WO2022190715A1 - Film piézoélectrique - Google Patents
Film piézoélectrique Download PDFInfo
- Publication number
- WO2022190715A1 WO2022190715A1 PCT/JP2022/003906 JP2022003906W WO2022190715A1 WO 2022190715 A1 WO2022190715 A1 WO 2022190715A1 JP 2022003906 W JP2022003906 W JP 2022003906W WO 2022190715 A1 WO2022190715 A1 WO 2022190715A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- piezoelectric
- layer
- conductive
- electrode layer
- piezoelectric film
- Prior art date
Abstract
L'invention concerne un film piézoélectrique hautement flexible capable d'assurer une conduction suffisante à travers une couche d'électrode. Le film piézoélectrique comprend une couche piézoélectrique, des couches d'électrodes formées respectivement sur les deux côtés de la couche piézoélectrique, et des couches protectrices, chacune stratifiée sur la surface de chaque couche d'électrode sur le côté opposé de la surface sur le côté de la couche piézoélectrique, dans lequel une couche protectrice a une partie de trou qui passe à travers une couche d'électrode à partir de la surface et a un élément conducteur flexible qui est disposé à l'intérieur de la partie de trou et comprend au moins un parmi un tissu conducteur, un tissu métallique et une mousse d'uréthane conductrice qui connecte électriquement la couche d'électrode et un conducteur.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2023505209A JPWO2022190715A1 (fr) | 2021-03-11 | 2022-02-02 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2021-039014 | 2021-03-11 | ||
JP2021039014 | 2021-03-11 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022190715A1 true WO2022190715A1 (fr) | 2022-09-15 |
Family
ID=83226702
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2022/003906 WO2022190715A1 (fr) | 2021-03-11 | 2022-02-02 | Film piézoélectrique |
Country Status (3)
Country | Link |
---|---|
JP (1) | JPWO2022190715A1 (fr) |
TW (1) | TW202236704A (fr) |
WO (1) | WO2022190715A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP4061008A4 (fr) * | 2019-11-12 | 2023-08-02 | FUJIFILM Corporation | Élément piézoélectrique |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2016015354A (ja) * | 2014-06-30 | 2016-01-28 | 富士フイルム株式会社 | 電気音響変換フィルムおよび電気音響変換フィルムの導通方法 |
WO2017073317A1 (fr) * | 2015-10-27 | 2017-05-04 | 株式会社村田製作所 | Dispositif piézoélectrique et procédé de fabrication de dispositif piézoélectrique |
WO2019093092A1 (fr) * | 2017-11-09 | 2019-05-16 | 株式会社村田製作所 | Composant piézoélectrique, capteur et actionneur |
-
2022
- 2022-02-02 WO PCT/JP2022/003906 patent/WO2022190715A1/fr active Application Filing
- 2022-02-02 JP JP2023505209A patent/JPWO2022190715A1/ja active Pending
- 2022-02-17 TW TW111105732A patent/TW202236704A/zh unknown
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2016015354A (ja) * | 2014-06-30 | 2016-01-28 | 富士フイルム株式会社 | 電気音響変換フィルムおよび電気音響変換フィルムの導通方法 |
WO2017073317A1 (fr) * | 2015-10-27 | 2017-05-04 | 株式会社村田製作所 | Dispositif piézoélectrique et procédé de fabrication de dispositif piézoélectrique |
WO2019093092A1 (fr) * | 2017-11-09 | 2019-05-16 | 株式会社村田製作所 | Composant piézoélectrique, capteur et actionneur |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP4061008A4 (fr) * | 2019-11-12 | 2023-08-02 | FUJIFILM Corporation | Élément piézoélectrique |
US11895463B2 (en) | 2019-11-12 | 2024-02-06 | Fujifilm Corporation | Piezoelectric element |
Also Published As
Publication number | Publication date |
---|---|
JPWO2022190715A1 (fr) | 2022-09-15 |
TW202236704A (zh) | 2022-09-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP7137690B2 (ja) | 圧電フィルム、積層圧電素子および電気音響変換器 | |
JP7265625B2 (ja) | 電気音響変換フィルムおよび電気音響変換器 | |
JP7166428B2 (ja) | 電気音響変換器 | |
WO2020261822A1 (fr) | Film piézoélectrique | |
TW202118314A (zh) | 壓電膜及壓電膜之製造方法 | |
TWI827851B (zh) | 高分子複合壓電體及壓電薄膜 | |
JP7137689B2 (ja) | 圧電フィルム、積層圧電素子および電気音響変換器 | |
JP7259075B2 (ja) | 圧電素子 | |
WO2021157288A1 (fr) | Film piézoélectrique | |
WO2022190715A1 (fr) | Film piézoélectrique | |
JP7177268B2 (ja) | 高分子複合圧電体および圧電フィルム | |
JP7288508B2 (ja) | 圧電フィルム | |
WO2022190807A1 (fr) | Film piézoélectrique et élément piézoélectrique stratifié | |
WO2023153280A1 (fr) | Film piézoélectrique et élément piézoélectrique stratifié | |
WO2023286544A1 (fr) | Film piézoélectrique | |
WO2023153126A1 (fr) | Élément piézoélectrique et transducteur électroacoustique | |
WO2023053750A1 (fr) | Élément piézoélectrique et convertisseur électro-acoustique | |
WO2024062863A1 (fr) | Film piézoélectrique | |
JP7286790B2 (ja) | 圧電素子 | |
WO2023188929A1 (fr) | Film piézoélectrique, élément piézoélectrique et transducteur électroacoustique | |
WO2023047958A1 (fr) | Élément piézoélectrique multicouche et transducteur électroacoustique | |
WO2022215524A1 (fr) | Film piézoélectrique | |
WO2023053751A1 (fr) | Élément piézoélectrique, et convertisseur électroacoustique | |
WO2023026726A1 (fr) | Film piézoélectrique et élément piézoélectrique | |
WO2023048022A1 (fr) | Élément piézoélectrique et haut-parleur piézoélectrique |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 22766681 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2023505209 Country of ref document: JP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 22766681 Country of ref document: EP Kind code of ref document: A1 |