CN100393910C - 镁合金表面柠檬酸盐化学转化膜处理溶液 - Google Patents
镁合金表面柠檬酸盐化学转化膜处理溶液 Download PDFInfo
- Publication number
- CN100393910C CN100393910C CNB2006100405395A CN200610040539A CN100393910C CN 100393910 C CN100393910 C CN 100393910C CN B2006100405395 A CNB2006100405395 A CN B2006100405395A CN 200610040539 A CN200610040539 A CN 200610040539A CN 100393910 C CN100393910 C CN 100393910C
- Authority
- CN
- China
- Prior art keywords
- citrate
- oxalate
- conversion film
- water
- chemical conversion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种柠檬酸盐化学转化膜,属于金属表面处理技术领域。其特征在于处理溶液组分及各组分的重量百分比为:柠檬酸盐:10-15%,草酸盐5-10%,有机醇:1-5%,有机胺:1-5%,水:75-80%。其中所述的柠檬酸盐为柠檬酸铵、柠檬酸钠中的一种,所述的草酸盐为草酸钾、草酸钛钾中的一种,所述的有机醇为三乙醇胺、丙三醇中的一种,所述的有机胺为苯胺、邻苯二胺中的一种,所述的水为蒸馏水、去离子水中的一种。本发明采用柠檬酸盐溶液,因而溶液的分散能力和深度能力均高于酸性溶液电镀黄铜,其通过开发研究的新的配方,很好的利用化学试剂的化学特性而且降低了成本,提高了效率。
Description
技术领域
本发明涉及的是一种镁合金表面化学转化膜处理溶液,特别是一种柠檬酸盐环保型化学转化膜处理溶液,属于表面处理技术领域。
背景技术
镁合金在各种腐蚀介质中很容易腐蚀。通常用表面处理或合金化的方法提高其耐蚀性。镁合金表面化学转化膜处理是为了保障其在空气介质下有一定的耐蚀性,同时提高其表面的油漆附着力。柠檬酸盐化学转化膜层处理的原理是镁合金表面在柠檬酸盐的溶液中发生反应,形成一层柠檬酸盐化合物,附着在其表面,达到防护的目的。专利00118832.1与200510200038.4分别叙述了一种镁合金表面处理溶液的配方,但前者配方含有磷化物,会对环境造成污染,尤其是有机磷化物对环境的污染十分严重;后者配方用高锰酸钾不但对环境造成污染,而且要求在零下摄氏度冷却的苛刻条件。
发明内容
本发明针对以上的不足,提供一种环保型柠檬酸盐化学转化膜处理溶液。本发明利用化学试剂的化学特性,降低了成本,提高了效率,且这种转化膜的配方适合几乎所有的镁合金化学转化膜处理工艺。
本发明是通过以下技术方案实现的:
本发明所述柠檬酸盐化学转化膜处理溶液组分及各组分的重量百分比为:柠檬酸盐:10-15%,草酸盐5-10%,有机醇:1-5%,有机胺:1-5%,水:75-80%;
所述的柠檬酸盐为柠檬酸铵、柠檬酸钠中的一种,所述的草酸盐为草酸钾、草酸钛钾中的一种,所述的有机醇为三乙醇胺、丙三醇中的一种,所述的有机胺为苯胺、邻苯二胺中的一种,所述的水为蒸馏水,去离子水中的一种。
以下对本发明工艺作进一步的说明,具体内容如下:
首先配制转化膜层处理溶液,在一个槽中取2/3的水,分别溶解柠檬酸盐和草酸盐,槽中试剂全部溶解之后,将有机醇和有机胺先后在快速搅拌下倒入槽液中,直至完全混合均匀,最后加水至计算体积。
本发明具有实质性特点和显著进步,本发明采用柠檬酸盐溶液,因而溶液的分散能力和深镀能力较好,其通过开发研究的配方,很好的利用化学试剂的化学特性而且降低了成本,提高了效率。
具体实施方式
结合本发明技术方案提供以下实施例:
实施例1
首先在一个10L槽中取2/3的蒸馏水,依次溶解1500g柠檬酸钠和800g草酸钾,等槽中试剂全部溶解之后,将100mL三乙醇胺和100mL邻苯二胺在快速搅拌下倒入槽液中,直至完全混合均匀,最后加水至10L。
实施例2
首先在一个10L槽中取2/3的去离子水,依次溶解的1200g柠檬酸铵和1000g草酸钛钾,等槽中试剂全部溶解之后,将200mL丙三醇和100mL苯胺在快速搅拌下倒入槽液中,直至完全混合均匀,最后加水至10L。
实施例3
首先在一个10L槽中取2/3的蒸馏水,依次溶解1000g柠檬酸铵和600g草酸钛钾,等槽中试剂全部溶解之后,将300mL丙三醇和500mL邻苯二胺在快速搅拌下倒入槽液中,直至完全混合均匀,最后加水至10L。
Claims (1)
1.镁合金表面柠檬酸盐化学转化膜处理溶液,其特征在于各组分的重量百分比为:柠檬酸盐:10-15%,草酸盐5-10%,有机醇:1-5%,有机胺:1-5%,水:75-80%;其中所述的柠檬酸盐为柠檬酸铵、柠檬酸钠中的一种,所述的草酸盐为草酸钾、草酸钛钾中的一种,所述的有机醇为三乙醇胺、丙三醇中的一种,所述的有机胺为苯胺、邻苯二胺中的一种,所述的水为蒸馏水、去离子水中的一种。