WO2023275493A1 - Substrat revêtu d'au moins une couche de carbone de type diamant protégée par une couche temporaire à base de germanium ou à base d'oxyde de germanium - Google Patents
Substrat revêtu d'au moins une couche de carbone de type diamant protégée par une couche temporaire à base de germanium ou à base d'oxyde de germanium Download PDFInfo
- Publication number
- WO2023275493A1 WO2023275493A1 PCT/FR2022/051298 FR2022051298W WO2023275493A1 WO 2023275493 A1 WO2023275493 A1 WO 2023275493A1 FR 2022051298 W FR2022051298 W FR 2022051298W WO 2023275493 A1 WO2023275493 A1 WO 2023275493A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- germanium
- layers
- dlc
- substrate
- Prior art date
Abstract
Description
Claims