CN100378187C - 聚合物速效防水胶 - Google Patents
聚合物速效防水胶 Download PDFInfo
- Publication number
- CN100378187C CN100378187C CNB2004100168136A CN200410016813A CN100378187C CN 100378187 C CN100378187 C CN 100378187C CN B2004100168136 A CNB2004100168136 A CN B2004100168136A CN 200410016813 A CN200410016813 A CN 200410016813A CN 100378187 C CN100378187 C CN 100378187C
- Authority
- CN
- China
- Prior art keywords
- waterproof glue
- weight part
- agent
- waterproof
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种多用途速效防水胶,其组成配方重量百分比为:苯丙乳液或纯丙乳液45~60,无机分散剂0.1~0.2,有机分散剂0.1~0.2,消泡剂0.1~0.3,普通硅酸盐水泥30~40,重质碳酸钙5~15,水泥速凝剂0.1~1。按照上述配比范围配制成液、粉两组份,在使用时候后搅拌混合均匀后,涂覆在施工基面上,能以较快速度凝固成具有高拉伸强度、高潮湿基面粘结强度,且有相当断裂延伸性的弹性防水涂膜。此外该速效防水胶又能作为粘结剂,粘结瓷砖、地砖和聚苯乙烯发泡保温板,效果十分明显。
Description
技术领域
本发明涉及一种聚合物速效防水胶。
背景技术
目前常见的聚合物水泥基防水涂料(简称“JS”涂料)是建设部推荐产品,该产品采用有机材料(合成高分子乳液)与无机材料(水泥)复配而成,使用时安全卫生,无刺激性气味,属环保型产品,因此在住宅建筑中的卫生间、厨房及地下室隔潮层均采用它作为防水层。然而该涂料在施工时一次涂层不能太厚,否则涂膜在干燥固化时会开裂,因此要达到规定厚度(1~1.5mm),工程需2~3天才能完工。所以从施工速度方面它不如反应固化型的聚氨酯涂料,存在施工周期较长的不足。
发明内容
本发明目的在于提供一种聚合物速效防水胶,可弥补常见聚合物水泥基防水涂料施工周期较长的不足。
本发明的任务是这样实现的:
其采用添加水泥速凝剂制成的快凝快固特种水泥代替了一般“JS”涂料均采用的普通水泥,从而使产品从水份挥发固化型转化为具有强水化活性的反应固化型,从而赋予产品不仅可以根据需要调节固化速度,同时可厚涂,一度施工即可达到要求厚度,且不会开裂,拉伸强度和潮湿基面的粘结强度均超过“JS”涂料,同时作特殊需要,它可作为防水层又可作为粘结剂,满足聚苯乙烯泡沫保温板的铺贴要求。
本发明的内容如下述:
原材料介绍:
1.合成乳液:可以是苯丙乳液,也可以是纯丙乳液
2.无机分散剂:磷酸盐分散剂,为三聚磷酸钠,六偏磷酸钠
3.有机分散剂:聚丙烯酸铵盐分散剂,也可是聚羧酸钠盐分散剂
4.消泡剂:含硅疏水型消泡剂
5.普通硅酸盐水泥:型号为325#、425#等
6.重质碳酸钙:400目以上
7.水泥速凝剂:711型速凝剂(粉剂),它是由铝钒土、纯碱、生石灰组成,是
一种市场销售普遍的一种水泥助剂
本发明的产品分为甲、乙两组分包装,使用时混合使用,配方范围如下:
①苯丙乳液或纯丙乳液 45~60(重量份)
②无机分散剂 0.1~0.2(重量份)
③有机分散剂 0.1~0.2(重量份)
④消泡剂 0.1~0.3(重量份)
⑤普通硅酸盐水泥 30~40(重量份)
⑥重质碳酸钙 5~15(重量份)
⑦水泥速凝剂 0.1~1(重量份)
按上述配方比例称取原材料,将①②③④混合配成甲液料组分,将⑤⑥混合配成乙粉料组分,使用时将两组分掺混。在使用时候后搅拌混合均匀后,涂覆在施工基面上,能以较快速度凝固成具有高拉伸强度、高潮湿基面粘结强度,且有相当断裂延伸性的弹性防水涂膜。此外该聚合物速效防水胶又能作为粘结剂,粘结瓷砖、地砖和聚苯乙烯发泡保温板,效果十分明显。
经上海市建筑材料及构件质量监督检验站测试结果如下:
检验结果汇总 | ||||
检验项目名称及单位 | 本产品技术指标 | 检验结果 | 单项判定 | |
外观 液体组份固体组份 | 无杂质、无凝胶的均匀乳液无杂质、无结块的粉末 | 无杂质、无凝胶的均匀乳液无杂质、无结块的粉末 | 合格合格 | |
潮湿面粘结强度,MPa | ≥0.5 | 1.1 | 合格 | |
不透水性 | 0.3MPa,30min,不透水 | 不透水 | 合格 | |
固体含量,% | ≥70 | 87 | 合格 | |
拉伸强度无处理,MPa热处理后保持率,%碱处理后保持率,% | ≥1.8≥80≥70 | 2.5135121 | 合格合格合格 | |
断裂伸长率无处理,MPa热处理后保持率,%碱处理后保持率,% | ≥120≥65≥80 | 1399085 | 合格合格合格 | |
干燥时间,h | 表干≤2,实干≤4 | 表干≤2,实干≤4 | 合格 | |
说明 | 1.以上检验项目是全性能检验;2.配比:液粉∶粉料=1∶0.8 |
将本产品的检验结果与中华人民共和国建材行业标准中的聚合物水泥防水涂料标准比较如下:
检验项目名称及单位 | 产品技术指标 | 本产品检验结果 | 单项判定 |
潮湿面粘结强度,MPa | ≥0.5 | 1.1 | 合格合格 |
不透水性 | 0.3MPa,30min,不透水 | 不透水 | 合格 |
固体含量,% | ≥65 | 87 | 合格 |
拉伸强度无处理,MPa热处理后保持率,%碱处理后保持率,% | ≥1.8≥80≥80 | 2.5135121 | 合格 |
断裂伸长率无处理,MPa热处理后保持率,%碱处理后保持率,% | ≥80≥65≥65 | 1399085 | 合格合格合格 |
干燥时间,h | 表干≤4,实干≤8 | 表干≤2,实干≤4 | 合格合格 |
由上述数据比较可见,本产品的各项检验结果均优于有关行业标准的相关各项指标,且其干燥时间仅为标准中的一半,能够有效地到达速效防水的目的。
具体实施方式:
本发明具体实施例见表(含量为重量百分比):
Claims (1)
1.一种速效防水胶,其特征在于配方为:
①苯丙乳液或纯丙乳液45~60(重量份)
②无机分散剂 0.1~0.2(重量份)
③有机分散剂 0.1~0.2(重量份)
④消泡剂 0.1~0.3(重量份)
⑤普通硅酸盐水泥 30~40(重量份)
⑥重质碳酸钙 5~15(重量份)
⑦水泥速凝剂 0.1~1(重量份)
将①②③④混合配成甲液料组分,将⑤⑥⑦混合配成乙粉料组分,使用时将两组分掺混。