AU2007317253A1

AU2007317253A1 - Polymer-based antimicrobial agents, methods of making said agents, and products and applications using said agents

Info

Publication number: AU2007317253A1
Application number: AU2007317253A
Authority: AU
Inventors: Ashraf A. Ismail; David Pinchuk; Leonard Pinchuk; Orley R. Pinchuk
Original assignee: Smart Anti-Microbial Solutions LLC
Current assignee: Smart Anti-Microbial Solutions LLC
Priority date: 2006-11-09
Filing date: 2007-11-09
Publication date: 2008-05-15
Also published as: MX2009004968A; CO6210718A2; WO2008058272A3; CA2669334A1; EP2086511A2; EP2086511A4; BRPI0718703A2; WO2008058272A2

Description

WO 2008/058272 PCT/US2007/084269 POLYMER-BASED ANTIMICROBIAL AGENTS, METHODS OF MAKING SAID AGENTS, AND PRODUCTS AND APPLICATIONS USING SAID AGENTS BACKGROUND OF THE INVENTION FIELD OF THE INVENTION [0001] The invention relates to antimicrobial agents, products incorporating such agents, and methods of making such products. More particularly, the invention relates to polymer-based antimicrobial agents. STATE OF THE ART [0002] Silver and silver salts are commonly used as antimicrobial agents. An early medicinal use of silver was the application of aqueous silver nitrate solutions to prevent eye infection in newborn babies. Silver salts, colloids, and complexes have also been used to prevent and to control infection. Other metals, such as gold, zinc, copper, and cerium, have also been found to possess antimicrobial properties, both alone and in combination with silver. These and other metals have been shown to provide antimicrobial behavior even in minute quantities, a property referred to as "oligodynamic." [0003] Metallic antimicrobials function by releasing metal ions into the microbe. The released ions react with protein and other anions (negative charged species) in the microbe and render the protein insoluble and thereby inactive. The inactive protein perturbs cellular function, disrupts membranes and prevents the normal activity and reproduction of DNA thereby essentially killing the microorganism. [0004] U.S. Pat. No. 6,306,419 to Vachon et al. discloses a polymer-based coating comprising a styrene sulfonate polymer with a carrier molecule bound to silver ion incorporated therein. The styrene sulfonate polymer is prepared by reacting an acetyl sulfate sulfonation agent with a styrene copolymer in 1,2-dichloroethane (DCE). The coating is hydrophilic such that it retains a relatively large amount of water or water containing fluid. There are several disadvantages to this composition. One such disadvantage is that larger quantities of the silver metal are required to provide effective antimicrobial activity. A second disadvantage is that the carrier molecule is required which renders it more expensive as well as more difficult to dispose of the carrier byproduct. A third disadvantage is that a solvent other than water (e.g. DCE) is WO 2008/058272 PCT/US2007/084269 2 required to prepare the polymer matrix. Such solvents are typically hazardous because of their reactive nature and thus require special care in handling and disposing of such solvents, which limits the widespread acceptance of such antimicrobial polymers in many applications. SUMMARY OF THE INVENTION [0005] It is therefore an object of the invention to provide a polymer-based antimicrobial agent that is readily soluble in a water solution. [0006] It is also an object of the invention to provide such a polymer-based antimicrobial agent that does not require relatively large quantities of the metal in order to provide effective antimicrobial activity. [0007] It is another object of the invention to provide methods of incorporating such an antimicrobial agent as part of a product or service, such as a paper product, for mold abatement in residential and/or commercial applications, or for treating and/or preventing citrus canker. [0008] In accord with these objects, which will be discussed in detail below, the antimicrobial agent of the present invention includes a water-soluble polymer and oligodynamic metal ions which interact with counter-ions of the polymer such that the metal ions are bound to corresponding counter-ions. The water-soluble polymer controls a sustained release of the metal ions. The oligodynamic metal ions preferably include small size metal particles (e.g., nano-sized silver particles) that sonically bond or are electrostatically bound to the water-soluble polymer as well as metal ions derived from one or more water-soluble oligodynamic metal compositions (e.g., metal sulfates and/or metal nitrates). The small-size particles can aid in reducing the photosensitivity of the agent, and thus counter the proclivity of the agent to change color when subjected to light. The agent may also include one or more acids, including organic acids (such as sulfates, carboxylic acids, amines, hydroxyls, nitrates, and phosphates) and/or non-organic acids (such as boric acid and dioctylborate). This allows the total concentration of oligodynamic metal in the agent to be reduced significantly while maintaining or even enhancing antimicrobial activity. [0009] Additional objects and advantages of the invention will become apparent to those skilled in the art upon reference to the detailed description.

WO 2008/058272 PCT/US2007/084269 3 DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS [0010] The following definitions are used in the description below. The terms "colloid" and "colloidal" refer to a solution consisting of particles suspended in a liquid medium. An "ion" is an atom or a group of atoms that has acquired a net electric charge. The term "ionic" refers to a condition where an ion has an electric charge. An "electrostatic charge" is a charge that can be induced in a substance, for example, metallic silver particles, by passing a current over the substance. An "electrostatic attraction" is when a substance or particle with an electrostatic charge is attracted to a second substance which contains the opposite charge to the substance. "Water soluble" means that the composition has a solubility of at least 2g in 1 OOg of water at room temperature. "Small size" in reference to metal particles means metal particles that have a size less than 1 pm in diameter and more preferably less than 0.01 pm in diameter. "Nano-size" or "Nano" in reference to metal particles means metal particles that have a size between 1 nm and 1 00nm in diameter. [0011] According to the invention, an antimicrobial agent is realized from a water soluble polymeric substance that has pendant hydrophilic groups that are capable of binding with one or more oligodynamic metal ions. Preferably, the hydrophilic groups of the polymer are capable of binding with one or more positively charged oligodynamic metal ions. Therefore, it is preferred that the water-soluble polymeric substance has negatively charged hydrophilic groups such as sulfates, phosphates, nitrates, carboxylates and the like. The water-soluble polymeric substance is dissolved in an aqueous solution. The aqueous solution preferably comprises water without any alcohols or other organic solvents. However, the aqueous solution can include one or more alcohols or other organic solvents (e.g., m-pyrol, dimethylformamide, dimethylacetamide, dimethyl sulfonamide, tetrahydrofuran, mixtures of the above, mixtures of the above with swelling solvents such as diethyl ether, xylene, toluene and the like) preferably in a range between 5% and 50% by weight. One or more compositions that include an oligodynamic metal are added to the polymeric aqueous solution. The oligodynamic metal(s) can be a noble metal (such as Ag, Au, Pt, Pd, Ir) or a heavy metal (such as Cu Sn, Sb, Bi and Zn). Preferably, the one or more oligodynamic metal compositions include small size metal particles (most preferably, nano-sized silver particles) that carry an electrostatic charge and that dissolve or WO 2008/058272 PCT/US2007/084269 4 disperse in the polymeric aqueous solution and sonically bond to the hydrophilic group of the polymer. Such small size metal particles can also remain suspended as a colloid in the polymeric aqueous solution wherein the electrostatic charge carried by the small size metal particles can maintain the particles within the polymer matrix (in contrast to residing solely in solution) by electrostatic attraction. The one or more oligodynamic metal compositions added to the polymeric aqueous solution also preferably include at least one water-soluble metal composition of an oligodynamic metal that dissolves in the polymeric aqueous solution and sonically bonds to the hydrophilic group of the polymer. One or more acids (e.g., organic acids and inorganic acids) can be added to the mixture. [0012] The range of total solids dissolved in water can be from 0.1% to 5%, preferably from 0.3% to 3% and more preferentially from 0.5 to 2.5%. Looking now only at the solid components without water, the range of small-size metal particles (e.g., nano-sized silver particles) is preferably from 0.05 to 5% and most preferably from 0.5 to 3%; the range of water soluble polymer is preferably from 1 to 20%, and most preferably from 5 to 6%; and the range of other oligodynamic metal compositions preferably in a range from 10 to 25%. The remaining solid content includes acids, organic and inorganic, that can comprise 50% to 75%, and most preferably from 70 to 75% of the solids component. This combination of reagents allows the total concentration of oligodynamic metal in the polymeric aqueous solution to be reduced significantly while maintaining or even enhancing antimicrobial activity. [0013] Examples of hydrophilic polymers which may be used to form the compositions include, but are not limited to, polyurethanes, including sulfonated polyether polyurethanes, sulfonated polyester polyurethanes, sulfonated polyurethaneureas, and their copolymers, especially the polyethleneoxide copolymers; polyvinylpyrrolidones; polyvinyl alcohols; polyethylene glycols and their copolymers; polypropylene glycols and their copolymers; polyoxyethylenes and their copolymers; polyacrylic acid; polyacrylamide; carboxymethyl cellulose; cellulose and its derivatives; dextrans and other polysaccharides; starches; guar; xantham and other gums and thickeners; collagen; gelatins; and other biological polymers. All the of these hydrophilic polymers can be reacted or co-polymerized with charged moieties to render them both water soluble as well as sonically charged. Examples of these charged WO 2008/058272 PCT/US2007/084269 5 moieties include, sulfonation of the aromatic rings on aromatic polyurethanes; addition of methacrylic acid in the vinyl-based polymers. Also included are normally hydrophobic polymers that are rendered both hydrophilic and anionic by the addition of functional groups; for example, polystyrene is hydrophobic but can be rendered water soluble by sulfonating the styrene group. Similarly, polyethylene terepthalate (PET) can be rendered hydrophilic and anionic by sulfonating the terepthalic groups. The preferred polymer is water soluble polystyrene with its copolymers, such as sulfonated polystyrene co-maleic acid. [0014] The antimicrobial agent of the invention is illustrated in the following example. A water-soluble sulfonated polystyrene is dissolved in water. Nano-size silver particles are added to the sulfonated polystyrene water solution and mixed together. The silver particles carry a positive electrostatic charge and dissolve or disperse in the polymeric aqueous solution and interact with the sulfonated polystyrene by ionic bonding wherein the sulfonate groups of the sulfonated polystyrene are the counter-ions to positively-charged silver ions. In this manner, the polymer controls a sustained release of the positively-charged silver ions. The silver particles can also remain suspended as a colloid in the polymeric aqueous solution wherein the positive electrostatic charge carried by the silver particles can maintain the silver particles within the sulfonated polystyrene matrix (in contrast to residing solely in solution) by electrostatic attraction. In this case, the positively electrostatically charged nano-sized silver particles are attracted to the polar sulfonate groups of the sulfonated polystyrene. Advantageously, the nano-size silver particles aid in reducing the photosensitivity of the resulting composition, and thus counter the proclivity of the antimicrobial agent to change color when subjected to light. It is therefore desirous that when nano-sized silver particles are used, the silver ion-bound silver is reduced accordingly. In other words, if more nano-sized silver particles with electrostatic charge is used, then other silver moieties such as colloidal silver salts or silver ion, from, for example, silver nitrate or silver sulfate can be reduced in quantity. [0015] Other water-soluble metal compositions that include an oligodynamic metal (or solutions based thereon) are added to the silver/sulfonated polystyrene water mixture and mixed together. Preferably, such water-soluble metal compositions include metal sulfates (such as copper (II) sulfate or zinc sulfate) and/or metal nitrates WO 2008/058272 PCT/US2007/084269 6 (such as silver nitrate, copper (II) nitrate and/or zinc nitrate). The ions of the oligodynamic metal composition(s) react with counter-ions of the polymer such that the metal ions are sonically bound to corresponding counter-ions, and the polymer controls a sustained release of the metal ions. [0016] One or more organic acids can be added to the oligodynamic metal/sulfonated polystyrene/water mixture and mixed together. This allows the total concentration of oligodynamic metal in the mixture to be reduced significantly while maintaining or even enhancing antimicrobial activity. Examples of organic acids include citric acid, malic acid, ascorbic acid, salicyclic acid, acetic acid, formic acid and the like. In addition to the organic acids, other mildly acidic acids can also be used in this cocktail such as boric acid, dioctylborate, and the like. [0017] Table 1 shows various concentrations of colloidal silver, metal compositions and acids that are mixed and reacted to a water-soluble sulfonated polymer carrier (showing actual amounts used and percentages). Chemical Grams Percent (Wt/Wt) Percent (Wt/Wt) including water without water nano-sized silver 0.050 0.005 2.444 sulfonated polystyrene 0.120 0.012 5.865 copper (II) sulfate 0.203 0.020 9.922 zinc sulfate 0.203 0.020 9.922 boric acid 0.490 0.049 23.949 malic acid 0.490 0.049 23.949 citric acid 0.490 0.049 23.949 water 1000 99.796 Total 1002.046 100 100 [0018] The specific example of Table 1 employs divalent metals; however, monovalent or multivalent metals can also be used. Also note that when the organic carboxylic acids shown are mixed with the sulfonated polymer and the oligodynamic metal composition, a competing reaction occurs where some portion of the metal will couple with the sulfonated polymer and another portion of the metal will couple with the organic carboxylic acid(s). In the case where the metal couples with the sulfonated WO 2008/058272 PCT/US2007/084269 7 polymer, the counter ion is the sulfonate group on the polymer. In the case where the metal couples with the organic carboxylic acid(s), the counter ion is the organic carboxylic acid. The result of this competing reaction will depend on the stoicheometry, relative affinity and strength of the ionic bond. [0019] The liquid mixture of materials described above can be dried and ground to a fine powder and commercialized as a powdered-form antimicrobial agent. In this case, the solid content of the powdered-form antimicrobial agent preferably includes the following: - small-size metal particles (e.g., nano-sized silver particles) in a range preferably from 0.05 to 5% and most preferably from 1 to 3%; - water soluble polymer in a range preferably from 1 to 20%, and most preferably from 5 to 7%; - acids in a range preferably from 10 to 75%, and most preferably from 70 to 75%; and - other oligodynamic metals in a range preferably from 5 to 25%. [0020] With such product, the user need only dilute the powder in an aqueous solution (which preferably includes only water but can include other solvents) to the desired concentration and spray, dip or drop the solution onto the substance to be coated. The powder may also be diluted in a water solution (or solvent solution) and added as part of an admixture during formation of the end product. For example, the admixture may be a pulp that is processed to form a paper product. Here the solids content can range from 0.001 to 10%; preferably 0.1 to 2% of the solution used to coat the product. When the water evaporates, a thin film of polymer remains on the substrate where the thin polymer film binds the anti-microbial agents. In such applications, the ions of the oligodynamic metal compositions therein interact with counter-ions of the water-soluble polymer such that the metal ions are bound to corresponding counter-ions and the polymer controls a sustained release of the metal ions. [0021] The powdered-form antimicrobial agent of the present invention has many potential applications, including the abatement of mold in residential and commercial applications as well as for treatment and prevention of citrus canker in citrus groves. When used for mold abatement, the powdered-form antimicrobial agent as described WO 2008/058272 PCT/US2007/084269 8 above is dissolved in an aqueous solution, which is applied in spray form onto wallboard, walls, floors, ceilings, or other home/building structural members. When used for treatment and prevention of citrus canker, the powdered-form antimicrobial agent as described above is dissolved in an aqueous solution, which is applied in spray form onto the leaves and/or branches and/or trunk of the citrus tree. For citrus canker applications, the solids concentrations of the powdered-form antimicrobial agent in the spraying mixture can range from 0.001 to 10%, and preferably from 0.1 to 2%. It is preferable that the mixture also contain a tackifier to help stick the antimicrobial mixture to the leaves and/or branches and/or trunk of the tree. An exemplary tackifier for this application includes one or more water soluble substances that are sticky; such as syrup (maple, corn, etc.), tree sap, polysaccharides, honey, vegetable oil derivatives and the like. The concentration of tackifier may comprise 0.1 to 2% of the diluted formulation. In addition, the viscosity of the solution may be increased, which will help suspend the additives in aqueous solution to help in spraying applications of the system. Thickening can be accomplished by adding more water soluble polymer or thickeners such as gums (agar, xanthum, guar, gellan, pectin), polysaccharide, gelatin, corn starch, and the like. The amount of thickener can range from 0.2 to 2%, with 0.5% of the total bath weight. [0022] There have been described and illustrated herein antimicrobial agents, products incorporating said agents and methods of making the antimicrobial agents and products incorporating them. While particular embodiments of the invention have been described, it is not intended that the invention be limited thereto, as it is intended that the invention be as broad in scope as the art will allow and that the specification be read likewise. It will therefore be appreciated by those skilled in the art that yet other modifications could be made to the provided invention without deviating from its spirit and scope as so claimed.

Claims

1. A method of producing a water-soluble antimicrobial agent comprising: preparing a solution that includes at least the following i) water; ii) a water-soluble polymer having a hydrophilic group; and iii) at least one oligodynamic metal composition having oligodynamic metal ions that interact with said hydrophilic group of said water-soluble polymer, wherein said at least one oligodynamic metal composition includes small size metal particles.

2. A method according to claim 1, wherein: the small size particles include nano-size particles.

3. A method according to claim 1, wherein: the solution further includes at least one acid.

4. A method according to claim 3, wherein: the at least one acid includes at least one organic acid.

5. A method according to claim 4, wherein: the at least one organic acid is selected from the group including acetic acid, citric acid, malic acid, ascorbic acid, salicyclic acid, and formic acid.

6. A method according to claim 3, wherein: the at least one acid includes at least one non-organic acid.

7. A method according to claim 6, wherein: the at least one non-organic acid is selected from the group including boric acid and dioctylborate.

8. A method according to claim 1, wherein: the at least one oligodynamic metal composition comprises at least one noble metal.

9. A method according to claim 8, wherein: the at least one noble metal is selected from the group including Ag, Au, Pt, Pd, and Ir.

10. A method according to claim 1, wherein: the at least one oligodynamic metal composition comprises at least one heavy metal. WO 2008/058272 PCT/US2007/084269 10

11. A method according to claim 10, wherein: the at least one heavy metal is selected from the group including Cu, Sn, Sb, Bi and Zn.

12. A method according to claim 1, wherein: the small size metal particles comprise silver particles.

13. A method according to claim 12, wherein: the silver particles have a size between 1nm and 100nm in diameter.

14. A method according to claim 1, wherein: the at least one oligodynamic metal composition comprises at least one metal sulfate.

15. A method according to claim 14, wherein: the at least one metal sulfate is selected from the group including copper (II) sulfate and zinc sulfate.

16. A method according to claim 1, wherein: the at least one oligodynamic metal composition comprises at least one metal nitrate.

17. A method according to claim 16, wherein: the at least one metal nitrate is selected from the group including silver nitrate, copper (II) nitrate, and zinc nitrate.

18. A method according to claim 1, wherein: the hydrophilic groups of the water-soluble polymer comprise at least one of sulfates, carboxylic acids, amines, hydroxyls, nitrates, and phosphates.

19. A method according to claim 1, wherein: the water-soluble polymer comprises a sulfonated polymer.

20. A method according to claim 19, wherein: said sulfonated polymer comprises a sulfonated polyurethane.

21. A method according to claim 19, wherein: said sulfonated polymer comprises a sulfonated polystyrene.

22. A method according to claim 1, further comprising: drying the solution into a solid form, and processing the solid form into a powder. WO 2008/058272 PCT/US2007/084269 11

23. A method according to claim 22, further comprising: diluting the powder in an aqueous solution.

24. A method according to claim 23, further comprising: adding a tactifier to the aqueous solution.

25. A method according to claim 24, wherein: the tactifier comprises at least one water soluble substance selected from the group including syrup, tree sap, polysaccharides, honey, vegetable oil derivatives.

26. An antimicrobial agent comprising: a water-soluble polymer having a hydrophilic group, at least one oligodynamic metal composition having oligodynamic metal ions that interact with said hydrophilic group of said water-soluble polymer, wherein said at least one oligodynamic metal composition includes small size metal particles.

27. An antimicrobial agent according to claim 26, wherein: the small size metal particles include nano-size metal particles.

28. An antimicrobial agent according to claim 26, further comprising: at least one acid.

29. An antimicrobial agent according to claim 28, wherein: the at least one acid is 10 to 75% of the solid content of the agent.

30. An antimicrobial agent according to claim 28, wherein: the at least one acid comprises at least organic acid.

31. An antimicrobial agent according to claim 30, wherein: the at least one organic acid is selected from the group including acetic acid, citric acid, malic acid, ascorbic acid, salicyclic acid, and formic acid.

32. An antimicrobial agent according to claim 28, wherein: the at least one acid comprises at least one non-organic acid.

33. An antimicrobial agent according to claim 32, wherein: the at least one non-organic acid is selected from the group including boric acid and dioctylborate.

34. An antimicrobial agent according to claim 26, wherein: said at least one oligodynamic metal composition comprises at least one noble metal. WO 2008/058272 PCT/US2007/084269 12

35. An antimicrobial agent according to claim 34, wherein: the at least one noble metal is selected from the group including Ag, Au, Pt, Pd, and Ir.

36. An antimicrobial agent according to claim 26, wherein: the at least one oligodynamic metal composition comprises at least one heavy metal.

37. An antimicrobial agent according to claim 36, wherein: the at least one heavy metal is selected from the group including Cu, Sn, Sb, Bi and Zn.

38. An antimicrobial agent according to claim 26, wherein: the small size metal particles comprise silver particles.

39. An antimicrobial agent according to claim 38, wherein: the silver particles are 0.05 to 5% of the solid content of the agent.

40. An antimicrobial agent according to claim 38, wherein: the silver particles have a size between 1 nm and 100nm in diameter.

41. An antimicrobial agent according to claim 26, wherein: the at least one oligodynamic metal composition comprises at least one metal sulfate.

42. An antimicrobial agent according to claim 41, wherein: the at least one metal sulfate is 5 to 25% of the solid content of the agent.

43. An antimicrobial agent according to claim 41, wherein: the at least one oligodynamic metal composition comprises a plurality of metal sulfates.

44. An antimicrobial agent according to claim 41, wherein: the at least one metal sulfate is selected from the group including copper (II) sulfate and zinc sulfate.

45. An antimicrobial agent according to claim 26, wherein: the at least one oligodynamic metal composition comprises at least one metal nitrate.

46. An antimicrobial agent according to claim 45, wherein: the at least one metal nitrate is selected from the group including silver nitrate, copper (II) nitrate, and zinc nitrate. WO 2008/058272 PCT/US2007/084269 13

47. An antimicrobial agent according to claim 26, wherein: the hydrophilic groups of the water-soluble polymer comprise at least one of sulfates, carboxylic acids, amines, hydroxyls, nitrates, and phosphates.

48. An antimicrobial agent according to claim 26, wherein: the water-soluble polymer is 1 to 20% of the solid content of the agent.

49. An antimicrobial agent according to claim 26, wherein: the water-soluble polymer comprises a sulfonated polymer.

50. An antimicrobial agent according to claim 49, wherein: said sulfonated polymer comprises a sulfonated polyurethane.

51. An antimicrobial agent according to claim 49, wherein: said sulfonated polymer comprises a sulfonated polystyrene.

52. An antimicrobial agent according to claim 26, wherein: said water-soluble polymer and at least one oligodynamic metal composition are diluted in an aqueous solution.

53. An antimicrobial agent according to claim 52, further comprising: a tactifier that is added to the aqueous solution.

54. An antimicrobial agent according to claim 53, wherein: the tactifier comprises at least one water soluble substance selected from the group including syrup, tree sap, polysaccharides, honey, vegetable oil derivatives.

55. A method for inhibiting microbial growth on a target comprising: providing an antimicrobial agent comprising a water-soluble polymer having a hydrophilic group, at least one oligodynamic metal composition having oligodynamic metal ions that interact with said hydrophilic group of said water-soluble polymer, wherein said at least one oligodynamic metal composition includes small size metal particles; diluting said antimicrobial agent in an aqueous solution; and applying said aqueous solution to said target.

56. A method according to claim 55, wherein: the aqueous solution is applied to said target as a coating or film by spraying or dipping.

57. A method according to claim 56, wherein: a tactifier is added to the aqueous solution for application to said target. WO 2008/058272 PCT/US2007/084269 14

58. A method according to claim 57, wherein: the tactifier comprises at least one water soluble substance selected from the group including syrup, tree sap, polysaccharides, honey, vegetable oil derivatives.

59. A method according to claim 56, wherein: the target comprises at least a portion of a citrus tree.

60. A method according to claim 55, wherein: the small size particles include nano-size particles.

61. A method according to claim 55, wherein: the small size metal particles comprise silver particles having a size between 1 nm and 100nm in diameter.

62. A method according to claim 55, wherein: the antimicrobial agent further comprises at least one of i) at least one organic acid; ii) at least one non-organic acid; iii) at least one noble metal; iv) at least one heavy metal; v) at least one metal sulfate; vi) at least one metal nitrate; and vii) a sulfonated polymer such as sulfonated polyurethane and/or sulfonated polystyrene.