WO2021234831A1 - 水素脆化寿命延長方法及びその装置 - Google Patents

水素脆化寿命延長方法及びその装置 Download PDF

Info

Publication number
WO2021234831A1
WO2021234831A1 PCT/JP2020/019852 JP2020019852W WO2021234831A1 WO 2021234831 A1 WO2021234831 A1 WO 2021234831A1 JP 2020019852 W JP2020019852 W JP 2020019852W WO 2021234831 A1 WO2021234831 A1 WO 2021234831A1
Authority
WO
WIPO (PCT)
Prior art keywords
hydrogen embrittlement
steel material
hydrogen
life extension
life
Prior art date
Application number
PCT/JP2020/019852
Other languages
English (en)
French (fr)
Inventor
拓哉 上庄
龍太 石井
昌幸 津田
Original Assignee
日本電信電話株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本電信電話株式会社 filed Critical 日本電信電話株式会社
Priority to PCT/JP2020/019852 priority Critical patent/WO2021234831A1/ja
Priority to JP2022524735A priority patent/JPWO2021234831A1/ja
Publication of WO2021234831A1 publication Critical patent/WO2021234831A1/ja

Abstract

鋼材（Ｓｔ）の水素脆化寿命を延長させる水素脆化寿命延長装置であって、鋼材（Ｓｔ）を電解質溶液（１１）に浸漬させる溶液浸漬部（１０）と、鋼材（Ｓｔ）と対極（２１）の間に所定の電流密度の電流を流す電流供給部（２０）と、鋼材（Ｓｔ）に所定の引張応力を付与する応力付与部（３０）とを備える。

Description

水素脆化寿命延長方法及びその装置
　本発明は、水素脆化寿命延長方法及びその装置に関する。
　高強度鋼材は水素を含むと延性が失われ、強度が著しく低下する。この現象は水素脆化と称される。鋼材の水素脆化に関し、鋼材の水素脆化耐性を向上させ、水素脆化により鋼材が使用不能になるまでの時間（水素脆化寿命）を延長させる方法が検討されている。
　例えば非特許文献１に、鋼材にＳｉとＣａを添加することで粒界の結合力を強化し水素吸蔵量を低下させる方法が開示されている。
高井健一、他３名、「高強度鋼の遅れ破壊特性に及ぼすＳｉ，Ｃａの複合店かの影響」、鉄と鋼,79(6), p67-73,(1993).
　しかしながら、従来の鋼材の水素脆化寿命延長方法は、材料の製造時に組成を変化させるものであり、既に製造された材料に対して後から実施することができない。また、製造中の材料全体の性質を変化させるものであり、特定の箇所のみに対して局所的に作用させることができない。このように従来の鋼材の水素脆化寿命延長方法は、製造後の材料に適用することができないという課題がある。
　本発明は、この課題に鑑みてなされたものであり、製造後の材料に対しても水素脆化寿命延長の効果を付与することができる水素脆化寿命延長方法及びその装置を提供することを目的とする。
　本発明の一態様に係る水素脆化寿命延長装置は、鋼材の水素脆化寿命を延長させる水素脆化寿命延長装置であって、前記鋼材を電解質溶液に浸漬させる溶液浸漬部と、前記鋼材と対極の間に所定の電流密度の電流を流す電流供給部と、前記鋼材に所定の引張応力を付与する応力付与部とを備えることを要旨とする。
　また、本発明の一態様に係る水素脆化寿命延長方法は、上記の水素脆化寿命延長装置が行う水素脆化寿命延長方法であって、電解質溶液に浸漬させた鋼材に所定の引張応力を付与する応力付与ステップと、前記引張応力が付与された前記鋼材に所定の電流密度の電流を流す電流供給ステップとを行うことを要旨とする。
　本発明によれば、製造後の材料に対しても水素脆化寿命延長の効果を付与することができる。
本発明の実施形態に係る水素脆化寿命延長装置の構成例を模式的に示す図である。 図１に示す対極の変形例を示す平面図である。 図１に示す水素脆化寿命延長装置が行う水素脆化寿命延長方法の処理手順を示すフローチャートである。
　以下、本発明の実施形態について図面を用いて説明する。複数の図面中同一のものには同じ参照符号を付し、説明は繰り返さない。
　〔水素脆化寿命延長装置〕
　図１は、本発明の実施形態に係る水素脆化寿命延長装置の構成例を模式的に示す図である。図１に示す水素脆化寿命延長装置１００は、対象の鋼材Ｓｔに対して水素脆化寿命評価に用いられる一般的な水素脆化加速試験方法を適用して水素脆化を進行させた後に、その鋼材Ｓｔを大気中に放置することで鋼材内部の水素を離脱させて水素脆化寿命を延長させる。
　水素脆化寿命延長装置１００は、溶液浸漬部１０、電流供給部２０、及び応力付与部３０を備える。
　溶液浸漬部１０は、鋼材Ｓｔを電解質溶液に浸漬させる。電解質溶液は、鋼材中への水素侵入を促進させる目的で、例えば0.13mol/Lのチオシアン酸アンモニウムを添加する。水素量増加効果のある他の添加物は、例えば、硫化ナトリウム、リン酸カルシウム、亜ヒ酸ナトリウム等がある。
　電流供給部２０は、鋼材Ｓｔと対極２１の間に所定の電流密度の電流を流す。電流密度は、例えば0.01mA/mm2程度である。
　応力付与部３０は、鋼材Ｓｔに所定の引張応力を付与する。所定の引張応力は、例えば、鋼材Ｓｔの引張強度の凡そ0.7倍の引張応力である。引張応力は、一般的な引張試験機を用いて付与する。なお、引張応力は、鋼材Ｓｔの引張強度の0.6～0.8であっても構わない。
　図１に示すように、例えば棒状の鋼材Ｓｔの上端を上部掴み具３２、下端を下部掴み具３１で掴み、下部掴み具３１を剛体（図示せず）に固定し、上部掴み具３２を引っ張る。応力付与部３０は、例えばモータと減速歯車で引張応力を生じさせる。
　水素脆化寿命延長装置１００を用いて所定時間の間水素を吸蔵させた鋼材Ｓｔは、水素脆化寿命延長装置１００から取り外して大気中に放置し、内部の水素を脱離させる。なお、常温では水素の脱離に時間を要するため加熱してもよい。
　以上説明した手順を踏んだ鋼材Ｓｔは、水素脆化寿命を増大させることができる。平均破断時間が1.0時間、最大破断時間が1.2時間である鋼材Ｓｔを対象に、水素脆化寿命延長装置１００を用いて水素脆化加速試験を45分間実施し、24時間大気中に放置して水素を脱離させた鋼材Ｓｔの破断時間は5.4時間であった。
　このように本実施形態に係る水素脆化寿命延長装置１００は、水素脆化寿命を延長させることができる。
　なお、水素脆化寿命を増大させることができる鋼材Ｓｔは、溶液浸漬部１０において電解質溶液に浸漬させた部分である。よって、必要に応じて溶液浸漬部１０の大きさを大きくする。なお、溶液浸漬部１０は、上部掴み具３２と下部掴み具３１を含めて鋼材Ｓｔの全体を浸漬させる大きさにしてもよい。
　以上説明したように本実施形態に係る水素脆化寿命延長装置１００は、鋼材Ｓｔの水素脆化寿命を延長させる水素脆化寿命延長装置であって、鋼材Ｓｔを電解質溶液に浸漬させる溶液浸漬部１０と、鋼材Ｓｔと対極２１の間に所定の電流密度の電流を流す電流供給部２０と、鋼材Ｓｔに所定の引張応力を付与する応力付与部３０とを備える。これにより、製造後の材料に対しても必要に応じて水素脆化寿命延長の効果を付与することが可能となる。
　水素脆化寿命を延長できる理由は次のように推察できる。予め鋼材Ｓｔの水素脆化を進行させておくことで鋼材内部の原子空孔を増加させる。そして、再び水素脆化が進行する場合に、増加させた原子空孔が水素のトラップサイトとなり水素の拡散を遅らせることによるものと考えられる。
　（変形例）
　図２は、対極２１の変形例を示す平面図である。図２（ａ）は、板状の対極２１ａ，２１ｂ、２１ｃ，２１ｄで鋼材Ｓｔを囲んだ例である。図２（ｂ）は対極２１を円形にした例である。
　このように、対極２１は、鋼材Ｓｔを取り囲む形状であってもよい。これにより鋼材Ｓｔへの水素の侵入を均一にでき、水素脆化寿命を延長させる効果を安定化することができる。
　（水素脆化寿命延長方法）
　図３は、水素脆化寿命延長装置１００（図１）が行う水素脆化寿命延長方法の処理手順を示すフローチャートである。
　図３に示すように、本実施形態に係る水素脆化寿命延長方法は、溶液浸漬（ステップＳ１）と、電流供給（ステップＳ２）と、応力付与（ステップＳ３）とを所定時間繰り返す（ステップＳ４）。つまり、電解質溶液に浸漬させた鋼材に所定の引張応力を付与する応力付与ステップＳ３と、引張応力が付与された鋼材Ｓｔに所定の電流密度の電流を流す電流供給ステップＳ２とを行う。
　なお、図３において、鋼材Ｓｔに吸蔵させた水素を一度脱離させるステップの表記は省略している。その理由は、水素脆化寿命延長装置１００を用いなくても鋼材Ｓｔを放置するだけで自ずと行えるからである。
　以上説明したように本実施形態に係る水素脆化寿命延長装置１００と水素脆化寿命延長方法によれば、鋼材の水素脆化寿命を延長させることができる。また、水素脆化加速試験では水素脆化の耐性が低い箇所ほどより水素脆化が進行するため、水素脆化の耐性が低い恐れのある個所に対して選択的に水素脆化寿命延長の効果を付与することができ、材料全体の性質を変える心配がない。
　なお、本発明は上記の実施形態に限定されない。例えば、予め水素を吸蔵させた後に引張応力を徐々に付与し、所定の応力に到達した時点で除力する方法を用いてもよい。また、水素の吸蔵は、鋼材Ｓｔを腐食させて水素を発生させる方法を用いてもよい。
　また、短時間で鋼材Ｓｔから水素を脱離させるためには、鋼材Ｓｔを加熱してもよい。ただし、高温で加熱すると原子空孔が減少し、水素脆化寿命の延長効果が消失してしまう場合もある。加熱する場合は、例えば200度未満の温度が好ましい。
　本発明は、上記の実施形態に限定されるものではなく、その要旨の範囲内で変形が可能である。例えば、応力付与部は鉛直方向に応力を生じさせる例を示したが、水平方向に応力を生じさせてもよい。また、応力の源はモータでなくても構わない。
　このように、本発明はここでは記載していない様々な実施形態等を含むことは勿論である。したがって、本発明の技術的範囲は上記の説明から妥当な特許請求の範囲に係る発明特定事項によってのみ定められるものである。
１０：溶液浸漬部
１１：電解質溶液
２０：電流供給部
２１：対極
３０：応力付与部
３１：下部掴み具
３２：上部掴み具
１００：水素脆化寿命延長装置

Claims (3)

  1. 　鋼材の水素脆化寿命を延長させる水素脆化寿命延長装置であって、
    　前記鋼材を電解質溶液に浸漬させる溶液浸漬部と、
    　前記鋼材と対極の間に所定の電流密度の電流を流す電流供給部と、
    　前記鋼材に所定の引張応力を付与する応力付与部と
    　を備える水素脆化寿命延長装置。
  2. 　前記対極は、
    　前記鋼材を取り囲む形状である請求項１に記載の水素脆化寿命延長装置。
  3. 　水素脆化寿命延長装置が行う水素脆化寿命延長方法であって、
    　電解質溶液に浸漬させた鋼材に所定の引張応力を付与する応力付与ステップと、
    　前記引張応力が付与された前記鋼材に所定の電流密度の電流を流す電流供給ステップと
    　を行う水素脆化寿命延長方法。
PCT/JP2020/019852 2020-05-20 2020-05-20 水素脆化寿命延長方法及びその装置 WO2021234831A1 (ja)