WO2022258648A1 - A process for the preparation of low-density abs composites - Google Patents
A process for the preparation of low-density abs composites Download PDFInfo
- Publication number
- WO2022258648A1 WO2022258648A1 PCT/EP2022/065468 EP2022065468W WO2022258648A1 WO 2022258648 A1 WO2022258648 A1 WO 2022258648A1 EP 2022065468 W EP2022065468 W EP 2022065468W WO 2022258648 A1 WO2022258648 A1 WO 2022258648A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- styrene
- process according
- acrylonitrile
- copolymer
- Prior art date
Abstract
Description
Claims