WO2022100883A1 - Élément de sécurité à effet optique variable et procédé de fabrication d'un élément de sécurité à effet optique variable - Google Patents

Élément de sécurité à effet optique variable et procédé de fabrication d'un élément de sécurité à effet optique variable Download PDF

Info

Publication number
WO2022100883A1
WO2022100883A1 PCT/EP2021/025426 EP2021025426W WO2022100883A1 WO 2022100883 A1 WO2022100883 A1 WO 2022100883A1 EP 2021025426 W EP2021025426 W EP 2021025426W WO 2022100883 A1 WO2022100883 A1 WO 2022100883A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
microstructure
optically variable
security element
dependent
Prior art date
Application number
PCT/EP2021/025426
Other languages
German (de)
English (en)
Inventor
Raphael DEHMEL
Christian Fuhse
Maik Rudolf Johann SCHERER
Kai Herrmann SCHERER
Michael Rahm
Tobias Sattler
Manfred Heim
Original Assignee
Giesecke+Devrient Currency Technology Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Giesecke+Devrient Currency Technology Gmbh filed Critical Giesecke+Devrient Currency Technology Gmbh
Priority to CN202180075682.0A priority Critical patent/CN116568520A/zh
Priority to EP21805837.8A priority patent/EP4244071A1/fr
Publication of WO2022100883A1 publication Critical patent/WO2022100883A1/fr

Abstract

L'invention concerne un élément de sécurité à effet optique variable présentant une séquence de couches à partir d'une face supérieure. La séquence de couches contient une microstructure (2) présentant un motif visible par la face supérieure, d'une période de 2 μm à 50 μm et achromatique. La séquence de couches présente également une couche de réflexion (4) qui est disposée sur la microstructure (2) et qui réfléchit la lumière incidente, et une couche (6; 14) fonction de l'angle d'observation (6; 14), la couche de réflexion (4) ou la couche fonction de l'angle d'observation (6; 14) présentant au moins un évidement (15) et respectivement l'autre couche étant non structurée, la couche pourvue de l'évidement (15) étant, vu par la face supérieure, située sur l'autre couche qui est non structurée. A la place d'un évidement et d'une couche de réflexion, l'élément de sécurité peut présenter une couche (6; 14) fonction de l'angle d'observation et non structurée, et une couche de réflexion (16; 18) partiellement ransparente et non structurée.
PCT/EP2021/025426 2020-11-10 2021-11-03 Élément de sécurité à effet optique variable et procédé de fabrication d'un élément de sécurité à effet optique variable WO2022100883A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN202180075682.0A CN116568520A (zh) 2020-11-10 2021-11-03 光学可变的防伪元件和用于制造光学可变的防伪元件的方法
EP21805837.8A EP4244071A1 (fr) 2020-11-10 2021-11-03 Élément de sécurité à effet optique variable et procédé de fabrication d'un élément de sécurité à effet optique variable

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102020006902.9A DE102020006902A1 (de) 2020-11-10 2020-11-10 Optisch variables Sicherheitselement und Verfahren zum Erzeugen eines optisch variablen Sicherheitselementes
DE102020006902.9 2020-11-10

Publications (1)

Publication Number Publication Date
WO2022100883A1 true WO2022100883A1 (fr) 2022-05-19

Family

ID=78592801

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2021/025426 WO2022100883A1 (fr) 2020-11-10 2021-11-03 Élément de sécurité à effet optique variable et procédé de fabrication d'un élément de sécurité à effet optique variable

Country Status (4)

Country Link
EP (1) EP4244071A1 (fr)
CN (1) CN116568520A (fr)
DE (1) DE102020006902A1 (fr)
WO (1) WO2022100883A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2001003945A1 (fr) 1999-07-08 2001-01-18 Flex Products, Inc. Surfaces de diffraction avec arriere-plans a changement de couleur
EP1506096B1 (fr) 2002-05-14 2008-09-17 LEONHARD KURZ Stiftung & Co. KG Element optiquement variable
EP2390106A2 (fr) 2000-06-28 2011-11-30 De La Rue International Limited Dispositif de sécurité optiquement variable avec une structure en relief et un filtre réfléchissant à couche mince
DE102010049600A1 (de) * 2010-10-26 2012-01-19 Giesecke & Devrient Gmbh Sicherheitselement mit optisch variablem Flächenmuster

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102012020550A1 (de) 2012-10-19 2014-04-24 Giesecke & Devrient Gmbh Optisch variables Flächenmuster
WO2018225801A1 (fr) 2017-06-06 2018-12-13 凸版印刷株式会社 Structure optique
DE102018005447A1 (de) 2018-07-09 2020-01-09 Giesecke+Devrient Currency Technology Gmbh Optisch variables Sicherheitselement mit reflektivem Flächenbereich

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2001003945A1 (fr) 1999-07-08 2001-01-18 Flex Products, Inc. Surfaces de diffraction avec arriere-plans a changement de couleur
EP2390106A2 (fr) 2000-06-28 2011-11-30 De La Rue International Limited Dispositif de sécurité optiquement variable avec une structure en relief et un filtre réfléchissant à couche mince
EP1506096B1 (fr) 2002-05-14 2008-09-17 LEONHARD KURZ Stiftung & Co. KG Element optiquement variable
DE102010049600A1 (de) * 2010-10-26 2012-01-19 Giesecke & Devrient Gmbh Sicherheitselement mit optisch variablem Flächenmuster

Also Published As

Publication number Publication date
CN116568520A (zh) 2023-08-08
EP4244071A1 (fr) 2023-09-20
DE102020006902A1 (de) 2022-05-12

Similar Documents

Publication Publication Date Title
EP3820714B1 (fr) Élément de sécurité optiquement variable à zone de surface réfléchissante
EP2953798B1 (fr) Dessin de surface à variabilité optique
EP1747100B1 (fr) Element de securite se presentant sous la forme d'un corps en pellicule multicouche
EP2795376B1 (fr) Élément de sécurité pour papiers de sécurité, documents de valeurs ou similaires
EP2710416B1 (fr) Réseau à deux dimensions périodiques pour le filtrage chromatique
EP3233512B1 (fr) Élément de sécurité transparent variable optiquement
EP2708371B1 (fr) Elément de sécurité optique variable avec effet visuel supplémentaire de réflexion/transmission
EP3898253B1 (fr) Procédé de fabrication d'un élément de sécurité optiquement variable
WO2013079542A2 (fr) Élément optiquement variable
EP3820715A1 (fr) Élément de sécurité optiquement variable à zone de surface réfléchissante
EP3606765B1 (fr) Elément de sécurité avec structure en relief et son procédé de fabrication
EP3317111B1 (fr) Élément de sécurité comportant une grille filtrant les couleurs
WO2018114034A1 (fr) Élément de sécurité holographique et son procédé de fabrication
EP2821242B1 (fr) Élément de sécurité pour documents de valeur
EP3034315B1 (fr) Élement de securite, son procede de fabrication et support de donnees dote d'un element de securite
WO2022100883A1 (fr) Élément de sécurité à effet optique variable et procédé de fabrication d'un élément de sécurité à effet optique variable
EP3651997A1 (fr) Produit ou emballage de produit avec élément structural
WO2020015848A1 (fr) Élément de sécurité muni d'une image lenticulaire
EP3609718B1 (fr) Élément de sécurité et son procédé de fabrication
CH690232A5 (de) Flächenmuster.
EP3606766B1 (fr) Elément de sécurité et son procédé de fabrication
DE102022002470A1 (de) Optisch variables Flächenmuster, Wertdokument mit optisch variablem Flächenmuster und Verfahren zur Herstellung eines optisch variablen Flächenmusters

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21805837

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 202180075682.0

Country of ref document: CN

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2021805837

Country of ref document: EP

Effective date: 20230612