AU2020101333A4 - An ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile preparation method - Google Patents
An ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile preparation method Download PDFInfo
- Publication number
- AU2020101333A4 AU2020101333A4 AU2020101333A AU2020101333A AU2020101333A4 AU 2020101333 A4 AU2020101333 A4 AU 2020101333A4 AU 2020101333 A AU2020101333 A AU 2020101333A AU 2020101333 A AU2020101333 A AU 2020101333A AU 2020101333 A4 AU2020101333 A4 AU 2020101333A4
- Authority
- AU
- Australia
- Prior art keywords
- resistant
- parts
- ultraviolet
- electromagnetic
- radiation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
a b s t r a c t
The invention discloses an ultraviolet-resistant and electromagnetic-radiation-resistant
multifunctional textile preparation method,which comprises: firstly, preparing an
ultraviolet-resistant and electromagnetic-radiation-resistant finishing agent; and secondly, finishing
a textile base cloth with the ultraviolet-resistant and electromagnetic-radiation-resistant finishing
5 agent to obtain the ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional
textile, wherein the ultraviolet-resistant and electromagnetic-radiation-resistant finishing agent
comprises the following constituents based on parts by weight: 5-8 parts of nanometer titanium
dioxide, 3-4 parts of nanometer zirconium oxide, 3-4 parts of nanosilver particle, 5-6 parts of
chitosan, 6-8 parts of fullerene carbon nanomaterial, 5-6 parts of polydimethylsiloxane, 3-4 parts of
10 modified polysiloxane, 8-10 parts of methylbenzene, 1-2 parts of silicone emulsion, 2-4 parts of
alkylphenol ethoxylate, 2-3 parts of 2-butoxyethanol and 4-5 parts of glycerol. Furthermore,
toughness, strength and hand feeling of the obtained ultraviolet-resistant and
electromagnetic-radiation-resistant multifunctional textile are not substantially affected, and the
ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile has excellent
15 ultraviolet-resistant and electromagnetic-radiation-resistant properties.
Description
Editorial Note 2020101333 There is only five pages of the description
[0001] The present invention relates to the technical field of textile auxiliaries, in particular to an ultraviolet-resistant and electromagnetic-radiation-resistant
multifunctional textile preparation method.
[0002] Ultraviolet ray accounts for about 6% of sunlight. An appropriate amount of ultraviolet radiation has a bactericidal effect and can promote the synthesis of vitamin D,
thereby being beneficial for human health. However, UV-A can penetrate through
epidermal tissue, resulting in elasticity losing muscle and rough skin to form wrinkles,
and UV-B is correlated to carcinogenic substances. Ultraviolet-resistant textiles are
textiles having high absorption and reflection ability on ultraviolet rays. With the
development of science and technology, the influence of electromagnetic radiation on the
life and work of people is more and more serious. CN104047173A discloses a permanent
electromagnetic shielding fabric, which can effectively shield electromagnetic waves and
is good in shielding property, while it is poor in binding strength with fabrics and poor in
corrosion resistance, and can affect the flexibility of the fabrics. At present, after
multifunctional coating fabric finishing agents capable of resisting to ultraviolet ray and
also having electromagnetic shielding property is used, some fabrics are poor in
ultraviolet-resistant property, and some fabrics vary significantly in toughness, strength,
and hand feeling before processing although having ultraviolet-resistant and
electromagnetic-radiation-resistant properties. Therefore, an ultraviolet-resistant and
electromagnetic-radiation-resistant multifunctional textile are desirable, which can ensure ultraviolet-resistant and electromagnetic-radiation-resistant properties and also maintain the stability of toughness, strength, and hand feeling of the textile.
[0003] The present invention aims to provide an ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile preparation method.
[0004] In over to achieve the above purposes, the present invention adopts the following content:
[0005] An ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile preparation method comprises: firstly, preparing an ultraviolet-resistant and electromagnetic-radiation-resistant finishing agent; and secondly, finishing a textile base cloth with the ultraviolet-resistant and electromagnetic-radiation-resistant finishing agent to obtain the ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile, wherein the ultraviolet-resistant and electromagnetic-radiation-resistant finishing agent comprises the following constituents based on parts by weight: 5-8 parts of nanometer titanium dioxide, 3-4 parts of nanometer zirconium oxide, 3-4 parts of nanosilver particle, 5-6 parts of chitosan, 6-8 parts of fullerene carbon nanomaterial, 5-6 parts of polydimethylsiloxane, 3-4 parts of modified polysiloxane, 8-10 parts of methylbenzene, 1-2 parts of silicone emulsion, 2-4 parts of alkylphenol ethoxylate, 2-3 parts of 2-butoxyethanol and 4-5 parts of glycerol.
[0006] Furthermore, finishing comprises: placing the ultraviolet-resistant and electromagnetic-radiation-resistant finishing agent in an immersion tank, and then impregnating and finishing the textile base cloth to obtain the ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile.
[0007] Furthermore, impregnating and finishing comprise: carrying out drying after impregnation for twice.
[0008] Furthermore, impregnating and finishing comprise: firstly, placing the ultraviolet resistant and electromagnetic-radiation-resistant finishing agent in the immersion tank, and impregnating the textile base cloth at room temperature for 25-30 minutes; secondly, pumping an impregnating system to negative pressure, and impregnating for 10-15 minutes, wherein vacuum degree is 0.04-0.05MPa; and finally, drying at 65-67 DEG C for 1-1.5 hours, and standing at the room temperature for 22-24 hours to prepare the ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile.
[0009] The present invention has the following advantages: according to the ultraviolet resistant and electromagnetic-radiation-resistant multifunctional textile preparation method, raw materials are low in cost and available, the process is simple, and no stimulation to a human body is generated. Toughness, strength, and hand feeling of the obtained ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile are not substantially affected, and the ultraviolet-resistant and electromagnetic radiation-resistant multifunctional textile has excellent ultraviolet-resistant and electromagnetic-radiation-resistant properties and is washable.
[0010] For clearer descriptions of the present invention, the present invention is described in detail below regarding the preferred embodiments. Those skills in the art
shall understand that the contents described in detail below are intended to be illustrative
and not restrictive, and the protection scope of the present invention shall not be limited
by these contents.
[0011] Embodiment 1
[0012] An ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile preparation method comprises: firstly, preparing an ultraviolet-resistant and
electromagnetic-radiation-resistant finishing agent, wherein the ultraviolet-resistant and
electromagnetic-radiation-resistant finishing agent comprises the following constituents
based on parts by weight: 6 parts of nanometer titanium dioxide, 4 parts of nanometer
zirconium oxide, 4 parts of nanosilver particle, 6 parts of chitosan, 6 parts of fullerene
carbon nanomaterial, 5 parts of polydimethylsiloxane, 3 parts of modified polysiloxane, 8
parts of methylbenzene, 1 part of silicone emulsion, 2 parts of alkylphenol ethoxylate, 2
parts of 2-butoxyethanol and 4 parts of glycerol, and the ultraviolet-resistant and
electromagnetic-radiation-resistant finishing agent is prepared by mixing and dispersing the raw materials; secondly, placing the ultraviolet-resistant and electromagnetic radiation-resistant finishing agent in an immersion tank, and impregnating a textile base cloth at a room temperature for impregnation for 26 minutes; thirdly, pumping an impregnating system to a negative pressure, and impregnating for 12 minutes, wherein vacuum degree is 0.045MPa; and finally, drying at 66 DEG C for 1.2 hours, and standing at the room temperature for 24 hours to prepare the ultraviolet-resistant and electromagnetic-radiation-resistant multifunctionaltextile.
[0013] Tests on hand feeling, toughness, and strength find out that the toughness, the strength, and the hand feeling of the ultraviolet-resistant and electromagnetic-radiation
resistant multifunctional textile obtained in the embodiment 1 are not substantially
affected.
[0014] Ultraviolet-resistant property test: ultraviolet-resistant property test and evaluation are carried out on the ultraviolet-resistant and electromagnetic-radiation-resistant
multifunctional textile sample obtained in embodiment 1 after being washed for 50 times.
Ultraviolet-resistant property test is carried out by standard GB/T18830-2009 TEXTILE
EVALUATION FOR SOLAR ULTRAVIOLET PROTECTIVE PROPERTIES, the
ultraviolet-resistant product standard has been reached, and the ultraviolet-resistant and
electromagnetic-radiation-resistant multifunctional textile has an excellent ultraviolet
protective function.
[0015] Electromagnetic-radiation-resistant property test: electromagnetic-radiation
resistant property test and evaluation are carried out on the ultraviolet-resistant and
electromagnetic-radiation-resistant multifunctional textile sample obtained in
embodiment 1 after being washed for 50 times. Measurement is carried out by GB/T
26383-2011 WORSTED FABRIC WITH RADIORESISTANCE, shielding effectiveness
of the fabric is 75.3dB, and the fabric has excellent electromagnetic shielding
effectiveness.
[0016] Contrast
[0017] Different from the embodiment 1, the difference only lies in that a contrasting textile is prepared without a fullerene carbon nanomaterial and nanosilver, property test on the contrast textile finds out that hand feeling of the textile obtained from the contrast becomes poor, UPF is smaller than 40, and the shielding effectiveness is 45.0dB.
[0018] Various constituents of the nanometer titanium dioxide, the nanometer zirconium oxide, the nanosilver particle, the chitosan, the fullerene carbon nanomaterial and the like
are used in the present invention and interact with each other, the method is simple to
manufacture, and raw materials are low in cost and availability. According to the
ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile
preparation method, the raw materials are low in cost and available, the process is simple,
and no stimulation to a human body is generated. Toughness, strength, and hand feeling
of the obtained ultraviolet-resistant and electromagnetic-radiation-resistant
multifunctional textile are not substantially affected, and the ultraviolet-resistant and
electromagnetic-radiation-resistant multifunctional textile has excellent ultraviolet
resistant and electromagnetic-radiation-resistant properties and is washable.
[0019] Apparently, the above embodiments of the present invention are merely illustrative of the present invention and are not intended to limit implementation modes
of the present invention. Based on the above descriptions, change or variation in other
different forms can be also apparent to those ordinary skills in the art, and all
embodiments of the present cannot be exhaustive herein. The obvious change or variation
derived from the technical solution of the present invention still falls within the
protection scope of the present invention.
Claims (4)
1. An ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile
preparation method is characterized in that it comprises: firstly, preparing an ultraviolet-resistant
and electromagnetic-radiation-resistant finishing agent; and secondly, finishing a textile base cloth
with the ultraviolet-resistant and electromagnetic-radiation-resistant finishing agent to obtain the
ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile, wherein the
ultraviolet-resistant and electromagnetic-radiation-resistant finishing agent comprises the following
constituents based on parts by weight: 5-8 parts of nanometer titanium dioxide, 3-4 parts of
nanometer zirconium oxide, 3-4 parts of nanosilver particle, 5-6 parts of chitosan, 6-8 parts of
fullerene carbon nanomaterial, 5-6 parts of polydimethylsiloxane, 3-4 parts of modified
polysiloxane, 8-10 parts of methylbenzene, 1-2 parts of silicone emulsion, 2-4 parts of alkylphenol
ethoxylate, 2-3 parts of 2-butoxyethanol and 4-5 parts of glycerol.
2. An ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile
preparation method according to Claim 1 is characterized in that the finishing comprises: placing
the ultraviolet-resistant and electromagnetic-radiation-resistant finishing agent in an immersion tank,
and then impregnating and finishing the textile base cloth to obtain the ultraviolet-resistant and
electromagnetic-radiation-resistantmultifunctionaltextile.
3. An ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile
preparation method according to Claim 1 is characterized in that the impregnating and finishing
comprises: carrying out drying after impregnation twice.
4. An ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile
preparation method according to Claim 1 is characterized in that the impregnating and finishing
comprises: firstly, placing the ultraviolet-resistant and electromagnetic-radiation-resistant finishing
agent in the immersion tank, and impregnating the textile base cloth at room temperature for 25-30
minutes; secondly, pumping an impregnating system to negative pressure, and impregnating for
10-15 minutes, wherein vacuum degree is 0.04-0.05MPa; and finally, drying at 65-67 DEG C for
1-1.5 hours, and standing at the room temperature for 22-24 hours to prepare the
ultraviolet-resistant and electromagnetic-radiation-resistant multifunctional textile.