BR112014014401A2 - material de aço para soldagem com alta entrada de calor - Google Patents

material de aço para soldagem com alta entrada de calor

Info

Publication number
BR112014014401A2
BR112014014401A2 BR112014014401A BR112014014401A BR112014014401A2 BR 112014014401 A2 BR112014014401 A2 BR 112014014401A2 BR 112014014401 A BR112014014401 A BR 112014014401A BR 112014014401 A BR112014014401 A BR 112014014401A BR 112014014401 A2 BR112014014401 A2 BR 112014014401A2
Authority
BR
Brazil
Prior art keywords
less
heat input
steel material
high heat
welding
Prior art date
Application number
BR112014014401A
Other languages
English (en)
Other versions
BR112014014401B1 (pt
Inventor
Hase Kazukuni
Mitao Shinji
Yokota Tomoyuki
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of BR112014014401A2 publication Critical patent/BR112014014401A2/pt
Publication of BR112014014401B1 publication Critical patent/BR112014014401B1/pt

Abstract

resumo patente de invenção: "material de aço para soldagem com alta entrada de calor". material de aço para soldagem com alta entrada de calor tendo um limite de elasticidade de 460 mpa ou mais, excelente em termos de resistência (resistência ao amolecimento) e tenacidade de uma zona afetada pelo calor da soldagem mesmo no caso em que uma soldagem com alta entrada de calor é executada com uma entrada de calor maior que 300 kj/cm. material de aço para soldagem com alta entrada de calor tem uma composição química contendo, em % em massa, c, si, mn, p, e s em certas quantidades e também contendo al: 0,005% ou mais e 0,100% ou menos, nb: 0,003% ou mais e 0,030% ou menos, ti: 0,003% ou mais e 0,030% ou menos, n: 0,0025% ou mais e 0,0070% ou menos, b: 0,0003% ou mais e 0,0025% ou menos, um carbono equivalente ceq representado pela equação (1): 0,330 ou mais e 0,450 ou menos, e o saldo sendo fe e as inevitáveis impurezas, no qual a microestrutura da porção mais amolecida de uma zona afetada pelo calor inclui 3% em volume ou mais e 12% em volume ou menos de uma fase martensita. 21401162v1 1/1 21401162v1
BR112014014401-0A 2011-12-14 2012-12-12 Material de aço para soldagem com alta entrada de calor BR112014014401B1 (pt)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2011-273288 2011-12-14
JP2011273288 2011-12-14
PCT/JP2012/007953 WO2013088715A1 (ja) 2011-12-14 2012-12-12 大入熱溶接用鋼材

Publications (2)

Publication Number Publication Date
BR112014014401A2 true BR112014014401A2 (pt) 2017-06-13
BR112014014401B1 BR112014014401B1 (pt) 2022-09-20

Family

ID=48612189

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112014014401-0A BR112014014401B1 (pt) 2011-12-14 2012-12-12 Material de aço para soldagem com alta entrada de calor

Country Status (6)

Country Link
JP (1) JP5796636B2 (pt)
KR (1) KR101608239B1 (pt)
CN (1) CN103987869B (pt)
BR (1) BR112014014401B1 (pt)
TW (1) TWI589708B (pt)
WO (1) WO2013088715A1 (pt)

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013128650A1 (ja) * 2012-03-01 2013-09-06 Ｊｆｅスチール株式会社 大入熱溶接用鋼材
KR101930181B1 (ko) * 2014-10-17 2018-12-17 제이에프이 스틸 가부시키가이샤 대입열 용접용 강재
CN108637532B (zh) * 2018-04-09 2020-04-24 浙江江奥机械科技有限公司 一种抗电渣焊接头软化的方法
MX2021011387A (es) * 2019-03-26 2021-10-13 Nippon Steel Corp Lamina de acero y miembro.
CN112746218B (zh) * 2019-12-30 2021-11-16 宝钢湛江钢铁有限公司 低成本、高止裂、可大热输入焊接yp420级钢板及其制造方法
CN113106336B (zh) * 2021-03-17 2022-06-10 唐山钢铁集团有限责任公司 一种降低激光焊接头软化程度的超高强双相钢及生产方法

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4226626B2 (ja) * 2005-11-09 2009-02-18 新日本製鐵株式会社 音響異方性が小さく溶接性に優れる、板厚中心部も含めて降伏応力４５０ＭＰａ以上かつ引張強さ５７０ＭＰａ以上の高張力鋼板およびその製造方法
JP4770415B2 (ja) * 2005-11-15 2011-09-14 Ｊｆｅスチール株式会社 溶接性に優れた高張力厚鋼板およびその製造方法
JP4976905B2 (ja) 2007-04-09 2012-07-18 株式会社神戸製鋼所 Ｈａｚ靭性および母材靭性に優れた厚鋼板
JP5439887B2 (ja) * 2008-03-31 2014-03-12 Ｊｆｅスチール株式会社 高張力鋼およびその製造方法
EP2434027B1 (en) * 2009-05-22 2015-08-19 JFE Steel Corporation Steel material for high heat input welding
JP5493659B2 (ja) * 2009-09-30 2014-05-14 Ｊｆｅスチール株式会社 大入熱溶接熱影響部の靭性に優れた高強度鋼
JP5434437B2 (ja) * 2009-09-30 2014-03-05 Ｊｆｅスチール株式会社 大入熱溶接用鋼
JP5493658B2 (ja) * 2009-09-30 2014-05-14 Ｊｆｅスチール株式会社 大入熱溶接熱影響部靱性に優れた非調質厚肉高張力鋼の製造方法。
JP5526685B2 (ja) * 2009-09-30 2014-06-18 Ｊｆｅスチール株式会社 大入熱溶接用鋼

Also Published As

Publication number Publication date
TW201331387A (zh) 2013-08-01
CN103987869A (zh) 2014-08-13
CN103987869B (zh) 2017-06-27
TWI589708B (zh) 2017-07-01
BR112014014401B1 (pt) 2022-09-20
KR20140090682A (ko) 2014-07-17
WO2013088715A1 (ja) 2013-06-20
KR101608239B1 (ko) 2016-04-01
JPWO2013088715A1 (ja) 2015-04-27
JP5796636B2 (ja) 2015-10-21

Similar Documents

Publication Publication Date Title
BR112014014401A2 (pt) material de aço para soldagem com alta entrada de calor
BR112012018552A2 (pt) chapa de aço laminada a frio de alta resistência e método de produção da mesma
BR112019025042A2 (pt) Vergalhão laminado para aço para mola
BR112014015715A8 (pt) tubo de aço de alta resistência e chapa de aço de alta resistência excelentes em capacidade de deformação e tenacidade a baixa temperatura, e método de produção da chapa de aço
BR112014017042A8 (pt) chapa de aço laminada a frio e processo de fabrica-ção da mesma
BR112015005216A2 (pt) Liga de aço para aço de alta resistência e baixa liga
BR112019005395A2 (pt) material de aço, tubo de aço de poço de petróleo e método para produzir material de aço
BR112014030346A2 (pt) aço para materiais tubulares de campos de petróleo e método de produção do mesmo
BRPI0614604B1 (pt) tubo sem costura soldável e processo para produzir o mesmo
MX2019001794A (es) Lamina de acero laminada en frio de alta resistencia y el metodo para su produccion.
BR112015024854A2 (pt) chapa de aço laminada a quente e método para sua produção
BR112018068914A2 (pt) cano de aço inoxidável sem costura de alta resistibilidade para poço de óleo
MX2015007724A (es) Lamina de acero laminada en frio de alta resistencia con bajo limite de elasticidad y metodo para la fabricacion de la misma.
MX2014014205A (es) Estabilizador hueco y tuberia de acero para estabilizadores huecos y metodo de produccion de los mismos.
BR112015011302A2 (pt) chapa de aço laminada a quente com alta resistência que tem excelente endurecibilidade por cozimento e tenacidade de baixa temperatura com resistência à tração máxima de 980 mpa ou mais
BR112014029392A2 (pt) tubo de aço inoxidável sem costura de alta resistência para materiais tubulares de campos petrolíferos e método para produção do mesmo
BR112014002875A2 (pt) chapa de aço laminada a quente de alta razão de rendimento que tem excelente absorção de energia de impacto à baixa temperatura e resistência de amolecimento da haz, e método de produção da mesma
MX2012011254A (es) Tubo de acero sin costuras para tuberia y metodo para fabricar el mismo.
BR112014015440A2 (pt) chapa de aço de alta resistência revestida por imersão a quente para trabalho de prensagem excelente em tenacidade a baixa temperatura e resistência à corrosão e método para produção da mesma
BR112015032684A2 (pt) Junta soldada a ponto, conjunto de duas folhas de aço, método para produzir uma junta soldada a ponto, parte estrutural e veículo
MX2014011470A (es) Acero de alta resistencia con boro añadido para pernos y perno de alta resistencia que tiene una excelente resistencia a fractura retardada.
BRPI0813917A8 (pt) Liga de ferro-níquel-cromo-silício
BR112016015486A2 (pt) Cano de ferro e aço que contém cromo à base de martensita para poço de óleo
BRPI0805824A2 (pt) aço para forjamento
BR112018017191B8 (pt) Tubo de aço sem costura de alta resistência e de baixa liga para produtos tubulares de campos de petróleo

Legal Events

Date Code Title Description
B06T Formal requirements before examination [chapter 6.20 patent gazette]
B07A Application suspended after technical examination (opinion) [chapter 7.1 patent gazette]
B09B Patent application refused [chapter 9.2 patent gazette]
B12B Appeal against refusal [chapter 12.2 patent gazette]
B350 Update of information on the portal [chapter 15.35 patent gazette]
B16A Patent or certificate of addition of invention granted [chapter 16.1 patent gazette]

Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 12/12/2012, OBSERVADAS AS CONDICOES LEGAIS