BG64797B1 - Composition of paint for rusty steel surfaces - Google Patents

Composition of paint for rusty steel surfaces Download PDF

Info

Publication number
BG64797B1
BG64797B1 BG105719A BG10571901A BG64797B1 BG 64797 B1 BG64797 B1 BG 64797B1 BG 105719 A BG105719 A BG 105719A BG 10571901 A BG10571901 A BG 10571901A BG 64797 B1 BG64797 B1 BG 64797B1
Authority
BG
Bulgaria
Prior art keywords
pigments
composition
composition according
paint composition
surface paint
Prior art date
Application number
BG105719A
Other languages
Bulgarian (bg)
Other versions
BG105719A (en
Inventor
Иванка ЙОРДАНОВА
Original Assignee
"Оргахим" Ад
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by "Оргахим" Ад filed Critical "Оргахим" Ад
Priority to BG105719A priority Critical patent/BG64797B1/en
Publication of BG105719A publication Critical patent/BG105719A/en
Publication of BG64797B1 publication Critical patent/BG64797B1/en

Abstract

The invention relates to composition of paint for rusty steel surfaces, forming, in application, of smooth coatings having the effect of wrought iron. The composition shall find application in the manufacture of paints, which shall be directly applied on rusty steel surfaces in use residentially and in industry. It guarantees excellent adhesion of the products of the corrosion with the metal surface, their conversion into a solid base for anticorrosion and decorative protection, increased chemical resistance of the coating under different operational conditions in marine, tropical climates, in the petrochemical and the chemical industries. The paint includes synthetic resins, pigments, organic solvents, antiprecipitants, anticorrosion pigments, high molecular surfactants and in some case - fillers, anti-skin-formations, siccatives, structural additive, thixotropic additive, and additionally contains rust converter and penetration agent.

Description

(54) СЪСТАВ НА БОЯ ЗА РЪВДЯСАЛИ СТОМАНЕНИ ПОВЪРХНОСТИ(54) PAINT COMPOSITION for rusty steel surfaces

Област на техникатаTechnical field

Съставът е предназначен за получаване на боя, която се нанася директно върху ръждясали стоманени повърхности като парапети, огради, резервоари, електроносни съоръжения, мостови конструкции и други.The composition is intended to produce paint that is applied directly to rusty steel surfaces such as railings, fences, tanks, electronic equipment, bridge structures and more.

Предшестващо състояние на техникатаBACKGROUND OF THE INVENTION

Известен е състав за антикорозионна защита на повърхности от черни метали (1), който съдържа полиестерна смола и епокси модифицирана полиестерна смола или новолачна епокси смола, втвърдяващ агент, антикорозионен пигмент - стронциев хромат и/или калциев хромат или цинков фосфат, титанов двуокис.A composition for anticorrosive protection of ferrous metal surfaces (1) is known, which contains polyester resin and epoxy modified polyester resin or novolac epoxy resin, curing agent, anti-corrosion pigment - strontium chromate and / or calcium chromate or zinc phosphate, zinc phosphate.

Известен е състав за превантивна антикорозионна защита (2), съдържащ водно стъкло, натриев молибдат, амониев молибдат, цинккалциев молибдат, амониев молибдат, натриев фосфомолибдат, цинков прах.A composition for preventive corrosion protection (2) is known comprising water glass, sodium molybdate, ammonium molybdate, zinc-calcium molybdate, ammonium molybdate, sodium phosphomolybdate, zinc powder.

Известен е състав (3) за защита от корозия на стоманени повърхности, съдържащ следните компоненти: водоразтворими смоли - карбоксиетилцелулоза, хидроксиметилцелулоза, поливинилалкохол, полиакриламид и други, фосфорна киселина, натриев бензоат, калиев хромат, калиев бихромат или калиев триполифосфат, вода.Known composition (3) for corrosion protection of steel surfaces containing the following components: water-soluble resins - carboxyethylcellulose, hydroxymethylcellulose, polyvinyl alcohol, polyacrylamide and the like, phosphoric acid, sodium benzoate, potassium chromate, potassium bichromate.

Тези състави са предназначени за антикорозионна защита на метални повърхности, несъдържащи продукти от корозията на желязото или тези продукти са предварително отстранени по механичен път.These formulations are intended for the corrosion protection of metal surfaces which do not contain iron corrosion products or have been mechanically removed beforehand.

Техническа същност на изобретениетоSUMMARY OF THE INVENTION

Съставът съгласно изобретението съдържа синтетични смоли от 10,0 до 80,0, противоутаители 0,15-0,4, пигменти от 3,0 до 25,0, антикорозионни пигменти от 3,0 до 14,0, органични разтворители от 2,0 до 15,0, повърхностно активно вещество 0,15-0,5 и в даден случай структурна добавка до 0,2, сикативи до 5,0, пълнители до 50,0, противокожообразувател до 0,6, тиксотропираща добавка до 0,3. За осъществяване на по-дълбокото проникване в микропорите на ръждата и преобразува нето й в трудноразтворими съединения на желязото и осъществяване на антикорозионната защита. Съставът на боята за ръждясали стоманени повърхности допълнително съдържа следните компоненти: преобразувател на ръждата 1,5-5,0, пенетриращ агент 0,1-0,5, като преобразувател се използва танин в комбинация с органични естери на фосфорната киселина, като пенетриращ агент се използва смес от селекционирани алкохолсулфати или карбоксилен функционален полимер.The composition according to the invention contains synthetic resins from 10.0 to 80.0, anti-precipitation 0.15-0.4, pigments from 3.0 to 25.0, anti-corrosion pigments from 3.0 to 14.0, organic solvents from 2, 0 to 15.0, surfactant 0.15-0.5 and optionally structural additive up to 0.2, desiccants up to 5.0, fillers up to 50.0, antifoaming agent up to 0.6, thixotropic additive up to 0, 3. For deeper penetration into the micropores of rust and converting it into difficultly soluble compounds of iron and for corrosion protection. The composition of the rusty steel surface paint further comprises the following components: rust converter 1.5-5.0, penetrating agent 0.1-0.5, using tannin in combination with organic phosphoric acid esters as penetrating agent a mixture of selected alcohol sulfates or a carboxyl functional polymer is used.

Изобретението се отнася за състав на боя за защита от корозия на ръждясали повърхности от черни метали, образуваща при нанасяне гладки или с ефект на ковано желязо покрития. Той изпълнява функцията едновременно на преобразувател на ръждата грунд и декоративно покритие. Нанася се в 2-3 слоя с обща дебелина от 70 до 90 μ.The invention relates to a composition of paint for corrosion protection of rusty surfaces of ferrous metals, forming on the application of smooth or wrought iron coatings. It performs the function of both a rust primer and a decorative coating. Apply in 2-3 coats with a total thickness of 70 to 90 μ.

Съгласно изобретението в състава на боята за ръждясали стоманени повърхности синтетичните смоли са средномаслени алкидни смоли на база слънчогледови или соеви масла или мастни киселини със съдържание на сухо вещество от 55 до 60%, или нискомаслени алкидни смоли, или акрилатни смоли с втвърдител изоцианати, или епоксидни смоли с втвърдяващи агенти полиамиди или амини, или епоксиестери.According to the invention, the composition of the rust steel surface paint synthetic resins are medium-fat alkyd resins based on sunflower or soybean oils or fatty acids with a dry matter content of 55 to 60%, or low-fat alkyd resins or acrylate resins with isocyanate hardener or resins with curing agents polyamides or amines or epoxy esters.

Като противоутаители се използва електронеутрална сол на поликарбонова киселина с аминопроизводни в съчетание със силикон.The neutralizer is a polycarboxylic acid electroneutral salt with amine derivatives in combination with silicone.

Противокожообразувателят е метилетилкетоксим.The antagonist is methyl ethyl ketoxime.

Пълнителите са талк или бариев сулфат. Като пигменти обект на изобретението се използват - титанов двуокис и/или железоокисни пигменти и/или фталоцианинови органични пигменти и/или сажди.The fillers are talc or barium sulfate. The pigments of the invention are titanium dioxide and / or iron oxide pigments and / or phthalocyanine organic pigments and / or carbon black.

Като антикорозионни пигменти се използват цинков фосфат или цинков фосфат-алуминиев фосфат или цинков прах или алуминиев прах.Zinc phosphate or zinc phosphate-aluminum phosphate or zinc powder or aluminum powder are used as anti-corrosion pigments.

Като нискомолекулно повърхностно активно вещество се използват емулгатори от анионактивен тип алкилфосфати или алкилсукцинати или Na-алкил фенол пол игликолов етер сулфат или нафталинсулфонати или от нейоногенен тип - етоксилирани алкилфеноли или етоксилирани алкохоли.As an low molecular weight surfactant, anionic emulsifiers of the alkyl phosphates or alkyl succinate or Na-alkyl phenol sex needles ether sulfate or naphthalenesulfonates or non-ionic type - ethoxylated alkylphenols or ethoxylated.

Като тиксотропираща добавка в състава на боята за ръждясали стоманени повър хности се използват бентонити.Benthonite is used as a thixotropic additive in the composition of the paint for rusty steel surfaces.

Структурната добавка е силиконово масло.The structural additive is silicone oil.

Органичните разтворители са: бутанол и/ или ксилол, и/или толуол, и/или метилизобутилкетон, и/или бутилацетат, и/или метоксипропилацетат.The organic solvents are: butanol and / or xylene, and / or toluene, and / or methyl isobutyl ketone, and / or butyl acetate, and / or methoxypropyl acetate.

Сикативите са оловен нафтенат -11% и/ или кобалтов нафтенат - 4%, и/или калциев нафтенат -10%.The desiccants are lead naphthenate -11% and / or cobalt naphthenate-4% and / or calcium naphthenate -10%.

Съставът на боята за ръждясали стоманени повърхности съгласно изобретението осигурява дълбоко проникване на отделните компоненти в микропорите на ръждата и преобразуването й в трудно разтворими комплексни соли на желязото. Той осигурява отлична антикорозионна защита и химическа устойчивост в различни условия на експлоатация - морски, тропически климат, в химическата и нефтопреработващата индустрия.The composition of the rusty steel surface paint according to the invention provides deep penetration of the individual components into the micropores of the rust and its transformation into difficultly soluble complex salts of iron. It provides excellent corrosion protection and chemical resistance in various operating conditions - marine, tropical, chemical and petroleum industries.

Съставът осигурява регулирана скорост на съхнене на покритието, което е в непосредствена връзка с високата му пенетрираща способност.The composition provides an adjustable drying rate of the coating that is directly related to its high penetrating power.

Съставът на боята за ръждясали стоманени повърхности дава възможност за отлично сцепление на продуктите от корозията с металната повърхност и превръщането им в здрава основа за антикорозионна и декоративна защита.The composition of the paint for rusty steel surfaces enables excellent adhesion of the corrosion products to the metal surface and turns them into a solid base for corrosion and decorative protection.

Примери за изпълнение на изобретениетоExamples of carrying out the invention

Пример 1. Съставът е в тегл.ч.: Example 1. The composition is in parts by weight: Средномаслена алкидна Medium oil alkyd смола 55 - 60% resin 55 - 60% 58,0 58,0 Титанов двуокис Titanium dioxide 20,0 20,0 Цинков фосфат Zinc phosphate 6,5 6.5 Преобразувател Converter 3,0 3.0 Оловен талат 11% Lead Talat 11% 2,2 2.2 Кобалтов нафтенат 4% Cobalt naphthenate 4% 0,7 0.7 Калциев нафтенат 10% Calcium naphthenate 10% 0,2 0.2 Пенетриращ агент Penetrating agent 0,3 0.3 Противоутаител Counterweight 0,17 0.17 Бентоне 38 Benton 38 0,1 0.1 Бутанол Butanol 0,2 0.2 Ортоксилол Orthoxylol 7,0 7.0 Повърхностно активно Surface active вещество substance 0,15 0.15 Метил етилкетоксим Methyl ethylethoxime 0,5 0.5 В съд, снабден с дисолвер, се дозират They are dispensed in a dish equipped with a dissolver

част от алкидната смола, част от о-ксилола, преобразувателят, цинков фосфат, титанов двуокис, пенетриращ агент, противоутаителят, повърхностно активното вещество, приготвената предварително паста от Бентоне 38 в бутанол и о-ксилол. Сместа се хомогенизира 15-20 min на дисолвер с 650-1200 об./min. Подготвената паста се диспергира на перлова мелница. В хомогенизатор се дозират останалата част от алкидната смола, о-ксилола, сикативите, метил етилкетоксим. При непрекъснато разбъркване се дозира пастата, диспергирана на перловата мелница. След приключване на диспергирането на пастата, сместа в хомогенизатора се разбърква още около 20 min.part of the alkyd resin, part of o-xylene, transducer, zinc phosphate, titanium dioxide, penetrating agent, antioxidant, surfactant, pre-prepared bentone 38 paste in butanol and o-xylene. The mixture was homogenized for 15-20 minutes on a 650-1200 rpm dissolver. The prepared paste is dispersed on a pearl mill. The rest of the alkyd resin, o-xylene, desiccants, methyl ethylketoxime are dosed in the homogenizer. With continuous stirring, the paste dispersed on the pearl mill is dosed. After the paste has been dispersed, the mixture in the homogenizer is stirred for about 20 minutes.

Пример 2. Съставът е в тегл.ч. :Example 2. The composition is in wt. :

Съставът и изпълнението са, както в пример 1, като вместо титанов двуокис се дозират 12,0 тегл.ч. железоокисни пигменти и вместо цинков фосфат се дозират 9,0 тегл.ч. цинков фосфат - алуминиев фосфат.The composition and embodiment are as in Example 1, with 12.0 parts by weight instead of titanium dioxide. iron oxide pigments and 9.0 parts by weight instead of zinc phosphate. zinc phosphate - aluminum phosphate.

Пример 3. Съставът е в тегл.ч.Example 3. The composition is in parts by weight.

Съставът и изпълнението са, както в пример 1, като вместо титанов двуокис се дозират 7,0 тегл.ч. фталоцианинови органични пигменти или комбинация от 15,0 тегп.ч. титанов двуокис и 2,7 тегл.ч. фталоцианинови органични пигменти.The composition and embodiment are as in Example 1, with 7.0 parts by weight instead of titanium dioxide. phthalocyanine organic pigments or a combination of 15.0 ppm titanium dioxide and 2.7 parts by weight phthalocyanine organic pigments.

Пример 4. Съставът е в тегл.ч.Example 4. The composition is by weight.

Съставът и изпълнението са както в пример 1, като вместо титанов двуокис се дозират 3,0 тегл.ч. сажди.The composition and embodiment are as in Example 1, with 3.0 parts by weight instead of titanium dioxide. soot.

Пример 5. Съставът е в тегл.ч. Example 5. The composition is by weight. Средномаслена алкидна Medium oil alkyd смола 55 - 60% resin 55 - 60% 74,0 74,0 Алуминиева паста Aluminum paste 9,0 9.0 Преобразувател Converter 5,0 5.0 Повърхностно активно Surface active вещество substance 0,2 0.2 Оловен талат 11% Lead Talat 11% 2,7 2.7 Кобалтов нафтенат 4% Cobalt naphthenate 4% 0,9 0.9 Калциев нафтенат 10% Calcium naphthenate 10% 0,2 0.2 Противоутаител Counterweight о,з oh, with Ортоксилол Orthoxylol 7,5 7.5 Пенетриращ агент Penetrating agent о,з oh, with Метил етилкетоксим Methyl ethylethoxime 0,5 0.5 В съд с дисолвер с 650-1200 об./min при In a dishwasher with 650-1200 rpm at

непрекъснато разбъркване се дозират съставните компоненти в следния ред: алкидна смола, о-ксилол, противоутаител, преобразувател, сикативи, алуминиева паста, метилетилкетоксим, пенетриращ агент, повърхностно активно вещество. Сместа се хомогенизира от 20 до 30 min при промяна на оборотите във възходящ ред.The constituents are dosed continuously in the following order: alkyd resin, o-xylene, antioxidant, transducer, desiccants, aluminum paste, methyl ethyl ketoxime, penetrating agent, surfactant. The mixture was homogenized for 20 to 30 min as the rpm changes.

Полученият състав на боята за ръждясали стоманени повърхности намира приложение за изготвяне на покрития за електропреносни съоръжения. Покритията с дебелина 80-90 μ имат устойчивост на 3% разтвор на натриевThe resulting composition of paint for rusty steel surfaces is used for the preparation of coatings for power transmission equipment. Coatings 80-90 μm thick have a resistance to 3% sodium solution

хлорид - 500 - 700 h. chloride - 500 - 700 h. Пример 6. Съставът е в тегл.ч. EXAMPLE 6 The composition is by weight. Средномаслена алкидна Medium oil alkyd смола 55 - 60% resin 55 - 60% 71,0 71,0 Алуминиева паста Aluminum paste 6,0 6.0 Титанов двуокис Titanium dioxide 0,7 0.7 Микроталк Microtalk 6,0 6.0 Толуол Toluene 8,0 8.0 Преобразувател Converter 3,5 3.5 Повърхностно активно Surface active вещество substance 0,2 0.2 Оловен талат 11% Lead Talat 11% 2,5 2.5 Кобалтов нафтенат 4% Cobalt naphthenate 4% 0,8 0.8 Калциев нафтенат 10% Calcium naphthenate 10% 0,2 0.2 Противоутаител Counterweight о,з oh, with Структурна добавка Structural additive 0,09 0.09 Пенетриращ агент Penetrating agent 0,35 0.35 Метилетилкетоксим Methyl ethyl ketoxime 0,5 0.5 В съд с дисолвер с 650- In a 650- 1200 об./min 1200 rpm

дозират част от алкидната смола, част от о-ксилола, титанов двуокис, микроталк, противоутаител, пенетриращ агент, повърхностно активно вещество. След разбъркване 15-20 min на дисолвера при възходяща промяна на оборотите от 650 до 1200 об./min, пастата се диспергира на перлова мелница. В съд с дисолвер с 650-1200 об./min се дозират останалите компоненти: алкидна смола, о-ксилол, алуминиева паста, преобразувател, сикативи, структурна добавка, метилетилкетоксим, диспергираната паста на перлова мелница. Сместа се хомогенизира 20 min при 650-1200 об./min на дисолвер.dosage part of the alkyd resin, part of o-xylene, titanium dioxide, microtalc, anti-precipitation agent, penetrating agent, surfactant. After stirring for 15-20 min at the disolver at an ascending change in speed from 650 to 1200 rpm, the paste was dispersed on a pearl mill. The other components are dosed in a 650-1200 rpm dissolver container: alkyd resin, o-xylene, aluminum paste, transducer, siccatives, structural additive, methyl ethyl ketoxime, pearl mill dispersed paste. The mixture was homogenized for 20 min at 650-1200 rpm per dissolver.

Полученият състав е с ефект на ковано желязо на покритията. Намира приложение за боядисване на ръждясали стоманени повърхности в бита, приборостроенето и други.The resulting composition has the effect of wrought iron coatings. Finds application for painting of rusty steel surfaces in everyday life, instrument making and others.

Пример 7. Съставът е в тегл.ч.EXAMPLE 7 The composition is by weight.

Съставът и изпълнението е, както в пример 6, като вместо титанов двуокис се използват 0,8 тегл.ч. фталоцианинови органични пигменти или 0,7 тегл.ч. сажди.The composition and embodiment is as in Example 6, using 0.8 parts by weight instead of titanium dioxide. phthalocyanine organic pigments or 0.7 parts by weight soot.

Пример 8. Съставът е в тегл.ч.EXAMPLE 8 The composition is by weight.

Нискомаслена алкидна смола 60% в ксилол 60,0Low fat alkyd resin 60% in xylene 60.0

Титанов двуокис Titanium dioxide 18,0 18,0 Цинков фосфат Zinc phosphate 9,0 9.0 Преобразувател Converter 4,0 4.0 Пенетриращ агент Penetrating agent 0,4 0.4 Противоутаител Counterweight о,з oh, with Повърхностно активно Surface active вещество substance о,з oh, with Бентоне38 Benton38 0,2 0.2 Бутанол Butanol 0,2 0.2 Ортоксилол Orthoxylol 7,5 7.5 Втвърдител - изоцианати Hardener - isocyanates 1,6 1.6 Диспергирането на пигментите се извър- The dispersion of the pigments is carried out

шва на дисолвер с обороти 650-1200 об./min и перлова мелница, както в пример 1.a seam of a dissolver with revolutions 650-1200 rpm and a pearl mill, as in example 1.

Съставът на боята за ръждясали стоманени повърхности е предназначен за формулиране на ал кидуретанови покрития за експлоатация в нормален, влажен и тропически климат, в химическата и нефтопреработваща индустрия.The composition of the paint for rusty steel surfaces is intended for the formulation of al-kydurethane coatings for use in normal, humid and tropical climates, in the chemical and petroleum industries.

Пример 9. Съставът е в тегл.ч.EXAMPLE 9 The composition is by weight.

Съставът и изпълнението е както в пример 8, като вместо цинков фосфат се дозират 9,0 тегл.ч. цинков фосфат алуминиев фосфат и вместо титанов двуокис се дозират 8,0 тегл.ч. фталоцианинови органични пигменти.The composition and embodiment are as in Example 8, with 9.0 parts by weight instead of zinc phosphate. zinc phosphate aluminum phosphate and instead of titanium dioxide are dosed 8.0 parts by weight. phthalocyanine organic pigments.

Пример 10. Съставът е в тегл.ч.EXAMPLE 10 The composition is by weight.

Съставът и изпълнението е, както в пример 8, като вместо титанов двуокис се дозират 12,0 тегл.ч. железоокисни пигменти или комбинация от 5,0 тегл.ч. железоокисни пигменти и 12,0 тегл.ч. титанов двуокис.The composition and embodiment was as in Example 8, with 12.0 parts by weight of titanium dioxide instead. iron oxide pigments or a combination of 5.0 parts by weight iron oxide pigments and 12.0 parts by weight titanium dioxide.

Пример 11. Съставът е в тегл.ч. Example 11. The composition is by weight. Нискомаслена алкидна Low fat alkyd смола 60% в ксилол resin 60% in xylene 80,0 80,0 Алуминиева паста Aluminum paste 10,0 10,0 Преобразувател Converter 3,0 3.0 Повърхностно активно Surface active вещество substance 0,3 0.3 Противоутаител Counterweight 0,2 0.2 Пенетриращ агент Penetrating agent 0,45 0.45 Ортоксилол Orthoxylol 6,0 6.0 Втвърдител - изоцианати Hardener - isocyanates 1,5 1.5 Изпълнението на състава е както в при- The performance of the composition is as in Пример 12. Съставът е в тегл.ч. EXAMPLE 12 The composition is by weight. Нискомаслена алкидна Low fat alkyd смола 60% в ксилол resin 60% in xylene 73,0 73,0 Титанов двуокис Titanium dioxide 10,0 10,0 Алуминиева паста Aluminum paste 5,5 5.5 Толуол Toluene 8,5 8.5 Структурна добавка Structural additive 0,085 0,085

Пенетриращ агент Penetrating agent 0,5 0.5 Преобразувател Converter 3,0 3.0 Повърхностно активно Surface active вещество substance 0,2 0.2 Втвърдител - изоцианати Hardener - isocyanates 1,8 1.8 Изпълнението на състава е, The performance of the composition is, както в при- as in

мер 6. Покритията са с ефект на ковано желязо.measure 6. The coatings are wrought iron.

Пример 13. Съставът е в тегл.ч.EXAMPLE 13 The composition is by weight.

Съставът и изпълнението е, както в пример 12, като вместо титанов двуокис се използват 2,5 тегл.ч. фталоцианинови органични пигменти или 7,0 тегл.ч. сажди.The composition and embodiment is as in Example 12, using 2.5 parts by weight instead of titanium dioxide. phthalocyanine organic pigments or 7.0 parts by weight soot.

Формулираните покрития са с ефект на ковано желязо.The formulated coatings are wrought iron.

Пример 14. Съставът е в тегл.ч. EXAMPLE 14 The composition is by weight. Епоксидна смола Epoxy resin 40,0 40,0 Титанов двуокис Titanium dioxide 15,0 15.0 Цинков фосфат Zinc phosphate 9,0 9.0 Бариев сулфат Barium sulphate 20,0 20,0 Бентоне 38 Benton 38 0,7 0.7 Метилизобутилкетон Methyl isobutyl ketone 8,0 8.0 Бутанол Butanol 0,2 0.2 Метоксипропилацетат Methoxypropyl acetate 2,0 2.0 Повърхностно активно Surface active вещество substance 0,15 0.15 Преобразувател Converter 4,5 4.5 Пенетриращ агент Penetrating agent о,з oh, with Противоутаител Counterweight 0,2 0.2 Втвърдител - полиамиди Hardener - polyamides 2,7 2.7 Редът и последователността на дозира- The order and sequence of dosage-

не на съставните компоненти, диспергирането на перлова мелница е, както в пример 1.not of the constituent components, the dispersion of a pearl mill is as in Example 1.

Полученият състав на боята за ръждясали стоманени повърхности намира приложение за изготвяне на химически устойчиви покрития за химическата и нефтопреработвателната индустрия.The resulting paint composition for rusty steel surfaces is used for the preparation of chemically resistant coatings for the chemical and petroleum refining industries.

Пример 15. Съставът е в тегл.ч.EXAMPLE 15 The composition is by weight.

Съставът и изпълнението е, както в пример 14, като вместо цинков фосфат се дозира 8,0 тегл.ч. цинков фосфат-алуминиев фосфат.The composition and embodiment was as in Example 14, with a dose of 8.0 parts by weight instead of zinc phosphate. zinc phosphate-aluminum phosphate.

Пример 16. Съставът е в тегл.ч.EXAMPLE 16 The composition is by weight.

Съставът и изпълнението е, както в пример 14, като вместо титанов двуокис се дозират 6,0 тегл.ч. фталоцианинови органични пигменти.The composition and embodiment were as in Example 14, with 6.0 parts by weight of titanium dioxide instead. phthalocyanine organic pigments.

Пример 17. Съставът е в тегл.ч.EXAMPLE 17 The composition is by weight.

Съставът и изпълнението е както в пример 14, като вместо титанов двуокис се дозират 9,0 тегл.ч. железоокисни пигменти и вместо цинков фосфат се дозира 9,0 тегл.ч. цинковThe composition and embodiment were as in Example 14, with 9.0 parts by weight of titanium dioxide instead. iron oxide pigments and 9.0 parts by weight instead of zinc phosphate. zinc

фосфат - алуминиев фосфат и вместо phosphate - aluminum phosphate instead втвър- hard- дител - полиамиди се използват 2,7 Diethyl Polyamides 2.7 are used тегл.ч. wt.h. аминни - втвърдители. amine - hardeners. Пример 18. Съставът е в тегл.ч. EXAMPLE 18 The composition is by weight. Въздушно съхнещ Air-drying епоксиестер - 60% epoxy ester - 60% 12,0 12,0 Цинков прах Zinc dust 75,0 75,0 Бентоне 38 Benton 38 0,7 0.7 Бутанол Butanol 0,2 0.2 Повърхностно активно Surface active вещество substance о,з oh, with Преобразувател Converter 1,5 1.5 Пенетриращ агент Penetrating agent 0,1 0.1 Кобалтов нафтенат 4% Cobalt naphthenate 4% 0,9 0.9 Ортоксилол Orthoxylol 9,0 9.0 Изпълнението на състава се осъществя- Composition of the composition is carried out- ва в ред и последователност, както в пример 1. in order and sequence as in Example 1. Пример 19. Съставът е в тегл.ч. EXAMPLE 19 The composition is by weight. Акрилатна смола - 60% Acrylate resin - 60% 63,0 63.0 Титанов двуокис Titanium dioxide 18,0 18,0 Бентоне 38 Benton 38 0,2 0.2 Повърхностно активно Surface active вещество substance 0,15 0.15 Преобразувател Converter 0,45 0.45 Пенетриращ агент Penetrating agent 0,3 0.3 Цинков фосфат - алуминиев Zinc phosphate is aluminum фосфат phosphate 0,7 0.7 Бутанол Butanol 0,2 0.2 Бутил ацетат Butyl acetate 5,0 5.0 Ортоксилол Orthoxylol 2,0 2.0 Противоутаител Counterweight 0,3 0.3 Втвърдител-изоцианати Isocyanate hardener 1,9 1.9 Изпълнението на състава се осъществя- Composition of the composition is carried out-

ва в ред и последователност, както в пример 1. Съставът на боята за ръждясали стоманени повърхности е предназначен за формулиране на акрилатуретанови покрития за експлоатация в химически агресивна среда, тропически климат.The composition of the paint for rusty steel surfaces is intended for the formulation of acryl-urethane coatings for use in chemically aggressive environments, tropical climates.

Пример 20. Съставът е в тегл.ч.EXAMPLE 20 The composition is by weight.

Съставът и изпълнението е, както в пример 19, като вместо титанов двуокис се използват 0,8 тегл.ч. фталоцианинови органични пигменти или комбинация от 13,0 тегл.ч. титанов двуокис и 3,0 тегл.ч. фталоцианинови органични пигменти.The composition and embodiment is as in Example 19, using 0.8 parts by weight instead of titanium dioxide. phthalocyanine organic pigments or a combination of 13.0 parts by weight titanium dioxide and 3.0 parts by weight phthalocyanine organic pigments.

Пример 21. Съставът е в тегл.ч.EXAMPLE 21 The composition is by weight.

Съставът и изпълнението е, както в пример 19, като вместо титанов двуокис се използват 12,0 тегл.ч. железоокисни пигменти и вместо цинков фосфат-алуминиев фосфат се дозират 8,5 тегл.ч. цинков фосфат.The composition and embodiment is as in Example 19, using 12.0 parts by weight of titanium dioxide instead. iron oxide pigments and 8.5 parts by weight instead of zinc phosphate-aluminum phosphate. zinc phosphate.

Claims (11)

Патентни претенцииClaims 1. Състав на боя за ръждясали стоманени повърхности, образуваща при нанасяне гладки или с ефект на ковано желязо покри- $ тия, съдържащ синтетични смоли, пигменти, органични разтворители, противоутаители, антикорозионни пигменти, нискомолекулно повърхностно активно вещество и в дадени случаи пълнители, противокожообразуватели, сикативи, структурни добавки, тиксотропираща добавка, характеризиращ се с това, че допълнително съдържа в комбинация следните компоненти: преобразувател на ръждата 1,5-5,0 и пенетриращ агент 0,1-0,5, като преобразувателят на ръждата е танин в комбинация с органични естери на фосфорната киселина, а пенетриращият агент е смес от селекционирани алкохолсулфати или карбоксилен функционален полимер, а останалите компоненти са в следните количества - синтетични смоли от 10,0 20 до 80,0, пигменти от 3,0 до 25,0, противоутаители 0,15-0,4, антикорозионни пигменти от 3,0 до 14,0, нискомолекулно повърхностно активно вещество 0,15-0,5, органични разтворители от 2,0 до 15,0, тиксотропираща добавка до 0,3, 25 сикативи до 5,0, структурна добавка до 0,2, противокожообразувател до 0,6, пълнители до 50,0.1. Composition of paint for rusted steel surfaces forming smooth or wrought-iron coatings containing synthetic resins, pigments, organic solvents, anti-corrosion agents, anticorrosive pigments, low molecular weight surfactants and, in some cases, the fullest , desiccants, structural additives, thixotropic additive, characterized in that it further comprises in combination the following components: a rust converter 1.5-5.0 and a penetrating agent 0.1-0.5 as the converter the t of rust is tannin in combination with the organic esters of phosphoric acid, the penetrating agent is a mixture of selected alcohol sulfates or a carboxyl functional polymer and the other components are in the following amounts - synthetic resins from 10.0 to 20.0, 80.0, pigments from 3 , 0 to 25.0, anti-precipitation 0.15-0.4, anti-corrosion pigments 3.0 to 14.0, low molecular weight surfactant 0.15-0.5, organic solvents 2.0 to 15.0, thixotropic additive up to 0.3, 25 siccatives up to 5.0, structural additive up to 0.2, antifoam up to 0.6, fillers up to 50.0. 2. Състав на боя за ръждясали стоманени повърхности съгласно претенция 1, характеризиращ се с това, че синтетичните смоли зо са средномаслени алкидни смоли на база слънчогледови или соеви масла или мастни киселини със съдържание на сухо вещество от 55 до 60% или нискомаслени алкидни смоли с втвърдител изоцианати, или акрилатни смоли с втвърдител изоцианати или епоксидни смоли с втвърдяващи аген ти полиамиди или амини, или епоксиестери.2. A rusty steel surface paint composition according to claim 1, characterized in that the synthetic resins 3o are medium-fat alkyd resins based on sunflower or soybean oils or fatty acids with a dry matter content of 55 to 60% or low-fat alkyd resins with isocyanate hardener or acrylate resins with isocyanate hardener or epoxy resins with curing agents polyamides or amines or epoxy esters. 3. Състав на боя за ръждясали стоманени повърхности съгласно претенция 1, характеризи ращ се с това, че пигментите са титанов двуокис и/или железооксидни пигменти, и/или фталоцианинови органични пигменти, и/или сажди.3. The composition of the rusty steel surface paint according to claim 1, characterized in that the pigments are titanium dioxide and / or iron oxide pigments and / or phthalocyanine organic pigments and / or carbon black. 4. Състав на боя за ръждясали стоманени повърхности съгласно претенция 1, харак теризиращ се с това, че противоутаителят е електронеутрална сол на поликарбонова кисе лина с аминопроизводни в съчетание със силикон.A rust-proofed steel surface paint composition according to claim 1, characterized in that the antifouling agent is an electroneutral salt of polycarboxylic acid with amine derivatives in combination with silicone. 5. Състав на боя за ръждясали стоманени повърхности съгласно претенция 1, характеризиращ се с това, че тиксотропиращата добавка е бентонит.5. A rusty steel surface paint composition according to claim 1, characterized in that the thixotropic additive is bentonite. 6. Състав на боя за ръждясали стоманени повърхности съгласно претенция 1, характеризиращ се с това, че структурната добавка е силиконово масло.6. Rusted steel surface paint composition according to claim 1, characterized in that the structural additive is silicone oil. 7. Състав на боя за ръждясали стоманени повърхности съгласно претенция 1, характеризиращ се с това, че сикативите са оловен нафтенат 11% и/или кобалтов нафтенат 4%, и/ или калциев нафтенат 10%.7. The composition of the paint for rusted steel surfaces according to claim 1, characterized in that the desiccants are lead naphthenate 11% and / or cobalt naphthenate 4% and / or calcium naphthenate 10%. 8. Състав на боя за ръждясали стоманени повърхности съгласно претенция 1, характеризиращ се с това, че органичните разтворители са бутанол и/или ксилол, и/или толуол, и/или мстилизобутилкетон, и/или бутилацетат, и/или метоксипропилацетат.A corrosion-resistant steel surface paint composition according to claim 1, characterized in that the organic solvents are butanol and / or xylene and / or toluene and / or mystyl isobutyl ketone and / or butyl acetate and / or methoxypropyl acetate. 9. Състав на боя за ръждясали стоманени повърхности съгласно претенция 1, характеризиращ се с това, че противокожообразувателят е метилетилкетоксим.9. A corrosion-resistant steel surface paint composition according to claim 1, characterized in that the antipyretic is methylethylketoxime. 10. Състав на боя за ръждясали стоманени повърхности съгласно претенция 1, характеризиращ се с това, че пълнителите са микроталк или бариев сулфат.A rust steel surface paint composition according to claim 1, characterized in that the fillers are microtalc or barium sulphate. И. Състав на боя за ръждясали повърхности съгласно претенция 1, характеризиращ се с това, че нискомолекулното повърхностно вещество е емулгатор от анионактивен тип - алкилфосфати или алкилсукцинати, или Na - алкилфенолполигликолов етер сулфат, или нафталинсулфонати, или от нейоногенен тип - етоксилирани алкилфеноли, или етоксилирани алкохолиI. A rusty surface paint composition according to claim 1, characterized in that the low molecular weight surfactant is an anionic type emulsifier - alkylphosphates or alkyl succinates, or Na - alkylphenolpolyglycol ether sulfate, or naphthalenol, or naphthalenol, or naphthalenol ethoxylated alcohols 12. Състав на боя за ръждясали стоманени повърхности съгласно претенция 1, характеризиращ се с това, че антикорозионните пигменти са цинков фосфат или цинков фосфат-алуминиев фосфат, или цинков прах, или алуминиев прах.A rust-proofed steel paint composition according to claim 1, characterized in that the anti-corrosion pigments are zinc phosphate or zinc phosphate-aluminum phosphate or zinc powder or aluminum powder.
BG105719A 2001-07-19 2001-07-19 Composition of paint for rusty steel surfaces BG64797B1 (en)