WO2023048206A1 - Composition de revêtement photoluminescente de type solvant organique et procédé de formation de film de revêtement multicouche - Google Patents

Composition de revêtement photoluminescente de type solvant organique et procédé de formation de film de revêtement multicouche Download PDF

Info

Publication number
WO2023048206A1
WO2023048206A1 PCT/JP2022/035305 JP2022035305W WO2023048206A1 WO 2023048206 A1 WO2023048206 A1 WO 2023048206A1 JP 2022035305 W JP2022035305 W JP 2022035305W WO 2023048206 A1 WO2023048206 A1 WO 2023048206A1
Authority
WO
WIPO (PCT)
Prior art keywords
organic solvent
mass
coating film
coating composition
resin
Prior art date
Application number
PCT/JP2022/035305
Other languages
English (en)
Japanese (ja)
Inventor
健吾 前田
龍介 村本
Original Assignee
関西ペイント株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 関西ペイント株式会社 filed Critical 関西ペイント株式会社
Publication of WO2023048206A1 publication Critical patent/WO2023048206A1/fr

Abstract

La présente invention vise à fournir une composition de revêtement photoluminescente de type solvant organique qui présente une excellente stabilité de précipitation et une excellente aptitude à la circulation et à partir de laquelle un film de revêtement qui présente un excellent brillant de ton métallique ou nacré peut être formé. La présente invention concerne une composition de revêtement photoluminescente de type solvant organique qui contient une résine liante (A), un modificateur de viscosité à base de cellulose (B), un modificateur de viscosité à base de polyurée (C), et un pigment photoluminescent (D), et qui a un pourcentage de teneur en matières solides de 1 à 20 % en masse. La quantité contenue du modificateur de viscosité à base de polyurée (C) se situe dans une plage de 0,1 à 3 parties en masse pour 100 parties en masse de la teneur en matières solides de la composition de revêtement photoluminescente de type solvant organique.
PCT/JP2022/035305 2021-09-23 2022-09-22 Composition de revêtement photoluminescente de type solvant organique et procédé de formation de film de revêtement multicouche WO2023048206A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021-154950 2021-09-23
JP2021154950 2021-09-23

Publications (1)

Publication Number Publication Date
WO2023048206A1 true WO2023048206A1 (fr) 2023-03-30

Family

ID=85720778

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/035305 WO2023048206A1 (fr) 2021-09-23 2022-09-22 Composition de revêtement photoluminescente de type solvant organique et procédé de formation de film de revêtement multicouche

Country Status (2)

Country Link
TW (1) TW202323456A (fr)
WO (1) WO2023048206A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013040293A (ja) * 2011-08-18 2013-02-28 Kansai Paint Co Ltd 多成分系のベースコート塗料、調色方法及び補修塗装方法
KR20130080636A (ko) * 2012-01-05 2013-07-15 아크조노벨코팅스인터내셔널비.브이. 패턴 형성 조성물 및 이를 이용한 패턴 형성 방법
CN103540177A (zh) * 2013-10-09 2014-01-29 丹阳市永生涂料有限公司 一种环氧云铁灰底漆
JP2015510022A (ja) * 2012-03-14 2015-04-02 ビーエーエスエフ コーティングス ゲゼルシャフト ミット ベシュレンクテル ハフツングＢＡＳＦ Ｃｏａｔｉｎｇｓ ＧｍｂＨ 金属顔料を含む溶剤型顔料ペーストおよび効果付与する溶剤型被覆剤を製造するための前記溶剤型顔料ペーストの使用
CN111303731A (zh) * 2020-03-14 2020-06-19 上海立邦长润发涂料有限公司 一种用于静电喷涂的uv白色底漆及其制备方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013040293A (ja) * 2011-08-18 2013-02-28 Kansai Paint Co Ltd 多成分系のベースコート塗料、調色方法及び補修塗装方法
KR20130080636A (ko) * 2012-01-05 2013-07-15 아크조노벨코팅스인터내셔널비.브이. 패턴 형성 조성물 및 이를 이용한 패턴 형성 방법
JP2015510022A (ja) * 2012-03-14 2015-04-02 ビーエーエスエフ コーティングス ゲゼルシャフト ミット ベシュレンクテル ハフツングＢＡＳＦ Ｃｏａｔｉｎｇｓ ＧｍｂＨ 金属顔料を含む溶剤型顔料ペーストおよび効果付与する溶剤型被覆剤を製造するための前記溶剤型顔料ペーストの使用
CN103540177A (zh) * 2013-10-09 2014-01-29 丹阳市永生涂料有限公司 一种环氧云铁灰底漆
CN111303731A (zh) * 2020-03-14 2020-06-19 上海立邦长润发涂料有限公司 一种用于静电喷涂的uv白色底漆及其制备方法

Also Published As

Publication number Publication date
TW202323456A (zh) 2023-06-16

Similar Documents

Publication Publication Date Title
JP6921822B2 (ja) 光輝性顔料分散体
JP6979558B2 (ja) 複層塗膜及び複層塗膜形成方法
EP3330009B1 (fr) Procédé de formation d'un film de revêtement multicouche
JP7164785B2 (ja) 複層塗膜形成方法
JP7019593B2 (ja) 複層塗膜形成方法
US11285509B2 (en) Method for forming multilayer coating film
JP7146815B2 (ja) 複層塗膜形成方法
JP7297667B2 (ja) 複層塗膜形成方法
JP7286632B2 (ja) 光輝性顔料分散体及び複層塗膜形成方法
JP7305545B2 (ja) 複層塗膜形成方法
WO2020044672A1 (fr) Procédé de formation d'un film de revêtement multicouche
CA3081165C (fr) Procede de formation de film de revetement multicouche
WO2023048206A1 (fr) Composition de revêtement photoluminescente de type solvant organique et procédé de formation de film de revêtement multicouche
JP7066926B1 (ja) 光輝性顔料分散体及び複層塗膜形成方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22872957

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2023549734

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE