WO2024022873A1 - Buse d'entrée immergée - Google Patents

Buse d'entrée immergée Download PDF

Info

Publication number
WO2024022873A1
WO2024022873A1 PCT/EP2023/069815 EP2023069815W WO2024022873A1 WO 2024022873 A1 WO2024022873 A1 WO 2024022873A1 EP 2023069815 W EP2023069815 W EP 2023069815W WO 2024022873 A1 WO2024022873 A1 WO 2024022873A1
Authority
WO
WIPO (PCT)
Prior art keywords
carbon
submerged entry
cao
refractory material
refractory
Prior art date
Application number
PCT/EP2023/069815
Other languages
English (en)
Inventor
Enno Wolfram ZINNGREBE
Original Assignee
Tata Steel Ijmuiden B.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tata Steel Ijmuiden B.V. filed Critical Tata Steel Ijmuiden B.V.
Publication of WO2024022873A1 publication Critical patent/WO2024022873A1/fr

Abstract

L'invention concerne une buse d'entrée immergée à travers laquelle de l'acier fondu peut être versé à partir d'un panier de coulée dans un moule, ladite buse comprenant : un corps sensiblement tubulaire constitué d'un matériau réfractaire lié au carbone, s'étendant d'une première extrémité à une seconde extrémité ; une paroi de buse interne entourant un passage venant en contact lors de l'utilisation avec l'acier fondu, s'étendant à travers ledit corps tubulaire le long d'un axe longitudinal de ladite première extrémité vers ladite seconde extrémité ; un ou plusieurs orifices ou ouvertures de sortie, débouchant dans ledit passage dans une région adjacente à ladite seconde extrémité ; et le matériau réfractaire étant un matériau réfractaire lié au carbone contenant 2 à 40 % en poids de carbone, au moins 60 % en poids d'un ou plusieurs oxydes métalliques dont au moins 60 % en poids sont de l'alumine, la teneur totale en autres composants étant de 10 % en poids ou moins, et au moins une partie de la paroi de buse interne étant pourvue d'une couche de frittage assisté par fusion solide comprenant de l'aluminate de calcium formant une couche imperméable aux gaz. L'invention concerne également un procédé de fabrication d'une buse d'entrée immergée.
PCT/EP2023/069815 2022-07-28 2023-07-17 Buse d'entrée immergée WO2024022873A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP22187506 2022-07-28
EP22187506.5 2022-07-28

Publications (1)

Publication Number Publication Date
WO2024022873A1 true WO2024022873A1 (fr) 2024-02-01

Family

ID=82781069

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2023/069815 WO2024022873A1 (fr) 2022-07-28 2023-07-17 Buse d'entrée immergée

Country Status (1)

Country Link
WO (1) WO2024022873A1 (fr)

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3991815A (en) 1974-06-25 1976-11-16 Vereinigte Osterreichische Eisen- Und Stahlwerke-Alpine Montan Aktiengesellschaft Casting tube with a bottom opening for continuously casting steel strands
US5681499A (en) * 1994-06-15 1997-10-28 Vesuvius Crucible Company Method and compositions for making refractory shapes having dense, carbon free surfaces and shapes made therefrom
EP1036614A1 (fr) 1999-03-18 2000-09-20 Shinagawa Refractories Co., Ltd. Busette de coulée submergée utilisée dans la coulée continue
JP2010131634A (ja) * 2008-12-04 2010-06-17 Kurosaki Harima Corp 連続鋳造用ノズル用の耐火物及び連続鋳造用ノズル
EP2226141A2 (fr) 2006-06-01 2010-09-08 Refractory Intellectual Property GmbH & Co. KG Buse de coulee
EP2441740A1 (fr) 2010-05-07 2012-04-18 Krosakiharima Corporation Réfractaire, buse à coulée continue comprenant le réfractaire, procédé de fabrication de buse à coulée continue, et procédé de coulée continue utilisant la buse à coulée continue
US20140103079A1 (en) 2011-07-06 2014-04-17 Refractory Intellectual Property Gmbh & Co. Kg Nozzle for guiding a metal melt
WO2015158439A1 (fr) 2014-04-15 2015-10-22 Tata Steel Ijmuiden B.V. Busette immergée pour coulée continue
US20160082509A1 (en) 2013-06-20 2016-03-24 Refractory Intellectual Property Gmbh & Co. Kg Refractory submerged entry nozzle
WO2019101389A1 (fr) 2017-11-22 2019-05-31 Refractory Intellectual Property Gmbh & Co. Kg Buse d'entrée immergée

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3991815A (en) 1974-06-25 1976-11-16 Vereinigte Osterreichische Eisen- Und Stahlwerke-Alpine Montan Aktiengesellschaft Casting tube with a bottom opening for continuously casting steel strands
US5681499A (en) * 1994-06-15 1997-10-28 Vesuvius Crucible Company Method and compositions for making refractory shapes having dense, carbon free surfaces and shapes made therefrom
EP1036614A1 (fr) 1999-03-18 2000-09-20 Shinagawa Refractories Co., Ltd. Busette de coulée submergée utilisée dans la coulée continue
EP2226141A2 (fr) 2006-06-01 2010-09-08 Refractory Intellectual Property GmbH & Co. KG Buse de coulee
JP2010131634A (ja) * 2008-12-04 2010-06-17 Kurosaki Harima Corp 連続鋳造用ノズル用の耐火物及び連続鋳造用ノズル
EP2441740A1 (fr) 2010-05-07 2012-04-18 Krosakiharima Corporation Réfractaire, buse à coulée continue comprenant le réfractaire, procédé de fabrication de buse à coulée continue, et procédé de coulée continue utilisant la buse à coulée continue
US20140103079A1 (en) 2011-07-06 2014-04-17 Refractory Intellectual Property Gmbh & Co. Kg Nozzle for guiding a metal melt
US20160082509A1 (en) 2013-06-20 2016-03-24 Refractory Intellectual Property Gmbh & Co. Kg Refractory submerged entry nozzle
WO2015158439A1 (fr) 2014-04-15 2015-10-22 Tata Steel Ijmuiden B.V. Busette immergée pour coulée continue
WO2019101389A1 (fr) 2017-11-22 2019-05-31 Refractory Intellectual Property Gmbh & Co. Kg Buse d'entrée immergée

Similar Documents

Publication Publication Date Title
US5370370A (en) Liner for submerged entry nozzle
US5691061A (en) Refractory shape having an external layer capable of forming a layer impermeable to gases and process for its preparation
US5185300A (en) Erosion, thermal shock and oxidation resistant refractory compositions
US4870037A (en) Prevention of Al2 O3 formation in pouring nozzles and the like
US5681499A (en) Method and compositions for making refractory shapes having dense, carbon free surfaces and shapes made therefrom
US20160039719A1 (en) Zirconia based coating for refractory elements and refractory element comprising of such coating
JPS591229B2 (ja) 溶鋼の連続鋳造用浸漬ノズル
KR100393233B1 (ko) 기체에불침투성인층을형성할수있는외부층을갖는캐스팅과그것의제조공정
WO2024022873A1 (fr) Buse d'entrée immergée
CA1168019A (fr) Buse d'immersion pour la coulee continue de l'acier
JP3128515B2 (ja) 鋼の連続鋳造用ノズル
AU730801B2 (en) A continuous casting nozzle for casting molten steel
US20060071041A1 (en) Gas purged nozzle
US5858261A (en) Continuous casting nozzle for casting molten steel
US5975382A (en) Continuous casting nozzle for casting molten steel
US6533146B1 (en) Continuous casting nozzle for molten steel
JP2020083678A (ja) ジルコニア−炭素含有耐火物
AU751983B2 (en) A continuous casting nozzle for molten steel
AU748092B2 (en) Continuous casting nozzle
AU746450B2 (en) Continuous casting nozzle
JP3563918B2 (ja) 鋼の連続鋳造用ノズル
JP3750965B2 (ja) 鋼の連続鋳造用ノズル
Hoggard et al. Prevention of Al 2 O 3 formation in pouring nozzles and the like
JPH06170504A (ja) 連続鋳造用ノズル
JPH03133554A (ja) 連続鋳造用ノズル

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23742087

Country of ref document: EP

Kind code of ref document: A1