WO2023228308A1 - 磁気抵抗効果素子 - Google Patents

磁気抵抗効果素子 Download PDF

Info

Publication number
WO2023228308A1
WO2023228308A1 PCT/JP2022/021362 JP2022021362W WO2023228308A1 WO 2023228308 A1 WO2023228308 A1 WO 2023228308A1 JP 2022021362 W JP2022021362 W JP 2022021362W WO 2023228308 A1 WO2023228308 A1 WO 2023228308A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
magnetoresistive element
ferromagnetic layer
ferromagnetic
nonmagnetic
Prior art date
Application number
PCT/JP2022/021362
Other languages
English (en)
French (fr)
Inventor
智生 佐々木
振尭 唐
Original Assignee
Tdk株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tdk株式会社 filed Critical Tdk株式会社
Priority to PCT/JP2022/021362 priority Critical patent/WO2023228308A1/ja
Priority to US17/971,775 priority patent/US20230389444A1/en
Publication of WO2023228308A1 publication Critical patent/WO2023228308A1/ja

Abstract

この磁気抵抗効果素子は、第１強磁性層と第２強磁性層と非磁性層とを備え、前記非磁性層は、前記第１強磁性層と前記第２強磁性層との間に有り、前記非磁性層は、前記積層方向と直交する平坦面に対してうねっている。

Description

磁気抵抗効果素子
　本発明は、磁気抵抗効果素子に関する。
　磁気抵抗効果素子は、磁気抵抗効果により積層方向の抵抗値が変化する素子である。磁気抵抗効果素子は、２つの強磁性層とこれらに挟まれた非磁性層とを備える。非磁性層に導体が用いられた磁気抵抗効果素子は、巨大磁気抵抗（ＧＭＲ）素子と言われ、非磁性層に絶縁層（トンネルバリア層、バリア層）が用いられた磁気抵抗効果素子は、トンネル磁気抵抗（ＴＭＲ）素子と言われる。
　磁気抵抗効果素子は、磁気センサ、高周波部品、磁気ヘッド及び不揮発性ランダムアクセスメモリ（ＭＲＡＭ）等の様々な用途への応用が可能である（例えば、特許文献１及び２）。例えば、特許文献３には、磁気抵抗効果素子の積層方向に電流を流すことで生ずるスピントランスファートルク（ＳＴＴ）を利用して、磁化の向きを制御する方法が記載されている。この方法は、スピン注入磁化反転方式と呼ばれている。
特許第５５８６０２８号公報 特許第５９８８０１９号公報 特開第２０１５－１５６５０１号公報
　磁化反転を容易にするために、磁化反転に必要なエネルギーを小さくしたいという要望がある。
　本発明は上記事情に鑑みてなされたものであり、少ないエネルギーで磁化反転する磁気抵抗効果素子を提供することを目的とする。
　本発明は、上記課題を解決するため、以下の手段を提供する。
（１）第１の態様にかかる磁気抵抗効果素子は、第１強磁性層と第２強磁性層と非磁性層とを備える。前記非磁性層は、前記第１強磁性層と前記第２強磁性層との間に有る。前記非磁性層は、前記積層方向と直交する基準面に対してうねっている。
（２）上記態様にかかる磁気抵抗効果素子は、前記基準面に対して上方に突出する凸部の頂点間距離の平均値が、前記非磁性層の幅の３０％以下でもよい。
（３）上記態様にかかる磁気抵抗効果素子は、前記基準面に対して上方に突出する凸部の頂点間距離の平均値が、３０ｎｍ以下でもよい。
（４）上記態様にかかる磁気抵抗効果素子は、前記非磁性層の幅が、前記非磁性層のうねりの２周期分以上でもよい。
（５）上記態様にかかる磁気抵抗効果素子は、前記非磁性層の最高点と最低点との差が、前記非磁性層の膜厚の２倍以下でもよい。
（６）上記態様にかかる磁気抵抗効果素子は、磁気誘起層をさらに備えてもよい。前記磁気誘起層と前記非磁性層とは、前記第１強磁性層を挟む。
（７）上記態様にかかる磁気抵抗効果素子は、スペーサ層と第３強磁性層とをさらに備えてもよい。前記スペーサ層は、前記第２強磁性層に接し、前記第２強磁性層と前記第３強磁性層とは、前記スペーサ層を挟む。
（８）上記態様にかかる磁気抵抗効果素子は、下地層をさらに備えてもよい。前記下地層と前記非磁性層との間にある層は、前記積層方向と直交する基準面に対してうねっていてもよい。
　本発明にかかる磁気抵抗効果素子は、少ないエネルギーで磁化反転できる。
第１実施形態にかかる磁気メモリの回路図である。 第１実施形態にかかる磁気メモリの特徴部分の断面図である。 第１実施形態にかかる磁気抵抗効果素子の断面図である。 第１実施形態にかかる磁気抵抗効果素子の平面図である。 第１実施形態にかかる磁気抵抗効果素子の特徴部分の拡大図である。 実施例１～４及び比較例の結果をまとめた図である。
　以下、本実施形態について、図を適宜参照しながら詳細に説明する。以下の説明で用いる図面は、特徴をわかりやすくするために便宜上特徴となる部分を拡大して示している場合があり、各構成要素の寸法比率などは実際とは異なっていることがある。以下の説明において例示される材料、寸法等は一例であって、本発明はそれらに限定されるものではなく、本発明の効果を奏する範囲で適宜変更して実施することが可能である。
　まず方向について定義する。後述する基板Ｓｕｂ（図２参照）の一面の一方向をｘ方向、ｘ方向と直交する方向をｙ方向とする。ｚ方向は、ｘ方向及びｙ方向と直交する方向である。ｚ方向は、各層が積層される積層方向の一例である。以下、＋ｚ方向を「上」、－ｚ方向を「下」と表現する場合がある。上下は、必ずしも重力が加わる方向とは一致しない。
　本明細書で「接続」とは、物理的に接続される場合に限定されない。例えば、二つの層が物理的に接している場合に限られず、二つの層の間が他の層を間に挟んで接続している場合も「接続」に含まれる。また本明細書での「接続」は電気的な接続も含む。
「第１実施形態」
　図１は、第１実施形態にかかる磁気メモリ１００の構成図である。磁気メモリ１００は、複数の磁気抵抗効果素子１０と、複数のソース線ＳＬと、複数のビット線ＢＬと、複数の第１スイッチング素子Ｓｗ１と、を備える。
　磁気抵抗効果素子１０は、例えば、行列状に配列している。磁気抵抗効果素子１０のそれぞれは、ソース線ＳＬ、ビット線ＢＬに接続されている。ソース線ＳＬは、電源と１つ以上の磁気抵抗効果素子１０とを電気的に接続する。ビット線ＢＬは、基準電位と１つ以上の磁気抵抗効果素子１０とを電気的に接続する。基準電位は、例えば、グラウンドである。電源は、使用時に磁気メモリ１００に接続される。
　磁気抵抗効果素子１０への電流の流れは、第１スイッチング素子Ｓｗ１で制御される。磁気抵抗効果素子１０は、第１スイッチング素子Ｓｗ１をＯＮにすることで、データの書き込み、読出しが行われる。磁気抵抗効果素子１０は、積層方向に電流が流れることで、スピントランスファートルクを用いてデータの書き込みを行う。
　第１スイッチング素子Ｓｗ１は、電流の流れを制御する素子である。第１スイッチング素子Ｓｗ１は、例えば、トランジスタ、オボニック閾値スイッチ（ＯＴＳ：Ovonic Threshold Switch）のように結晶層の相変化を利用した素子、金属絶縁体転移（ＭＩＴ）スイッチのようにバンド構造の変化を利用した素子、ツェナーダイオード及びアバランシェダイオードのように降伏電圧を利用した素子、原子位置の変化に伴い伝導性が変化する素子である。
　図２は、第１実施形態に係る磁気メモリ１００の特徴部分の断面図である。図２に示す第１スイッチング素子Ｓｗ１は、トランジスタＴｒである。トランジスタＴｒは、例えば電界効果型のトランジスタであり、ゲート電極Ｇとゲート絶縁膜ＧＩと基板Ｓｕｂに形成されたソースＳ及びドレインＤとを有する。ソースＳとドレインＤは、電流の流れ方向によって既定されるものであり、これらは同一の領域である。ソースＳとドレインＤの位置関係は、反転していてもよい。基板Ｓｕｂは、例えば、半導体基板である。
　トランジスタＴｒと磁気抵抗効果素子１０とは、ビア配線Ｖ、電極１１及び電極１２を介して、電気的に接続されている。またトランジスタＴｒとビット線ＢＬとは、ビア配線Ｖで接続されている。ビア配線Ｖは、例えば、ｚ方向に延びる。ソース線ＳＬは、電極１２を介して磁気抵抗効果素子１０に接続されている。ビア配線Ｖ、電極１１、１２は、導電性を有する材料を含む。ビア配線Ｖと電極１１は一体化していてもよい。またソース線ＳＬと電極１２とは一体化していてもよい。すなわち、電極１１はビア配線Ｖの一部でもよく、電極１２はソース線ＳＬの一部でもよい。
　磁気抵抗効果素子１０の周囲は、絶縁層９０で覆われている。絶縁層９０は、多層配線の配線間や素子間を絶縁する絶縁層である。絶縁層９０は、例えば、酸化シリコン（ＳｉＯｘ）、窒化シリコン（ＳｉＮｘ）、炭化シリコン（ＳｉＣ）、窒化クロム、炭窒化シリコン（ＳｉＣＮ）、酸窒化シリコン（ＳｉＯＮ）、酸化アルミニウム（Ａｌ２Ｏ３）、酸化ジルコニウム（ＺｒＯｘ）、酸化マグネシウム（ＭｇＯ）、窒化アルミニウム（ＡｌＮ）等である。
　図３は、磁気抵抗効果素子１０の断面図である。図３は、磁気抵抗効果素子１０の中心を通るｘｚ平面で磁気抵抗効果素子１０を切断した断面である。図４は、磁気抵抗効果素子１０をｚ方向から見た平面図である。
　磁気抵抗効果素子１０は、データを記録、保存する素子である。磁気抵抗効果素子１０は、ｚ方向の抵抗値でデータを記録する。磁気抵抗効果素子１０のｚ方向の抵抗値は、ｚ方向に書き込み電流を印加することで変化する。磁気抵抗効果素子１０のｚ方向の抵抗値は、磁気抵抗効果素子１０のｚ方向に読出し電流を印加することで読み出すことができる。
　磁気抵抗効果素子１０は、第１強磁性層１と第２強磁性層２と非磁性層３とを備える。非磁性層３は、第１強磁性層１と第２強磁性層２との間に位置する。磁気抵抗効果素子１０は、これらの他に、バッファ層４、シード層５、強磁性層６、スペーサ層７、磁気誘起層８を有してもよい。バッファ層４、シード層５、強磁性層６及びスペーサ層７は、第１強磁性層１と電極１１との間に位置し、磁気誘起層８は、第２強磁性層２と電極１２との間に位置する。
　磁気抵抗効果素子１０は、柱状の積層体である。磁気抵抗効果素子１０のｚ方向から見た平面視形状は、特に問わない。例えば、図２に示すように、ｘ方向の幅Ｗ１とｙ方向の幅Ｗ２が一致する円形でもよい。幅Ｗ１と幅Ｗ２は一致する必要はなく、平面視形状は楕円形、オーバル、矩形でもよい。磁気抵抗効果素子１０の幅Ｗ１，Ｗ２は、例えば、１０ｎｍ以上２０００ｎｍ以下であり、好ましくは３０ｎｍ以上５００ｎｍ以下である。
　第１強磁性層１及び第２強磁性層２は、例えば、ｚ方向に磁化容易軸を有する垂直磁化膜である。第１強磁性層１及び第２強磁性層２は、ｘｙ面内のいずれかの方向に磁化容易軸を有する面内磁化膜でもよい。
　第１強磁性層１と第２強磁性層２はそれぞれ、強磁性体を含む。第１強磁性層１の磁化は、例えば、第２強磁性層２の磁化より動きにくい。所定の外力を加えた場合に、第１強磁性層１の磁化の向きは変化せず（固定され）、第２強磁性層２の磁化の向きは変化する。第１強磁性層１は、磁化固定層と言われる。第２強磁性層２は、磁化自由層と言われる。図３に示す磁気抵抗効果素子１０は、磁化固定層が磁化自由層より基板Ｓｕｂの近くにあり、ボトムピン構造と呼ばれる。第１強磁性層１と第２強磁性層２との位置関係は反対でもよい。第１強磁性層１の磁化と第２強磁性層２の磁化との相対角の変化に応じて、磁気抵抗効果素子１０の抵抗値は変化する。
　第１強磁性層１と第２強磁性層２それぞれは、例えば、Ｃｒ、Ｍｎ、Ｃｏ、Ｆｅ及びＮｉからなる群から選択される金属、これらの金属を１種以上含む合金、これらの金属とＢ、Ｃ、及びＮの少なくとも１種以上の元素とが含まれる合金等である。第１強磁性層１と第２強磁性層２それぞれは、例えば、Ｃｏ－Ｆｅ、Ｃｏ－Ｆｅ－Ｂ、Ｎｉ－Ｆｅ、Ｃｏ－Ｈｏ合金、Ｓｍ－Ｆｅ合金、Ｆｅ－Ｐｔ合金、Ｃｏ－Ｐｔ合金、ＣｏＣｒＰｔ合金である。また、第１強磁性層１と第２強磁性層２それぞれは、例えば、ＣｏとＰｔやＣｏとＮｉを複数回積層した多層膜を含んでもよい。
　第１強磁性層１及び第２強磁性層２は、ホイスラー合金を含んでもよい。ホイスラー合金は、ＸＹＺまたはＸ２ＹＺの化学組成をもつ金属間化合物を含む。Ｘは周期表上でＣｏ、Ｆｅ、Ｎｉ、あるいはＣｕ族の遷移金属元素または貴金属元素であり、ＹはＭｎ、Ｖ、ＣｒあるいはＴｉ族の遷移金属又はＸの元素種であり、ＺはＩＩＩ族からＶ族の典型元素である。ホイスラー合金は、例えば、Ｃｏ２ＦｅＳｉ、Ｃｏ２ＦｅＧｅ、Ｃｏ２ＦｅＧａ、Ｃｏ２ＭｎＳｉ、Ｃｏ２Ｍｎ１－ａＦｅａＡｌｂＳｉ１－ｂ、Ｃｏ２ＦｅＧｅ１－ｃＧａｃ等である。ホイスラー合金は高いスピン分極率を有する。
　非磁性層３は、非磁性体を含む。非磁性層３が絶縁体の場合（トンネルバリア層である場合）、その材料としては、例えば、Ａｌ２Ｏ３、ＳｉＯ２、ＭｇＯ、及び、ＭｇＡｌ２Ｏ４等を用いることができる。また、これらの他にも、Ａｌ、Ｓｉ、Ｍｇの一部が、Ｚｎ、Ｂｅ等に置換された材料等も用いることができる。これらの中でも、ＭｇＯやＭｇＡｌ２Ｏ４はコヒーレントトンネルが実現できる材料であるため、スピンを効率よく注入できる。非磁性層３が金属の場合、その材料としては、Ｃｕ、Ａｕ、Ａｇ等を用いることができる。さらに、非磁性層３が半導体の場合、その材料としては、Ｓｉ、Ｇｅ、ＣｕＩｎＳｅ２、ＣｕＧａＳｅ２、Ｃｕ（Ｉｎ，Ｇａ）Ｓｅ２等を用いることができる。
　図５は、第１実施形態にかかる磁気抵抗効果素子１０の特徴部分の拡大図である。非磁性層３は、基準面Ｓ１に対してうねっている。基準面Ｓ１は、非磁性層３のｚ方向の最高点と最低点との間の中点を通り、積層方向と直交するｘｙ面内に広がる面である。基準面Ｓ１に対してうねっているとは、基準面Ｓ１に対して上に凸の部分と下に凸の部分とが一方向に交互に並ぶことをいう。
　非磁性層３は、例えば、基準面Ｓ１に対して上に凸の部分と下に凸の部分とが一方向に周期的に配列する。非磁性層３のうねりの周期ｐは、非磁性層３の幅Ｗ１の３０％以下であることが好ましい。非磁性層３のうねりの周期ｐは、例えば、３０ｎｍ以下であることが好ましい。当該条件を満たすと、第２強磁性層２の磁化を反転させるために必要な反転電流密度を特に下げることができる。
　周期ｐは、基準面Ｓ１に対して上方に突出する凸部の頂点間距離の平均値として求めることができる。凸部の頂点間距離の平均値は、隣接する凸部の頂点２Ｔの距離のそれぞれを求め、その平均値を算出することで求められる。隣接する凸部の頂点２Ｔの距離は、例えば、走査型電子顕微鏡で測定できる。周期ｐは、基準面Ｓ１に対して下方に突出する凸部の頂点間距離の平均値として求めてもよい。
　非磁性層３は、例えば、ｘｙ面内のいずれかの方向に２周期分以上のうねりを有する。例えば、非磁性層３の幅Ｗ１又は幅Ｗ２が、うねりの２周期分（２ｐ）以上であることが好ましい。非磁性層３の長軸方向の幅は、例えば、うねりの２周期分（２ｐ）以上であることが好ましい。当該条件を満たすと、第２強磁性層２の磁化を反転させるために必要な反転電流密度を特に下げることができる。
　非磁性層３の最高点と最低点との高さの差ｈは、例えば、非磁性層３の膜厚ｔの２倍以下である。非磁性層３の最高点と最低点との高さの差ｈは、ｚ方向の最高点から、ｚ方向の最低点を通りｘｙ面内に広がる面に下した垂線の高さである。非磁性層３の膜厚ｔは、ｘｙ面内の異なる１０点で測定した非磁性層３の膜厚の平均値である。非磁性層３の最高点と最低点との高さの差ｈ及び非磁性層３の膜厚ｔは、走査型電子顕微鏡で測定できる。非磁性層３の膜厚ｔは、例えば、０．５ｎｍ以上１０．０ｎｍ以下であり、１．０ｎｍ以上５．０ｎｍ以下である。
　非磁性層３のうねりの高さが上記範囲であると、第２強磁性層２の磁化Ｍ２がｚ方向に対する傾きの程度が所定の範囲内となる。第２強磁性層２の磁化Ｍ２が傾きが所定の範囲内であれば、磁気抵抗効果素子１０のＭＲ比の低下を抑制できる。
　バッファ層４及びシード層５は、下地層と言われる。バッファ層４は、異なる結晶間の格子不整合を緩和する層である。バッファ層４は、例えば、Ｔａ、Ｔｉ、Ｚｒ及びＣｒからなる群から選択される少なくとも一種の元素を含む金属又は、Ｔａ、Ｔｉ、Ｚｒ及びＣｕからなる群から選択される少なくとも一種の元素を含む窒化物である。より具体的には、バッファ層４は、例えば、Ｔａ（単体）、ＴａＮ（窒化タンタル）、ＣｕＮ（窒化銅）、ＴｉＮ（窒化チタン）、ＮｉＡｌ（ニッケルアルミニウム）である。バッファ層４の膜厚は、例えば、１ｎｍ以上５ｎｍ以下である。バッファ層４は、例えば、非晶質である。バッファ層４は、例えば、シード層５と電極１１との間に位置し、電極１１に接する。バッファ層４は、電極１１の結晶構造が第１強磁性層１の結晶構造に影響を及ぼすことを抑制する。
　シード層５は、シード層５上に積層される層の結晶性を高める。シード層５は、例えば、バッファ層４と強磁性層６との間に位置し、バッファ層４上にある。シード層５は、例えば、例えば、（００１）配向したＮａＣｌ構造を有する化合物である。シード層５は、例えば、Ｐｔ、Ｒｕ、Ｚｒ、ＮｉＣｒ合金、ＮｉＦｅＣｒである。シード層５の膜厚は、例えば、１ｎｍ以上５ｎｍ以下である。
　強磁性層６は、例えば、第１強磁性層１と磁気結合する。磁気結合は、例えば、反強磁性的な結合であり、ＲＫＫＹ相互作用により生じる。第１強磁性層１の磁化の向きと強磁性層６の磁化の向きとは反平行の関係である。強磁性層６を構成する材料は、例えば、第１強磁性層１と同様である。強磁性層６、スペーサ層７、第１強磁性層１は、シンセティック反強磁性構造（ＳＡＦ構造）となる。シンセティック反強磁性構造は、非磁性層を挟む二つの磁性層からなる。第１強磁性層１と強磁性層６とが反強磁性カップリングすることで、強磁性層６を有さない場合より第１強磁性層１の保磁力が大きくなる。
　スペーサ層７は、第２強磁性層２と強磁性層６との間に位置する。スペーサ層７は、磁気結合層とも呼ばれる。スペーサ層７は、例えば、Ｒｕ、Ｉｒ等である。
　磁気誘起層８は、例えば、第２強磁性層２の磁気異方性を強める。磁気誘起層８は、例えば、第２強磁性層２の垂直磁気異方性を強める。磁気誘起層８は、例えば酸化マグネシウム、Ｗ、Ｔａ、Ｍｏ等である。磁気誘起層８が酸化マグネシウムの場合は、導電性を高めるために、酸化マグネシウムが酸素欠損していることが好ましい。磁気誘起層８の膜厚は、例えば、０．５ｎｍ以上５．０ｎｍ以下である。
　磁気抵抗効果素子１０において、非磁性層３以外の各層は、非磁性層３と同様に、基準面Ｓ１と平行な面に対してうねっていてもよい。
　例えば、第１強磁性層１と第２強磁性層２のそれぞれは、基準面Ｓ１と平行な面に対してうねっていてもよい。第１強磁性層１と第２強磁性層２のうねりの周期は、非磁性層３のうねりの周期と略一致する。第１強磁性層１と第２強磁性層２のうねりの高さは、非磁性層３のうねりの高さと略一致する。第１強磁性層１と第２強磁性層２のそれぞれは、例えば、非磁性層３の形状を反映している。
　また例えば、下地層（バッファ層４及びシード層５）と第１強磁性層１との間にある層（例えば、強磁性層６、スペーサ層７）は、基準面Ｓ１と平行な面に対してうねっていてもよい。これらの層のうねりの周期は、非磁性層３のうねりの周期と略一致する。これらの層のそれぞれは、例えば、非磁性層３の形状を反映している。
　次いで、磁気抵抗効果素子１０の製造方法について説明する。磁気抵抗効果素子１０は、各層の積層工程と、各層の一部を所定の形状に加工する加工工程により形成される。各層の積層は、スパッタリング法、化学気相成長（ＣＶＤ）法、電子ビーム蒸着法（ＥＢ蒸着法）、原子レーザデポジッション法等を用いることができる。各層の加工は、フォトリソグラフィー等を用いて行うことができる。
　まず電極１１上にバッファ層４を形成し、バッファ層４を所定の形状に加工する。そして、バッファ層４の周囲を絶縁層９０で覆う。
　次いで、バッファ層４の表面が露出するまで、化学機械研磨（ＣＭＰ）を行う。化学機械研磨の条件によって、バッファ層４の表面に凹凸が形成される。化学機械研磨の条件は、化学機械研磨の圧力、化学機械研磨の時間、研磨剤の種類、バッファ層４を構成する材料、絶縁層９０を構成する材料によって異なる。バッファ層４に形成される凹凸の周期、高さ等は、これらの条件を変化させることで調整できる。
　ＣＭＰ研磨の条件は、装置依存、研磨剤の種類、バッファ層４を構成する材料、絶縁層９０を構成する材料、研磨圧力、研磨時間によって変動する。そのため、ＣＭＰ研磨の条件は、複数回の条件出しを行い、フィードバックを複数回行い、事前に決定する。同じ条件で作製したサンプルを用いてこれらのパラメータを変更した事前検討を行うことで、ＣＭＰ研磨の条件は求められる。同条件で作製したサンプルに対して同条件でＣＭＰ研磨を行うと、再現性よくバッファ層４の表面状態を制御できる。
　次いで、ＣＭＰ研磨を行ったバッファ層４上に、シード層５、強磁性層６、スペーサ層７、第１強磁性層１、非磁性層３、第２強磁性層２、磁気誘起層８を順に成膜する。これらの各層は、バッファ層４の表面形状を追従し、湾曲する。その結果、これらの各層は、面内方向に広がる平坦面に対してうねる形状となる。
　次いで、成膜した各層を所定の形状に加工し、その周囲を絶縁層９０で覆う。そして、磁気誘起層８の表面が露出するまで、絶縁層９０を除去する。その後、磁気誘起層８上に、電極１２を形成する。
　磁気抵抗効果素子１０は、非磁性層３がうねっているため、第２強磁性層２の磁化を反転させるために必要な反転電流密度を下げることができる。これは、第２強磁性層２の磁化が非磁性層３の表面に沿って僅かに傾くためと考えられる。
　図５に示すように、第２強磁性層２の磁化Ｍ２は、非磁性層３の表面に対して直交するように配向する。磁化Ｍ２は、ｚ方向に対して傾斜している。磁化Ｍ２は、第１強磁性層１からスピンが注入されると、歳差運動を行いながら反転する。磁化Ｍ２が初期状態で傾いていると、磁化Ｍ２が磁化反転のための歳差運動を行いやすくなり、磁化反転に必要なエネルギーが小さくなる。その結果、本実施形態に係る磁気抵抗効果素子１０は、第２強磁性層２の磁化を反転させるために必要な反転電流密度を小さくできると考えられる。
　以上、第１実施形態に係る磁気抵抗効果素子１０の一例を示したが、本発明の趣旨から逸脱しない範囲内で、構成の付加、省略、置換、及びその他の変更が可能である。
　ここでは磁気抵抗効果素子１０を磁気メモリ１００に適用する例を示したが、この例に限られるものではない。例えば、磁気抵抗効果素子１０を磁気ヘッド、磁気センサ等に用いてもよい。この場合、磁気抵抗効果素子１０の幅Ｗ１，Ｗ２は、例えば、０．０１μｍ以上１０μｍ以下であり、好ましくは０．０６μｍ以上１０μｍ以下である。この場合のうねりの周期は、例えば、５ｎｍ以上３００ｎｍ以下であり、好ましくは１０ｎｍ以上１５０ｎｍ以下である。また磁気ヘッドの場合は、好ましくは０．０１μｍ以上１μｍ以下である。
「実施例１」
　直径１００ｎｍの磁気抵抗効果素子を作製した。磁気抵抗効果素子は、基板に近い側から順に、バッファ層（ＴｉＮ）、シード層（ＮｉＣｒ合金）、強磁性層（ＣｏＦｅ合金）、磁気結合層（Ｒｕ）、第１強磁性層（ＣｏＦｅ合金）、非磁性層（ＭｇＯ）、第２強磁性層（ＣｏＦｅ合金）、磁気誘起層（ＭｇＯ）を有する。バッファ層を成膜後に、表面をＣＭＰ研磨し、バッファ層の表面に凹凸を作製した。非磁性層は、バッファ層の凹凸に応じて、うねっていた。非磁性層のうねりの周期は、２０ｎｍであった。
　作製した実施例１の磁気抵抗効果素子を用いて反転電流密度を測定した。実施例１の反転電流密度は、５．１５ＭＡ／ｃｍ２であった。
「実施例２～４」
　実施例２～４は、非磁性層のうねりの周期を変えた点が実施例１と異なる。非磁性層のうねりの周期は、バッファ層をＣＭＰ研磨する際の条件を変えて変更した。実施例２のうねりの周期は３０ｎｍ、実施例３のうねりの周期は４０ｎｍ、実施例４のうねりの周期は６０ｎｍとした。そして、実施例２～４のそれぞれの磁気抵抗効果素子を用いて反転電流密度を測定した。
「比較例１」
　比較例１は、非磁性層が平坦である点が実施例１と異なる。バッファ層をＣＭＰ研磨する際の条件を変えて、バッファ層の表面を平坦にすることで、非磁性層は平坦になった。比較例１の磁気抵抗効果素子を用いて反転電流密度を測定した。
　実施例１～４及び比較例１の結果を図６にまとめた。図６において、比較例１はうねりがないため、凸部の距離を磁気抵抗効果素子の幅（１００ｎｍ）として表記した。図６に示すように、非磁性層３がうねっていると、磁気抵抗効果素子の反転電流密度が小さくなった。またうねりの周期が、磁気抵抗効果素子の幅の３０％以下となると、特に磁気抵抗効果素子の反転電流密度が小さくなった。
１…第１強磁性層、２…第２強磁性層、２Ｔ…頂点、３…非磁性層、４…バッファ層、５…シード層、６…強磁性層、７…スペーサ層、８…磁気誘起層、１０…磁気抵抗効果素子、１１，１２…電極、９０…絶縁層、１００…磁気メモリ、Ｓ１…基準面

Claims (8)

  1. 　第１強磁性層と第２強磁性層と非磁性層とを備え、
    　前記非磁性層は、前記第１強磁性層と前記第２強磁性層との間に有り、
    　前記非磁性層は、積層方向と直交する基準面に対してうねっている、磁気抵抗効果素子。
  2. 　前記基準面に対して上方に突出する凸部の頂点間距離の平均値が、前記非磁性層の幅の３０％以下である、請求項１に記載の磁気抵抗効果素子。
  3. 　前記基準面に対して上方に突出する凸部の頂点間距離の平均値が、３０ｎｍ以下である、請求項１に記載の磁気抵抗効果素子。
  4. 　前記非磁性層の幅が、前記非磁性層のうねりの２周期分以上である、請求項１に記載の磁気抵抗効果素子。
  5. 　前記非磁性層の最高点と最低点との差が、前記非磁性層の膜厚の２倍以下である、請求項１に記載の磁気抵抗効果素子。
  6. 　磁気誘起層をさらに備え、
    　前記磁気誘起層と前記非磁性層とは、前記第２強磁性層を挟む、請求項１に記載の磁気抵抗効果素子。
  7. 　スペーサ層と第３強磁性層とをさらに備え、
    　前記スペーサ層は、前記第１強磁性層に接し、
    　前記第１強磁性層と前記第３強磁性層とは、前記スペーサ層を挟む、請求項１に記載の磁気抵抗効果素子。
  8. 　下地層をさらに備え、
    　前記下地層と前記非磁性層との間にある層が、前記積層方向と直交する基準面に対してうねっている、請求項１に記載の磁気抵抗効果素子。
PCT/JP2022/021362 2022-05-25 2022-05-25 磁気抵抗効果素子 WO2023228308A1 (ja)