CN100392149C - 含可溶性淀粉的磷化液及其制备方法 - Google Patents

含可溶性淀粉的磷化液及其制备方法 Download PDF

Info

Publication number
CN100392149C
CN100392149C CNB2006100191004A CN200610019100A CN100392149C CN 100392149 C CN100392149 C CN 100392149C CN B2006100191004 A CNB2006100191004 A CN B2006100191004A CN 200610019100 A CN200610019100 A CN 200610019100A CN 100392149 C CN100392149 C CN 100392149C
Authority
CN
China
Prior art keywords
soluble starch
phosphatization liquid
component
added
starch
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2006100191004A
Other languages
English (en)
Other versions
CN1851047A (zh
Inventor
陈纪纲
钟汉珍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan University of Technology WUT
Original Assignee
Wuhan University of Technology WUT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan University of Technology WUT filed Critical Wuhan University of Technology WUT
Priority to CNB2006100191004A priority Critical patent/CN100392149C/zh
Publication of CN1851047A publication Critical patent/CN1851047A/zh
Application granted granted Critical
Publication of CN100392149C publication Critical patent/CN100392149C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明含可溶性淀粉的磷化液，按总体积为1L计，其组成比例为：可溶性淀粉0.5～5g/L、成膜剂11～15g/L、H3PO438～45g/L、促进剂50～70g/L、络合剂3.5～8g/L、缓冲剂3～7g/L、水余量。其制备方法为：按上述的组成比例配料；将ZnO投入反应容器中，加入少量水调成糊状，加入磷酸，再加入促进剂、络合剂、缓冲剂形成组分一；将可溶性淀粉加入余量水中，加热到70～85℃并搅拌直至完全溶解，冷却至室温，形成组份二；将组份二加入到组份一中，充分搅拌均匀即可。本发明的磷化液添加可溶性淀粉作为稳定剂，通过改变溶液性质提高磷化液使用过程中的稳定性，提高磷化膜质量。

Description

含可溶性淀粉的磷化液及其制备方法
技术领域
本发明涉及金属表面处理技术领域。特别是涉及用于钢铁漆前表面处理的含可溶性淀粉的磷化液及其制备方法。
背景技术
钢铁零件在含有锌、锰、钙、铁或碱金属磷酸盐溶液中进行化学处理，在其表面形成一层不溶于水的磷酸盐膜的过程，称为磷化处理。磷化处理在机械、化工、汽车、船舶、航空航天及家用电器等行业有广泛的应用。
在磷化液的使用过程中，由于工厂工况条件及原材料的纯度不同，磷化液中会含有一些有害杂质或金属盐，造成磷化液的使用稳定性较差，从而也造成了工件磷化处理的质量不同。
发明内容
本发明所要解决的技术问题是：提供一种含可溶性淀粉的磷化液及其制备方法，以克服现有技术存在的不足。
本发明按下述技术方案解决其技术问题：
本发明提供的含可溶性淀粉的磷化液，按总体积为1L计，其组成比例为：可溶性淀粉0.5～5g/L、成膜剂11～15g/L、H3PO438～45g/L、促进剂50～70g/L、络合剂3.5～8g/L、缓冲剂3～7g/L、水余量。其中，成膜剂为ZnO，促进剂为Zn(NO3)2、NaNO2或KClO3，络合剂为EDTA。
本发明提供的含可溶性淀粉的磷化液，其制备步骤如下：
(1)配料：按上述的含可溶性淀粉的磷化液组成比例配料。
(2)制备：将ZnO投入反应容器中，加入少量水调成糊状，加入磷酸，再加入促进剂、络合剂、缓冲剂形成组分一；将可溶性淀粉加入余量水中，加热到70～85℃并搅拌直至完全溶解，冷却至室温，形成组份二；将组份二加入到组份一中，充分搅拌均匀即可。
本发明在磷化液中添加可溶性淀粉作为稳定剂，通过改变溶液性质提高磷化液使用过程中的稳定性，提高磷化膜质量，从而提高了工件磷化处理的质量。本发明提供的含可溶性淀粉的磷化液，其制备工艺简单，便于推广。
具体实施方式
本发明提供的是一种含可溶性淀粉的磷化液，按总体积为1L计，其组成比例为：可溶性淀粉0.5～5g/L、成膜剂11～15g/L、H3PO438～45g/L、促进剂50～70g/L、络合剂3.5～8g/L、缓冲剂3～7g/L、水余量。其中，成膜剂为ZnO，促进剂为Zn(NO3)2、NaNO2或KClO3，络合剂为EDTA。
本发明提供的含可溶性淀粉的磷化液，其制备步骤如下：
(1)配料：按上述的含可溶性淀粉的磷化液组成比例配料。
(2)制备：将ZnO投入反应容器中，加入少量水调成糊状，加入磷酸，再加入促进剂、络合剂、缓冲剂形成组分一；将可溶性淀粉加入余量水中，加热到70～85℃并搅拌直至完全溶解，冷却至室温，形成组份二；将组份二加入到组份一中，充分搅拌均匀即可。
下面结合具体实例对本发明磷化液的组成作进一步说明。
实施例1：
按总体积为1L计，本发明磷化液的组成比例为：可溶性淀粉1.5g/L，ZnO11g/L，H3PO438g/L，Zn(NO3)250g/L，EDTA4g/L，水杨酸3g/L，水余量。
实施例2：
按总体积为1L计，本发明磷化液的组成比例为：可溶性淀粉3g/L，ZnO12g/L，H3PO439g/L，NaNO250g/L，EDTA3.5g/L，酒石酸3g/L，水余量。
实施例3：
按总体积为1L计，本发明磷化液的组成比例为：可溶性淀粉4g/L，ZnO11g/L，H3PO438g/L，Zn(NO3)250g/L，EDTA6g/L，水杨酸3g/L，水余量。
实施例4：
按总体积为1L计，本发明磷化液的组成比例为：可溶性淀粉5g/L，ZnO11g/L，H3PO438g/L，KClO370g/L，EDTA7g/L，柠檬酸3.5g/L，水余量。
实施例5：
按总体积为1L计，本发明磷化液的组成比例为：可溶性淀粉0.5g/L，ZnO15g/L，H3PO445g/L，NaNO260g/L，EDTA8g/L，草酸8g/L，水余量。
实施例6：
按总体积为1L计，本发明磷化液的组成比例为：可溶性淀粉0.5g/L，ZnO15g/L，H3PO445g/L，NaNO260g/L，EDTA8g/L，水杨酸2g/L，草酸6g/L，水余量。
实施例7：
实验表明，可溶性淀粉在磷化液中以3～4g/L为最佳。按总体积为1L计，本发明磷化液的组成优化配比为：可溶性淀粉3.5g/L，ZnO13g/L，H3PO440g/L，NaNO250g/L，EDTA7g/L，柠檬酸4g/L，水余量。
本发明中所用的原材料均为市购品。
本发明含可溶性淀粉的磷化液在使用时，其使用工艺流程包括：脱脂、水洗、除锈、水洗、表面调整、水洗、磷化(浸渍法)、水洗、后处理和干燥。

Claims (4)

1.一种磷化液，含有成膜剂、H3PO4、促进剂、络合剂和缓冲剂，其特征是添加了可溶性淀粉，构成一种含可溶性淀粉的磷化液，其组成比例为：按总体积为1L计，可溶性淀粉0.5～5g/L、成膜剂11～15g/L、H3PO438～45g/L、促进剂50～70g/L、络合剂3.5～8g/L、缓冲剂3～7g/L、水余量，
上述的组成中，成膜剂为ZnO，促进剂为Zn(NO3)2、NaNO2或KClO3，络合剂为EDTA。
2.根据权利要求1所述的磷化液，其特征是：缓冲剂为有机酸。
3.根据权利要求2所述的磷化液，其特征是：有机酸为草酸、酒石酸、水杨酸、柠檬酸中的一种，或多种混合物。
4.如权利要求1、2或3所述的磷化液的制备方法，其特征是按下述步骤制备含可溶性淀粉的磷化液：
(1)配料：按上述的含可溶性淀粉的磷化液组成比例配料，
(2)制备：
将ZnO投入反应容器中，加入少量水调成糊状，加入磷酸，再加入促进剂、络合剂、缓冲剂形成组分一；将可溶性淀粉加入余量水中，加热到70～85℃并直至完全溶解，冷却至室温，形成组份二；将组份二加入到组份一中，充分搅拌均匀即可。
CNB2006100191004A 2006-05-18 2006-05-18 含可溶性淀粉的磷化液及其制备方法 Expired - Fee Related CN100392149C (zh)