CA2947382C - Method for producing a cold-rolled flat steel product with high yield strength and flat cold-rolled steel product - Google Patents

Method for producing a cold-rolled flat steel product with high yield strength and flat cold-rolled steel product Download PDF

Info

Publication number
CA2947382C
CA2947382C CA2947382A CA2947382A CA2947382C CA 2947382 C CA2947382 C CA 2947382C CA 2947382 A CA2947382 A CA 2947382A CA 2947382 A CA2947382 A CA 2947382A CA 2947382 C CA2947382 C CA 2947382C
Authority
CA
Canada
Prior art keywords
cold
less
rolled
steel product
flat steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CA2947382A
Other languages
English (en)
French (fr)
Other versions
CA2947382A1 (en
Inventor
Brigitte Hammer
Frank Hisker
Thomas Heller
Almir DZAFIC
Richard G. THIESSEN
Shinjiro Kaneko
Fusae SHIIMORI
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ThyssenKrupp Steel Europe AG
Original Assignee
ThyssenKrupp Steel Europe AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ThyssenKrupp Steel Europe AG filed Critical ThyssenKrupp Steel Europe AG
Publication of CA2947382A1 publication Critical patent/CA2947382A1/en
Application granted granted Critical
Publication of CA2947382C publication Critical patent/CA2947382C/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
    • B22D11/001—Continuous casting of metals, i.e. casting in indefinite lengths of specific alloys
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/26—Methods of annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/60—Ferrous alloys, e.g. steel alloys containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/285—Thermal after-treatment, e.g. treatment in oil bath for remelting the coating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
CA2947382A 2014-04-15 2015-04-14 Method for producing a cold-rolled flat steel product with high yield strength and flat cold-rolled steel product Active CA2947382C (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
DE102014105396.6 2014-04-15
DE102014105396 2014-04-15
PCT/EP2015/058101 WO2015158731A1 (en) 2014-04-15 2015-04-14 Method for producing a cold-rolled flat steel product with high yield strength and flat cold-rolled steel product

Publications (2)

Publication Number Publication Date
CA2947382A1 CA2947382A1 (en) 2015-10-22
CA2947382C true CA2947382C (en) 2022-07-12

Family

ID=53002660

Family Applications (1)

Application Number Title Priority Date Filing Date
CA2947382A Active CA2947382C (en) 2014-04-15 2015-04-14 Method for producing a cold-rolled flat steel product with high yield strength and flat cold-rolled steel product

Country Status (8)

Country Link
US (1) US10435763B2 (OSRAM)
EP (1) EP3132063B1 (OSRAM)
JP (1) JP6533528B2 (OSRAM)
KR (1) KR102419630B1 (OSRAM)
CN (1) CN106232852B (OSRAM)
CA (1) CA2947382C (OSRAM)
MX (1) MX378118B (OSRAM)
WO (1) WO2015158731A1 (OSRAM)

Families Citing this family (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3266894B1 (en) 2015-03-03 2020-03-04 JFE Steel Corporation High-strength steel sheet and method for producing same
WO2017125773A1 (en) 2016-01-18 2017-07-27 Arcelormittal High strength steel sheet having excellent formability and a method of manufacturing the same
CN110709528A (zh) * 2017-04-11 2020-01-17 蒂森克虏伯钢铁欧洲股份公司 经冷轧、罩式退火的扁钢产品及其制造方法
US20210087662A1 (en) * 2017-07-25 2021-03-25 Thyssenkrupp Steel Europe Ag Metal Sheet Component, Manufactured by Hot Forming a Flat Steel Product and Method for Its Manufacture
KR102075222B1 (ko) * 2017-12-26 2020-02-07 주식회사 포스코 재질편차가 적고, 신장플랜지성 및 실수율이 우수한 고강도 냉연강판 및 그 제조방법
KR20210127922A (ko) 2019-02-18 2021-10-25 타타 스틸 이즈무이덴 베.뷔. 기계적 특성이 개선된 고강도 강
CN113825846B (zh) * 2019-05-07 2024-08-23 美国钢铁公司 生产连续铸造热轧高强度钢片产品的方法
CN110117755B (zh) * 2019-05-21 2020-11-03 安徽工业大学 一种980MPa级低屈强比冷轧中锰钢的制备方法
CN111187893B (zh) * 2020-02-24 2021-06-29 攀钢集团攀枝花钢铁研究院有限公司 增强780dp高扩孔冷轧双相钢均一性的方法
EP3872193A1 (de) 2020-02-26 2021-09-01 ThyssenKrupp Steel Europe AG Verfahren zur herstellung eines warmgewalzten stahlflachprodukts und stahlflachprodukt
EP3872206B1 (de) 2020-02-28 2023-06-21 ThyssenKrupp Steel Europe AG Verfahren zur herstellung eines nachbehandelten, kaltgewalzten stahlflachprodukts und nachbehandeltes, kaltgewalztes stahlflachprodukt
CN113737108A (zh) * 2020-05-27 2021-12-03 宝山钢铁股份有限公司 一种耐延迟开裂的电镀锌超强双相钢及其制造方法
CN114058941A (zh) * 2020-07-31 2022-02-18 宝山钢铁股份有限公司 一种冷轧钢板及制造方法和汽车用冲裁件
SE545210C2 (en) * 2020-12-23 2023-05-23 Voestalpine Stahl Gmbh Coiling temperature influenced cold rolled strip or steel
CN114763595B (zh) * 2021-01-15 2023-07-07 宝山钢铁股份有限公司 一种冷轧钢板以及冷轧钢板的制造方法
WO2022184811A1 (de) * 2021-03-03 2022-09-09 Thyssenkrupp Steel Europe Ag Stahlflachprodukt, verfahren zu seiner herstellung und verwendung eines solchen stahlflachprodukts
CN116065103A (zh) * 2021-11-01 2023-05-05 上海梅山钢铁股份有限公司 一种低成本屈服强度550MPa级高扩孔热轧酸洗钢板
CN116065105B (zh) * 2022-09-06 2025-02-18 上海大学 一种超高强自回火钢板及其制备方法
EP4403662A1 (en) * 2023-01-18 2024-07-24 voestalpine Stahl GmbH A cold rolled steel and a production process to it
CN117187667A (zh) * 2023-09-07 2023-12-08 攀钢集团攀枝花钢铁研究院有限公司 高屈服强度780MPa级连退用双相钢及其制备方法

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101399741B1 (ko) * 2007-10-25 2014-05-27 제이에프이 스틸 가부시키가이샤 가공성이 우수한 고강도 용융 아연 도금 강판 및 그 제조 방법
JP5365217B2 (ja) * 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5365216B2 (ja) 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
JP5369663B2 (ja) * 2008-01-31 2013-12-18 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5376927B2 (ja) 2008-12-11 2013-12-25 日新製鋼株式会社 曲げ加工性に優れた高比例限鋼板の製造方法
MX338319B (es) 2009-12-21 2016-04-12 Tata Steel Ijmuiden Bv Tira de acero galvanizado por inmersion en caliente de alta resistencia.
JP5446886B2 (ja) 2010-01-06 2014-03-19 新日鐵住金株式会社 冷延鋼板の製造方法
EP2551359B1 (en) 2010-03-24 2021-04-07 JFE Steel Corporation Method for producing ultra high strength member
EP2402472B2 (de) * 2010-07-02 2017-11-15 ThyssenKrupp Steel Europe AG Höherfester, kaltumformbarer Stahl und aus einem solchen Stahl bestehendes Stahlflachprodukt
EP2489748B1 (de) * 2011-02-18 2017-12-13 ThyssenKrupp Steel Europe AG Aus einem Komplexphasenstahl hergestelltes warmgewalztes Stahlflachprodukt und Verfahren zu dessen Herstellung
WO2013061545A1 (ja) * 2011-10-24 2013-05-02 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板の製造方法
KR20200106559A (ko) 2011-11-28 2020-09-14 아르셀러미탈 인베스티가시온 와이 데살롤로 에스엘 연성이 향상된 높은 규소 베어링 이중상 강들
DE102012013113A1 (de) 2012-06-22 2013-12-24 Salzgitter Flachstahl Gmbh Hochfester Mehrphasenstahl und Verfahren zur Herstellung eines Bandes aus diesem Stahl mit einer Mindestzugfestigkleit von 580MPa
ES2614465T3 (es) * 2012-07-10 2017-05-31 Thyssenkrupp Steel Europe Ag Producto plano de acero laminado en frío y procedimiento para su fabricación
EP3219821B1 (en) * 2015-01-15 2019-11-13 JFE Steel Corporation High-strength galvanized steel sheet and method for producing the same

Also Published As

Publication number Publication date
JP2017514989A (ja) 2017-06-08
KR20160145656A (ko) 2016-12-20
CN106232852B (zh) 2018-12-11
MX2016011987A (es) 2017-04-06
WO2015158731A1 (en) 2015-10-22
EP3132063A1 (en) 2017-02-22
US10435763B2 (en) 2019-10-08
KR102419630B1 (ko) 2022-07-11
EP3132063B1 (en) 2021-01-13
CA2947382A1 (en) 2015-10-22
CN106232852A (zh) 2016-12-14
JP6533528B2 (ja) 2019-06-19
MX378118B (es) 2025-03-10
US20170029917A1 (en) 2017-02-02

Similar Documents

Publication Publication Date Title
US10435763B2 (en) Method for producing a cold-rolled flat steel product with high yield strength and flat cold-rolled steel product
US10995386B2 (en) Double annealed steel sheet having high mechanical strength and ductility characteristics, method of manufacture and use of such sheets
EP3221476B1 (en) Method for manufacturing a high strength steel product and steel product thereby obtained
KR102073442B1 (ko) 강, 강판 제품 및 강판 제품을 제조하기 위한 방법
CA2932315C (en) Martensitic steel with delayed fracture resistance and manufacturing method
EP2653582B1 (en) Hot-dip galvanized steel sheet and manufacturing method thereof
EP2778247A1 (en) Steel sheet for hot press forming, hot press forming member, and manufacturing method thereof
US9963756B2 (en) Method for production of martensitic steel having a very high yield point and sheet or part thus obtained
US11655518B2 (en) Steel material for taylor welded blank and method for manufacturing hot-stamped part using same steel
WO2011125738A1 (ja) 加工性に優れた高降伏比高強度の溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板
KR20180128977A (ko) 오스테나이트계 매트릭스를 가지는 twip 강 시트를 제조하는 방법
RU2734216C1 (ru) Способ изготовления плоского стального продукта из стали с содержанием марганца и такой плоский стальной продукт
RU2749270C2 (ru) Способ изготовления горячей или холодной полосы и/или гибко-катаного плоского стального продукта из высокопрочной марганцевой стали и плоский стальной продукт, изготовленный таким способом
KR20230016218A (ko) 열처리 냉연 강판 및 그 제조 방법
EP3730651A1 (en) High yield ratio-type high-strength steel sheet and method for manufacturing same
KR101115790B1 (ko) 점용접 특성 및 내지연파괴 특성이 우수한 냉연강판 및 그 제조방법
KR101736634B1 (ko) 연성과 구멍가공성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법
RU2844799C1 (ru) Сталь с покрытием, стойкая к водородному охрупчиванию
HK1140235A (en) Method of thermomechanical shaping a final product with very high strength and a product produced thereby

Legal Events

Date Code Title Description
EEER Examination request

Effective date: 20200403

MPN Maintenance fee for patent paid

Free format text: FEE DESCRIPTION TEXT: MF (PATENT, 10TH ANNIV.) - STANDARD

Year of fee payment: 10

U00 Fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U00-U101 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE REQUEST RECEIVED

Effective date: 20250325

U11 Full renewal or maintenance fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U11-U102 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE FEE PAYMENT DETERMINED COMPLIANT

Effective date: 20250325