CN100374264C - 秸秆纤维的制备方法 - Google Patents

秸秆纤维的制备方法 Download PDF

Info

Publication number
CN100374264C
CN100374264C CNB2006100968249A CN200610096824A CN100374264C CN 100374264 C CN100374264 C CN 100374264C CN B2006100968249 A CNB2006100968249 A CN B2006100968249A CN 200610096824 A CN200610096824 A CN 200610096824A CN 100374264 C CN100374264 C CN 100374264C
Authority
CN
China
Prior art keywords
fiber
separation
fibre
crude separation
crop straw
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2006100968249A
Other languages
English (en)
Other versions
CN1944010A (zh
Inventor
周定国
梅长彤
徐咏兰
张洋
周哓燕
徐信武
华毓坤
潘明珠
李晓平
李良真
谢崇界
李冉
朱培志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Forestry University
Original Assignee
Nanjing Forestry University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Forestry University filed Critical Nanjing Forestry University
Priority to CNB2006100968249A priority Critical patent/CN100374264C/zh
Publication of CN1944010A publication Critical patent/CN1944010A/zh
Application granted granted Critical
Publication of CN100374264C publication Critical patent/CN100374264C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明是秸秆纤维制备方法及其应用，将农作物秸秆原料经粗磨机使秸秆单元在常温常压下粗分离，加入稻壳和亚硫酸钠，然后加温、加压细分离，使农作物秸秆粗分离的纤维顺利进入水平蒸煮器，选择适合于农作物秸秆纤维分离的磨片，经热磨机热磨达到形态完整均匀要求纤维，用于制造高中密度纤维板、软质板和保温纤维的原料。优点：由于采用二步法分离，并在二步分离间加入稻壳，使混合原料的摩擦力增加，使农作物秸秆粗分离的纤维顺利进入水平蒸煮器，形成密闭体，不易产生反喷；并加入0.5-1.5%亚硫酸钠，使秸秆纤维和稻壳混合物料在100-150℃更容易软化分离；用复合型磨片齿形的热磨机内热磨，热磨出来的纤维达到形态完整均匀的要求。应用于制造高中密度纤维板、软质板和保温纤维板。

Description

秸秆纤维的制备方法
技术领域
本发明涉及的是一种可以应用于农作物秸秆高中密度纤维板、软质板和保温纤维工业化生产的秸秆纤维制备方法，属于人造板制造领域。
背景技术
目前，由于各国对环境及森林资源的保护，木材工业的不断发展和国外一些国家对木材资源出口的限制，使木材原料价格不断上涨，一些人造板企业因原料不足或原料价格过高而停工。为了解决这些问题，利用我国丰富的农作物秸秆资源(如稻草和麦秸等)为原料生产高中密度纤维板、软质板和保温纤维，可以缓减人造板厂木材原料不足或价格过高的问题。实现高中密度纤维板、软质板工业化生产关键技术是如何分离合格的秸秆纤维，因此，需要设计出应用于高中密度纤维板、软质板和保温纤维工业化生产的分离农作物秸秆纤维方法。现有技术的分离只是针对木材原料，经过削片机加工成木片、然后经筛选机筛选去除过细的碎料后送入热磨机内，一般软化温度160-180℃，磨片齿形只适合木材原料。
发明内容
本发明的目的是提供一种适合于高中密度纤维板、软质板和保温纤维工业化生产的秸秆纤维的制备方法。
本发明的技术解决方案：秸秆纤维的制备方法，具体工艺步骤分一、常温常压粗分离，将农作物秸秆原料经过粗磨机使秸秆单元在常温常压下粗分离；二、加温加压细分离，在常温常压粗分离的秸秆纤维中加入占农作物秸秆原料总重量20％左右的稻壳，使农作物秸秆粗分离的纤维顺利进入水平蒸煮器，形成密闭体(木塞)，并加入化学添加剂亚硫酸钠，其加入量为秸秆纤维总量的0.5-1.5％。混合原料通过水平蒸煮器，使其软化。水平蒸煮器内温度为100-150℃，压力0.1-0.5Mpa软化时间1-3min，选择适合于农作物秸秆纤维分离的磨片，经热磨机的磨室体中的由斜齿、直齿复合而成的复合型磨片齿形的热磨，热磨温度保持在100-150℃，使热磨出来的纤维达到形态完整均匀要求，用于制造高中密度纤维板、软质板和保温纤维的原料。
本发明的优点：农作物秸秆粗纤维在加入0.5-1.5％亚硫酸钠和加温加压下，纤维之间原来具有的天然粘接力下降，有助于利用较小的研磨压力(不容易损伤纤维形态)就可以使农作物秸秆粗纤维分离成最终要求的纤维。加入20％左右的稻壳，使混合原料的摩擦力增加，使农作物秸秆粗分离的纤维顺利进入水平蒸煮器，形成密闭体，不易产生反喷；加入0.5-1.5％亚硫酸钠，使秸秆纤维和稻壳混合物料在100-150℃更容易软化分离。经热磨机的磨室体中的由斜齿、直齿复合而成的复合型磨片齿形的热磨，热磨出来的纤维达到形态完整均匀的要求。可以用于制造高中密度纤维板、软质板和保温纤维。
具体实施方式
实施例1，秸秆纤维的制备方法，具体工艺步骤分一、常温常压粗分离，将农作物秸秆原料经过粗磨机使秸秆单元在常温常压下粗分离；二、加温加压细分离，在常温常压粗分离的秸秆纤维中加入占农作物秸秆原料总重量15％的稻壳，增加混合原料的摩擦力，使农作物秸秆粗分离的纤维顺利进入水平蒸煮器，形成密闭体(木塞)，不易产生反喷；同时加入1.5％亚硫酸钠，使秸秆纤维和稻壳混合物料更容易软化分离；水平蒸煮器内软化温度100℃，压力0.1Mpa，软化时间1min，选择适合于农作物秸秆纤维分离的磨片，经热磨机的磨室体中的由斜齿、直齿复合而成的复合型磨片齿形的热磨，热磨温度保持在100℃，使热磨出来的纤维达到形态完整均匀要求，用于制造高中密度纤维板、软质板和保温纤维的原料。
实施例2，秸秆纤维的制备方法，具体工艺步骤分一、常温常压粗分离，将农作物秸秆原料经过粗磨机使秸秆单元在常温常压下粗分离；二、加温加压细分离，在常温常压粗分离的秸秆纤维中加入占农作物秸秆原料总重量20％的稻壳，增加混合原料的摩擦力，使农作物秸秆粗分离的纤维顺利进入水平蒸煮器，形成密闭体(木塞)，不易产生反喷，同时加入0.5％亚硫酸钠，使秸秆纤维和稻壳混合物料更容易软化分离；水平蒸煮器内软化温度150℃，压力0.5Mpa，软化时间1min，选择适合于农作物秸秆纤维分离的磨片，经热磨机的磨室体中的由斜齿、直齿复合而成的复合型磨片齿形的热磨，热磨温度保持在150℃，使热磨出来的纤维达到形态完整均匀要求，用于制造高中密度纤维板、软质板和保温纤维的原料。
实施例3，秸秆纤维的制备方法，具体工艺步骤分一、常温常压粗分离，将农作物秸秆原料经过粗磨机使秸秆单元在常温常压下粗分离；二、加温加压细分离，在常温常压粗分离的秸秆纤维中加入占农作物秸秆原料总重量25％的稻壳，增加混合原料的摩擦力，使农作物秸秆粗分离的纤维顺利进入水平蒸煮器，形成密闭体(木塞)，不易产生反喷，同时加入1.5％亚硫酸钠，使秸秆纤维和稻壳混合物料更容易软化分离；水平蒸煮器内软化温度135℃，压力0.3Mpa，软化时间2min，选择适合于农作物秸秆纤维分离的磨片，经热磨机的磨室体中的由斜齿、直齿复合而成的复合型磨片齿形的热磨，热磨温度保持在135℃，使热磨出来的纤维达到形态完整均匀要求，用于制造高中密度纤维板、软质板和保温纤维的原料。

Claims (1)

1.秸秆纤维的制备方法，其特征是它的具体工艺步骤分为一、常温常压粗分离，将农作物秸秆原料经过粗磨机使秸秆单元在常温常压下粗分离；二、加温加压细分离，在常温常压粗分离的秸秆纤维中加入占农作物秸秆原料总重量20％左右的稻壳，使农作物秸秆粗分离的纤维顺利进入水平蒸煮器，形成密闭体，并加入0.5-1.5％亚硫酸钠，使秸秆纤维和稻壳混合物料在100-150℃更容易软化分离；水平蒸煮器内软化温度100-150℃，压力0.1-0.5Mpa，软化时间1-3min，选择适合于农作物秸秆纤维分离的磨片，经热磨机的磨室体中的由斜齿、直齿复合而成的复合型磨片齿形的热磨，热磨温度保持在100-150℃，使热磨出来的纤维达到形态完整均匀要求。
CNB2006100968249A 2006-10-19 2006-10-19 秸秆纤维的制备方法 Expired - Fee Related CN100374264C (zh)