃ of solidification values, 1 hour set time), then regelate (180 ℃ of solidification values, 2 hours set times) obtains water white resin cured matter.
The line exapnsion rate of resin cured matter is measured according to JIS K 7197, and the extrapolation point that line exapnsion rate is changed is as second-order transition temperature.Cut out 2 samples from identical casting thing, measuring glass transition point under 40 ℃ to 400 ℃ the scope is 221.5 ℃.
Resin cured matter is to use the TG/DTA device under the air ambient of per minute 200ml, and the speed from 40 ℃ to 400 ℃ with 10 ℃ of per minutes heats up, and measures through heating resin cured matter is decomposed, and weight shows the temperature when reducing.
Compare with starting weight, weight shows that the temperature that reduces by 3 weight % is 294.9 ℃, and the temperature when reducing by 5 weight % is 304.8 ℃.
The cooperation of each composition composition and resulting result are as shown in table 3 below in embodiment 5~8 and the comparative example 9~10.
Table 3
Embodiment 5 Embodiment 6 Embodiment 7 Embodiment 8 Comparative example 9 Comparative example 10
Dicyclohexyl-3,3 '-the diene diepoxide 100 parts 100 parts 100 parts 100 parts
CEL 2021P 100 parts 100 parts
サンエイドSI-60L 0.6 part 0.6 part
MH-700 139.1 part 139.1 part 139.1 part 139.1 part
Ethylene glycol
1 part 1 part 1 part 1 part
DBU 0.5 part 0.5 part 0.5 part 0.5 part
Viscosity 50mPa·s 60mPa·s 60mPa·s 60mPa·s 240mPa·s 110mPa·s
The one-step solidification condition 35 ℃, 5 hours 110 ℃, 2 hours 110 ℃, 2 hours 120 ℃, 1 hour 65 ℃, 2 hours 120 ℃, 1 hour
The regelate condition 150 ℃, 1 hour 150 ℃, 1 hour 150 ℃, 1 hour 180 ℃, 2 hours 150 ℃, 1 hour 180 ℃, 2 hours
Second-order transition temperature (℃) Can't observe with TMA, DSC 120.4 121.0 205.4 159.8 221.5
3% heat decomposition temperature (℃) 272.6 197.9 223 233.6 217.5 294.9
5% heat decomposition temperature (℃) 288.1 231.7 263.9 270.8 257.5 304.8
Thermotolerance × ×
Can know obviously that by above-mentioned table 3 glass transition point of cured article is high to measuring among the embodiment 5, compares to know being excellent with the comparative example 9 that is carried out under the similar condition.And the viscosity of composition is all low than comparative example 9 and 10 among the embodiment 5~8, handles more or less freely as can be known.
The represented alicyclic diepoxy compound of formula (1) as resinous principle (A) necessary in the curable epoxy resin composition of the present invention (2), owing to do not contain ester group at intramolecularly, cationic catalyst is shown high reactivity, therefore, reduce the necessary solidification value of curing of composition, have the effect that shortens set time.
The present invention (2) low viscosity is handled the curable epoxy resin composition of easy alicyclic diepoxy compound as neccessary composition, various solidifying agent are had hyperergy, low viscosity and excellent in workability.And, pair few advantage of operating environment influence is also arranged.
This curable epoxy resin composition solidifies the cured article that obtains, and compares with the situation of using Resins, epoxy to solidify the cured article that obtains, and the transparency, thermotolerance etc. show very superperformance in the past.And this cured article is comprising the rerum natura that shows one's usefulness aspect purposes such as coating, printing ink, tackiness agent, seal gum, sealing material various.
The embodiment and the comparative example of<invention (3) 〉
With each components matching, mixing, the preparation formed material, and for the purpose of its evaluating characteristics, measure its eddy flow, solidify moment of torsion, water-intake rate.The mensuration of each characteristic and condition, as described below.
1. eddy flow
With the formed material after the preparation,, use eddy flow to measure and use mould, at 175 ℃ of die temperatures, injection pressure 70kgf/cm according to EMMI-I-66 2, measure down 2 minutes set times.Eddy flow (cm) is mobile parameter, and numerical value is bigger, and the expression flowability better.
2. curing moment of torsion
The formed material that use is mixed with uses Q-Lars spy (キ ユ ラ ス ト) meter (オ リ エ Application テ Star Network (strain) system, the special meter in JSR Q-Lars, PS type), is determined at 175 ℃, the moment of torsion of heating after 45 seconds.The torque value (kgfcm) that adopts the special meter in Q-Lars to record is the solidified nature parameter, and this value is bigger, and solidified nature better.
3. water-intake rate
Use the transfer molding machine at 175 ℃ of die temperatures, injection pressure 75kg/cm 2, 2 minutes set times condition under, be shaped to the circle version of diameter 50mm, thick 3mm, 175 ℃ solidified in 8 hours after, dipping is 24 hours in 23 ℃ of distilled water, measures changes in weight in the hope of water-intake rate (weight %).
Embodiment 9
According to the following proportioning of note, mix each composition, and use hot-rolling 95 ℃ mixing 8 minutes, after the cooling, the resin combination that obtains pulverizing.Evaluation result is as shown in table 4.
Gradation composition comprises: as embodiment 1 resulting alicyclic diepoxy compound 5 weight parts of (a) composition, the conduct of Tian Jiaing optionally (e) composition with biphenyl type epoxy resin as the resin of main component [the cresols phenolic resin varnish type epoxy resin EOCN-1020 that Japanese chemical drug limited-liability company makes, epoxy equivalent (weight) 185,105 ℃ of fusing points] 95 weight parts, resol [the resol PR-53195 that ベ one Network ラ イ ト (strain) in Sumitomo makes as (b) composition, hydroxyl equivalent 167,73 ℃ of softening temperatures] 51.8 weight parts, as 1 of (c) composition, 8-diazabicylo (5,4,0) hendecene-7 (DBU) 1.2 weight parts, fusion spherical silica (median size 15 μ) 725 weight parts, carbon black 2 weight parts, carnauba wax 2 weight parts.
Embodiment 10~13
Adopt each cooperation shown in the table 4 to form, operation is mixed with formed material similarly to Example 9.Evaluation result is as shown in table 4.
Comparative example 11~12
Adopt each proportioning shown in the table 4 (continuing), operation similarly to Example 9, the preparation formed material is estimated respectively.Evaluation result is shown in table 4 (continuing).
Table 4
Embodiment 9 Embodiment 10 Embodiment 11 Embodiment 12 Embodiment 13
The epoxy compounds of embodiment 1 5 30 60
The epoxy compounds of embodiment 2 20 75
EOCN-1020 95 70 40 80 25
PR-53195 51.8 64.8 79.7 60.5 90.7
DBU 1.2 1.0 1.4
TPP 0.9 0.9
The spherical silica of fusion 725 787 880
Broken shape silica 802 950
Carbon black 2 2 2.5 2 2.5
Carnauba wax 2 2 2.5 2 2.5
Eddy flow 102 120 132 125 130
Solidify moment of torsion 100 114 127 115 132
Water-intake rate (%) 0.22 0.20 0.28 0.24 0.29
EOCN-1020: Japanese chemical drug limited-liability company makes, the cresols phenolic resin varnish type epoxy resin
RP-53195: the resol that ベ one Network テ イ ト (strain) in Sumitomo makes;
DBU:1,8-diazabicylo (5,4,0) hendecene-7
TPP: triphenylphosphine
Table 4 (continuing)
Comparative example 11 Comparative example 12
CEL-2021P 5 25
ECON-1020 95 75
PR-53195 52.9 58.8
DBU 1.26
TPP 0.79
The spherical silica of fusion 765
Broken shape silica 711
Carbon black 2 2
Carnauba wax 2 2
Eddy flow 111 114
Solidify moment of torsion 108 120
Water-intake rate (%) 0.57 0.89
Can obviously know by table 4, the words that use the present invention's (3) electronic part encapsulation compares with cured article among the resulting embodiment 10~13 of composition epoxy resin and the cured article among the comparative example 11-12, show the low water absorption value, very excellent as electronic part encapsulation with composition epoxy resin.
And, can know obviously by the eddy flow value that in table 4 the present invention (3) the electronic part encapsulation composition epoxy resin that uses the represented alicyclic diepoxy compound (a) of general formula (I) is mobile good, that is, and the formability excellence.
The embodiment and the comparative example of<invention (4) 〉
Sample 1 (the cooperation base oil 1 in the table 5): polypropylene glycol diacetate esters (molecular weight 3000, kinetic viscosity is 9.8cSt in the time of 100 ℃)
Sample 2 (the cooperation base oil 2 in the table 5): the mixture of 2-Methyl Butyric Acid and caproic acid (mol ratio=1: 1) and the full ester of tetramethylolmethane (100 ℃ time kinetic viscosity be 4.2cSt).
Embodiment 14~16, comparative example 13~17
In model, add organic acid, prepare the electric insulation oil of composition as shown in table 5 after, get per 500 grams and pack in the beaker, on one side 60 ℃ of following heated and stirred, get sample measurement acid number after a while on one side.The result is as shown in table 6, and the acid number of each embodiment lowers sharp.
Again, cooperate the initial stage acid number of base oil, sample 1 is 0.02, and sample 2 is 0.01.
Embodiment 17~21, comparative example 18~21
Moreover, composition shown in the table 7 is packed in the SUS-316 type autoclave, in 150 ℃ of heating 10 days in air.Kinetic viscosity (cSt of unit), acid number (mgK0H/ gram) after the evaluation heat test.
Oxidation stability is measured according to JIS C2101-93.
Table 5
Cooperate base oil Additive The addition of epoxy Organic acid Organic acid addition (weight %)
Embodiment 14 1 The epoxy of embodiment 1 3 Acetic acid 3
Embodiment 15 2 The epoxy of embodiment 1 3 Caproic acid 3
Embodiment 16 2 The epoxy of embodiment 2 3 Caproic acid 5
Comparative example 13 1 Epoxidised soybean oil 3 Acetic acid 3
Comparative example 14 2 Epoxidised soybean oil 3 Caproic acid 3
Comparative example 15 2 Phenyl glycidyl ether 3 Caproic acid 3
Comparative example 16 1 The diepoxide of vinyl cyclohexene 3 Acetic acid 3
Comparative example 17 2 セロキサイド2021 3 Acetic acid 3
The epoxy compounds of comparative example 13~14 uses epoxidised soybean oil ( イ マ Star Network S-300, ダ イ セ Le chemical industry system).
Comparative example 15 uses phenyl glycidyl ether.
セ ロ キ サ イ ト 2021 is 3 of ダ イ セ Le chemical industry Co., Ltd. system in the comparative example 17,4-epoxycyclohexyl methyl (3, the 4-epoxycyclohexane carboxylate).
Table 6
Acid number (mgK0H/g) after adding Acid number after 2 hours Acid number after 6 hours Acid number after 12 hours
Embodiment 14 1.98 0.86 0.13 0.05
Embodiment 15 1.06 0.32 0.10 0.02
Embodiment 16 1.22 0.50 0.21 0.05
Comparative example 13 1.91 0.85 0.51 0.24
Comparative example 14 1.39 1.10 0.82 0.35
Comparative example 15 1.23 0.64 0.50 0.38
Comparative example 18 1.90 0.50 0.21 0.02
Comparative example 19 1.88 0.79 0.48 0.18
Table 7
Figure C0381894900401
Figure C0381894900411
セ ロ キ サ イ De 2021 is 3 of ダ イ セ Le chemical industry limited-liability company manufacturing in the comparative example 21,4-epoxycyclohexyl methyl (3, the 4-epoxycyclohexane carboxylate).
Shown in table 5~7, the present invention's (4) insulation stabilizers, the represented alicyclic diepoxy compound of general formula (I) and add its electric insulation oil just, the acid number number is low, can improve the transformer oil characteristic.
The embodiment and the comparative example of<invention (5) 〉
At first, prepare following alicyclic diepoxy compound (a-1) and Resins, epoxy (a-2), acid anhydrides 1~2, curing catalyst 1~2, inanimate matter packing material 1~2.
Alicyclic diepoxy compound (a-1) uses resulting alicyclic diepoxy compound among the embodiment 1, and epoxy compounds (a-2) uses following Resins, epoxy 2~4.
Resins, epoxy 2:CEL-2021P (3,4-epoxycyclohexyl methyl-3,4-epoxycyclohexyl carboxylicesters, ダ イ セ Le chemical industry system)
Resins, epoxy 3:YD-128 (Dongdu changes into manufacturing, bisphenol A type epoxy resin, epoxy equivalent (weight) 190, viscosity 13600mPas/25 ℃)
Resins, epoxy 4:HBE-100 (new Japanese physics and chemistry manufacturing, hydrogenation bisphenol-A diglycidyl ether type epoxy resin, epoxy equivalent (weight) 210, viscosity 2210mPas/25 ℃)
[acid anhydrides 1] methyl six hydrogen anhydride phthalic acids (trade(brand)name リ カ シ Star De MH-700: new Japanese physics and chemistry company makes)
[acid anhydrides 2] methyl norbornene dicarboxylic acids acid anhydride (trade(brand)name HNA: new Japanese physics and chemistry company makes)
[curing catalyst 1] ethylene glycol
[curing catalyst 2] DBU (diazabicylo hendecene)
[inanimate matter packing material 1] globular fused silica (the following particle of median size 50 μ m is more than all 99 weight %)
[inanimate matter packing material 2] fused alumina (the following particle of median size 50 μ m is more than all 99 weight %)
Embodiment 17~24, comparative example 22~25
Each composition shown in the following table 8~table 9, cooperate with the ratio shown in the table, (3~5Torr) use " THINKY makes, and the chestnut bird is practiced too youth AR-100 " to mix, to obtain insulativity casting composition epoxy resin under about 25 ℃ temperature decompression.And, use above-mentioned insulativity casting composition epoxy resin, by casting method forming and hardening, make the moulded products of the shape that formalizes.Again, in table 8~table 9, the use level of each composition is all represented with weight part separately.
Table 8
Embodiment 17 Embodiment 18 Embodiment 19 Embodiment 20 Embodiment 21 Embodiment 22 Embodiment 23 Embodiment 24
Resins, epoxy a-1 50 20 10 50 20 20 75 40
Resins, epoxy 2 50 80 90
Resins, epoxy 3 50 80
Resins, epoxy 4 80 25 60
Acid anhydrides 1 132 123 114 50 94 44 126 108
Acid anhydrides 2 63 40
Curing catalyst 1 2.3 2.2 2.1 2.1 1.9 1.8 2.3 2.1
Curing catalyst 2 2.3 2.2 2.1 2.1 1.9 1.8 2.3 2.1
Weighting agent 1 (weight % in the composition) 220 (52.7) 220 (54.0) 220 (50.9)
Weighting agent 2 (weight % in the composition) 150 (38.8) 150 (39.7) 200 (47.8) 300 (58.0) 300 (56.5)
Table 9
Comparative example 22 Comparative example 23 Comparative example 24 Comparative example 25
Resins, epoxy a-1
Resins, epoxy 2 5
Resins, epoxy 3 100 95
Resins, epoxy 4 5 100 95
Acid anhydrides 1 81 77 69 71
Acid anhydrides 2 1.8 1.8 1.7 1.7
Curing catalyst 1 1.8 1.8 1.7 1.7
Weighting agent 1 220 220
Weighting agent 2 300 300
The embodiment electrical isolation of the gained like this composition epoxy resin of casting composition epoxy resin and comparative example, under the fixed condition (140 ℃ * 2 hours+170 ℃ * 10 hours) with electrology characteristic (the dielectric loss tangent of solidified cured article, specific inductivity), mechanical characteristics (flexural strength) and second-order transition temperature (Tg), each test conditions shown in following is measured down.The result is shown in table 10~table 11.Again, following each test is to be tried to achieve by the mean value of 5 sample numbers.
Table 10
Embodiment 17 Embodiment 18 Embodiment 19 Embodiment 20 Embodiment 21 Embodiment 22 Embodiment 23 Embodiment 24
Dielectric loss tangent (%) 0.2 0.3 0.2 0.2 0.3 0.2 0.3 0.3
Specific inductivity (ε) 3.5 4.0 4.1 4.1 4.0 3.8 3.2 4.2
Flexural strength (kg/mm 2) 20 21 23 21 22 20 18 19
Tg(℃) 241 230 218 215 175 170 218 183
Table 11
Comparative example 22 Comparative example 23 Comparative example 24 Comparative example 25
Dielectric loss tangent (%) 0.3 0.4 0.3 0.3
Specific inductivity (ε) 5.7 5.4 4.9 4.8
Flexural strength (kg/mm 2) 17 16 14 15
Tg(℃) 148 142 129 152
[dielectric loss tangent and specific inductivity]
Main electrode and lead electrode on every side thereof, counter electrode, forming on the face He on another face by electrically conducting coating respectively, to make the sample of thickness 1mm * diameter 60mm.And this sample adopts transformer electrode method to measure electrical capacity and electric conductivity value respectively and (measures frequency number: 50Hz), and obtain dielectric loss tangent (tan δ) and specific inductivity (ε) by its result according to following formula in thermostatic bath under 100 ℃.
Dielectric loss tangent (tan δ)=Gx/2 π fCx
Specific inductivity (ε)=Cx/C 0
Cx: the capacitance value during bridge-balance (pF)
C 0: the electrostatic capacitance amount (pF) of calculating ε=1 by the area and the sample thickness of main electrode
Gx: the electric conductivity value of sample (S)
F: measure frequency number (Hz)
[flexural strength]
Make the sample of wide 10mm * long 100mm * thick 4mm,,, try to achieve the maximum load of bending when breaking in central authorities pressurizations applying load at the two supports of interval 64mm.
[Tg (second-order transition temperature: ℃)]
Make the sample of size 5 * 5 * 10mm, dimensional change and mapping when measuring with 5 ℃ of/minute intensifications with hot exapnsion assay method (セ イ コ-イ Application ス Star Le メ Application ト company makes, thermo-mechanical analysis device TMA/SS6100).And, try to achieve second-order transition temperature (Tg) from the displacement point of hot exapnsion rate.
From the result of table 10 and table 11 as can be known, solidify the cured article of the present invention's (5) electrical isolation with casting composition epoxy resin gained, its flexural strength and Tg height, and specific inductivity is low, has tangible excellent specific property.
Utilize possibility on the industry
From specific alicyclic diolefin compound, can cheapness and the good represented alicyclic diepoxy compound of the highly purified above-mentioned general formula of manufacturing (I) of yield. The curable epoxy resin composition that is consisted of by this alicyclic diepoxy compound and curing agent etc., when the solidfied material through solidifying gained is compared with the solidfied material that uses epoxy resin cure gained in the past, the performance that showing transparency property, heat resistance etc. are very good, this solidfied material can be used for the purposes such as coating, printing ink, adhesive, fluid sealant, encapsulant. And this curable epoxy resin composition also is useful with casting composition epoxy resin and electronic part encapsulation with composition epoxy resin as electric insulation. And this alicyclic diepoxy compound is also useful as the electric insulation stabilizers.

Claims (1)

1. the manufacture method of an alicyclic diepoxy compound of representing with general formula I,
Figure C038189490002C1
In the formula, R 1~R 18Both can distinguish identical also can be different, it is hydrogen atom, halogen atom or can contains the alkyl of Sauerstoffatom or halogen atom or can contain substituent alkoxyl group, it is characterized in that,
(i) the alicyclic diolefin compound that following general formula I I is represented is through peroxyacetic acid epoxidation in addition,
(ii) peracetic acid obtains by come the corresponding aldehyde of oxidation with oxygen, and has the following water-content of 0.8 weight %,
(iii) peracetic acid is the solution in vinyl acetic monomer,
(iv) epoxidised temperature of reaction is 20~70 ℃,
(, add 1.0~3.0 moles peracetic acid v) with respect to 1 mole of the unsaturated group of the alicyclic diolefin compound of representing with general formula I I.
CNB038189496A 2002-09-05 2003-09-04 Process for preparation of alicyclic diepoxy compounds, curable epoxy resin compositions, epoxy resin compositions for the encapsulation of electronic components, stabilizers for electrical insulating Expired - Lifetime CN100404519C (en)