WO2022197358A1 - Systèmes et procédés de traitement d'un substrat - Google Patents

Systèmes et procédés de traitement d'un substrat Download PDF

Info

Publication number
WO2022197358A1
WO2022197358A1 PCT/US2022/012961 US2022012961W WO2022197358A1 WO 2022197358 A1 WO2022197358 A1 WO 2022197358A1 US 2022012961 W US2022012961 W US 2022012961W WO 2022197358 A1 WO2022197358 A1 WO 2022197358A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
ppm
metal
substrate
total weight
Prior art date
Application number
PCT/US2022/012961
Other languages
English (en)
Inventor
Kuldeep Kumar
Elizabeth Stephenie BROWN-TSENG
Rachel Dory HARRIS
Mark William Mcmillen
Original Assignee
Ppg Industries Ohio, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ppg Industries Ohio, Inc. filed Critical Ppg Industries Ohio, Inc.
Priority to CN202280022497.XA priority Critical patent/CN117043390A/zh
Priority to US18/551,019 priority patent/US20240167164A1/en
Priority to EP22703500.3A priority patent/EP4308747A1/fr
Publication of WO2022197358A1 publication Critical patent/WO2022197358A1/fr

Abstract

Est divulguée ici une composition comprenant un premier métal de la série des lanthanides, la composition ayant un pH inférieur à 2,0 et étant sensiblement exempte de peroxyde. Est également divulguée ici une composition comprenant un premier métal de la série des lanthanides et au moins un élément parmi un second métal de la série des lanthanides, du cuivre, un composé phosphate inorganique, un composé organophosphate et un composé organophosphonate; la composition est sensiblement exempte de peroxyde. Sont également divulgués ici des systèmes et des procédés de traitement d'un substrat métallique. Sont également divulgués des substrats traités au moyen des systèmes et des procédés.
PCT/US2022/012961 2021-03-19 2022-01-19 Systèmes et procédés de traitement d'un substrat WO2022197358A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN202280022497.XA CN117043390A (zh) 2021-03-19 2022-01-19 用于处理基材的体系和方法
US18/551,019 US20240167164A1 (en) 2021-03-19 2022-01-19 Systems and methods for treating a substrate
EP22703500.3A EP4308747A1 (fr) 2021-03-19 2022-01-19 Systèmes et procédés de traitement d'un substrat

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US202163163353P 2021-03-19 2021-03-19
US63/163,353 2021-03-19

Publications (1)

Publication Number Publication Date
WO2022197358A1 true WO2022197358A1 (fr) 2022-09-22

Family

ID=80445718

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2022/012961 WO2022197358A1 (fr) 2021-03-19 2022-01-19 Systèmes et procédés de traitement d'un substrat

Country Status (4)

Country Link
US (1) US20240167164A1 (fr)
EP (1) EP4308747A1 (fr)
CN (1) CN117043390A (fr)
WO (1) WO2022197358A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0797691A1 (fr) * 1994-10-07 1997-10-01 McMASTER UNIVERSITY Procede de traitement a base d'elements terres rares pour ameliorer la resistance a la corrosion des metaux et alliages
WO2003093532A2 (fr) * 2002-04-29 2003-11-13 Ppg Industries Ohio, Inc. Revetements de conversion comprenant des complexes alcalino-terreux de fluorure metallique
US6797387B2 (en) 2000-09-21 2004-09-28 Ppg Industries Ohio Inc. Modified aminoplast crosslinkers and powder coating compositions containing such crosslinkers
US7432333B2 (en) 2002-05-31 2008-10-07 Ppg Industries Ohio, Inc. Powder coating of amino-urea or urethane catalyst and epoxy/hydroxy and/or siloxane resin
US20090045071A1 (en) 2007-08-15 2009-02-19 Ppg Industries Ohio, Inc. Electrodeposition coatings for use over aluminum substrates
US20090065101A1 (en) * 2004-12-01 2009-03-12 Deft, Inc. Corrosion Resistant Conversion Coatings

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0797691A1 (fr) * 1994-10-07 1997-10-01 McMASTER UNIVERSITY Procede de traitement a base d'elements terres rares pour ameliorer la resistance a la corrosion des metaux et alliages
US6797387B2 (en) 2000-09-21 2004-09-28 Ppg Industries Ohio Inc. Modified aminoplast crosslinkers and powder coating compositions containing such crosslinkers
WO2003093532A2 (fr) * 2002-04-29 2003-11-13 Ppg Industries Ohio, Inc. Revetements de conversion comprenant des complexes alcalino-terreux de fluorure metallique
US7432333B2 (en) 2002-05-31 2008-10-07 Ppg Industries Ohio, Inc. Powder coating of amino-urea or urethane catalyst and epoxy/hydroxy and/or siloxane resin
US7470752B2 (en) 2002-05-31 2008-12-30 Ppg Industries Ohio, Inc. Powder coating of amino-urea or urethane catalyst and epoxy and/or siloxane resin
US20090065101A1 (en) * 2004-12-01 2009-03-12 Deft, Inc. Corrosion Resistant Conversion Coatings
US20090045071A1 (en) 2007-08-15 2009-02-19 Ppg Industries Ohio, Inc. Electrodeposition coatings for use over aluminum substrates

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
"Handbook of Chemistry and Physics", 1983
LIGHTCAPPUCCINO: "Determination of fluoride in toothpaste using an ion-selective electrode", J. CHEM. EDUC., vol. 52, no. 4, April 1975 (1975-04-01), pages 247 - 250

Also Published As

Publication number Publication date
CN117043390A (zh) 2023-11-10
EP4308747A1 (fr) 2024-01-24
US20240167164A1 (en) 2024-05-23

Similar Documents

Publication Publication Date Title
KR102255735B1 (ko) 박막 전처리 및 밀봉 조성물을 통한 금속 기판 처리를 위한 시스템 및 방법
CA3032691C (fr) Composition de scellement
US10113070B2 (en) Pretreatment compositions and methods of treating a substrate
US10435806B2 (en) Methods for electrolytically depositing pretreatment compositions
US20240050983A1 (en) Systems and methods for treating a substrate
US20240076781A1 (en) Systems and methods for treating a metal substrate
US20240167164A1 (en) Systems and methods for treating a substrate
WO2023132989A1 (fr) Compositions, systèmes et procédés de traitement d'un substrat
WO2023015060A1 (fr) Systèmes et procédé de traitement d'un substrat
KR102367049B1 (ko) 전처리 조성물
WO2022197357A1 (fr) Systèmes et procédés de traitement d'un substrat
WO2023102284A1 (fr) Systèmes et procédés de traitement d'un substrat
KR20210126140A (ko) 밀봉 조성물

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22703500

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 18551019

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: 202280022497.X

Country of ref document: CN

WWE Wipo information: entry into national phase

Ref document number: 2022703500

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2022703500

Country of ref document: EP

Effective date: 20231019