CN100358948C - 环保改性沥青 - Google Patents
环保改性沥青 Download PDFInfo
- Publication number
- CN100358948C CN100358948C CNB2004100614902A CN200410061490A CN100358948C CN 100358948 C CN100358948 C CN 100358948C CN B2004100614902 A CNB2004100614902 A CN B2004100614902A CN 200410061490 A CN200410061490 A CN 200410061490A CN 100358948 C CN100358948 C CN 100358948C
- Authority
- CN
- China
- Prior art keywords
- materials
- present
- asphalt
- rubber
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种环保改性沥青，其原料配方的重量百分比为：10#～60#石油沥青 45%～70%；旧轮胎橡胶 12%～35%；废弃润滑油 10%～25%； 生漆 0.5%～3；%；桐油 0.5%～3%；松节油 1%～5%；本发明的改性沥青，可作道路路面、水泥混凝土(含砖混)构筑物的嵌缝用料，作屋面、地下工程、仓库、水池等防水、防潮层施工用料及其它用石油沥青配料的产品用料。由于用部分废弃物替代高价原料，不仅降低了成本，且有利于环保，充分利用资源。
Description
技术领域
本发明涉及建筑材料沥青。
背景技术
沥青用途广泛，除了用于防水等场合外，筑路所需沥青占了所有沥青用量的一大部分。但单纯的建筑石油沥青存在很多缺奌，例如易老化、抗水剥离性差、抗低温裂性差等。建筑10#石油沥青的针入度、延度都很低，软化奌却很高。目前已出现了许多改性沥青，其中最为常见的有加入橡胶、树脂等原料生产的改性沥青。现有的改性沥青虽然克服了纯沥青的许多不足之处，使沥青的使用范围大为增加，但一般价格偏高，而且制作改性沥青大多只考虑如何使产品具有更好的性能，而很少考虑如何能更好地利用废物、保护环境。
发明内容
本发明要解决的技术问题是提供一种利用部分对环境有害的废物来生产改性沥青，同时达到改善沥青性能、减少环境污染的改性沥青的生产方法。
本发明以如下技术方案解决上述技术问题：
原料配方：(重量％)
10#～60#石油沥青45％～70％ 旧轮胎橡胶12％～35％
废弃润滑油 10％～25％ 生漆 0.5％～3％
桐油 0.5％～3％ 松节油 1％～5％
制备方法：
旧轮胎橡胶切成小块，废弃润滑油沉淀过滤除去杂质；除松节油外的五种原料同时混合搅拌加热，至橡胶全部熔化后停止加热，搅匀，冷却至120℃～150℃时加入松节油，充分搅匀得成品。
用本发明的方法制备的改性沥青，与水泥混凝土親和力强，粘附牢固而耐久，时间越长粘附越牢，不渗水，不离层，在-20℃～60℃的环境下均适用，长久保持弹性；且生产工艺简单、投资少、规模可大可小。热铺热拌其混合料可作道路路面，配以耐磨石料、防滑级配时雨天行车不打滑；可作水泥混凝土(含砖混)构筑物的施工缝、伸缩缝、沉降缝等嵌缝用料，作屋面、地下工程、仓库、水池等防水、防潮层施工用料，及其它使用石油沥青配料加工的产品用料。用部分废弃物替代高价的原料，不仅降低了成本，且有利于环保，充分利用了自然资源。
具体实施方式
在石油沥青中加入橡胶可以从多方面改善沥青性能的特性己为众所周知，用本发明的方法生产改性沥青，主要是利用社会公害之一的废旧轮胎中的橡胶取代价格较高的商品橡胶，对环境保护、降低成本都有利。加入废弃润滑油不仅具有与加入废旧轮胎相同的环保意义，而且在提高沥青的针入度、延度有明显作用，但润滑油的加入比例随母本石油沥青的标号增大而应相应递减。废旧轮胎橡胶和废弃润滑油加入的数量不同，可使本发明的改性沥青具有不同的凝固时间，供不同气候地区选用。加入少量生漆和桐油对提高沥青的耐老化性有显著意义。松节油的主要作用在于可以调节改性沥青的稠度，使之可以增加标号，滿足不同的要求。
实施例1
配方：
10#建筑石油沥青3.4kg 旧轮胎橡胶0.7kg
废弃润滑油 0.5kg 生漆 0.15kg
桐油 0.15kg 松节油 0.25kg
制备方法：
旧轮胎橡胶切成约2cm～3cm大的小块，废弃润滑油经沉淀过滤，与生漆、桐油同置入锅内，边加热边搅拌，加热至300℃左右，废轮胎橡胶全部熔化，停止加热，自然降温至约150℃时加入松节油，搅拌均匀得成品。成品的三大质量指标为：
针入度(25℃ 100g 1/10mm) 74
延度(25℃ cm) ≥100
软化点(℃) 53
实施例2：
配方：
10#建筑石油沥青2.75kg 旧轮胎橡胶1.15kg
废弃润滑油 0.9kg 生漆 0.05kg
桐油 0.05kg 松节油 0.1kg
制备方法与实施例1同。成品的三大质量指标为：
针入度(25℃ 100g 1/10mm) 88
延度(25℃ cm) ≥100
软化点(℃) 49
实施例3：
配方：
10#建筑石油沥青2.25kg 旧轮胎橡胶1.5kg
废弃润滑油 1.15kg 生漆 0.025kg
桐油 0.025kg 松节油 0.05kg
制备方法与实施例1同。成品的三大质量指标为：
针入度(25℃ 100g 1/10mm) 107
延度(25℃ cm) ≥100
软化点(℃) 45
Claims (1)
1.一种环保改性沥青，在改性沥青产品中加有橡胶，其特征是：
原料配方的重量百分比为：
10#～60#石油沥青45％～70％ 旧轮胎橡胶 12％～35％
废弃润滑油 10％～25％ 生漆 0.5％～3％
桐油 0.5％～3％ 松节油 1％～5％
制备方法是：
旧轮胎橡胶切成小块后与石油沥青、废弃润滑油、生漆、桐油同时混合搅拌加热至300℃橡胶全部熔化后停止加热，搅匀，冷却至120℃～150℃时加入松节油，充分搅匀得成品。