WO2023128384A1 - 탄산칼슘을 포함하는 슬러리 판상엽 시트를 포함하는 흡연 물품 - Google Patents

탄산칼슘을 포함하는 슬러리 판상엽 시트를 포함하는 흡연 물품 Download PDF

Info

Publication number
WO2023128384A1
WO2023128384A1 PCT/KR2022/019988 KR2022019988W WO2023128384A1 WO 2023128384 A1 WO2023128384 A1 WO 2023128384A1 KR 2022019988 W KR2022019988 W KR 2022019988W WO 2023128384 A1 WO2023128384 A1 WO 2023128384A1
Authority
WO
WIPO (PCT)
Prior art keywords
smoking article
smoking
slurry
calcium carbonate
sheet
Prior art date
Application number
PCT/KR2022/019988
Other languages
English (en)
French (fr)
Inventor
곽효민
안병용
이정래
전은영
Original Assignee
주식회사 케이티앤지
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 케이티앤지 filed Critical 주식회사 케이티앤지
Publication of WO2023128384A1 publication Critical patent/WO2023128384A1/ko

Abstract

본 발명은, 탄산칼슘을 10 내지 60 중량%로 포함하는 슬러리 판상엽 시트를 포함하는 흡연 물품에 관한 것이다. 상기 흡연 물품은, 탄산칼슘을 포함하는 슬러리 판상엽을 사용함으로써 끽미와 풍미가 우수한 것을 특징으로 한다.

Description

탄산칼슘을 포함하는 슬러리 판상엽 시트를 포함하는 흡연 물품
본 발명은, 탄산칼슘을 포함하는 슬러리 판상엽 시트를 포함하는 흡연 물품에 관한 것이다.
담배 제품의 제조에는 담배 잎 이외에도 균질화 담배 물질이 사용될 수 있다. 이 균질화 담배 물질은 통상적으로 담배 줄기 또는 담배 가루 등과 같이 궐련의 제조에 덜 적합한 담배 식물의 부분으로 제조된다. 통상적으로, 담배 가루는 제조 중에 담배 잎을 취급하는 동안 부산물로서 생성된다.
일반적인 균질화 담배 물질의 형태는 재생 담배 시트(reconstituted tobacco sheet) 및 캐스트 리프(cast leaf)이다. 균질화 담배 물질 시트는 담배 가루와 결합제를 혼합하여 슬러리를 형성하고, 슬러리를 사용하여 담배 웹을 생성하며, 움직이는 금속 벨트 상으로 점성 슬러리를 주조하여 제조할 수 있다. 또는, 점도가 낮고 수분 함량이 높은 슬러리를 사용하여 제지 공정과 유사한 공정에서 재구성한 담배를 생산할 수도 있다. 균질화 담배 웹은 궐련 및 기타 흡연 물품에 적합한 담배 절단 필러를 제조하기 위해 전체 잎담배와 유사한 방식으로, 판상엽 각초 형태로 절단될 수 있다.
선행기술문헌
특허문헌
(특허문헌 1) 공개특허 제2021-0115609호
본 발명은, 탄산칼슘을 포함하여 연기 성분을 저감시킬 수 있는 슬러리 판상엽 시트와 이를 포함하는 흡연 물품을 제공하는 것이다.
그러나, 본 발명이 해결하고자 하는 과제는 이상에서 언급한 것들로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 해당 분야 통상의 기술자에게 명확하게 이해될 수 있을 것이다.
본 발명의 일 실시예에 따라, 흡연물질부와 상기 흡연물질부보다 하류에 위치된 필터부를 구비한 흡연물품으로서,
상기 흡연물질부는 슬러리 판상엽 시트를 포함하고,
상기 슬러리 판상엽 시트는 탄산칼슘을 10 내지 60 중량%로 포함하는 것인, 흡연 물품에 관한 것이다.
본 발명의 일 실시예에 따라, 상기 탄산칼슘은, 0.5 μm 이하의 직경을 갖는 것일 수 있다.
본 발명의 일 실시예에 따라, 상기 슬러리 판상엽 시트는, 바인더를 더 포함하는 것일 수 있다.
본 발명의 일 실시예에 따라, 상기 바인더는 메틸셀룰로오스를 포함하는 것일 수 있다.
본 발명의 일 실시예에 따라, 상기 흡연 물질부는, 궐련 각초를 더 포함하는 것일 수 있다.
본 발명의 일 실시예에 따라, 상기 흡연 물질부는, 슬러리 판상엽 시트 및 궐련 각초를 25-75 : 75-25 의 혼합 중량비로 포함하는 것일 수 있다.
본 발명의 일 실시예에 따라, 상기 흡연 물질부는, 보습제를 포함하지 않는 것일 수 있다.
본 발명의 일 실시예에 따라, 상기 흡연 물품은, 연소식 궐련형 흡연 물품인 것일 수 있다.
본 발명은, 탄산칼슘을 포함하여 제조한 슬러리 판상엽 시트를 흡연 물품의 흡연 물질부에 포함하여, 특정연기성분이 저감되었으며 이와 동시에 끽미강도, 연기량, 목넘김 등이 우수한 흡연 물품을 제공할 수 있다.
도 1은 본 발명의 일 실시예에 따라, 슬러리 판상엽 시트가 포함되는 흡연물질부; 및 필터부를 포함하는 흡연 물품을 예시적으로 나타낸 것이다.
도 2는 본 발명의 일실시예에 따른 슬러리 판상엽 시트를 포함하는 흡연물품의 궐련당 연기 성분 분석 결과를 확인한 결과를 나타낸 것이다.
도 3은 본 발명의 일실시예에 따른 슬러리 판상엽 시트를 포함하는 흡연물품의 양목당 연기 성분 분석 결과를 확인한 결과를 나타낸 것이다.
도 4는 본 발명의 일실시예에 따른 슬러리 판상엽 시트를 포함하는 흡연물품의 바인더 종류에 따른 연기 성분 분석 결과를 확인한 결과를 나타낸 것이다.
도 5는 본 발명의 일실시예에 따른 슬러리 판상엽 시트를 포함하는 흡연물품의 관능평가 결과를 나타낸 것이다.
이하 첨부된 도면을 참조하여 본 발명의 실시예들을 상세히 설명한다. 본 발명을 설명함에 있어서, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략할 것이다. 또한, 본 명세서에서 사용되는 용어들은 본 발명의 바람직한 실시예를 적절히 표현하기 위해 사용된 용어들로서, 이는 사용자, 운용자의 의도 또는 본 발명이 속하는 분야의 관례 등에 따라 달라질 수 있다. 따라서, 본 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다. 각 도면에 제시된 동일한 참조 부호는 동일한 부재를 나타낸다.
명세서 전체에서, 어떤 부재가 다른 부재 "상에" 위치하고 있다고 할 때, 이는 어떤 부재가 다른 부재에 접해 있는 경우뿐 아니라 두 부재 사이에 또 다른 부재가 존재하는 경우도 포함한다.
명세서 전체에서, 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 다른 구성요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다.
명세서 전체에서, 용어 "상류" 및 "하류"는 사용자가 흡연 물품을 사용하여 외부 공기를 흡입할 때, 흡연 물품의 외부로부터 내부로 공기가 들어오는 부분이 "상류"이고, 흡연 물품의 내부로부터 외부로 공기가 나가는 부분이 "하류"이다. 용어 "상류" 및 "하류"는 흡연 물품을 구성하는 부분 또는 세그먼트들 간의 상대적인 위치 또는 방향을 나타내기 위해 사용될 수 있다.
이하, 본 발명의 탄산칼슘을 10 내지 60 중량%로 포함하는 슬러리 판상엽 시트를 포함하는 흡연 물품에 대하여 실시예 및 도면을 참조하여 구체적으로 설명하도록 한다. 그러나, 본 발명이 이러한 실시예 및 도면에 제한되는 것은 아니다.
본 발명은, 흡연물질부와 상기 흡연물질부보다 하류에 위치된 필터부를 구비한 흡연물품으로서, 탄산칼슘을 10 내지 60 중량%로 포함하는 슬러리 판상엽 시트를 포함하는 흡연물품을 제공한다.
본 발명에서 "흡연 물품" (smoking article)이란, 담배, 담배 파생물, 팽화처리 담배(expanded tobacco), 재생 담배(reconstituted tobacco), 또는 담배 대용물에 기반하느냐에 상관없이 흡연 가능한 임의의 제품 또는 흡연 체험을 제공할 수 있는 임의의 제품을 의미할 수 있다. 상기 흡연물품(100)은, 도 1을 참조하면, 필터 래퍼(110a)가 감싸진 필터부(110), 흡연물질 래퍼(120a)가 감싸진 흡연 물질부(120), 및 상기 필터부(110) 및 흡연물질부(120)를 결합시키는 팁페이퍼(130)를 포함하는, 연소식 흡연물품일 수 있다.
본 발명의 일 실시예에 따라, 상기 탄산칼슘은, 0.5 μm 이하의 직경을 갖는 것일 수 있다. 본 발명에서 사용되는 탄산칼슘은 중질 탄산칼슘으로서, 표면적이 25 m2/g 이하일 수 있다. 본 발명에서는, 상기 범위를 만족하는 조건의 탄산칼슘을 사용하여, 연기성분이 저감되었으며 이와 동시에 끽미강도, 연기량, 목넘김, 조화미, 이취미, 뒷맛 등이 모두 우수한 흡연 물품을 제조하였다.
본 발명의 슬러리 판상엽 시트는, 통상의 판상엽 시트와 같이, 담배 각초, 담배 부산물 등을 포함하는 것이다. 상기 담배 부산물은 궐련의 제조 과정 중에 발생하는 부산물을 의미하는 것으로, 예시로서 상기 부산물은 담배 잎 줄기, 담배 가루 등을 포함하는 것일 수 있다. 상기 담배는 황색종, 버어리종 및 오리엔트종으로 이루어지는 군으로부터 선택되는 1종 이상의 것일 수 있다.
본 발명의 일 실시예에 따라, 상기 슬러리 판상엽 시트는, 바인더를 더 포함할 수 있다. 상기 바인더로 인해 담배 부산물과 탄산칼슘이 강력하게 접착될 수 있으며, 바람직하게는 시트에 5 내지 20 중량%로 포함될 수 있다. 특히, 상기 바인더로는 메틸셀룰로오스가 사용되는 것이 바람직하다. 상기 메틸셀룰로오스는 특히 탄산칼슘 및 담배부산물과 혼합되어 콜로이드를 형성함으로써, 포름알데하이드와 같은 연기 성분을 감소시킬 수 있다.
본 발명의 다른 실시예에 따라, 상기 흡연물질부에는 슬러리 판상엽 시트에 더하여, 궐련 각초를 더 포함할 수 있다. 상기 흡연 물질부는, 슬러리 판상엽 시트 및 궐련 각초를 25-75 : 75-25 의 혼합 중량비로 포함할 수 있으며, 바람직하게는 본 발명에서 연기성분 저감 효과가 우수한 것으로 확인한 45-55 : 55-45의 범위, 보다 바람직하게는 50:50의 중량비로 혼합될 수 있다. 상기 궐련 각초는, 황색종, 버어리종 및 오리엔트종으로 이루어지는 군으로부터 선택되는 1종 이상의 담배를 썰어 제조한 것일 수 있다.
본 발명의 일 실시예에 따라, 상기 흡연물질부는 보습제를 포함하지 않는 것을 특징으로 한다. 이에 더하여 상기 흡연물질부는, 액상의 에어로졸 발생 물질도 포함하지 않는다. 상기 흡연물품은 상술한 것과 같이, “연소식” 흡연 물품으로서, 전기 가열식 궐련이 아닌 불을 붙여 사용되는 전통형 궐련에 해당하는 것이다.
상기 흡연 물질부에는 보습제와 에어로졸 발생 물질을 포함하지는 않으나, 풍미제를 더 추가할 수는 있다. 상기 풍미제는 감초, 자당, 과당 시럽, 이소감미제(isosweet), 코코아, 라벤더, 시나몬, 카르다몸, 셀러리, 호로파, 카스카릴라, 백단, 베르가못, 제라늄, 벌꿀 에센스, 장미 오일, 바닐라, 레몬 오일, 오렌지 오일, 민트 오일, 계피, 케러웨이, 코냑, 자스민, 카모마일, 멘톨, 계피, 일랑일랑, 샐비어, 스피어민트, 생강, 고수 또는 커피 등을 포함할 수 있다.
본 발명의 또다른 실시예에 따른 흡연물품에서 상기 슬러리 판상엽 시트에 포함되는 탄산칼슘은, 바람직하게는 55 내지 65 중량%, 보다 바람직하게는 60 중량%로 포함될 수 있다. 상기 함량은 본 발명의 실시예에서 연기성분을 감소하는 것으로 확인된 범위이다.
본 발명에서 상기 흡연 물품은, 연소 시 특정 연기 성분이 감소한 것을 특징으로 한다. 상기 특정 연기 성분은, 니코틴, 타르, 일산화탄소(CO), 포름알데하이드 (Formaldehyde), 아세트알데하이드 (Acetaldehyde), 아크롤레인 (Acrolein), 1,3-부타디엔 (1,3-Butadiene), 벤젠 (Benzene) 및 벤조피렌 (Benzopyrene)으로 이루어지는 군으로부터 선택되는 1종 이상일 수 있다.
본 발명에서, 상기 흡연물질부(120)는, 흡연 물질 래퍼(120a)에 의해 감싸질 수 있다. 예를 들어, 종이 또는 셀룰로오스 권지로 형성될 수 있다. 다만, 본 개시가 이에 반드시 제한되는 것은 아니다.
본 발명에서, 상기 흡연 물품은 필터부(110)를 포함한다. 예를 들어, 상기 필터부는 모노 필터, 이중 필터 또는 삼중 필터일 수 있다. 또한, 상기 필터부는 다공성 매트릭스 구조, 튜브 구조 및 지관 구조(paper tube) 중 적어도 하나 이상의 필터를 포함할 수 있다. 상기 필터는 고분자, 종이, 셀룰로오스 아세테이트, 활성탄 및 탄소 중 적어도 하나를 포함하는 섬유상, 필라멘트상 또는 이 둘을 포함하는 필터 토우를 포함하는 것일 수 있다. 그러나, 이에 한정되는 것은 아니다.
상기 필터 물질은 탄소를 포함하는 흡착제, 활성탄 등과 같이 당해 기술 분야에서 널리 알려진 적어도 하나의 필터 물질을 더 포함할 수 있다.
필터부의 내부에는 캡슐(미도시)이 포함될 수 있다. 캡슐은 향료를 포함하는 내용액을 피막으로 감싼 구조일 수 있고, 예를 들면, 캡슐은 구형 또는 원통형의 형상을 가질 수 있다. 캡슐의 피막을 형성하는 재료는 천연소재, 전분 및/또는 겔화제일 수 있다. 예를 들어, 천연소재의 피막의 경우 한천, 펙틴, 소디움 알지네이트 및 글리세린 등으로 조성될 수 있다. 겔화제로서는 젤란 검이나 젤라틴이 사용될 수 있다. 또한, 캡슐의 피막을 형성하는 재료로서 겔화 조제가 더 이용될 수도 있다. 겔화 조제로서는, 예를 들면 염화 칼슘이 사용될 수 있다. 또한, 캡슐의 피막을 형성하는 재료로서 가소제가 더 이용될 수도 있다. 여기에서, 가소제로서는 글리세린 및/또는 소르비톨이 이용될 수 있다. 또한, 캡슐의 피막을 형성하는 재료로서 착색료가 더 이용될 수도 있다. 캡슐의 내용액에 포함되는 향료의 용매로서는, 예를 들면, 중쇄지방산 트리글리세라이드(medium chain fatty acid triglyceride; MCTG)가 이용될 수 있다. 또한, 내용액은 색소, 유화제(乳化劑), 증점제(增粘劑) 등의 다른 첨가제를 함유할 수도 있으나, 이에 제한되는 것은 아니다. 아울러 캡슐의 내용액에는 멘톨, 식물의 정유(精油) 등의 향료가 포함될 수 있으나, 이에 제한되지 않는다.
또한, 상기 필터부는, 필터를 감싸는 팁페이퍼를 더 포함할 수 있으며, 상기 팁페이퍼는 예로서 종이 소재일 수 있으나, 이에 제한되는 것은 아니다. 상기 팁페이퍼는, 천공이 형성되어 있지 않을 수 있다. 본 발명의 흡연 물품은, 팁페이퍼에 천공이 형성되지 않았음에도, 우수한 연기 성분 저감 효과를 가지고 있는 것을 특징으로 하는 것이다.
이하에서, 첨부된 도면을 참조하여 실시예들을 상세하게 설명한다. 그러나, 실시예들에는 다양한 변경이 가해질 수 있어서 특허출원의 권리 범위가 이러한 실시예들에 의해 제한되거나 한정되는 것은 아니다. 실시예들에 대한 모든 변경, 균등물 내지 대체물이 권리 범위에 포함되는 것으로 이해되어야 한다.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 실시예가 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.
[실시예]
<슬러리 판상엽 제조>
탄산칼슘을 60%로 포함하는 슬러리를, 하기 표 1의 조성에 따라 제조하였다. 상기 성분들을 혼합한 후, 물을 첨가하여 판상엽 슬러리를 제조하였다.
구 분 예비실시예 1 예비실시예 2 예비실시예 3 예비실시예 4 예비실시예 5 예비실시예 6
탄산칼슘(%) 60 60 60 60 20 40
Methyl Cellulose (%) 5 5 0 0 5 5
구아검(%) 5 5 5 5 5 5
담배 부산물(%) 30 30 35 35 70 50
합계(%) 100 100 100 100 100 100
물 (적의) 320 320 320 320 320 320
분쇄정도 조쇄 미쇄 조쇄 미쇄 미쇄 미쇄
상기 슬러리를 사출한 후 건조하여 판상엽을 제조하였고, 그 결과 예비실시예 2의 판상엽이 부스러지는 현상 없이 양호한 형태를 보였으며, 실제 흡연시 담배맛에서도 우수한 효과를 보여, 이후 실험에서는 예비실시예 2의 판상엽 슬러리를 사용하였다.
<수궐련 제조>
상기 실시예에서 제조한 슬러리 판상엽과 일반 궐련 각초를, 표 2에 나타낸 무게비로 혼합해 무천공 수궐련을 제조하였다 (n=3). 슬러리 판상엽 특성상, 부풀성이 일반 각초 대비 낮으므로, 충진량(실제 양목)은 일반 각초에 비해 다소 많았다. 제조된 수궐련에 대하여 흡인저항 및 경도를 측정하여, 표 2에 나타내었다.
구분 RB+SR
(wt.)		 실제 양목 (mg) UPD*
(mmH2O)		 경도
(%)
비교예 1 RB 100% 552±5 127±6 65±1
실시예 1 RB 75% + SR 25% 647±10 119±5 66±1
실시예 2 RB 50% + SR 50% 759±16 116±3 66±1
실시예 3 SR 100% 1136±16 110±3 69±2
그 결과, 담배 각초만을 사용한 수궐련과 비교하여 본 발명의 슬러리 판상엽을 포함하는 수궐련은 경도 및 흡인저항에서 대등 수준인 것이 확인되었다.
<연기 성분 확인>
제조된 수궐련에 대하여 연소시켜 발생되는 연기성분을 분석하고, 그 결과를 도 2 및 도 3과, 하기 표 3에 나타내었다. 도 3과 표 3은, 양목 당 연기 성분 발생량으로 환산한 값을 나타낸 것이고, 도 2는 궐련당 연기성분 감소량을 나타낸 것이다.
연기성분(/mg 양목) 비교예 1 실시예 1 실시예 2 실시예 3
TPM 100%a 90%a 69%b 30%c
TAR 100%a 96%a 71%b 30%c
Nic 100%a 88%ab 67%b 28%c
CO 100%a 90%ab 77%b 38%c
Water 100%a 82%a 64%b 30%c
Formaldehyde 100%a 90%ab 83%b 82%b
Acetaldehyde 100%a 83%b 65%c 32%d
Acetone 100%a 82%b 63%c 28%d
Acrolein 100%a 83%b 63%c 31%d
Propionaldehyde 100%a 80%b 63%c 34%d
Crotaonaldehyde 100%a 84%b 65%c 35%d
MEK 100%a 86%b 66%c 33%d
Butyraldehyde 100%a 82%b 62%c 27%d
1,3-Butadiene 100%a 76%ab 53%b 15%c
Isoprene 100%a 83%a 50%b 9%c
Acrylonitrile 100%a 84%a 62%b 16%c
Benzene 100%a 88%b 64%c 27%d
Toluene 100%a 82%ab 64%b 22%c
Benzopyrene 100%a 89%a 72%b 41%c
알파벳이 동일할 경우, 통계적으로 유의미한 차이가 없는 것을 의미함(p>0.05)
상기 결과로부터, 슬러리 판상엽을 포함하는 실시예의 수궐련에서, CO, Formaldehyde, Acetaldehyde, Acrolein, 1,3-Butadiene, Benzene, Benzopyrene 함량이 모두 일반 각초를 포함하는 비교예 1과 비교하여 감소하였음을 알 수 있고, 특히 슬러리 판상엽의 비율이 높아질수록 연기성분 감소량이 증가하는 것을 알 수 있다.
또한 양목 함량을 고려하지 않고, 궐련 하나의 흡연 시 발생하는 기체 성분을 측정하여 하기 표 4(일반성분) 및 표 5(특수성분)에 나타내었다.
구분 TPM
(mg) 		Tar
(mg/cig) 		Nicotine
(mg/cig) 		CO
(mg/cig) 		Puff No.
(count)
비교예 1 33.08 19.8 1.84 23.5 8.10
실시예 1 35.11 22.3 1.91 24.8 8.58
실시예 2 31.23 19.5 1.68 24.9 8.08
실시예 3 20.17 12.1 1.06 18.4 8.87
구분 Carbonyls
(ug/cig) 		VOCs
(ug/cig) 		B(a)P
(ng/cig)
비교예 1 2081.1 1076.1 16.5
실시예 1 2028.0 1044.3 17.3
실시예 2 1857.6 786.4 16.4
실시예 3 1421.8 281.3 13.8
실시예 1 내지 3의 궐련은 슬러리의 배합에 따라 양목량이 높아지긴 했으나, 모든 Puff는 비교예 1과 유사하게 8.05~8.9 수준으로 확인되었다. 특히 슬러리의 함량이 증가할수록 일반성분 및 특수 성분에서 모두 연기 성분이 감소하는 것이 확인되어, 탄산칼슘의 함량이 높아질수록 연기성분이 감소하는 것을 확인할 수 있었다.
<바인더의 종류에 따른 효과 확인>
상기 예비실시예 2의 슬러리 판상엽과 상기 예비실시예 3의 슬러리 판상엽을 이용하여 궐련을 제조한 후, 그 연기성분을 측정하여 그 결과를 도 4에 나타내었다.
도 4에 나타낸 것과 같이, 구아검을 사용하는 것보다 바인더로 메틸셀룰로오스를 사용할 때, 포름알데히드의 함량이 저감되는 것이 확인되었다.
<관능평가>
상기 비교예 1 및 실시예 2, 3에 대하여, 끽미강도, 연기량, 목넘김, 조화미, 이취미 및 뒷맛깔끔함에 대한 관능평가를 실시하였고 그 결과를 도 5와 표 6에 나타냈다. 관능평가는 제조 후 2주가 경과된 실시예별 궐련들을 이용하여 25명의 평가 패널원을 대상으로 실시하였으며, 총 9점 만점을 기준으로 하였다.
평가 시료 끽미강도 연기량 목넘김 조화미 이취미 뒷맛깔끔함
비교예 1 4.5 5.5 4.1 4.7 3.5 4.3
실시예 2 4.4 5.6 4.6 4.9 4.0 4.4
실시예 3 3.6 4.9 4.6 4.2 3.8 4.8
상기 결과로부터, 본 발명의 흡연제품은, 연기 성분이 감소하였음에도 불구하고, 일반 각초를 포함하는 궐련과 비교하여 유사 수준의 관능 평가 결과를 가지는 것이 확인되었다.
이상과 같이 실시예들이 비록 한정된 실시예와 도면에 의해 설명되었으나, 해당 기술분야에서 통상의 지식을 가진 자라면 상기의 기재로부터 다양한 수정 및 변형이 가능하다. 예를 들어, 설명된 기술들이 설명된 방법과 다른 순서로 수행되거나, 및/또는 설명된 구성요소들이 설명된 방법과 다른 형태로 결합 또는 조합되거나, 다른 구성요소 또는 균등물에 의하여 대치되거나 치환되더라도 적절한 결과가 달성될 수 있다. 그러므로, 다른 구현들, 다른 실시예들 및 특허청구범위와 균등한 것들도 후술하는 특허청구범위의 범위에 속한다.
부호의 설명
100 : 흡연물품 110 : 필터부 110a : 필터 래퍼
120 : 흡연물질부 120a : 흡연물질 래퍼
130 : 팁페이퍼

Claims (8)

  1. 흡연물질부와 상기 흡연물질부보다 하류에 위치된 필터부를 구비한 흡연물품으로서,
    상기 흡연물질부는 슬러리 판상엽 시트를 포함하고,
    상기 슬러리 판상엽 시트는 탄산칼슘을 10 내지 60 중량%로 포함하는 것인, 흡연 물품.
  2. 제1항에 있어서,
    상기 탄산칼슘은, 0.5 μm 이하의 직경을 갖는 것인, 흡연 물품.
  3. 제1항에 있어서,
    상기 슬러리 판상엽 시트는, 바인더를 더 포함하는 것인, 흡연 물품.
  4. 제3항에 있어서,
    상기 바인더는 메틸셀룰로오스를 포함하는 것인, 흡연 물품.
  5. 제1항에 있어서,
    상기 흡연 물질부는, 궐련 각초를 더 포함하는 것인, 흡연 물품.
  6. 제5항에 있어서,
    상기 흡연 물질부는, 슬러리 판상엽 시트 및 궐련 각초를 25-75 : 75-25 의 혼합 중량비로 포함하는 것인, 흡연 물품.
  7. 제1항에 있어서,
    상기 흡연 물질부는, 보습제를 포함하지 않는 것인, 흡연물품.
  8. 제1항에 있어서,
    상기 흡연 물품은, 연소식 궐련형 흡연 물품인 것인, 흡연 물품.
PCT/KR2022/019988 2021-12-31 2022-12-09 탄산칼슘을 포함하는 슬러리 판상엽 시트를 포함하는 흡연 물품 WO2023128384A1 (ko)