CN100335588C - 有机硅活性防水粉及其制造方法 - Google Patents

有机硅活性防水粉及其制造方法 Download PDF

Info

Publication number
CN100335588C
CN100335588C CNB2005100343873A CN200510034387A CN100335588C CN 100335588 C CN100335588 C CN 100335588C CN B2005100343873 A CNB2005100343873 A CN B2005100343873A CN 200510034387 A CN200510034387 A CN 200510034387A CN 100335588 C CN100335588 C CN 100335588C
Authority
CN
China
Prior art keywords
water
powder
sio
active
meant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005100343873A
Other languages
English (en)
Other versions
CN1746256A (zh
Inventor
陈俊光
林博
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2005100343873A priority Critical patent/CN100335588C/zh
Publication of CN1746256A publication Critical patent/CN1746256A/zh
Application granted granted Critical
Publication of CN100335588C publication Critical patent/CN100335588C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种有机硅活性防水粉的制造方法包括：将二官能含氢硅油、乳化剂、水混合，加入烃基烷氧基硅烷，在20-40℃下进行乳化反应；加入与烃基烷氧基硅烷等量的无机填料和水，在30℃～40℃，含氢量控制在0.1～0.15%重量，PH值为5.5，进行混合、混炼；得到的有机硅活性防水粉主要链节单元为：[R1SiO1.5]mMe3SiO[MeHSiO]nSiMe3[SiO2填料]，R1＝CaH2a+1，a＝6～17，m＝1～100，n＝1～100；外观为无定形粉末，添加于建筑材料中共同施工，其干燥后，有特异的防水防潮功能，并能增加建筑材料的韧性和强力，施工方便，添加量为建筑材料的0.3～0.5%，是有机硅在建筑材料中优良的添加剂。

Description

有机硅活性防水粉及其制造方法
技术领域
本发明涉及化工领域，具体是固态的有机硅活性防水粉的制造方法。
背景技术
有机硅防水剂主要用于砖、石、水泥、陶瓷、木材等材料的防水处理，现有的有机硅防水剂以水和溶液为载体的液体，或者是膏状半流体物。在运输途中和现场施工不方便，为了提高其施工性能，就要使产物的分子量缩聚得很高，成为固体物质。而固体物在使用性能上可难以满足施工要求。
发明内容
本发明的目的在于提供一种固态的有机硅活性防水粉的制造方法，得到固体产品，运输安全便宜，施工性能达到满意要求。
本发明的目的还在于提供所述方法制造的有机硅活性防水粉。
本发明的有机硅活性防水粉的制造方法包括如下步骤：
(1)按二官能含氢硅油、乳化剂、水的质量比为2～3∶2.5～3∶150～160混合，加入用量为0.1％-20％的烃基烷氧基硅烷，在20-40℃下进行乳化反应；
(2)加入与烃基烷氧基硅烷等量的无机填料和水，在30℃～40℃，含氢量控制在0.1～0.15％重量，PH值为5.5，进行混合、混炼得糊状白色能流动的膏状半固体为有机硅活性防水粉。
本发明各组分可以是本领域通用的组分，本发明最佳选择如下：
所述二官能含氢硅油是三甲基硅基封端甲基含氢硅油；
所述乳化剂是指含有亲水基团和亲油基团的化合物，具体是脂肪醇聚乙二醇醚等。
所述烃基烷氧基硅烷是指R1Si(R2O)3，R1＝CaH2a+1，a＝6～17，R2＝CbH2b+1 b＝1～4；
所述无机填料是指白碳黑。
得到的有机硅活性防水粉的主要链节单元为：
[R1SiO1.5]m Me3SiO[MeH SiO]nSiMe3[SiO2填料]，R1＝CaH2a+1 a＝6～17，m＝1～100，n＝1～100。
本发明与现有技术相比具有如下优点：
1、提供一种固态的有机硅活性防水粉剂，具有独创性；
2、本产品施工使用方便，在建筑施工使简单加入，可达到长时间的防水要求；
3、本品生产使用过程中均无废物和有害物资排出，属于环保型产品。
具体实施方式
实施例1
(1)按三甲基硅基封端甲基含氢硅油、乳化剂月桂醇聚乙二醇醚、水的质量比为2∶3∶160混合，加入用量为20％的己基三乙氧基硅烷，在40℃下进行乳化反应；
(2)加入与己基三乙氧基硅烷等量的白碳黑和水，在30℃，含氢量控制在0.15％重量，PH值为5.5，进行混合、混炼得糊状白色能流动的膏状半固体为有机硅活性防水粉，其主要链节单元为：
[R1SiO1.5]m Me3SiO[MeH SiO]nSiMe3[SiO2填料]，R1＝C6H13 m＝15，n＝60
其特征指标如下：
项目                 数量       说明
外观白色粉沫                    白色不定形粉沫
平均粒径um           75
粒径分布um           10-270     此表面积为30-35m2/g-1
相对密度25℃         0.98
表现密度             0.31
含水量％             ＜0.9-2
PH值                 5.5-6
热失重量％           4-5         300℃
                     15-17       700℃
实施例2
(1)按三甲基硅基封端甲基含氢硅油、乳化剂棕榈醇聚乙二醇醚、水的质量比为3∶2.5∶150混合，加入用量为30％的辛基三乙氧基硅烷，在20℃下进行乳化反应；
(2)加入与辛基三乙氧基硅烷等量的白碳黑和水，在30℃，含氢量控制在0.1％重量，PH值为5.5，进行混合、混炼得糊状白色能流动的膏状半固体为有机硅活性防水粉，其主要链节单元为：
[R1SiO1.5]m Me3SiO[MeH SiO]nSiMe3[SiO2填料]，R1＝C8H17 m＝25，n＝30
其特征指标如下：
项目                  数量        说明
外观白色粉沫                      白色不定形粉沫
平均粒径um            75
粒径分布um            10-270      此表面积为30-35m2/g-1
相对密度25℃          0.98
表现密度              0.31
含水量％              ＜0.9-2
PH值                  5.5-6
热失重量％            4-5         300℃
                      15-17       700℃
实施例3
(1)按三甲基硅基封端甲基含氢硅油、乳化剂硬脂醇聚乙二醇醚、水的质量比为2.5∶2.8∶155混合，加入用量为50％的十二烷基三乙氧基硅烷，在30℃下进行乳化反应；
(2)加入与十二烷基三乙氧基硅烷等量的白碳黑和水，在35℃，含氢量控制在0.13％重量，PH值为5.5，进行混合、混炼得糊状白色能流动的膏状半固体为有机硅活性防水粉，其主要链节单元为：
[R1SiO1.5]m Me3SiO[MeH SiO]nSiMe3[SiO2填料]，R1＝C12H25 m＝45，n＝30
其特征指标如下：
项目                  数量        说明
外观白色粉沫                      白色不定形粉沫
平均粒径um            75
粒径分布um            10-270      此表面积为30-35m2/g-1
相对密度25℃          0.98
表现密度              0.31
含水量％              ＜0.9-2
PH值                  5.5-6
热失重量％            4-5         300℃
                      15-17       700℃

Claims (4)

1、一种有机硅活性防水粉的制造方法，其特征在于包括如下步骤：
(1)按二官能含氢硅油、乳化剂、水的质量比为2～3∶2.5～3∶150～160混合，加入用量为0.1％-20％的烃基烷氧基硅烷，在20-40℃下进行乳化反应；
(2)加入与烃基烷氧基硅烷等量的无机填料和水，在30℃～40℃，含氢量控制在0.1～0.15％重量，PH值为5.5，进行混合、混炼；
所述二官能含氢硅油是指三甲基硅基封端甲基含氢硅油；所述无机填料是指白碳黑。
2、根据权利要求1所述的方法，其特征在于所述乳化剂是指含有亲水基团和亲油基团的表面活性剂。
3、根据权利要求1或2所述的方法，其特征在于所述述烃基烷氧基硅烷是指
R1Si(R2O)3，R1＝CaH2a+1，a＝6～17，R2＝CbH2b+1，b＝1～4。
4、权利要求1-3之一所述方法制造得到的有机硅活性防水粉，其特征在于主要链节单元为：
[R1SiO1.5]mMe3SiO[MeHSiO]nSiMe3[SiO2填料]，R1＝CaH2a+1 a＝6～17，m＝1～100，n＝1～100。
CNB2005100343873A 2005-04-28 2005-04-28 有机硅活性防水粉及其制造方法 Expired - Fee Related CN100335588C (zh)