WO2021230400A1 - 항균 마스크 - Google Patents

항균 마스크 Download PDF

Info

Publication number
WO2021230400A1
WO2021230400A1 PCT/KR2020/006377 KR2020006377W WO2021230400A1 WO 2021230400 A1 WO2021230400 A1 WO 2021230400A1 KR 2020006377 W KR2020006377 W KR 2020006377W WO 2021230400 A1 WO2021230400 A1 WO 2021230400A1
Authority
WO
WIPO (PCT)
Prior art keywords
antibacterial
mask
present
polyethylene
zinc oxide
Prior art date
Application number
PCT/KR2020/006377
Other languages
English (en)
French (fr)
Inventor
박동일
이수정
허나영
심준엽
이재홍
Original Assignee
주식회사 알앤에프케미칼
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 알앤에프케미칼 filed Critical 주식회사 알앤에프케미칼
Publication of WO2021230400A1 publication Critical patent/WO2021230400A1/ko

Abstract

본 발명은 베이스 수지 및 항균성 조성물을 포함하는 외층과 내층으로 이루어진 마스크 본체부와, 폴리에틸렌 또는 폴리프로필렌을 포함하는 부직포 내피부와, 상기 마스크 본체부와 부직포 내피부의 양 측면에 연결된 귀걸이부를 포함하여 구성되되, 상기 마스크 본체부에는 결합구가 구비되는 것인 항균 마스크에 관한 것이다.

Description

항균 마스크
본 발명은 항균 마스크에 관한 것이다. 보다 상세하게는, 본 발명은 항바이러스성 및 항균성을 보유한 항균필름을 포함하는 우수한 비말 차단성과 영구적 항균성을 갖는 항균 마스크에 관한 것이다.
최근 전염성이 높은 바이러스의 출현에 따른 질병에 대한 위험성이 증가함에 따라 개인 위생과 더불어 타인과의 접촉이 많은 공공 공간에서의 항균에 대한 요구가 급증하고 있다.
일반적으로 마스크는 기본적으로는 호흡이 양호해야 되며, 보건 위생상 병균, 먼지 등의 흡입 및 비산을 막기 위한 것으로, 통상적으로는 면직물 또는 부직포 등을 외피, 내피 및 필터부로 중첩하여 박음질하고, 그 양쪽에는 귀에 걸 수 있는 밴드를 구성하게 되며, 세균 등으로 오염된 환경이나 오염 가능성이 있는 환경에서 개인 또는 타인의 위생을 위해 사용되어져 왔다.
마스크는 호흡과정에서 발생하는 입김과 외부의 습기로 인하여 항상 습도가 높은 상태로 유지되어 세균이 쉽게 증식할 수 있는 환경적 특징을 가지고 있다. 또한 마스크의 사용기간이 긴 경우에는 마스크에 대량의 세균이 증식하여 사용자의 건강을 해칠 수 있는 가능성도 배제할 수 없다.
본 발명은 면직물 또는 부직포 등으로 구성된 내피/필터/외피의 구성에서 탈피하여 항균 및 항바이러스 특성을 갖는 항균필름으로 외피를 구성하고 (항균)부직포를 내피로 구성하여 항균작용과 항바이러스 작용이 우수하며, 소독 및 세척후 재사용이 가능하고, 장시간 사용이 가능한 마스크를 만들고자 하는데 목적이 있다.
상기 목적의 달성을 위하여, 본 발명의 일 실시예는 베이스 수지 및 항균성 조성물을 포함하는 외층과 내층으로 이루어진 마스크 본체부와, 폴리에틸렌 또는 폴리프로필렌을 포함하는 부직포 내피부와, 상기 마스크 본체부와 부직포 내피부의 양 측면에 연결된 귀걸이부를 포함하여 구성되되, 상기 마스크 본체부에는 결합구가 구비되는 것인 항균 마스크를 제공한다.
본 발명에 따른 항균 마스크는 항균 및 항바이러스 특성을 갖는 항균필름으로 외피를 구성하고 (항균)부직포를 내피로 구성함으로써 항균작용과 항바이러스 작용이 우수할 뿐만 아니라, 소독 및 세척후 재사용이 가능하다.
본 발명의 항균 마스크는 마스크 본체가 플라스틱 항균필름으로 제조되어 소수성 표면을 가짐으로써 마스크 착용자 및 상대방의 양방향으로 완벽한 비말(침방울) 차단이 가능하다.
본 발명의 항균 마스크는 항균제가 필름 표면 및 내부에도 전체적으로 고르게 분포되어 있어 마모되지 않는 항균성, 즉 영구적인 항균성을 제공할 수 있다.
본 발명의 항균 마스크는 마스크 본체가 플라스틱 항균필름으로 이루어져 손 씻듯이 세척/소독이 용이하고, 세척/소독 후 재사용이 가능할 뿐만 아니라, 세척 또는 소독에 의한 항균성 저하 및 마스크 본연의 미세먼지, 세균 및 바이러스 차단 기능저하가 없다.
본 발명의 항균 마스크는 마스크 착용시 착용자 턱 아래 부분에 위치하는 부위에 개구부를 구비함으로써 턱 아래 통로를 통한 편안한 호흡이 가능하여 장시간 착용, 나아가 스포츠 활동이 가능할 뿐 아니라 호흡과정에서 발생하는 입김과 외부의 습기로 인하여 항상 습도가 높은 상태로 유지되어 세균이 쉽게 증식할 수 있는 문제점을 해결할 수 있다. 이러한 이유로, 본 발명의 항균 마스크을 착용할 경우 안경 김서림이 발생하지 않을 수 있다.
본 발명의 항균 마스크는 항균필름 본체 만으로도 타인의 비말에 대한 차단이 가능하며, 투명 항균필름을 사용하여 대화 시 상대방의 안면 표정 및 입모양 확인이 가능하다.
도 1은 외층(110)과 내층(120)의 2중층으로 이루어진 본 발명의 마스크 본체부(항균 필름)을 개략적으로 나타낸 것이다.
도 2는 본 발명에 따른 항균 마스크의 전체적인 형태를 표현하는 사시도이다.
도 3은 본 발명에 따른 항균 마스크의 정면을 표현하는 도면이다.
도 4는 본 발명에 따른 항균 마스크의 항균 필름과 부직포를 분리한 상태를 나타낸 분해사시도이다.
도 5는 본 발명에 따른 항균 마스크를 착용 상태를 나타낸 사용상태도이다.
이하, 첨부된 도면을 참조하여 본 발명에 따른 바람직한 실시예를 상세히 설명하되, 도면 부호에 관계없이 동일하거나 유사한 구성 요소는 동일한 참조 번호를 부여하고 이에 대한 중복되는 설명은 생략하기로 한다.
또한, 본 발명을 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다. 또한, 첨부된 도면은 본 발명의 사상을 쉽게 이해할 수 있도록 하기 위한 것일 뿐, 첨부된 도면에 의해 본 발명의 사상이 제한되는 것으로 해석되어서는 아니 됨을 유의해야 한다.
본 명세서에서, "항균"이란 용어는 미생물 집단에서 살균 활성 또는 미생물 성장 저해를 뜻한다. 본 명세서에서 사용된 바와 같이, "항균"이란 용어는 24시간 후에 측정하였을 때 미생물의 수가 대조군에 비하여 로그적으로 감소함을 의미한다.
도 1은 외층(110)과 내층(120)의 2중층으로 이루어진 본 발명의 마스크 본체부(항균 필름)(100)을 나타낸 것이다.
본 발명에 따른 항균 마스크는 베이스 수지 및 항균성 조성물을 포함하는 외층(110)과 내층(120)으로 이루어진 마스크 본체부(100)와, 폴리에틸렌 또는 폴리프로필렌을 포함하는 부직포 내피부(200)와, 상기 마스크 본체부와 부직포 내피부의 양 측면에 연결된 귀걸이부를 포함하여 구성되되, 상기 마스크 본체부에는 결합구(140)가 구비되는 것일 수 있다
본 발명의 마스크 본체부의 재질에는 소프트(soft)한 플라스틱 재질하기만 하면 특별한 제한은 없다. 본 발명의 항균 마스크는 마스크 본체가 플라스틱 필름으로 제조되어 소수성 표면을 가짐으로써 마스크 착용자 및 상대방의 양방향으로 완벽한 비말(침방울) 차단이 가능하다. 본 발명의 항균 마스크는 마스크 본체부가 플라스틱 필름으로 제조되지만 마스크 착용시 착용자 턱 아래 부분에 위치하는 부위에 후술하는 개구부를 구비함으로써 턱 아래 통로를 통한 자연 호흡이 가능하다. 따라서 마스크 본체부의 재질로 다양한 플라스틱 수지를 사용할 수 있다. 그 결과 본 발명의 항균 마스크는 마스크 본체가 플라스틱 항균필름으로 이루어져 손 씻듯이 세척/소독이 용이하고, 세척/소독 후 재사용이 가능하다.
본 발명의 일 실시예에 따르면, 상기 베이스 수지는 폴리올레핀, 열가소성 폴리우레탄, 폴리에틸렌 플라스토머, 폴리에틸렌 엘라스토머, 메탈로센 폴리에틸렌 및 생분해성 수지로 이루어진 군에서 선택되는 1종 이상의 수지일 수 있다.
상기 생분해성 수지는 PLA, PBAT, PBS 등일 수 있다.
상기 마스크 본체부는 상기한 재질 단독으로 이루어지거나, 서로 블렌딩된 재질로 이루어진 항균 투명 필름일 수 있다.
일 례로, 상기 외층은 PO(Polyolefin) 계열 소재로 이루어질 수 있다. 상기 PO 소재는 용도에 따라서 서로 블렌딩하여 적용할 수 있다.
다른 례로, 상기 외층은 열가소성 폴리우레탄 수지로 이루어질 수 있다.
또 다른 례로, 상기 외층은 폴리에틸렌 플라스토머, 폴리에틸렌 엘라스토머 등으로 이루어질 수 있다.
본 발명의 일 실시예에 따르면, 상기 외층의 두께는 전체 항균 필름의 30~70%일 수 있다.
본 발명의 일 실시예에 따르면, 상기 외층에 특수한 외관을 부여하기 위해 Matt 공법을 적용할 수 있다.
일 례로, 상기 내층은 PO(Polyolefin) 계열 소재로 이루어질 수 있다. 상기 PO 소재는 용도에 따라서 서로 블렌딩하여 적용할 수 있다.
다른 례로, 상기 내층은 열가소성 폴리우레탄 수지로 이루어질 수 있다.
또 다른 례로, 상기 내층은 폴리에틸렌 플라스토머, 폴리에틸렌 엘라스토머 등우로 이루어질 수 있다.
본 발명의 일 실시예에 따르면, 상기 내층의 두께는 전체 항균 필름의 30~70%일 수 있다.
본 발명의 일 실시예에 따르면, 상기 내층에 특수한 외관을 부여하기 위해 Matt 공법을 적용할 수 있다.
본 발명의 일 실시예에 따르면, 상기 항균성 조성물은 폴리올레핀, 열가소성 폴리우레탄, 폴리에틸렌 플라스토머, 폴리에틸렌 엘라스토머 및 생분해성 수지로 이루어진 군에서 선택되는 1종 이상의 베이스 수지; 산화아연; 항균 구리; 및 첨가제를 포함할 수 있다. 본 발명에서는 상기 '항균성 조성물'을 '항균 마스터배치'라고 부르기도 한다.
본 발명의 바람직한 실시예에 따르면, 상기 항균성 조성물은 폴리올레핀, 열가소성 폴리우레탄, 폴리에틸렌 플라스토머, 폴리에틸렌 엘라스토머 및 생분해성 수지로 이루어진 군에서 선택되는 1종 이상의 베이스 수지 75~85 중량%; 산화아연 3~10 중량%; 항균 구리 5~10 중량%; 및 첨가제 0.1~1 중량%를 포함할 수 있다.
일 례로, 상기 항균 마스터배치는 LLDPE, LDPE, HDPE, ULDPE, PP, PVC, TPU 수지 등을 베이스 소재(Base material)로 하여 산화아연, 항균구리 이외에 분산 및 가공성을 위한 기타 첨가제를 포함하는 것일 수 있다.
본 발명의 일 실시예에 따르면, 상기 항균성 조성물(항균 마스터배치)은 마스터 배치 배합 또는 컴파운딩 배합에 의해 사출 성형되는 것일 수 있다.
본 발명의 바람직한 실시예에 따르면, 상기 항균성 조성물(항균 마스터배치)은 폴리올레핀, 열가소성 폴리우레탄, 폴리에틸렌 플라스토머, 폴리에틸렌 엘라스토머 및 생분해성 수지로 이루어진 군에서 선택되는 1종 이상의 베이스 수지 75~85 중량%; 산화아연 3~10 중량%; 항균 구리 5~10 중량%; 및 첨가제 0.1~1 중량%를 포함할 수 있다.
본 발명에서는, 상기 외층과 내층에 균일하고 영구적인 항균력 및 항바이러스력을 부여하기 위해 상기 베이스 수지에 항균성 조성물(항균 마스터 배치)를 첨가하여 항균 필름을 제조하였다.
본 발명의 일 실시예에 따르면, 항균 마스터 배치의 첨가량은 3 내지 15 중량%일 수 있다.
상기 항균 구리는 구형 분말과 플레이크형 분말이 혼합된 항균동 분말일 수 있다.
본 발명의 일 실시예에 따르면, 상기 항균동 분말은 구형이 60 내지 80%, 바람직하게는 70%이고, 플레이크형이 20 내지 40%, 바람직하게는 30%인 것일 수 있다.
본 발명의 일 실시예에 따르면, 상기 항균동 분말은 평균 직경이 15 ~ 75㎛인 구형 분말을 70% 포함하는 것일 수 있다.
본 발명의 일 실시예에 따르면, 상기 항균동 분말은 길이 10 ~ 75㎛, 폭 10 ~75㎛, 두께 3~10㎛ 분말로 가공한 플레이크형 분말 30% 를 혼합한 것일 수 있다.
본 발명의 일 실시예에 따르면, 상기 산화아연에 대한 항균 구리의 비율은 3:7 내지 7:3일 수 있다.
상기 산화아연은 비정형 산화아연 파우더(이하 ZOIr)와 마름쇠(Tetrapod) 형상의 산화아연 파우더(이하 ZOT)가 혼합된 것일 수 있다.
본 발명의 일 실시예에 따르면, 상기 산화아연은 항균력 극대화를 위해 비정형 산화아연 파우더와 마름쇠(Tetrapod) 형상의 산화아연 파우더가 8:2 내지 2:8의 비율로 혼합된 것일 수 있다.
본 발명의 일 실시예에 따르면, 상기 항균 마스터 배치에 필요에 따라 유기항균제가 첨가될 수 있다.
본 발명의 일 실시예에 따르면, 항바이러스력 효과의 극대화를 위해 아연 이온운반체로 알려진 Pyrithione, Zinc Pyrithione 를 첨가할 수 있다.
본 발명의 일 실시예에 따르면, 항바이러스력 효과의 극대화를 위해 PEG(Polyethylene Glycol)을 첨가할 수 있다.
상기 귀걸이부는 마스크에서 귀까지의 길이 조절이 가능한 구조일 수 있다. 일 례로 길이 조절이 가능한 마스크 밴드일 수 있다.
본 발명의 일 실시예에 따르면, 상기 항균 마스크에는 통기성을 부여하기 위해 하단에 개구부(130)가 설치될 수 있다. 기존 마스크는 장시간 착용시 마스크의 차단 및 밀폐구조로 호흡이 불편하나, 도 2 및 도 5에 나타낸 바와 같이, 본 발명의 마스크는 하단에 호흡구로서 개구부(130)가 설치됨으로써 턱 아래 통로를 통한 편안한 호흡이 가능하다. 또한, 본 발명의 마스크는 개구부의 위치가 하향으로 설계되어 타인의 비말이 착용자의 안면에 직접적인 접촉이 방지된다. 또한, 본 발명의 마스크는 개구부를 구비함으로써 마스크 착용시 발생하는 입김과 외부의 습기로 인하여 항상 습도가 높은 상태로 유지되어 세균이 쉽게 증식할 수 있는 환경을 예방할 수 있다.
상기 부직포는 항균부직포 또는 일반 부직포일 수 있다. 부직포 내피부의 재질은 폴리에틸렌 또는 폴리프로필렌일 수 있다. 사용자는 부직포로 천, 또는 손수건 등을 사용할 수도 있다.
상기 부직포는 별도의 테이핑없이 필름-마스크의 형상에 맞는 형태를 가짐으로써 후단에 삽입되어 간편하게 사용될 수 있다.
상기 부직포는 오염되면 교체할 수 있고, 상기 항균 필름(마스크 본체부)는 세정이 필요하면 물과 비누, 가정용 소독제를 이용하여 세척할 수 있어 본 발명의 항균 마스크는 반영구적으로 사용가능하다.
100: 마스크 본체부
110: 외층
120: 내층
130: 개구부
140: 결합구
200: 부직포 내피부

Claims (9)

  1. 베이스 수지 및 항균성 조성물을 포함하는 외층과 내층으로 이루어진 마스크 본체부와, 폴리에틸렌 또는 폴리프로필렌을 포함하는 부직포 내피부와, 상기 마스크 본체부와 부직포 내피부의 양 측면에 연결된 귀걸이부를 포함하여 구성되되, 상기 마스크 본체부에는 결합구가 구비되는 것인 항균 마스크.
  2. 제1항에 있어서,
    상기 베이스 수지는 폴리올레핀, 열가소성 폴리우레탄, 폴리에틸렌 플라스토머, 폴리에틸렌 엘라스토머, 메탈로센 폴리에틸렌 및 생분해성 수지로 이루어진 군에서 선택되는 1종 이상의 수지인 것인 항균 마스크.
  3. 제1항에 있어서,
    상기 항균성 조성물은 폴리올레핀, 열가소성 폴리우레탄, 폴리에틸렌 플라스토머, 폴리에틸렌 엘라스토머 및 생분해성 수지로 이루어진 군에서 선택되는 1종 이상의 베이스 수지; 산화아연; 항균 구리; 및 첨가제를 포함하는 것인 항균 마스크.
  4. 제3항에 있어서,
    상기 산화아연은 비정형 산화아연 파우더와 마름쇠(Tetrapod) 형상의 산화아연 파우더가 8:2 내지 2:8의 비율로 혼합된 것인 항균 마스크.
  5. 제3항에 있어서,
    상기 항균 구리는 구형 분말과 플레이크형 분말이 혼합된 항균동 분말인 것인 항균 마스크.
  6. 제1항에 있어서,
    상기 항균성 조성물은 마스터 배치 배합 또는 컴파운딩 배합에 의해 사출 성형되는 것인 항균 마스크.
  7. 제3항에 있어서,
    상기 산화아연에 대한 항균 구리의 비율은 3:7 내지 7:3인 것인 항균 마스크.
  8. 제1항에 있어서,
    상기 항균성 조성물은 폴리올레핀, 열가소성 폴리우레탄, 폴리에틸렌 플라스토머, 폴리에틸렌 엘라스토머 및 생분해성 수지로 이루어진 군에서 선택되는 1종 이상의 베이스 수지 75~85 중량%; 산화아연 3~10 중량%; 항균 구리 5~10 중량%; 및 첨가제 0.1~1 중량%를 포함하는 것인 항균 마스크.
  9. 제1항에 있어서,
    상기 항균 마스크는 통기성을 부여하기 위해 하단에 개구부가 설치되는 것인 항균 마스크.
PCT/KR2020/006377 2020-05-13 2020-05-14 항균 마스크 WO2021230400A1 (ko)