AT212250B - Roller for rolling semi-finished or intermediate products made of steel or non-ferrous metals

Info

Publication number: AT212250B
Application number: AT416459A
Authority: AT
Original assignee: Inter Continentaler Huettenbau
Priority date: 1959-06-03
Filing date: 1959-06-03
Publication date: 1960-12-12

Description

  

   <Desc/Clms Page number 1> 
 



  Walze zum Walzen von Halbzeug oder von Zwischenprodukten aus Stahl   oder Nichteisenmetallen    
 EMI1.1 
 

 <Desc/Clms Page number 2> 

 zuerstDurch   diesebeiden aufeinanderfolgendenbehandlungen erhält   die Walzenoberfläche Druckspannungen in solcher Verteilung aufgeprägt, dass die Entstehung von Brandrissen weitestgehend vermieden wird. Aber auch in Fällen, bei denen abnormale Beanspruchungen der Walzenoberfläche, wie   z.     B."Steckenbleiber",   zu Brandrissen Rühren, werden diese infolge der durch das beschriebene Verfahren entstandenen Spannungverteilung so abgelenkt, dass sie sich nicht als Rundrisse oder achsparallele Risse ausweiten können. Da- durch wirkt sich der Erfindungsvorschlag zusätzlich auch auf die Lebensdauer der Walzen günstig aus. 



   In der Zeichnung ist die Erfindung veranschaulicht. Fig. l zeigt das Rändelrad zur Durchführung der erfindungsgemässen Rändelung von Walzen, Fig. 2 einen vergrösserten Ausschnitt aus der Oberfläche der mit dem Rändelrad nach Fig. l hergestellten Walze in Ansicht, Fig. 3 einen Querschnitt gemäss Fig. 2 in
Richtung A-A. 



   Das   Rändelrad   ist also hienach mit kleinen Pyramiden besetzt, deren Höhe kleiner als 0, 3 mm ist.



   <Desc / Clms Page number 1>
 



  Roller for rolling semi-finished or intermediate products made of steel or non-ferrous metals
 EMI1.1
 

 <Desc / Clms Page number 2>

 First, through these two consecutive treatments, the roller surface receives compressive stresses distributed in such a way that the development of fire cracks is largely avoided. But also in cases where abnormal stresses on the roll surface, such as B. "Stuck", stir to fire cracks, these are deflected as a result of the stress distribution created by the method described so that they cannot expand as round cracks or axially parallel cracks. As a result, the proposed invention also has a favorable effect on the service life of the rollers.



   The invention is illustrated in the drawing. FIG. 1 shows the knurled wheel for performing the knurling according to the invention on rolls, FIG. 2 shows an enlarged section of the surface of the roll manufactured with the knurled wheel according to FIG. 1, FIG. 3 shows a cross section according to FIG
Direction A-A.



   The knurled wheel is then occupied with small pyramids, the height of which is less than 0.3 mm.

Claims

PATENT CLAIM: Roller for rolling semi-finished products or intermediate products made of steel or non-ferrous metals, with depressions in the form of pyramid patterns to prevent hot cracks on the roller surface, which are impressed by a knurled wheel on the outer surface, characterized in that the pyramids directly next to and behind one another are arranged in association, a depth of less than 0.3 mm and in plan, as is known, are diamond-shaped and that one diagonal of the Pyramid base, which, as known, runs in the direction of rotation of the roller, with the edges of the Pyramid base each includes an angle of more than 15, but less than 450.