WO2022102387A1 - Plaque de polarisation et dispositif d'affichage d'image comprenant ladite plaque de polarisation - Google Patents

Plaque de polarisation et dispositif d'affichage d'image comprenant ladite plaque de polarisation Download PDF

Info

Publication number
WO2022102387A1
WO2022102387A1 PCT/JP2021/039253 JP2021039253W WO2022102387A1 WO 2022102387 A1 WO2022102387 A1 WO 2022102387A1 JP 2021039253 W JP2021039253 W JP 2021039253W WO 2022102387 A1 WO2022102387 A1 WO 2022102387A1
Authority
WO
WIPO (PCT)
Prior art keywords
polarizing plate
image display
polarizing
polarizing element
less
Prior art date
Application number
PCT/JP2021/039253
Other languages
English (en)
Japanese (ja)
Inventor
幸弘 宇田
寿和 松本
智康 竹内
邦智 齋藤
成志 中里
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Priority to CN202180069710.8A priority Critical patent/CN116324543A/zh
Priority to KR1020237012482A priority patent/KR20230098791A/ko
Publication of WO2022102387A1 publication Critical patent/WO2022102387A1/fr

Abstract

Le but de la présente invention est de fournir : une plaque de polarisation qui, même lorsqu'elle est utilisée dans un dispositif d'affichage d'image ayant une structure de remplissage de couche intermédiaire, est empêchée de jaunissement et présente une excellente durabilité à haute température ; et un dispositif d'affichage d'image. La plaque de polarisation comprend : un élément polarisant obtenu par adsorption d'iode sur un alcool poly(vinylique) une couche de résine à base de résine et une orientation ; et un film protecteur transparent superposé sur au moins une surface de l'élément polarisant. La plaque de polarisation a une teneur en alcool de 4 μg/cm2 à 230 μg/cm2, et l'élément polarisant a une teneur en eau non inférieure à la teneur en eau d'équilibre à une température de 20 °C et à 20 % d'humidité relative mais pas supérieure à la teneur en eau d'équilibre à une température de 20 °C et à 50 % d'humidité relative.
PCT/JP2021/039253 2020-11-13 2021-10-25 Plaque de polarisation et dispositif d'affichage d'image comprenant ladite plaque de polarisation WO2022102387A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN202180069710.8A CN116324543A (zh) 2020-11-13 2021-10-25 偏振板以及使用了该偏振板的图像显示装置
KR1020237012482A KR20230098791A (ko) 2020-11-13 2021-10-25 편광판 및 그 편광판을 이용한 화상 표시 장치

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020189235A JP2022078508A (ja) 2020-11-13 2020-11-13 偏光板並びにその偏光板を用いた画像表示装置
JP2020-189235 2020-11-13

Publications (1)

Publication Number Publication Date
WO2022102387A1 true WO2022102387A1 (fr) 2022-05-19

Family

ID=81601101

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/039253 WO2022102387A1 (fr) 2020-11-13 2021-10-25 Plaque de polarisation et dispositif d'affichage d'image comprenant ladite plaque de polarisation

Country Status (5)

Country Link
JP (1) JP2022078508A (fr)
KR (1) KR20230098791A (fr)
CN (1) CN116324543A (fr)
TW (1) TW202229009A (fr)
WO (1) WO2022102387A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004099859A1 (fr) * 2003-05-12 2004-11-18 Hopnic Laboratory Co., Ltd. Procede de production de lentilles polarisantes a indice de refraction eleve
JP2016031533A (ja) * 2014-07-25 2016-03-07 住友化学株式会社 偏光板の製造方法
WO2016121582A1 (fr) * 2015-01-27 2016-08-04 富士フイルム株式会社 Plaque de polarisation, panneau avant d'un élément d'affichage, dispositif d'affichage, substrat de panneau tactile, panneau tactile résistif et panneau tactile capacitif
JP2019113743A (ja) * 2017-12-25 2019-07-11 日東電工株式会社 光学部材の梱包物の製造方法
JP2020128470A (ja) * 2019-02-07 2020-08-27 日東電工株式会社 粘着シート、光学積層体、および画像表示装置

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3539170B2 (ja) 1997-12-15 2004-07-07 セイコーエプソン株式会社 液晶パネル、電子機器、及び、電子機器の製造方法
JP6071459B2 (ja) 2012-11-19 2017-02-01 日東電工株式会社 偏光板および画像表示装置、ならびにそれらの製造方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004099859A1 (fr) * 2003-05-12 2004-11-18 Hopnic Laboratory Co., Ltd. Procede de production de lentilles polarisantes a indice de refraction eleve
JP2016031533A (ja) * 2014-07-25 2016-03-07 住友化学株式会社 偏光板の製造方法
WO2016121582A1 (fr) * 2015-01-27 2016-08-04 富士フイルム株式会社 Plaque de polarisation, panneau avant d'un élément d'affichage, dispositif d'affichage, substrat de panneau tactile, panneau tactile résistif et panneau tactile capacitif
JP2019113743A (ja) * 2017-12-25 2019-07-11 日東電工株式会社 光学部材の梱包物の製造方法
JP2020128470A (ja) * 2019-02-07 2020-08-27 日東電工株式会社 粘着シート、光学積層体、および画像表示装置

Also Published As

Publication number Publication date
JP2022078508A (ja) 2022-05-25
CN116324543A (zh) 2023-06-23
KR20230098791A (ko) 2023-07-04
TW202229009A (zh) 2022-08-01

Similar Documents

Publication Publication Date Title
WO2021095541A1 (fr) Plaque de polarisation et dispositif d'affichage d'image utilisant ladite plaque de polarisation
WO2022075146A1 (fr) Plaque de polarisation, et dispositif d'affichage d'image
WO2022075148A1 (fr) Plaque de polarisation, et dispositif d'affichage d'image
WO2022102387A1 (fr) Plaque de polarisation et dispositif d'affichage d'image comprenant ladite plaque de polarisation
JP7521999B2 (ja) 偏光板及び画像表示装置
JP7526631B2 (ja) 偏光板及び画像表示装置
JP7558764B2 (ja) 偏光板及び画像表示装置
JP7521994B2 (ja) 偏光板及び画像表示装置
WO2022085401A1 (fr) Plaque de polarisation, et dispositif d'affichage d'image
WO2022102363A1 (fr) Plaque de polarisation et dispositif d'affichage d'image
WO2023286576A1 (fr) Plaque de polarisation, et dispositif d'affichage d'image mettant en œuvre celle-ci
JP2024062155A (ja) 偏光板
KR20240035512A (ko) 편광 소자, 편광판, 및 화상 표시 장치
KR20240037952A (ko) 편광판 및 화상 표시 장치

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21891634

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21891634

Country of ref document: EP

Kind code of ref document: A1