WO2024112494A1 - Panneau isolant sous vide avec piège à gaz ayant une phase cristalline ti-al-v et son procédé de fabrication - Google Patents
Panneau isolant sous vide avec piège à gaz ayant une phase cristalline ti-al-v et son procédé de fabrication Download PDFInfo
- Publication number
- WO2024112494A1 WO2024112494A1 PCT/US2023/078489 US2023078489W WO2024112494A1 WO 2024112494 A1 WO2024112494 A1 WO 2024112494A1 US 2023078489 W US2023078489 W US 2023078489W WO 2024112494 A1 WO2024112494 A1 WO 2024112494A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- getter
- layer
- laser
- main seal
- vacuum insulating
- Prior art date
Abstract
Un panneau isolant sous vide comprend des premier et second substrats (par ex., des substrats en verre), un joint de bordure hermétique, un orifice de pompage et des entretoises intercalées entre au moins les deux substrats. L'espace entre les substrats peut être à une pression inférieure à la pression atmosphérique pour conférer des propriétés isolantes. Le panneau peut comprendre un piège à gaz. Le piège à gaz peut être activé par laser d'une manière qui amène le piège à gaz à se transformer et à réaliser une phase Ti-Al-V (par ex., Al3V0,333Ti0,667) de matériau cristallin. Le piège à gaz peut être un piège à gaz à couche mince et/ou peut être de forme allongée.
Applications Claiming Priority (12)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US202263427645P | 2022-11-23 | 2022-11-23 | |
US202263427657P | 2022-11-23 | 2022-11-23 | |
US202263427670P | 2022-11-23 | 2022-11-23 | |
US202263427661P | 2022-11-23 | 2022-11-23 | |
US63/427,661 | 2022-11-23 | ||
US63/427,645 | 2022-11-23 | ||
US63/427,657 | 2022-11-23 | ||
US63/427,670 | 2022-11-23 | ||
US202363540729P | 2023-09-27 | 2023-09-27 | |
US63/540,729 | 2023-09-27 | ||
US18/376,932 US20240165578A1 (en) | 2022-11-23 | 2023-10-05 | Vacuum insulated panel with getter having ti-al-v crystalline phase and method of making same |
US18/376,932 | 2023-10-05 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2024112494A1 true WO2024112494A1 (fr) | 2024-05-30 |
Family
ID=89158167
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2023/078489 WO2024112494A1 (fr) | 2022-11-23 | 2023-11-02 | Panneau isolant sous vide avec piège à gaz ayant une phase cristalline ti-al-v et son procédé de fabrication |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2024112494A1 (fr) |
Citations (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5124185A (en) | 1989-10-03 | 1992-06-23 | Ppg Industries, Inc. | Vacuum insulating unit |
US5657607A (en) | 1989-08-23 | 1997-08-19 | University Of Sydney | Thermally insulating glass panel and method of construction |
US5664395A (en) | 1992-01-31 | 1997-09-09 | The University Of Sydney | Thermally insulating glass panels |
US5935702A (en) | 1994-12-23 | 1999-08-10 | Saint-Gobain Vitrage | Glass substrates coated with a stack of thin layers having reflective properties in the infra-red and/or solar ranges |
US6042934A (en) | 1993-08-12 | 2000-03-28 | Saint-Gobain Vitrage | Transparent substrate provided with a stack of thin layers |
US6322881B1 (en) | 1996-12-12 | 2001-11-27 | Saint-Gobain Vitrage | Glazing assembly comprising a substrate provided with a stack of thin layers for solar protection and/or thermal insulation |
US7045181B2 (en) | 2001-12-25 | 2006-05-16 | Nippon Sheet Glass Co., Ltd. | Double glazing |
US7115308B2 (en) | 2001-10-25 | 2006-10-03 | Nippon Sheet Glass Co., Ltd. | Glass panel and method of manufacturing the glass panel |
US7314668B2 (en) | 2000-07-10 | 2008-01-01 | Guardian Industries Corp. | Low-E coated articles having zirconium inclusive dielectric layer |
US7342716B2 (en) | 2005-10-11 | 2008-03-11 | Cardinal Cg Company | Multiple cavity low-emissivity coatings |
US7632571B2 (en) | 2005-03-31 | 2009-12-15 | Cardinal Cg Company | Haze-resistant low-emissivity coatings |
US7858193B2 (en) | 2005-08-23 | 2010-12-28 | Saint Gobain Glass France | Low emissivity (low-E) thin coating stacks with intermediate antidiffusion layers |
US7910229B2 (en) | 2002-05-03 | 2011-03-22 | Ppg Industries Ohio, Inc. | Substrate having thermal management coating for an insulating glass unit |
US8821999B2 (en) | 2008-11-05 | 2014-09-02 | Corning Incorporated | Vacuum-insulated glass windows with glass-bump spacers |
US8951617B2 (en) | 2008-12-22 | 2015-02-10 | Saint-Gobain Glass France | Substrate provided with a multilayer coating having thermal properties and absorbent layers |
US9215760B2 (en) | 2012-01-10 | 2015-12-15 | Saint-Gobain Glass France | Transparent pane with electrically conductive coating |
US10153389B2 (en) | 2014-10-01 | 2018-12-11 | Ferro Gmbh | Tellurate joining glass having processing temperatures less than or equal to 420° C |
US10759693B2 (en) | 2018-07-16 | 2020-09-01 | Guardian Glass, LLC | Low-E matchable coated articles having absorber film and corresponding methods |
US20210270084A1 (en) * | 2018-07-31 | 2021-09-02 | Panasonic Intellectual Property Management Co., Ltd. | Method for manufacturing glass panel unit |
US11124450B2 (en) | 2017-11-10 | 2021-09-21 | Nippon Sheet Glass Company, Limited | Glass panel and glass window |
-
2023
- 2023-11-02 WO PCT/US2023/078489 patent/WO2024112494A1/fr unknown
Patent Citations (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5657607A (en) | 1989-08-23 | 1997-08-19 | University Of Sydney | Thermally insulating glass panel and method of construction |
US5124185A (en) | 1989-10-03 | 1992-06-23 | Ppg Industries, Inc. | Vacuum insulating unit |
US5664395A (en) | 1992-01-31 | 1997-09-09 | The University Of Sydney | Thermally insulating glass panels |
US6042934A (en) | 1993-08-12 | 2000-03-28 | Saint-Gobain Vitrage | Transparent substrate provided with a stack of thin layers |
US5935702A (en) | 1994-12-23 | 1999-08-10 | Saint-Gobain Vitrage | Glass substrates coated with a stack of thin layers having reflective properties in the infra-red and/or solar ranges |
US6322881B1 (en) | 1996-12-12 | 2001-11-27 | Saint-Gobain Vitrage | Glazing assembly comprising a substrate provided with a stack of thin layers for solar protection and/or thermal insulation |
US7314668B2 (en) | 2000-07-10 | 2008-01-01 | Guardian Industries Corp. | Low-E coated articles having zirconium inclusive dielectric layer |
US7115308B2 (en) | 2001-10-25 | 2006-10-03 | Nippon Sheet Glass Co., Ltd. | Glass panel and method of manufacturing the glass panel |
US7045181B2 (en) | 2001-12-25 | 2006-05-16 | Nippon Sheet Glass Co., Ltd. | Double glazing |
US7910229B2 (en) | 2002-05-03 | 2011-03-22 | Ppg Industries Ohio, Inc. | Substrate having thermal management coating for an insulating glass unit |
US7632571B2 (en) | 2005-03-31 | 2009-12-15 | Cardinal Cg Company | Haze-resistant low-emissivity coatings |
US7858193B2 (en) | 2005-08-23 | 2010-12-28 | Saint Gobain Glass France | Low emissivity (low-E) thin coating stacks with intermediate antidiffusion layers |
US7342716B2 (en) | 2005-10-11 | 2008-03-11 | Cardinal Cg Company | Multiple cavity low-emissivity coatings |
US8821999B2 (en) | 2008-11-05 | 2014-09-02 | Corning Incorporated | Vacuum-insulated glass windows with glass-bump spacers |
US8951617B2 (en) | 2008-12-22 | 2015-02-10 | Saint-Gobain Glass France | Substrate provided with a multilayer coating having thermal properties and absorbent layers |
US9215760B2 (en) | 2012-01-10 | 2015-12-15 | Saint-Gobain Glass France | Transparent pane with electrically conductive coating |
US10153389B2 (en) | 2014-10-01 | 2018-12-11 | Ferro Gmbh | Tellurate joining glass having processing temperatures less than or equal to 420° C |
US11124450B2 (en) | 2017-11-10 | 2021-09-21 | Nippon Sheet Glass Company, Limited | Glass panel and glass window |
US10759693B2 (en) | 2018-07-16 | 2020-09-01 | Guardian Glass, LLC | Low-E matchable coated articles having absorber film and corresponding methods |
US20210270084A1 (en) * | 2018-07-31 | 2021-09-02 | Panasonic Intellectual Property Management Co., Ltd. | Method for manufacturing glass panel unit |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US10465433B2 (en) | Vacuum insulating glass (VIG) unit with lead-free dual-frit seals and/or methods of making the same | |
KR102285744B1 (ko) | 진공 단열 유리(vig) 유닛에 이용되는 프릿, 및/또는 관련 방법 | |
JP6565700B2 (ja) | 複層ガラス、及びその製造方法 | |
WO2024112494A1 (fr) | Panneau isolant sous vide avec piège à gaz ayant une phase cristalline ti-al-v et son procédé de fabrication | |
US20240167327A1 (en) | Method of making vacuum insulated panel with pre-heating and laser heating | |
WO2024112407A1 (fr) | Panneau isolé sous vide avec getter allongé | |
WO2024112482A1 (fr) | Panneau isolant sous vide avec joint stratifié comprenant de l'oxyde de tellure et/ou de l'oxyde de vanadium | |
WO2024112484A1 (fr) | Panneau isolé sous vide avec joint en couches et/ou son procédé de fabrication | |
WO2024112500A1 (fr) | Joint d'étanchéité de panneau isolé sous vide | |
WO2024112493A1 (fr) | Panneau isolant sous vide avec joint stratifié et/ou son procédé de fabrication | |
WO2024112499A1 (fr) | Panneau isolé sous vide comprenant de l'oxyde de tellure et/ou du bore et un joint d'étanchéité comprenant de l'oxyde de bismuth | |
WO2024112408A1 (fr) | Panneau isolant sous vide avec joint pour tube de pompage et/ou son procédé de fabrication | |
WO2024112578A1 (fr) | Procédé de fabrication d'un panneau isolé sous vide avec une durée d'émission laser | |
WO2024112513A1 (fr) | Procédé de fabrication d'un panneau isolé sous vide avec un préchauffage et un chauffage au laser | |
WO2024112483A1 (fr) | Panneau isolé sous vide avec joint d'étanchéité comprenant de l'oxyde de tellure et/ou de l'oxyde de vanadium | |
WO2024112554A1 (fr) | Procédé de fabrication d'un panneau isolé sous vide avec une vitesse laser optimisée | |
WO2024112485A1 (fr) | Panneau isolé sous vide à joint en couches | |
WO2024112514A1 (fr) | Procédé de fabrication d'un panneau isolé sous vide à taille de faisceau laser optimisée | |
WO2024112487A1 (fr) | Panneau isolé sous vide à contrainte de compression et/ou de traction optimisée dans le verre | |
WO2024112552A1 (fr) | Procédé de fabrication d'un panneau isolé sous vide à l'aide d'un traitement au laser d'un matériau d'étanchéité pour changer la stoechiométrie et/ou un ou plusieurs états d'oxydation | |
US20220065029A1 (en) | Vacuum insulated glazing unit with dense side seal material | |
TW201237470A (en) | Reflective mirror and manufacturing method therefor | |
WO2024112624A1 (fr) | Panneau à isolation sous vide avec joint multi-rangées | |
WO2024112757A1 (fr) | Panneau à isolation sous vide avec couche de passivation | |
CN109265022A (zh) | 一种采用普通玻璃制备腔体内带有负压真空玻璃的方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 23821064 Country of ref document: EP Kind code of ref document: A1 |