WO2022030394A1 - Élément de chargement de surface de sélection de fréquence - Google Patents

Élément de chargement de surface de sélection de fréquence Download PDF

Info

Publication number
WO2022030394A1
WO2022030394A1 PCT/JP2021/028384 JP2021028384W WO2022030394A1 WO 2022030394 A1 WO2022030394 A1 WO 2022030394A1 JP 2021028384 W JP2021028384 W JP 2021028384W WO 2022030394 A1 WO2022030394 A1 WO 2022030394A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
fss
frequency
frequency selection
selection surface
Prior art date
Application number
PCT/JP2021/028384
Other languages
English (en)
Japanese (ja)
Inventor
章代 野上
達雄 長嶋
修 加賀谷
久二男 榊原
Original Assignee
Ａｇｃ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ａｇｃ株式会社 filed Critical Ａｇｃ株式会社
Priority to JP2022541507A priority Critical patent/JPWO2022030394A1/ja
Publication of WO2022030394A1 publication Critical patent/WO2022030394A1/fr

Abstract

Un mode de réalisation de la présente invention concerne un élément de chargement de surface de sélection de fréquence comprenant un élément stratifié qui comprend un total de n-nombre (n étant un entier supérieur ou égal à 3) de couches diélectriques stratifiées de manière séquentielle d'une première couche à une n-ième couche. Une surface de sélection de fréquence qui permet la transmission d'une onde électrique d'une fréquence prescrite F à travers celle-ci est fournie à au moins l'une des surfaces principales des couches diélectriques formant l'élément stratifié. La surface de sélection de fréquence a une partie conductrice et une partie non conductrice, et a une épaisseur totale supérieure ou égale à 1,5 mm.
PCT/JP2021/028384 2020-08-03 2021-07-30 Élément de chargement de surface de sélection de fréquence WO2022030394A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2022541507A JPWO2022030394A1 (fr) 2020-08-03 2021-07-30

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020131975 2020-08-03
JP2020-131975 2020-08-03

Publications (1)

Publication Number Publication Date
WO2022030394A1 true WO2022030394A1 (fr) 2022-02-10

Family

ID=80118015

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/028384 WO2022030394A1 (fr) 2020-08-03 2021-07-30 Élément de chargement de surface de sélection de fréquence

Country Status (2)

Country Link
JP (1) JPWO2022030394A1 (fr)
WO (1) WO2022030394A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015231111A (ja) * 2014-06-04 2015-12-21 ヤマハ株式会社 人工磁気導体及びアンテナ用反射器
JP2016145777A (ja) * 2015-02-09 2016-08-12 株式会社デンソー レーダ装置搭載構造
JP2018179706A (ja) * 2017-04-11 2018-11-15 株式会社デンソー 車載レーダ装置による物体の検知方法、及び車載レーダシステム
CN111146596A (zh) * 2019-12-30 2020-05-12 华中科技大学 一种复合窗口吸收体的吸波/透波装置

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015231111A (ja) * 2014-06-04 2015-12-21 ヤマハ株式会社 人工磁気導体及びアンテナ用反射器
JP2016145777A (ja) * 2015-02-09 2016-08-12 株式会社デンソー レーダ装置搭載構造
JP2018179706A (ja) * 2017-04-11 2018-11-15 株式会社デンソー 車載レーダ装置による物体の検知方法、及び車載レーダシステム
CN111146596A (zh) * 2019-12-30 2020-05-12 华中科技大学 一种复合窗口吸收体的吸波/透波装置

Also Published As

Publication number Publication date
JPWO2022030394A1 (fr) 2022-02-10

Similar Documents

Publication Publication Date Title
JP3243789B2 (ja) 電波吸収性パネル
CN112622391B (zh) 一种光学透明超宽带雷达与红外双隐身结构
US8872703B2 (en) Transparent, flat antenna, suitable for transmitting and receiving electromagnetic waves, method for the production thereof, and use thereof
CA2461028C (fr) Substrat revetu a surface a selection de frequence
EP0413580B1 (fr) Panneau pour blindage électromagnétique
KR101668136B1 (ko) 전기적으로 광범위하게 가열가능한 투명체, 그의 제조 방법 및 그의 용도
JP7439760B2 (ja) 電波透過性基板
KR102214745B1 (ko) 투명 도전성 기재 및 투명 도전성 기재의 제조방법
JP2012506112A (ja) 局所に限定され、構造化され、電気的に加熱可能である透明領域を有している透明物体、その製造方法および使用
EP1216147A1 (fr) Vitrage
RU2701521C2 (ru) Стеклянная панель с подогревом и электромагнитным экранированием
WO2022044958A1 (fr) Absorbeur d'ondes radio
WO2022030394A1 (fr) Élément de chargement de surface de sélection de fréquence
KR20140110909A (ko) 레이다 반사-흡수 글레이징
WO2022030395A1 (fr) Élément de charge de surface de sélection de fréquence et élément de fenêtre pour véhicule
JP2023113772A (ja) ガラス体
JP2023095367A (ja) 周波数選択表面装荷部材及び車両用窓部材
WO2023228715A1 (fr) Substrat réfléchissant les rayons thermiques et verre de fenêtre
WO2024014417A1 (fr) Substrat réfléchissant la chaleur, son procédé de fabrication et verre de fenêtre
WO2023032535A1 (fr) Corps en verre
KR100524637B1 (ko) 라디오 파 흡수 판넬
JP2018002534A (ja) 合わせガラスおよび閉鎖部材
EA041197B1 (ru) Проницаемая для радиоволн подложка
KR101664395B1 (ko) 사파이어 기판을 이용한 터치패널 및 그 제조방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21853598

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2022541507

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21853598

Country of ref document: EP

Kind code of ref document: A1