WO2023031930A1 - Marquage xrf de caoutchouc naturel - Google Patents

Marquage xrf de caoutchouc naturel Download PDF

Info

Publication number
WO2023031930A1
WO2023031930A1 PCT/IL2022/050953 IL2022050953W WO2023031930A1 WO 2023031930 A1 WO2023031930 A1 WO 2023031930A1 IL 2022050953 W IL2022050953 W IL 2022050953W WO 2023031930 A1 WO2023031930 A1 WO 2023031930A1
Authority
WO
WIPO (PCT)
Prior art keywords
latex
marker
rubber
xrf
coagulated
Prior art date
Application number
PCT/IL2022/050953
Other languages
English (en)
Inventor
Haggai ALON
Yekaterina ZELDICH
Tehila NACHUM
Michal FIRSTENBERG
Chen NACHMIAS
Nataly TAL
Michal BURCK ZALTZMAN
Original Assignee
Security Matters Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Security Matters Ltd. filed Critical Security Matters Ltd.
Publication of WO2023031930A1 publication Critical patent/WO2023031930A1/fr

Abstract

L'invention concerne un procédé d'identification d'un historique de production et/ou commercial de latex ou de caoutchouc ou de produits fabriqués à partir de ceux-ci.
PCT/IL2022/050953 2021-09-03 2022-08-31 Marquage xrf de caoutchouc naturel WO2023031930A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US202163260879P 2021-09-03 2021-09-03
US63/260,879 2021-09-03

Publications (1)

Publication Number Publication Date
WO2023031930A1 true WO2023031930A1 (fr) 2023-03-09

Family

ID=85412031

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IL2022/050953 WO2023031930A1 (fr) 2021-09-03 2022-08-31 Marquage xrf de caoutchouc naturel

Country Status (1)

Country Link
WO (1) WO2023031930A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0807603B1 (fr) * 1996-05-16 2003-12-17 Sumitomo Chemical Company Limited Hydroxyde d'aluminium, procédé de sa production et son utilisation
EP2905125A1 (fr) * 2014-02-10 2015-08-12 4JET Technologies GmbH Codage numérique d'articles en caoutchouc
WO2021009757A1 (fr) * 2019-07-15 2021-01-21 Security Matters Ltd. Polymères composites traçables et leurs procédés de préparation pour fournir une transparence dans des chaînes de valeur de production
US10969351B2 (en) * 2015-04-02 2021-04-06 Soreq Nuclear Research Center System and method for reading x-ray-fluorescence marking

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0807603B1 (fr) * 1996-05-16 2003-12-17 Sumitomo Chemical Company Limited Hydroxyde d'aluminium, procédé de sa production et son utilisation
EP2905125A1 (fr) * 2014-02-10 2015-08-12 4JET Technologies GmbH Codage numérique d'articles en caoutchouc
US10969351B2 (en) * 2015-04-02 2021-04-06 Soreq Nuclear Research Center System and method for reading x-ray-fluorescence marking
WO2021009757A1 (fr) * 2019-07-15 2021-01-21 Security Matters Ltd. Polymères composites traçables et leurs procédés de préparation pour fournir une transparence dans des chaînes de valeur de production

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
GOLUB MORTON A, HELLER JORGE: "THE REACTION OF POLYISOPRENE WITH TITANIUM TETRACHLORIDE", CANADIAN JOURNAL OF CHEMISTRY, vol. 41, no. 4, 1 April 1963 (1963-04-01), pages 937 - 953, XP093042255, DOI: 10.1139/v63-133 *
HSIUNG KAN-HSI, KANAMATSU TOSHIYA, IKEHARA KEN, USAMI KAZUKO, HORNG CHORNG-SHERN, OHKOUCHI NAOHIKO, OGAWA NANAKO O., SAITO SANEATS: "X-ray fluorescence core scanning, magnetic signatures, and organic geochemistry analyses of Ryukyu Trench sediments: turbidites and hemipelagites", PROGRESS IN EARTH AND PLANETARY SCIENCE, vol. 8, no. 1, XP093042265, DOI: 10.1186/s40645-020-00396-2 *
WAN LE, DENG CONG, ZHAO ZE-YONG, CHEN HONG, WANG YU-ZHONG: "Flame Retardation of Natural Rubber: Strategy and Recent Progress", POLYMERS, vol. 12, no. 2, pages 429, XP093042260, DOI: 10.3390/polym12020429 *

Similar Documents

Publication Publication Date Title
Knowles What we could do now: molecular pathology of bladder cancer
EP2383569A1 (fr) Appareil d'analyse d'image, procédé d'analyse d'image, programme d'analyse d'image et support d'enregistrement
Yu et al. Role of Diisocyanate Structure on Self‐Healing and Anticorrosion Properties of Waterborne Polyurethane Coatings
Shi et al. Novel wet-white tanning approach based on laponite clay nanoparticles for reduced formaldehyde release and improved physical performances
WO2023031930A1 (fr) Marquage xrf de caoutchouc naturel
Sendrea et al. The effect of gamma irradiation on shrinkage activity of collagen in vegetable tanned leather
CN108192236A (zh) 一种一次性可光降解的pvc手套及其制备方法
Hong et al. Approach to improve edible bird nest quality & establishing better bird nest cleaning process facility through best value approach
Diryak et al. Behavior of In Situ Cross‐Linked Hydrogels with Rapid Gelation Kinetics on Contact with Physiological Fluids
Lu et al. Pollutant-accelerated aging behaviors of fluorocarbon coating in tropical marine atmosphere
Kłosowski et al. Electron microscopy reveals structural and chemical changes at the nanometer scale in the osteogenesis imperfecta murine pathology
Magami et al. Gelation via cationic chelation/crosslinking of acrylic‐acid‐based polymers
CN106834461A (zh) 生物制品中动物源性成分的高通量二代测序的通用型检测方法
JP2024518311A (ja) 工業的に重要な原材料を管理するためのシステムおよび方法
Siimon et al. Increasing mechanical strength of electrospun gelatin nanofibers by the addition of aluminum potassium sulfate
Lv et al. Quantitative evaluation of fillers dispersion state in CaCO3/polypropylene composites through visualization and fractal analysis
Carsote et al. Effect of temperature and relative humidity on vegetable tanned leather studied by thermal analysis
WO2022224240A1 (fr) Système et procédé pour la gestion de matières premières d'importance industrielle
Buytaert et al. Study of Cu–Zn–Co ternary alloy-coated steel cord in cobalt-free skim compound
Cazzagon et al. Identification of the safe (r) by design alternatives for nanosilver-enabled wound dressings
US20200150619A1 (en) Manufacturing statistical process control in the presence of multiple batch effects
Beans et al. Sodium monometaphosphate and its acid hydration
Pomar-Portillo et al. Silver nanoparticles and nanowires release from cotton textiles during household washings
US20140123739A1 (en) Method for testing particulate materials
Titov et al. Cytological and molecular diagnosis of Hürthle cell thyroid tumors: Analysis of three cases

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22863799

Country of ref document: EP

Kind code of ref document: A1