CA2485877C

CA2485877C - Cathode catalyst for fuel cell

Info

Publication number: CA2485877C
Application number: CA002485877A
Authority: CA
Inventors: Tetsuo Ito; Tomoaki Terada; Hisao Kato; Tetsuo Nagami
Original assignee: Cataler Corp; Toyota Motor Corp
Current assignee: Cataler Corp; Toyota Motor Corp
Priority date: 2003-10-23
Filing date: 2004-10-22
Publication date: 2009-12-22
Anticipated expiration: 2024-10-22
Also published as: CN1610159A; JP4290524B2; US20050164074A1; CN1300878C; EP1526592A1; EP1526592B1; US7241717B2; DE602004017103D1; CA2485877A1; JP2005129358A

Abstract

It is an object of the present invention to provide a cathode catalyst for fuel cells containing platinum and iron which can maintain the durability of a battery and can make a battery high output. The cathode catalyst for fuel cells comprises a supporting layer which consists of an alloy containing platinum and iron and further containing the third component which has an affinity for iron including one or more sorts of elements selected from the group consisting of tungsten, titanium, molybdenum, rhenium, zinc, manganese, tin, tantalum and rhodium, and a support on which the supporting layer is loaded. A catalyst using an alloy containing platinum and iron enables the batteries to become high output. By alloying one or more sorts of elements of the third component which has an affinity for iron with an alloy containing platinum and iron, it is possible to prevent eluting of the iron into the electrolyte.

Description

CATHODE CATALYST FOR FUEL CELL
BACKGROUND OF THE INVENTION
Field of the Invention (0001) The present invention relates to a cathode catalyst for fuel cells. More specifically, it relates to a cathode catalyst for fuel cells which contains an alloy of platinum, iron and the third component including one or more sorts of elements selected from the group consisting of tungsten, titanium, molybdenum, rhenium, zinc, manganese, tin, tantalum and rhodium.
Description of the Related Art (0002) As for a catalyst used for the cathode of fuel cells, platinum has been conventionally used. In this case, it is known that, by alloying platinum and iron and using thereof for a cathode catalyst, the activity of oxygen reduction will be increased, so the batteries can become high output.

(0003) Forinstance,Japanese Unexamined Patent Publication(KOKAI) No. 60-7941 discloses an electrode catalyst containing a super-lattice structure platinum-iron alloy dispersed on the supports.

(0004) However, in a case where the acid electrolyte which consists of a high polymer material having S03H group, such as a perfluorocarbon acid ionomer, is used as the electrolyte of a fuel cell and the cathode catalyst of a fuel cell is made to contain a platinum-iron alloy, it may arise that the iron contained in a platinum-iron alloy elutes into the electrolyte of a fuel cell. That is, the electrolyte will become strong acid when having S03H group and swelled with water.
In such a case, if the cathode catalyst of a fuel cell is made to contain a platinum-iron alloy, a base metal like iron will be eluted out as ions. The eluting ions are ion-exchanged with the proton in the electrolyte, i.e., H' of S03H group. This leads to deterioration of the conductivity of the high polymer electrolyte.
As a result, it will arise the problem that the battery performance will be lowered and the life span of a fuel cell is unable to be extended.
SUMMARY OF THE INVENTION

(0005) It is therefore an object of the present invention to provide a cathode catalyst for fuel cells containing platinum and iron which can maintain the durability of a battery and can make a battery high output.

(0006) As a result of diligent study by the present inventors, they have invented a cathode catalyst for fuel cells used for the cathode of fuel cells comprising: a supporting layer which consists of an alloy containing platinum and iron and further containing the third component which has an affinity for iron including one or more sorts of elements selected from the group consisting of tungsten, titanium, molybdenum, rhenium, zinc, manganese, tin, tantalum and rhodium, and a support on which said supporting layer is loaded.

(0007) Namely, by adding platinum and iron and further adding the third component which has an affinity for iron including one or more sorts of elements selected from the group consisting of tungsten, titanium, molybdenum, rhenium, zinc, manganese, tin, tantalum and rhodium, and alloying preferentially iron and the element included in these third components, it is possible to prevent eluting of the iron into the electrolyte membrane. It is also possible to extend the life span of cathode catalysts. Further, since it contains platinum and iron, it is possible to make the batteries high output by increasing the reaction of oxygen reduction.

(0008) By using the cathode catalyst for fuel cells of the present invention, eluting of the iron which causes degradation of an electrolyte membrane can be prevented, and the durability of a fuel cell can be maintained. Moreover, since it contains iron, the batteries can be made high output.
BRIEF DESCRIPTION OF THE DRAWINGS

(0009) The form for carrying out the cathode catalyst for fuel cells of the present invention is explained below. A more complete appreciation of the present invention and many of its advantages will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawingsand detailedspecification, all of which forms a part of the disclosure. Fig. 1 illustrates the result of a comparative examination.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

(0010) A cathode catalyst for fuel cells is used as a cathode of fuel cells, namely, as the side of the electrode to which an oxidizing agent is supplied. For instance, in hydrogen-oxygen fuel cells, it can be used as a catalyst of the oxygen electrode.

(0011] The cathode catalyst for fuel cells of the present invention is characterized in having a supporting layer which consists of an alloy containing platinum and iron and further containing the third component which has an affinity for iron including one or more sorts of elements selected from the group consisting of tungsten, titanium, molybdenum, rhenium, zinc, manganese, tin, tantalum and rhodium, and a support on which the supporting layer is loaded.

(0012) A supporting layer of the cathode catalyst for fuel cells of the present invention consists of an alloy containing platinum and iron and further containing the third component which has an affinity for iron including one or more sorts of elements selected from the group consisting of tungsten, titanium, molybdenum, rhenium, zinc, manganese, tin, tantalum and rhodium.

(0013) That is, as for an alloy used here, an alloy which further added one sort of elements of the third component to platinum and iron can be used, i.e., a platinum-iron-tungsten alloy, a platinum-iron-titanium alloy, a platinum-iron-molybdenum alloy, a platinum-iron-rhenium alloy, a platinum-iron-zinc alloy, a platinum-iron-manganese alloy, a platinum-iron-tin alloy, a platinum-iron-tantalum alloy, a platinum-iron-rhodium alloy, etc.
Further, it is possible to arbitrarily combine two or more sorts of elements of the third component with platinum and iron, like a platinum-iron-tungsten-molybdenum alloy.

(0014) The ratio between platinum, iron and the third component can be, when platinum is taken as 100 by weight, iron approximately 0.5-10 by weight, and the third component approximately 5-50 by weight.

(0015) Among these alloys, the alloy which consists of platinum, iron and tungsten, and the alloy which consists of platinum, iron andtitanium are preferable. Itisbecause a platinum-iron-tungsten alloy arid a platinum-iron-titanium alloy show excellent durability as a cathode catalyst fox fuel cells. That is, it is because eluting of the iron into an electrolysis solution or an electrolysis membrane is prevented.

(0016) In the case of a platinum-iron-tungsten alloy, when platinum is taken as 100 by weight, iron can be approximately 0 . 5-10 by weight, tungsten approximately 5-50 by weight. More preferably, iron can be approximately 1.0-3.0 by weight and tungsten approximately 20-30 by weight.

(0017) In the case of a platinum-iron-titanium alloy, when platinum is taken as 100 by weight, iron can be approximately 0 . 5-10 by weight, titanium approximately 5-20 by weight.

(0018) Moreover, in addition to platinum, iron and metal of the third component, it is also possible to further contain metal other than these. For example, cobalt, nickel, chromium, etc. can be listed, however, it is not limited to these.

(0019) The support of the cathode catalyst for fuel cells of the present invention is a support on which the supporting layer mentioned above is loaded. A material suitable for such a support can be used.
For instance, carbon materials, such as a carbon powder, etc. can be used, however, it is not limited to this.

(0020) In addition, the ratio of a support and a supporting layer can be approximately 100 by weight of a support and 5-70 by weight of a supporting layer. More preferably, a supporting layer can be 20-60 by weight.

(0021) The cathode catalyst for fuel cells of the present invention can be produced by loading platinum, iron and an element of the third component on a material which is used as a support, such as a carbon powder, thereafter performing reducing treatment, alloying, washing and vacuum drying.

(0022] The cathode catalyst for fuel cells of the present invention produced in such a manner can be used in loading a cathode for fuel cells. In this case, it is suitable to use as a cathode catalyst of a polymer electrolyte fuel cell. As described above, in a case where the acid electrolyte which consists of a polymer having S03H
group, such as a perfluoro acid ionomer, is used as the electrolyte of a polymer electrolyte fuel cell, the electrolyte will become strong acid when swelled with water. In such a case, if the cathode catalyst of a fuel cell is made to contain a platinum-iron alloy, a base metal like iron will be eluted out as ions. In the present invention, however, since an element of the third component is also alloyed, eluting of the iron can be prevented.

(0023] In addition, as material which can be used as a cathode for fuel cells, the material of carbon group, such as a carbon cloth and a carbon paper, can be used. However, it is not limited to these.
It can be used to load by the suitable method for such material.
Examples (Example No. 1) (0024] First, 6 . 0 g of carbon powder were added to 1. 0 L of hexahydroxy-platinate nitrate solution containing 3 . 6 g of platinum and the carbon powder was sufficiently dispersed in this solution. Then, the resulting solution in which the carbon powder was dispersed was filtered and washed to obtain carbon powder on which platinum was loaded.

(0025] This carbon powder was uniformly dispersed in 0.5 L of deionized water, and 0 . 1 L of iron nitrate aqueous solution containing 0.2 g of iron was further added. Thereafter, 6 o by mass of the aqueous ammonia was dripped into the aqueous solution so that the pH (Hydrogen ion exponent ) was adj usted to 5 . 0-8 . 0, and iron hydroxide was precipitated. Filtering and washing of this aqueous solution which iron hydroxide was precipitated was carried out to obtain a carbon powder on which platinum and iron were loaded.

(0026) This carbon powder was uniformly dispersed in 0.5 L of deionized water, and 0.2 L of ammonium tungstate para pentahydrate aqueous solution containing 0.2 g of tungsten was further added.
Next, nitrate solution was dripped into the aqueous solution until the pH became 1.0 or less, and tungsten trioxide was precipitated.
Filtering and washing of this aqueous solution which tungsten trioxide was precipitated was carried out to obtain a carbon powder on which platinum, iron and tungsten were loaded.

(0027) Reducing treatment was performed to the resulting carbon powder at 600 °C in a hydrogen atmosphere for 0.5-1.0 hours, and subsequently alloying treatment was carried out at 650 °C in a nitrogen atmosphere for one hour. Then, this alloying treated powder was sufficiently washed with deionized water, dried in a vacuum drier at 100 °C for 4 hours to obtain a carbon catalyst powder loading a platinum-iron-tungsten alloy (1).

(0028) Thiscarbon catalyst powderloading a platinum-iron-tungsten alloy (1) had a platinum loading density of 36 ~ by mass, an iron loading density of 2 o by mass and a tungsten loading density of 2 ~ by mass.

(0029) Moreover, the particle diameter of an alloy of this carbon catalyst powder loading a platinum-iron-tungsten alloy (1) was measured by X-ray diffraction (XRD), it was 2.5-4.0 nm.

(0030) In addition, the particle diameter of an alloy was calculated from the peak position (around 40 degree) which belongs to (111) surface at half height. A platinum-iron-a-alloy is subject to distortion of a crystal when alloying, and the peak position which belongs to (111) surface is shifted to a high angle side. The peak position, which belongs to ( 111 ~ surface of an alloy of this carbon catalyst powder loading a platinum-iron-tungsten alloy (1) in X-ray diffraction, was 40.1 degree and alloying was confirmed.
(Example No. 2) (0031) By the same way as Example 1, 3.7 g of platinum and 0.2 g of iron were loaded on 6.0 g of carbon powder.

(0032) This carbon powder was uniformly dispersed in 0.5 L of deionized water, and 0.2 L of titanium chloride aqueous solution containing 0.1 g of titanium was further added. Subsequently, lg of sodiumborohydride were added to this aqueous solution as a reducing agent. Such solution was filtered and washed to obtain a carbon powder on which platinum, iron and titanium were loaded.

(0033) Reducing treatment, an alloying treatment, washing and vacuum drying was performed to this carbon powder like Example 1 to obtain a carbon catalyst powder loading a platinum-iron-titanium alloy (2) .

(0034) Thiscarbon catalystpowderloading a platinum-iron-titanium alloy (2) had a platinum loading density of 37 °s by mass, an iron loading density of 2 % by mass and a titanium loading density of 1 °s by mass.

(0035) Moreover, the particle diameter of an alloy of this carbon catalyst powder loading a platinum-iron-titanium alloy (2) was measured by X-ray diffraction (XRD) , it was 3. 5-6. 0 nm. In addition, the peak position, which belongs to (111) surface of an alloy of this catalyst powder (2) in X-ray diffraction, was 40.4 degree and alloying was confirmed.
(Example No. 3) (0036) By the same way as Example 1, 3.6 g of platinum and 0.2 g of iron were loaded on 6.0 g of carbon powder.

(0037) This carbon powder was uniformly dispersed in 0.5 L of deionized water, and 0.2 L of molybdenum chloride aqueous solution containing 0.2 g of molybdenum was further added. Then, 1 g of sodium borohydrate was added to this aqueous solution as a reducing agent.
Such solution was filtered and washed to obtain a carbon powder on which platinum, iron and molybdenum were loaded.

(0038) Reducing treatment, an alloying treatment, washing and vacuum drying was performed to this carbon powder like Example 1 to obtain a carbon catalyst powder loading a platinum-iron-molybdenum alloy (3) .

(0039) This carbon catalyst powder loading a platinum-iron-molybdenum alloy (3) had a platinum loading density of 36 % by mass, an iron loading density of 2 % by mass and a molybdenum loading density of 2 % by mass.

(0040) Moreover, the particle diameter of an alloy of this carbon catalyst powder loading a platinum-iron-molybdenum alloy (3) was measured by X-ray diffraction (XRD), it was 3.0-5.0 nm. Further, the peak position, which belongs to (111) surface of an alloy of this catalyst powder (3) in X-ray diffraction, was 40.3 degree and alloying was confirmed.
(Example No. 4) ( 0041 ) 6.0 g of carbon powder were added to 1.0 L of hexahydroxyplatinate nitrate solution containing 3.7 g of platinum and the carbon powder was sufficiently dispersed in this solution.

Then, 0.1 L of iron nitrate aqueous solution containing 0.2 g of iron and titanium chloride aqueous solution containing 0.1 g of titanium were added to this solution that the carbon powder was dispersed. Thereafter, 6 % by mass of the aqueous ammonia was dripped into this aqueous solution so that the pH (Hydrogen ion exponent) was adjusted to 6.0-8Ø Filtering and washing of this aqueous solution to obtain a carbon powder on which platinum, iron and titanium were loaded.
(0042 Reducing treatment, an alloying treatment, washing and vacuum drying were performed to this carbon powder like Example 1 to obtain a carbon catalyst powderloading a platinum-iron-titanium alloy (4).
(0043 Thiscarbon catalyst powderloading a platinum-iron-titanium alloy (4) had a platinum loading density of 37 % by mass, an iron loading density of 2 % by mass and a titanium loading density of 1 % by mass.
(0044) Moreover, the particle diameter of an alloy of this carbon catalyst powder loading a platinum-iron-titanium alloy (4) was measured by X-ray diffraction (XRD), it was 3.5-6.0 nm. Further, the peak position, which belongs to (111) surface of an alloy of this catalyst powder (4) in X-ray diffraction, was 40.2 degree and alloying was confirmed.
(Example No. 5) (0045) By the same way as Example 4, 6.0 g of carbon powder were suspended to a solution containing 3.6 g of platinum and 0.2 g of iron. That is, 6.0 g of carbon powder were added to 1.0 L of hexahydroxyplatinate nitrate solution containing 3.6 g of platinum and the carbon powder was sufficiently dispersed in this solution.
Then, 0.1 L of iron nitrate aqueous solution containing 0.2 g of iron was added to the resulting solution in which the carbon powder was dispersed. Instead of titanium chloride aqueous solution, a molybdenum chloride aqueous solution containing 0.2 g of molybdenum was added. Subsequently, 6~ by mass of the aqueous ammonia was dripped into this aqueous solution, and the pH (Hydrogen ion exponent) was adjusted to 6. 0-8 . 0. Filtering and washing of this aqueous solution was carried out to obtain a carbon powder on which platinum, iron and molybdenum were loaded.
(0046) Reducing treatment, an alloying treatment, washing and vacuum drying were performed to this carbon powder like Example 1 to obtain a carbon catalyst powder loading a platinum-iron-molybdenum alloy (5) .
(0047) This carbon catalyst powder loading a platinum-iron-molybdenum alloy (5) had a platinum loading density of 36 % by mass, an iron loading density of 2 o by mass and a molybdenum loading density of 2 % by mass.
(0048) Furthermore, the particle diameter of an alloy of this carbon catalyst powder loading a platinum-iron-molybdenum alloy (5) was measured by X-ray diffraction (XRD), it was 3.0-5.0 nm. The peak position that belongs to (111) surface of an alloy of this catalyst powder (4) in X-ray diffraction was 40.2 degree and alloying was confirmed.
(Example No. 6) (0049) By the same way as Example 1, 3.6 g of platinum and 0.2 g of iron were loaded on 6.0 g of carbon powder.
(0050) Reducing treatment, an alloying treatment, washing and vacuum drying were performed to this carbon powder like Example 1 to obtain a carbon catalyst powder loading a platinum-iron alloy.

X0051) This carbon catalyst powder loading a platinum-iron alloy was uniformly dispersed in 0.5 L of deionized water, and 0.2 L of ammonium tungstate para pentahydrate aqueous solution containing 0.2 g of tungsten was further added. Next, nitrate solution was dripped into the aqueous solution until the pH became 1.0 or less, and tungsten trioxide was precipitated. Filtering and washing of this aqueous solution which tungsten trioxide was precipitated was carried out to obtain a carbon catalyst powder on which a platinum-iron alloy was loaded.
X0052) Reducing treatment, an alloying treatment, washing and vacuum drying were performed to this carbon catalyst powder like Example 1 to obtain a carbon catalyst powder loading a platinum-iron- tungsten alloy (6).
(0053) Thiscarbon catalyst powderloading a platinum-iron-tungsten alloy (6) had a platinum loading density of 36 $ by mass, an iron loading density of 2 % by mass and a tungsten loading density of 2 °s by mass.
10054) Moreover, the particle diameter of an alloy of this carbon catalyst powder loading a platinum-iron-tungsten alloy (6) was measured by X-ray diffraction (XRD), it was 2.5-4.0 nm. The peak position that belongs to ( 111 ) surface of an alloy of this catalyst powder (6) in X-ray diffraction was 40.1 degree, and alloying was confirmed.
(Comparative Example No. 1) X0055) By the same way as Example 6, 3.8 g of platinum and 0.2 g of iron were loaded on 6.0 g of carbon powder.
(0056) Reducing treatment, an alloying treatment, washing and vacuum drying were performed to this carbon catalyst powder like Example 1 to obtain a carbon catalyst powder loading a platinum-iron alloy (7) .
(0057) This carbon catalyst powder loading a platinum-iron alloy ( 7 ) had a platinum loading density of 38 o by mass and an iron loading density of 2 o by mass.
(0058) Moreover, the particle diameter of an alloy of this carbon catalyst powder loading a platinum-iron alloy (7) was measured by X-ray diffraction (XRD) , it was 2. 5-4 . 0 nm. The peak position that belongs to (111) surface of an alloy of this catalyst powder (7) in X-ray diffraction was 40.1 degree, and alloying was confirmed.
(Comparative Examination) (0059) Using the resulting carbon catalyst powders ( 1 ) - ( 7 ) loading a platinum alloy, a cathode for polymer electrolyte-fuel cells were formed as follows . Namely, carbon catalyst powders ( 1 ) - ( 7 ) loading a platinum alloy, produced in the manner described above, were dispersed in a 10 o Nafion solution (a product of Aldrich Corporation) and an organic solvent. Subsequently, these dispersion solutions were sprayed on a carbon cloth to form a cathode. The amount of a carbon catalyst powder loading a platinum alloy was 0.3 mg per 1 cmz of this cathode.
(0060) The cathode that formed by spraying these carbon catalyst powders ( 1 ) - ( 7 ) loading a platinum alloy, and an anode were bonded by hot-pressing with a polymer electrolyte membrane in between them to form a fuel cell.
(006Z) In addition, the anode used here was formed by spraying, on a carbon paper, a catalyst that platinum was loaded on carbon black. Further, Vulcan XC72R, a product name of CABOT Corporation, was used here as carbon black. The ratio of carbon black to platinum was 40 to 60 by weight. As a polymer electrolyte membrane, Nafion, a product name of DuPont, was used. This Nafion is a polymer material having S03H group.
(0062) The electrode area of each cell composed as such was 13 cm2 .
Then, a back pressure of 0. 1 MPa was applied to the cathode and anode of this fuel cell, respectively. The cathode side was supplied with air at a flow rate of 1 L/min and the anode side was supplied with hydrogen at a flow rate of 0.5 L/min, respectively.
(0063) After repeating the cycle which the current density was increased at prefixed speed from open circuit (OCV) up to 2 A/cmz for two hours, the current density was fixed to 0.5 A/cm2 and the battery voltages were assessed.
(0064) The battery voltages of fuel cells, using carbon catalyst powders ( 1 ) - ( 7 ) loading a platinum alloy, were measured respectively after 100 hours, 200 hours, 300 hours, 400 hours, 500 hours, 600 hours, 700 hours, 800 hours and 900 hours. Fig. 1 illustrates the battery voltages using carbon catalyst powders (1)-(7) loading a platinum alloy in the result of a durability examination. In addition, a carbon catalyst powder loading a platinum alloy was only abbreviated to a catalyst powder in Fig, 1.
(0065) According to Fig. 1. , the batteries using carbon catalyst powders ( 1 ) - ( 6 ) loading a platinum-iron-the third element alloy had the higher durability of batteries than the battery using a carbon catalyst powder (7) loading a platinum-iron alloy. The difference in durability was obvious especially after two hours had passed.
Moreover, it can be observed that after 400 hours had passed, the batteries using carbon catalyst powders (1)-(6) loading a platinum-iron-the third element alloy had the voltage more than twice as large as the voltage of the battery using a carbon catalyst powder (7) loading a platinum-iron alloy. Considering the above, the durability of a battery can be improved by employing carbon catalyst powders using an alloy that consists of platinum, iron and the third element, e.g., tungsten, titanium, molybdenum, rhenium and thelike, compared to the carbon catalyst powder using an alloy that consists of platinum and iron.
(0066) Furthermore, among the batteries using carbon catalyst powders (1)-(6) loading a platinum-iron-the third element alloy, the batteries using carbon catalyst powders (1) and (6) loading a platinum-iron-tungsten alloy and the batteriesusing carbon catalyst powders (2 ) and ( 4 ) loading a platinum-iron-titanium alloy had higher durability of a battery than the batteries using carbon catalyst powders (3) and (5) loading a platinum-iron-rhenium alloy.
Therefore, it was proved that tungsten and titanium are more preferable to employ as the third element to form an alloy with platinum and iron.

Claims

1. A cathode catalyst for a fuel cell used for the cathode of fuel cells comprising:

a supporting layer which consists of an alloy containing platinum and iron and further containing the third component which has an affinity for iron including one or more elements selected from the group consisting of tungsten, titanium, molybdenum, rhenium, zinc, manganese, tin, tantalum and rhodium; and a support on which said supporting layer is loaded.

2. The cathode catalyst for a fuel cell set forth in claim 1, wherein said third component is one or more elements selected from tungsten and titanium.

3. The cathode catalyst for a fuel cell set forth in claim 2, wherein said third component is tungsten, comprising 0.5 - 6.2 of iron by percentage weight, 5 -31.3 of tungsten by percentage weight and 94.5 - 62.5 of platinum by percentage weight.

4. The cathode catalyst for a fuel cell set forth in claim 2, wherein said third component is titanium, comprising 0.5 - 6.2 of iron by percentage weight, 5 -31.3 of titanium by percentage weight and 94.5 - 62.5 of platinum by percentage weight.

5. The cathode catalyst for a fuel cell set forth in any one of claims 1 - 4, wherein said support is a carbon powder.

6. The cathode catalyst for a fuel cell set forth in any one of claims 1 - 5, wherein said fuel cell is a polymer electrolyte fuel cell.