WO2021214955A1 - エッグシェル型白金担持アルミナ触媒、その製造方法、及びその使用方法 - Google Patents

エッグシェル型白金担持アルミナ触媒、その製造方法、及びその使用方法 Download PDF

Info

Publication number
WO2021214955A1
WO2021214955A1 PCT/JP2020/017564 JP2020017564W WO2021214955A1 WO 2021214955 A1 WO2021214955 A1 WO 2021214955A1 JP 2020017564 W JP2020017564 W JP 2020017564W WO 2021214955 A1 WO2021214955 A1 WO 2021214955A1
Authority
WO
WIPO (PCT)
Prior art keywords
platinum
catalyst
supported
egg
shell type
Prior art date
Application number
PCT/JP2020/017564
Other languages
English (en)
French (fr)
Inventor
佳巳 岡田
今川　健一
政志 斉藤
健太 福留
治人 小林
Original Assignee
千代田化工建設株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 千代田化工建設株式会社 filed Critical 千代田化工建設株式会社
Priority to AU2020443246A priority Critical patent/AU2020443246A1/en
Priority to EP20932812.9A priority patent/EP4140578A4/en
Priority to US17/918,661 priority patent/US20230148027A1/en
Priority to JP2022516775A priority patent/JP7466634B2/ja
Priority to CA3176199A priority patent/CA3176199A1/en
Priority to PCT/JP2020/017564 priority patent/WO2021214955A1/ja
Priority to CN202080099978.1A priority patent/CN115485063A/zh
Priority to KR1020227040504A priority patent/KR20220158289A/ko
Priority to TW110114573A priority patent/TW202144076A/zh
Publication of WO2021214955A1 publication Critical patent/WO2021214955A1/ja

Abstract

【課題】　触媒寿命において優れた性能を有するエッグシェル型白金担持アルミナ触媒を提供する。 【解決手段】　エッグシェル型白金担持アルミナ触媒は、アルミナ担体と、アルミナ担体の外郭に分散して担持された白金と、バナジウム、クロム、モリブデン、及びリンの群から選ばれる１種又は２種以上の第２成分とを有する。白金の含有量は、白金元素として０．０５ｗｔ％以上５．０ｗｔ％以下であるとよい。第２成分の含有量は、各元素として０．１ｗｔ％以上５．０ｗｔ％以下であるとよい。アルミナ担体は、表面積が１５０ｍ２／ｇ以上、細孔容積が０．４０ｃｍ３／ｇ以上、平均細孔径が４０Å以上３００Å以下、及び全細孔容積に対して平均細孔径±３０Å以下の細孔が占める割合が６０％以上であるとよい。

Description

エッグシェル型白金担持アルミナ触媒、その製造方法、及びその使用方法
　この発明は、化学品製造、水素製造、ファインケミカル製造、排気ガス処理等の環境浄化等の触媒を利用するプロセスに用いられる金属触媒に係り、アルミナ担体に白金が担持されているエッグシェル型白金担持アルミナ触媒、その製造方法、及びその使用方法に関する。
　アルミナ担体に白金等を担持させた白金担持アルミナ触媒は、例えば、メチルシクロヘキサン、シクロヘキサン、デカリン、ジベンジルトルエン等の水素化芳香族類から対応する芳香族類と水素に脱水素する脱水素反応を始めとする様々な化合物の脱水素反応や水素化反応、改質反応等による燃料や石油化学品、医薬などのファインケミカル製造、自動車排ガスを始めとする環境浄化等、極めて広範な分野で工業的に用いられている。
　そして、これらの白金担持アルミナ触媒は、一般に、アルミナの金属酸化物からなる多孔性アルミナ担体を調製し、得られた多孔性アルミナ担体に塩化白金酸水溶液、塩化白金アンモニウム水溶液、アセチルアセトナト白金等の有機白金化合物の溶液等の触媒金属化合物の溶液を含浸させ、次いで乾燥させて触媒金属化合物担持乾燥物とした後、例えば３５０℃以上８００℃以下及び０．５時間以上２４時間以下の条件で焼成し、更に必要に応じて、得られた触媒金属化合物担持焼成物を例えば２５０℃以上８００℃以下及び０．５時間以上２４時間以下の条件で水素還元することにより製造されている。
　このような方法で製造される白金担持アルミナ触媒は、白金原子が原子量195と質量が大きく、白金源として利用される白金化合物の触媒担体に対する吸着力が強いことから、白金化合物がアルミナ担体の内部に拡散する前にアルミナ担体の外殻部のみに吸着されて固定されるため、触媒断面で白金金属の分散状態を観察した場合に、触媒の外周部のみに白金金属が担持されており、担体内部には白金金属が担持されていない、いわゆるエッグシェル（egg shell）型の白金担持触媒となることが知られている。
　触媒反応において原料の分子が大きい等の理由により触媒粒子内での拡散抵抗が大きい場合は、活性金属である白金が触媒の内部にまで担持されていても、原料の分子が触媒内部に拡散する速度が遅いため反応が十分に進行しないことから、反応が触媒粒子の外殻周辺で優先的に起こることが知られている。このような反応では、活性金属が触媒の外郭部のみに存在するエッグシェル型の方が有利である。しかしながら、触媒粒子の外殻のみに一定量の活性金属を担持した場合、活性金属粒子の密度が高くなるために、活性金属粒子の分散度を十分に実現できないという問題や、シンタリングやコーキングによる触媒劣化が起きやすいという問題等が発生する虞がある。このような観点から、触媒外郭部にのみ白金金属が担持される場合の白金金属の分散度を向上させた触媒が開発されている。特許文献１は、拡散抵抗が大きくならない程度に白金担持アルミナ触媒の細孔の大きさが揃っており、かつ白金の分散が良好なエッグシェル型白金担持アルミナ触媒を開示している。また、拡散抵抗が影響しない反応においては担体の有する表面積を十分に活用できるように、触媒の断面全体にわたって白金金属が良好に分散している触媒も開発されており、特許文献２はそのような均一型白金担持アルミナ触媒を開示している。
　触媒反応において原料の分子が大きい等の理由により触媒粒子内での拡散抵抗が大きい場合は、活性金属である白金が触媒の内部にまで担持されていても、原料の分子が触媒内部に拡散する速度が遅いため反応が十分に進行しないことから、反応が触媒粒子の外殻周辺で優先的に起こることが知られている。このような反応では、活性金属が触媒の外郭部のみに存在するエッグシェル型の方が有利である。しかしながら、触媒粒子の外殻のみに一定量の活性金属を担持した場合、活性金属粒子の密度が高くなるために、活性金属粒子の分散度を十分に実現できないという問題や、シンタリングやコーキングによる触媒劣化が起きやすいという問題等が発生する虞がある。このような観点から、触媒外郭部にのみ白金金属が担持される場合の白金金属の分散度を向上させた触媒が開発されている。特許文献１は、拡散抵抗が大きくならない程度に白金担持アルミナ触媒の細孔の大きさが揃っており、かつ白金の分散が良好な白金担持アルミナ触媒を開示している。また、拡散抵抗が影響しない反応においては担体の有する表面積を十分に活用できるように、触媒の断面全体にわたって白金金属が良好に分散している触媒も開発されており、特許文献２はそのような白金担持アルミナ触媒を開示している。
　白金担持アルミナ触媒は、古くから広範な分野における触媒プロセスで利用されているが、近年は水素エネルギーの貯蔵輸送技術として注目されている水素エネルギーキャリアの一つの方法である有機ケミカルハイドライド法に利用されている。従来の白金担持アルミナ触媒に比べて性能の高い白金担持アルミナ触媒の開発が進められるようになっており、特許文献１及び特許文献２は白金担持アルミナ触媒の用途として、有機ケミカルハイドライド法で必要な脱水素反応での利用を開示している。有機ケミカルハイドライド法は、化学反応によって、水素を化学品の分子構造の中に取り込んだ有機ケミカルハイドライド化合物（水素化有機化合物）として「貯める」「運ぶ」を行う方法である。有機ケミカルハイドライド法は、１９８０年代から提唱されていた方法であるが、水素を取り込んだ有機ケミカルハイドライドの化合物から水素を発生させる脱水素触媒の寿命が極めて短く、工業的な実施が困難であったために実用化されていない方法であり、技術開発の鍵は工業的に利用できる触媒寿命など十分な性能を有する新規な脱水素触媒の開発であった。現在では、上記のような高い性能を有する白金担持アルミナ触媒の適用によって、有機ケミカルハイドライド法による水素エネルギーキャリアシステムの開発は、大規模な国際間水素輸送実証が実施されるに至っており、技術的には商業化が可能な段階まで開発が進んでいる。非特許文献３及び４は、このような有機ケミカルハイドライド法の開発の経緯を開示している。
　日本国は水素エネルギーの実用化と普及を国策として進める方針を震災後の第４次エネルギー基本計画から盛り込んでおり、水素・燃料電池技術ロードマップの策定に続いて２０１７年に水素基本戦略を閣議決定している。上記の有機ケミカルハイドライド法は水素エネルギーを大規模に「貯める」「運ぶ」を行う水素エネルギーキャリアを提供することができ、水素基本戦略にその実用化が盛り込まれており、２０３０年までに水素供給価格目標として３０￥／Ｎｍ３、２０５０年目標として２０￥／Ｎｍ３を掲げている。これより、継続的な改良技術開発によるコストダウンが求められており、触媒性能、特に触媒寿命の向上はコストダウンに大きな影響を与える。触媒性能の中で、転化率、選択率とその積である収率については、これまでの開発で比較的に高いレベルまで開発が進んでおり、その性能をいかに長期間維持できるかの触媒寿命の改善がコストダウンに寄与する段階にある。更に、工業的な触媒製造工程において、硫黄を利用しないことによる工程の簡略化とプロセスの簡略化もコストダウンに寄与する要素技術となる。
特許第４６５２６９５号公報 特許第４１４２７３３号公報 岡田佳巳、エネルギー・資源、Ｖｏｌ.３３, Ｎｏ．３，１６８ （２０１８） 岡田佳巳、東京都高圧ガス協会会報、２０１９年８月号、９月号 資源エネルギー庁、水素基本戦略（２０１７年１２月）
　特許文献２の均一型白金担持アルミナ触媒は、比較的触媒寿命が長く、実用的にも有用であるが、更なる改善が望まれている。有機ケミカルハイドライド法における脱水素反応は吸熱反応及び反応により分子数が増大する平衡反応であるため、反応条件が高温かつ低圧であるほど効率が良い。一方、製造される水素は、利用用途によっては高圧であることが好ましいため、より高い反応温度でも使用可能な触媒が求められることがある。しかし、反応条件が高温になると、副反応が発生し易くなるため、触媒の選択性の向上が必要になる。また、反応条件が高温になると、触媒上にカーボンが生成され易くなり、触媒が劣化し易くなる。また、脱水素反応は、前述の通り、低圧での反応が好ましい。そのため、圧力損失の少ない触媒が求められ、粒子径が大きい触媒が有利になる。触媒の粒子径が大きくなると、触媒内部へのガス拡散が低下するため、触媒に使用される白金の効率を考慮すると、エッグシェル型の触媒が有利になる。
　上記の背景から、本発明者らは白金担持アルミナ触媒の性能向上を鋭意検討した結果、エッグシェル型白金担持アルミナ触媒においてアルカリ金属以外の第２成分の添加によって触媒寿命を改善できることを見出した。
　従って、本発明の目的は、原料の触媒細孔内での拡散速度が遅い場合に有利なエッグシェル型白金担持アルミナ触媒において、触媒活性や選択性、特に触媒寿命を向上させることにある。
　また、本発明の他の目的は、このように触媒活性や選択性、特に触媒寿命において優れた性能を有するエッグシェル型白金担持アルミナ触媒の製造方法、及びその使用方法を提供することにある。
　本発明の一態様は、エッグシェル型白金担持アルミナ触媒であって、アルミナ担体と、前記アルミナ担体の外郭に分散して担持された白金と、バナジウム、クロム、モリブデン、及びリンの群から選ばれる１種又は２種以上の第２成分とを有する。この態様によれば、触媒寿命を向上させることができる。
　前記白金の含有量は、白金元素として０．０５ｗｔ％以上５．０ｗｔ％以下であるとよい。前記第２成分の含有量は、各元素として０．１ｗｔ％以上５．０ｗｔ％以下であるとよい。前記アルミナ担体は、表面積が１５０ｍ２／ｇ以上、細孔容積が０．４０ｃｍ３／ｇ以上、平均細孔径が４０Å以上３００Å以下、及び全細孔容積に対して平均細孔径±３０Å以下の細孔が占める割合が６０％以上であるとよい。
　また、本発明の他の態様は、エッグシェル型白金担持アルミナ触媒の製造方法であって、アルミナ担体にバナジウム、クロム、モリブデン、及びリンからなる群から選ばれる１種又は２種以上の成分からなる化合物の水溶液を含浸させ、その後に乾燥・焼成を行うステップと、焼成後の前記アルミナ担体にエッグシェル型に白金を担持させるステップと、白金を担持させた前記アルミナ担体を水素雰囲気にて還元するステップとを有する。
　また、本発明の他の態様は、エッグシェル型白金担持アルミナ触媒を用いて水素化芳香族類を脱水素化する水素化芳香族類の脱水素方法を提供する。前記水素化芳香族類は、単環芳香族類の水素化物、２環芳香族類の水素化物、及び３環以上の芳香環を有する化合物の水素化物からなる群から選ばれる１種又は２種以上の混合物であるとよい。また、前記水素化芳香族類は、メチルシクロヘキサン、シクロヘキサン、ジメチルシクロヘキサン、テトラリン、デカリン、メチルデカリン、ビフェニル、ジフェニルメチル、ジベンゾトリオール、テトラデカヒドロアントラセンからなる群から選ばれる１種又は２種以上の混合物であるとよい。
　前述のように、均一型触媒は原料の触媒内部までの拡散が十分に行われる場合に有効であり、エッグシェル型触媒は触媒内部までの拡散が制限されて十分に行われない場合に有効なことから、これらの２種類の触媒は反応場における拡散の状態によって使い分けることが好ましい。また、同じ反応でも反応器内の位置によって、原料の触媒内部への拡散状態が異なる場合があり、反応が進行した出口近くでは原料濃度が低くなることから、触媒内部への拡散が制限され得る。このような場合には、反応器において均一型とエッグシェル型の触媒を併用することが好ましい。
　また、一般に触媒内部への原料の拡散度合いは触媒有効係数で表されるが、触媒ペレットの大きさや形状を変えることで触媒有効係数を制御することが可能である。これらより、均一型とエッグシェル型の両タイプの触媒について、触媒ペレットの大きさや形状を変えることで、さまざまな触媒有効係数を有する白金アルミナ触媒の製造が可能となる。
　本発明のエッグシェル型白金担持アルミナ触媒において、白金及び第２成分を存在させるアルミナ担体は、細孔のサイズをできるだけ均一に制御したものが好ましい。具体的には、硫黄含有多孔性金属酸化物が表面積１５０ｍ２／ｇ以上、細孔容積０．４ｃｍ３／ｇ以上、平均細孔径４０Å以上３００Å以下、及び全細孔容積に対して平均細孔径±３０Åの細孔が占める割合が６０％以上である多孔性金属酸化物が好ましい。
　特許文献１は、表面積１５０ｍ２／ｇ以上、細孔容積０．５５ｃｍ３／ｇ以上、平均細孔径９０Å以上３００Å以下、及び全細孔容積に対して細孔径９０Å以上３００Å以下の細孔が占める割合が６０％以上である多孔性γ-アルミナ担体に、白金が担持されていることを特徴とする白金担持アルミナ触媒を開示している。この触媒は前述のように一般的なエッグシェル型の白金担持アルミナ触媒であり、特許文献１では、触媒寿命を向上させる手段としてアルカリ金属を添加した触媒についても開示している。アルミナを担体とした触媒を利用する場合は、白金粒子上で起こる分解反応を抑制しただけでは十分ではなく、アルミナ上の酸点で起こる分解反応の抑制も必要となる。従って、これらの酸点をカリウムやリチウム等のアルカリ金属を用いてマスキングすることでアルミナ表面での分解反応を抑制することが行われることが多い。この観点から、特許文献１では、エッグシェル型白金担持触媒において、白金が高い分散度で担持されることで白金上での分解を抑制するとともに、アルカリを添加することでアルミナ上の酸点のマスキングを行って、触媒寿命向上において顕著な効果を見出したものである。
　一方、特許文献２はアルミナ担体に硫黄を含有させることによって、担持される白金の分散形態が均一型になるとともに分解反応を抑制することで触媒寿命の向上を図る均一型白金担持アルミナ触媒を開示している。特許文献２の発明時点では、硫黄又は硫黄化合物を含有させたアルミナ担体を利用する場合、その上にアルカリ金属による酸点のマスキングを実施しない場合でもそれと同等以上の分解反応抑制効果があると考えられた。詳細なメカニズムは不明であるが、硫黄元素がアルミナと共に複合酸化物を形成し、アルミナ単独の場合に残留する酸点を異なる構造に変化させているものと考えられた。その際、硫黄元素がアルミナと複合酸化物を形成した場合の形態は、一般的に硫酸根形態であることが考えられた。
　本発明のエッグシェル型白金担持アルミナ触媒の製造において、第２成分添加工程が増えることはコストアップの要因となるが、本発明による触媒の長寿命化によるコストダウン効果は、触媒製造費用のコストアップに比べて極めて高く、反応器での触媒の利用方法によって脱水素触媒の交換寿命を従来の１～２年から３から４年に長期化することが可能である。
　本触媒は、代表的に脱水素触媒として利用されるが、熱交換型の反応器の触媒反応管に充填して利用される。触媒反応管の本数は一般的な熱交換器と同様に、大型の反応器では数千本になる場合もある。このような反応器で利用される白金担持アルミナ触媒は、その性能が一定の収率に低下した時である触媒寿命に達したときに、新しい触媒に交換するために抜き出される。抜き出された廃触媒からは白金が回収されて、次の交換用触媒の製造にリサイクル利用される。抜き出し作業には数日が必要であり、新触媒の充填にはそれ以上の作業日数が必要であるため、触媒交換に２週間程度が必要になる。その間、製造が止まるため、交換頻度の低減はコストダウンに大きく寄与する。すなわち、特許文献１及び特許文献２が開示している触媒の寿命は１～２年であるが、本発明によるアルカリ添加均一型白金担持アルミナ触媒の寿命は４年であり、触媒交換頻度を半数以下に低減することが可能となる。
　本発明のエッグシェル型白金担持アルミナ触媒は、エッグシェル型白金担持アルミナ触媒に比べて高い触媒性能を有しており、特に触媒寿命の観点で優れた触媒である。また、これらの触媒は、本発明の製造方法によれば、既存の触媒製造設備で容易に大量製造することができる。これらの触媒は既存の白金担持アルミナ触媒の代替として利用できるほか、水素貯蔵輸送技術の一つである有機ケミカルハイドライド法におけるメチルシクロヘキサン等の脱水素触媒として好適に利用することができる。
（Ａ）エッグシェル型の金属担持触媒、（Ｂ）均一型の金属担持触媒を示す説明図
　先ず、図１を用いて、本発明でいうエッグシェル型の金属担持触媒と均一型の金属担持触媒とを説明する。エッグシェル型の金属担持触媒とは、成形された触媒の断面において担持される金属種が断面の外殻部分にのみ分散担持されている状態を指す。すなわち、多孔性の担体１の外郭部分に金属種が担持された金属担持部分２が形成されている。均一型の金属担持触媒は、触媒の断面の全体亘って金属種が分散し、多孔性の担体１の成形体の内部全般にわたって金属種が担持された金属担持部分２が形成されている状態をいう。
　エッグシェル型白金担持アルミナ触媒は、アルミナ担体と、アルミナ担体の外郭に分散して担持された白金と、バナジウム、クロム、モリブデン、及びリンの群から選ばれる１種又は２種以上の第２成分を有する。
　次に本発明において利用されるアルミナ担体について説明する。アルミナ担体は、表面積が１５０ｍ２/ｇ以上、細孔容積が０．４０ｃｍ３/ｇ以上、平均細孔径が４０Å以上３００Å以下、及び全細孔容積に対して平均細孔径±３０Å以下の細孔が占める割合が６０％以上である。
　アルミナ担体は、多孔性γ-アルミナ担体であるとよい。アルミナ担体は、例えば特公平６－７２００５号公報に開示されているように、アルミニウム塩の中和により生成した水酸化アルミニウムのスラリーを濾過洗浄し、得られたアルミナヒドロゲルを脱水乾燥した後、４００℃以上８００℃以下で１～６時間程度焼成することにより得られる多孔性γ-アルミナ担体であるのがよく、より好ましくはアルミナヒドロゲルのｐＨ値をアルミナヒドロゲル溶解ｐＨ領域とベーマイトゲル沈殿ｐＨ領域との間で交互に変動させると共に少なくともいずれか一方のｐＨ領域から他方のｐＨ領域へのｐＨ変動に際してアルミナヒドロゲル形成物質を添加してアルミナヒドロゲルの結晶を成長させるｐＨスイング工程を経て得られた多孔性γ-アルミナ担体であるのがよい。このｐＨスイング工程を経て得られた多孔性γ-アルミナ担体は、細孔分布の均一性に優れ成形後のアルミナ担体ペレットにおいても物理性状のばらつきが少なく、個々のペレット毎の物理性状が安定しているという点で優れている。
　本発明において、上記のアルミナ担体に担持させる第２成分添加量は、０．１ｗｔ％以上５．０ｗｔ％以下、好ましくは０．３ｗｔ％以上３．０ｗｔ％以下、さらに好ましくは０．５ｗｔ％以上２．０ｗｔ％以下である。第２成分の担持量が０．１ｗｔ％より少ないと触媒寿命が短く効果が低いという問題があり、反対に、第２成分の担持量が５．０ｗｔ％より多くなると、活性が低下すると共に触媒寿命が短くなるという問題が生じる。
　上記のアルミナ担体に第２成分を添加させる際に用いる第２成分の化合物としては、第２成分元素の塩化物、臭化物、ヨウ化物、硝酸塩、硫酸塩、酢酸塩、プロピオン酸塩等を例示でき、好ましくは水溶性のもの及び／又はアセトン等の有機溶媒に可溶のものがよく、例えば、塩化バナジウム、臭化バナジウム、ヨウ化バナジウム、メタバナジン酸アンモニウム、塩化バナジル、硫酸バナジル、酸化バナジウムアセチルアセテート、塩化クロム、臭化クロム、ヨウ化クロム、硝酸クロム、硫酸クロム、酢酸クロム、プロピオン酸クロム、塩化モリブデン、臭化モリブデン、ヨウ化モリブデン、モリブデン酸塩類、リン酸、リン酸二水素アンモニウム等の無機リン酸塩、及び有機リン酸化合物等を挙げることができる。
　また、エッグシェル型白金担持アルミナ触媒に第２成分元素を添加する際には、第２成分元素化合物の溶液を含浸させた後、室温以上２００℃以下及び０．５時間以上４８時間以下、好ましくは５０℃以上１５０℃以下及び０．５時間以上２４時間以下、より好ましくは８０℃以上１２０℃以下及び０．５時間以上５時間以下の乾燥条件で乾燥した後、３５０℃以上６００℃以下及び０．５時間以上４８時間以下、より好ましくは３５０℃以上４５０℃以下及び０．５時間以上５時間以下の条件で焼成するのがよい。
　本発明において、上記の第２成分を担持したアルミナ担体に担持させる白金の担持量は、０．０５ｗｔ％以上５．０ｗｔ％以下、好ましくは０．１ｗｔ％以上３．０ｗｔ％以下である。この白金の担持量が０．０５ｗｔ％より少ないと活性が低いという問題があり、反対に、５．０ｗｔ％より多くなると白金の粒子径が大きくなり、選択性が低下すると共にシンタリングし易くて劣化し易いという問題が生じる。
　本発明において、アルミナ担体に白金金属を担持させる場合、上記のアルミナ担体に白金化合物の溶液を含浸させ、乾燥したのち所定の温度で焼成すればよい。白金化合物は、白金の塩化物、臭化物、アンモニウム塩、カルボニル化合物、アミン及びアンミン錯体やアセチルアセトナト錯体等の各種の錯体化合物等を挙げることができる。白金化合物は、例えば、塩化白金酸、アセチルアセトナト白金、白金酸アンモニウム塩、臭化白金酸、二塩化白金、四塩化白金水和物、二塩化カルボニル白金二塩化物、ジニトロジアミン白金酸塩等の白金化合物が挙げられる。
　アルミナ担体に上記の白金化合物の溶液を含浸させた後は、白金化合物が付着したアルミナ担体を５０℃以上２００℃以下及び０．５時間以上４８時間以下の条件で乾燥した後、３５０℃以上６００℃以下及び０．５時間以上４８時間以下、より好ましくは３５０℃以上４５０℃以下及び０．５時間以上５時間以下の条件で焼成する。次いで、焼成したアルミナ担体を水素ガスの雰囲気下に、３５０℃以上６００℃以下及び０．５時間以上４８時間以下、好ましくは３５０℃以上５５０℃以下及び３時間以上２４時間以下の還元条件で水素還元処理を行う。この水素還元時の温度が３５０℃未満であると十分に白金が還元されないという問題があり、反対に、６００℃を超えると還元時に白金粒子がシンタリングして金属分散度が低下するという問題が生じる。
　エッグシェル型白金担持アルミナ触媒の製造方法は、アルミナ担体にバナジウム、クロム、モリブデン、及びリンからなる群から選ばれる１種又は２種以上の成分からなる化合物の水溶液を含浸させ、その後に乾燥・焼成を行うステップと、焼成後の前記アルミナ担体にエッグシェル型に白金を担持させるステップと、白金を担持させた前記アルミナ担体を水素雰囲気にて還元するステップとを有する。
　有機ケミカルハイドライド法システムの脱水素触媒のコストダウンでは、触媒の長寿命化の次に硫黄を利用しないことによる工程の簡素化が考えられる。発明者らは、硫黄を利用せずに同等の触媒寿命を得られる脱水素触媒について、鋭意検討した結果、アルカリ金属や硫黄に替えて白金以外の第２成分としてバナジウム、クロム、モリブデン、リンから選ばれる成分を添加することによって、同等の効果が得られることを見出して本発明を完成させるに至った。
　特許文献１は、アルミナ担体の物理性状が表面積１５０ｍ２／ｇ以上、細孔容積０．４０ｃｍ３／ｇ以上、平均細孔径４０Å以上３００Å以下、及び全細孔容積に対して平均細孔径±３０Å以下の細孔が占める割合が６０％以上のアルミナ担体に、白金元素として０．１以上３ｗｔ％以下の白金が担体断面の外郭に分散して担持されているエッグシェル型白金担持アルミナ触媒とこれにアルカリ金属を添加した触媒について開示している。
　すなわち、本発明は特許文献１に開示されているエッグシェル型白金担持アルミナ触媒にアルカリ金属ではなく、白金以外の第２成分としてバナジウム、クロム、モリブデン、リンから選ばれる成分を添加することによって、アルカリ金属添加エッグシェル型白金担持アルミナ触媒に比べて、優れた触媒性能、特に触媒寿命性能に優れていることを見出して本発明を完成させたものである。
　本発明のエッグシェル型白金担持アルミナ触媒は、例えば水素エネルギーの貯蔵輸送方法の一つである有機ケミカルハイドライド法において水素エネルギーキャリアとして利用される水素化芳香族類の脱水素触媒として使用される。水素化芳香族類は、単環芳香族類の水素化物、２環芳香族類の水素化物、及び３環以上の芳香環を有する化合物の水素化物からなる群から選ばれる１種又は２種以上の混合物であるとよい。また、水素化芳香族類は、メチルシクロヘキサン、シクロヘキサン、ジメチルシクロヘキサン、テトラリン、デカリン、メチルデカリン、ビフェニル、ジフェニルメチル、ジベンゾトリオール、テトラデカヒドロアントラセンからなる群から選ばれる１種又は２種以上の混合物であるとよい。
　白金担持アルミナ触媒を有機ケミカルハイドライド法におけるメチルシクロヘキサン等の水素化芳香族類の脱水素反応に供する場合、反応時間の経過とともに、徐々に性能が低下する触媒劣化が観察される。触媒劣化の要因はコーキングと呼ばれる炭素析出である。コーキングは、主としてメチルシクロヘキサン等の原料化合物の分解反応によって活性金属の白金金属の表面に炭素析出が起こり、その結果、活性金属の有効な活性点が覆われて機能しなくなる現象である。
　触媒反応の劣化現象は、反応試験おける転化率の低下として観察され、水素化芳香族類の脱水素反応の場合、直線的に転化率が低下する現象として観察されることが判明している。これより、反応試験における転化率の経時変化において、その低下の傾きによって、触媒寿命の相対的な優劣を評価することができる。更に、実際の反応条件ではなく、短時間での触媒寿命評価を目的とした加速反応試験においても直線的に低下することから、触媒寿命の評価が可能である。
　水素は１９７０年代からクリーンな二次エネルギーとして注目され、日本国では、１９７４年～１９９２年のサンシャイン計画、１９７８～１９９２年のムーンライト計画、１９９３年～２００１年のニューサンシャイン計画において水素製造技術や燃料電池の研究開発が進められた。水素の大規模貯蔵輸送技術は、１９９２年～２００２年のWE-NET計画において液化水素法の開発が開始されている。一方、有機ケミカルハイドライド法の開発の歴史は古く、１９８０年代にカナダのケベック州政府と欧州１２か国による国際研究開発プロジェクトとして実施されたユーロケベック計画にさかのぼる。この計画は、ケベック州に豊富に存在する余剰の水力電力を利用して水の電気分解を行って水素を製造し、大西洋を輸送して欧州で利用する計画であった。水素の輸送方法としては、第１候補として液体水素法、第２候補として液体アンモニア法、第３候補として有機ケミカルハイドライド法が検討されている。当時、有機ケミカルハイドライド法はMCH法と呼ばれていた。ユーロケベック計画は１９９２年ごろまで約１０年間のプロジェクトが遂行されたが、いずれの方法も実用化には至らずに計画は終了しており、以来、水素を大規模に貯蔵輸送する技術は実用化されていない。
　日本国では、１９９２年～２００２年に実施されたWE-NETプロジェクトにおいて、液化水素法の開発が進められる一方、有機ケミカルハイドライド法の研究は日本の大学を中心に進められていた。出願人は、２００２年から脱水素触媒の開発に着手後、初めての学術発表を２００４年に横浜で開催された世界水素会議で発表を行っているが、この時期から企業での研究開発例が発表されるようになり、現時点で大規模向けの水素貯蔵輸送技術の研究開発で実証レベルまで進められている技術は、液化水素法と出願人が提案する有機ケミカルハイドライド法のみである。
　有機ケミカルハイドライド法（OCH法：Organic Chemical Hydride Method）は、水素をトルエン(ＴＯＬ)などの芳香族と水素化反応させて、分子内に水素を取り込んだメチルシクロヘキサン(ＭＣＨ)などの飽和環状化合物に転換することで、常温・常圧の液体状態で「貯める」「運ぶ」を行い、利用場所で必要量の水素を脱水素反応で取り出して利用する方法であり、水素とトルエンを反応させる水素化反応（水素貯蔵反応）とＭＣＨから水素を発生させてトルエンを回収する脱水素反応（水素発生反応）からなる。水素を取り出した後に生成するＴＯＬは水素の入れ物（キャリア）として回収、繰り返し利用する。
　水素は爆発性の気体のため、水素のままの大規模に貯蔵輸送する場合は潜在的なリスクの高い物質である。本法ではガソリンや軽油の成分で常温・常圧の液体状態のＭＣＨの分子内に水素を取り込んで貯蔵輸送を行うため原理的に安全性が高い方法である。具体的には、本システムのタンクや反応器が火災に巻き込まれた場合でも、従来の製油所火災と同様であり、周辺の市街地に甚大な被害を与える可能性は極めて低いと考えられる。「事故は必ず起こる」の考え方は安全対策に非常に重要であり、原理的な安全が求められる所以である。
　この方法では、１ＬのＭＣＨの液体に、約５３０Ｌの水素ガスを貯蔵することができる。水素ガスの体積を物理的に１／５００以下に減容するには５００気圧以上に圧縮するか、－２５３℃以下に冷却して１／８００の体積の液体水素にする必要があるが、本法では、化学反応を利用することで常温・常圧下で１／５００の体積減容が可能である。また、ＴＯＬとＭＣＨは－９５℃以上１０１℃以下の広い温度範囲で液体状態のため、地球上のあらゆる環境下で水のような液体としてハンドリングすることが可能である。大規模なサプライチェーンの構築には、数十万トン単位のＴＯＬの調達が必要であるが、ＴＯＬはハイオクガソリンに１０ｗｔ％以上含まれている燃料基材であるほか、工業溶剤としても多く利用されており、年間２，０００万トン以上が世界で生産されている汎用化学品のため大量調達も容易である。
　上記より、水素を大規模に貯蔵輸送する際の潜在的なリスクを従来のガソリンの貯蔵輸送レベルの危険性にまで原理的に低減できる安全性が高い方法であることが本法の第一の特徴であり、出願人がこの方法に着目した第一の理由である。また、ＴＯＬ、ＭＣＨの大型タンクによる貯蔵や、ケミカルタンカー、ケミカルローリーによる輸送は古くから化学品として実用化されている。今後の自動車の電動化の潮流によって、ガソリンや軽油の自動車燃料の需要は減少が予想されており、これらの貯蔵タンク等の既存インフラの転用が可能なことも大きなメリットである。
　更に、将来に水素が発電燃料として大規模に利用されるようになった場合、現在の石油備蓄のように水素燃料の備蓄が必要になる時代が予想される。ＴＯＬやＭＣＨは長期間大規模に貯蔵しても化学的に変化することはなく、長期貯蔵に際して特段のエネルギー消費やロスを伴わないことから、現行の石油備蓄基地のタンクにＭＣＨを貯蔵することで、水素エネルギーの備蓄基地に転換することも可能である。
　出願人は、安全性が最も高く既存のインフラを転用できることからコスト的にも有利な有機ケミカルハイドライド法に着目して、２００２年から実用化の鍵である新規な脱水素触媒の開発に着手し、世界で初めて有機ケミカルハイドライド法に工業的に適用可能な新規脱水素触媒の開発に成功した。その後、システム全体の技術確立を目的として、脱水素プロセスに開発された触媒を利用するとともに、水素貯蔵反応となるトルエンの水素化プロセスと組み合わせて、同じ場所で水素貯蔵と水素発生を連続的に繰り返す実証デモプラントを２０１３年に建設して同年４月から２０１４年１１月までに延べ約１０，０００時間の実証運転を行い、設計通りの高い性能を安定に維持できることが確認されて技術確立を完了している。
　その後、開発の最終段階として、実際に約２００トンの水素を本システムによって東南アジアのブルネイ国から日本の川崎市臨海部に輸送する世界に先駆けた国際間水素サプライチェーン実証がＮＥＤＯ（新エネルギー・産業技術総合開発機構）のプロジェクトとして２０２０年度に実施される予定である。
　日本国は水素エネルギーの実用化と普及を国策として進める方針を震災後の第４次エネルギー基本計画から盛り込んでおり、水素・燃料電池技術ロードマップの策定に続いて２０１７年に水素基本戦略を閣議決定している。上記の有機ケミカルハイドライド法は水素エネルギーを大規模に「貯める」「運ぶ」を行う水素エネルギーキャリアとして、水素基本戦略にその実用化が盛り込まれており、２０３０年までに水素供給価格目標として３０￥／Ｎｍ３、２０５０年目標として２０￥／Ｎｍ３が掲げられている。これより、継続的な改良技術開発によるコストダウンが求められており、触媒の性能向上はコストダウンの重要な要素であることから、本発明は有機ケミカルハイドライド法の実用化に際して有効であり産業上の利用性が高い発明である。
　エッグシェル型白金担持アルミナ触媒は、触媒の用途のみではなく、吸着剤等としても有効に利用することができる。有機ケミカルハイドライド法への適用を始めとする本発明の触媒が適用できる触媒反応プロセスに不純物等を吸着する前処理等を目的としたガードカラムの充填物としても有用である。
　本実施形態に係るエッグシェル型白金担持アルミナ触媒は、均一型アルカリ添加白金担持アルミナ触媒と共に使用されてもよい。均一型アルカリ添加白金担持アルミナ触媒は、アルミナ担体と、アルミナ担体の断面全体に亘って分散した硫黄又は硫黄化合物と、アルミナ担体の断面全体に亘って分散して担持された白金と、ナトリウム、カリウム、及びカルシウムの群から選ばれる１種又は２種以上のアルカリ金属を有するとよい。アルミナ担体は、表面積が１５０ｍ２/ｇ以上、細孔容積が０．４０ｃｍ３/ｇ以上、平均細孔径が４０Å以上３００Å以下、及び全細孔容積に対して平均細孔径±３０Å以下の細孔が占める割合が６０％以上であるとよい。担体に含有せしめる硫黄の量は、硫黄分として０．１５ｗｔ％以上５ｗｔ％以下が好ましく、更に好ましくは０．１５ｗｔ％以上３．０ｗｔ％以下が好ましい。最も好適な硫黄含有量の範囲は０．１５ｗｔ％以上３．０ｗｔ％以下である。白金の担持量は、０．０５ｗｔ％以上５．０ｗｔ％以下、好ましくは０．１ｗｔ％以上３．０ｗｔ％以下であるとよい。アルカリ添加量は、０．１ｗｔ％以上５ｗｔ％以下、好ましくは０．３ｗｔ％以上３．０ｗｔ％以下、更に好ましくは０．５ｗｔ％以上１．５ｗｔ％以下であるとよい。均一型白金担持アルミナ触媒にアルカリ性金属を担持させる際に用いるアルカリ性金属の化合物としては、アルカリ性金属の塩化物、臭化物、ヨウ化物、硝酸塩、硫酸塩、酢酸塩、プロピオン酸塩等を例示でき、好ましくは水溶性のもの及び／又はアセトン等の有機溶媒に可溶のものがよく、例えば、塩化ナトリウム、臭化ナトリウム、ヨウ化ナトリウム、硝酸ナトリウム、硫酸ナトリウム、酢酸ナトリウム、プロピオン酸ナトリウム、塩化カリウム、臭化カリウム、ヨウ化カリウム、硝酸カリウム、硫酸カリウム、酢酸カリウム、プロピオン酸カリウム、塩化カルシウム、臭化カルシウム、ヨウ化カルシウム、硝酸カルシウム、硫酸カルシウム、酢酸カルシウム、プロピオン酸カルシウム等を挙げることができる。
　エッグシェル型白金担持アルミナ触媒と、均一型アルカリ添加白金担持アルミナ触媒とは、同一の反応器に充填されとよい。エッグシェル型白金担持アルミナ触媒と、均一型アルカリ添加白金担持アルミナ触媒とは直列に配置されてもよく、互いに混合して配置されてもよい。
　このように、エッグシェル型白金担持アルミナ触媒は、水素エネルギーキャリアとして利用されるメチルシクロヘキサン等の水素化芳香族類の脱水素反応に好適に利用でき、有機ケミカルハイドライド法水素貯蔵輸送システムの実用化に資するほか、白金担持アルミナ触媒が利用されている既存の触媒反応プロセスに広く適用できる可能性があり、産業上の利用性が非常に高い。
　以下、実施例及び比較例に基づいて、本発明の好適な実施の形態を具体的に説明する。
　［担体調製］
　熱希硫酸中に激しく撹拌しながら瞬時にアルミン酸ソーダ水溶液を加えることにより水酸化アルミニウムスラリーの懸濁液（ｐＨ１０）を得、これを種子水酸化アルミニウムとして、撹拌を続けながら熱希硫酸とアルミン酸ソーダ水溶液を交互に一定時間おいて加える操作を繰り返し、ろ過洗浄ケーキを得、これを押し出し成形して乾燥した後、５００℃で３時間焼成した。このようにして得られたアルミナ担体は、ＢＥＴ表面積２５７ｍ２／ｇ、水銀圧入法による細孔容積０．６６ｃｍ３／ｇ、平均細孔径９．３ｎｍであり、ほとんどの細孔が平均細孔径付近に集中したシャープな細孔分布を有しており、７－１３ｎｍの細孔径を有する細孔が占める容積は全細孔容積の８５％以上であり、この結果から得られた多孔性γ－アルミナ担体は、表面積が１５０ｍ２／ｇ以上、細孔容積が０．４０ｃｍ３／ｇ以上、平均細孔径が４０Å以上３００Å以下、及び全細孔容積に対して平均細孔径±３０Åの細孔が占める割合が６０％以上の要件を満たしている。
　［比較例１（触媒Ｎｏ．１）］
　実施例と比較する目的で比較例１に係るエッグシェル型白金担持アルミナ触媒（触媒Ｎｏ．１）を製造した。上記のように調製した多孔性γ-アルミナ担体２０ｇに、ｐＨ値が２．０になるように調製した０．０２６ｍｏｌ／Ｌの塩化白金酸水溶液４０ｍＬを添加し、３時間放置して含浸させた後、エバポレーターにより水を除去し、次いで１２０℃で３時間乾燥させてからマッフル炉により空気流通下に４５０℃で３時間焼成して、１ｗｔ％の白金を担持したエッグシェル型白金担持アルミナ触媒（触媒Ｎｏ．１）を調製した。
　［比較例２（触媒Ｎｏ．２）］
　比較例１と同様に調製して得られたエッグシェル型白金担持アルミナ触媒２０ｇに、０．０８５ｍｏｌ／Ｌの硝酸ナトリウム（Ｎａ）水溶液４０ｍＬを添加し、３時間放置して含浸させた後、エバポレーターにより水を除去した。次いで１２０℃で３時間乾燥させてからマッフル炉により空気流通下に４５０℃で３時間焼成して、０．８ｗｔ％のナトリウム（Ｎａ）と１ｗｔ％の白金とを担持したエッグシェル型アルカリ添加白金担持アルミナ触媒（触媒Ｎｏ．２）を得た。比較例２に係るエッグシェル型アルカリ添加白金担持アルミナ触媒は、上記の特許文献１に記載された触媒に相当する。
　［比較例３（触媒Ｎｏ．３）］
　前述の方法で調整した多孔性γ－アルミナ担体２０ｇに、濃度０．１６ｍｏｌ／Ｌの硫酸アンモニウム水溶液４０ｍＬを添加し、３時間放置して含浸させた後、エバポレーターにより水を除去した。次いで、１２０℃で３時間乾燥させてからマッフル炉により空気流通下に５００℃で３時間焼成して硫黄分を含むアルミナ担体を得た。このようにして調製した硫黄分を含むアルミナ担体２０ｇにｐＨ＝２．０に調製した濃度０．０２６ｍｏｌ／Ｌの塩化白金酸水溶液４０ｍＬを添加し、焼成後の白金担持量が１．０ｗｔ％となるように含浸させた後、エバポレーターにて水分を除去した。次いで１２０℃で３時間乾燥させてからマッフル炉により空気流通下に４５０℃で３時間焼成して、硫黄分１．０ｗｔ％を含み、１．０ｗｔ％の白金を分散担持した均一型硫黄－白金担持アルミナ触媒（触媒Ｎｏ．３）を得た。この方法は、特許文献２の実施例３に記載された調製方法に準じている。
　［比較例４（触媒Ｎｏ．４）］
　比較例３と同じ方法で調整した硫黄分を含むアルミナ担体２０ｇに、濃度０．１８ｍｏｌ／Ｌのジニトロジアミン白金水溶液５．６ｍLを用いて焼成後の白金担持量が１．０ｗｔ％となるように含浸させた後、エバポレーターにて水分を除去した。次いで１２０℃で３時間乾燥させてからマッフル炉により空気流通下に４５０℃で３時間焼成して、硫黄分１．０ｗｔ％を含み、１．０ｗｔ％の白金をエッグシェル型に担持したエッグシェル型硫黄－白金担持アルミナ触媒を得た。このようにして調製したエッグシェル型硫黄－白金担持アルミナ触媒２０ｇに、０．１７ｍｏｌ／Ｌの硝酸ナトリウム（Ｎａ）水溶液４０ｍＬを添加し、３時間放置して含浸させた後、エバポレーターにより水を除去した。次いで１２０℃で３時間乾燥させてからマッフル炉により空気流通下に４５０℃で３時間焼成して、０．８ｗｔ％のナトリウム（Ｎａ）と１ｗｔ％の白金とを担持したエッグシェル型アルカリ添加硫黄－白金担持アルミナ触媒（触媒Ｎｏ．４）を得た。
　［実施例１（触媒Ｎｏ．５）］
　担体調製にて記載した方法で調製した多孔性γ－アルミナ担体２０ｇに、０．１２ｍｏｌ／Ｌのメタバナジン酸アンモニウムに同重量のシュウ酸を加えて溶解させた水溶液を３３．２ｍL用いて含浸し、３時間放置した後、エバポレーターにより水を除去した。次いで、１２０℃で３時間乾燥させてからマッフル炉により空気流通下に５００℃で３時間焼成して、第二成分としてバナジウム（Ｖ）を１．２ｗｔ％含むアルミナ担体を得た。このようにして調製したバナジウムを含むアルミナ担体を用い、比較例４（触媒Ｎｏ．４）と同様の方法でジニトロジアミン白金水溶液を用いて白金担持を行い、１．２ｗｔ％のバナジウムと１．０ｗｔ％の白金とを担持したエッグシェル型バナジウム添加白金担持アルミナ触媒（触媒Ｎｏ．５）を得た。
　［実施例２（触媒Ｎｏ．６）］
　担体調製にて記載した方法で調製した多孔性γ－アルミナ担体２０ｇに、０．１２ｍｏｌ／Ｌの硝酸クロム水溶液を３２．０ｍＬ用いて含浸し、３時間放置した後、エバポレーターにより水を除去した。次いで、１２０℃で３時間乾燥させてからマッフル炉により空気流通下に５００℃で３時間焼成して、第二成分としてクロム（Ｃｒ）を１．２ｗｔ％含むアルミナ担体を得た。このようにして調製したクロムを含むアルミナ担体を用い、比較例４（触媒Ｎｏ．４）と同様の方法でジニトロジアミン白金水溶液を用いて白金担持を行い、１．２ｗｔ％のクロムと１．０ｗｔ％の白金とを担持したエッグシェル型クロム添加白金担持アルミナ触媒（触媒Ｎｏ．６）を得た。
　［実施例３（触媒Ｎｏ．７）］
　担体調製にて記載した方法で調製した多孔性γ－アルミナ担体２０ｇに、０．００９ｍｏｌ／Ｌのモリブデン酸アンモニウム水溶液を３２．０ｍＬ用いて含浸し、３時間放置した後、エバポレーターにより水を除去した。次いで、１２０℃で３時間乾燥させてからマッフル炉により空気流通下に５００℃で３時間焼成して、第二成分としてモリブデン（Ｍｏ）を１．３ｗｔ％含むアルミナ担体を得た。このようにして調製したモリブデンを含むアルミナ担体を用い、比較例４（触媒Ｎｏ．４）と同様の方法でジニトロジアミン白金水溶液を用いて白金担持を行い、１．３ｗｔ％のモリブデンと１．０ｗｔ％の白金とを担持したエッグシェル型モリブデン添加白金担持アルミナ触媒（触媒Ｎｏ．７）を得た。
　［実施例４（触媒Ｎｏ．８）］
　担体調製にて記載した方法で調製した多孔性γ－アルミナ担体２０ｇに、０．２０ｍｏｌ／Ｌのリン酸二水素アンモニウム水溶液を３２．０ｍＬ用いて含浸し、３時間放置した後、エバポレーターにより水を除去した。次いで、１２０℃で３時間乾燥させてからマッフル炉により空気流通下に５００℃で３時間焼成して、第二成分としてリン（Ｐ）を０．９ｗｔ％含むアルミナ担体を得た。このようにして調製したリンを含むアルミナ担体を用い、比較例４（触媒Ｎｏ．４）と同様の方法でジニトロジアミン白金水溶液を用いて白金担持を行い、０．９ｗｔ％のリンと１．０ｗｔ％の白金とを担持したエッグシェル型リン添加白金担持アルミナ触媒（触媒Ｎｏ．８）を得た。
　［実施例５、６（触媒Ｎｏ．９、１０）］
　実施例１と同様の方法で、メタバナジン酸アンモニウム水溶液の濃度を変更して、第二成分としてバナジウム（Ｖ）が０．５ｗｔ％と２．０ｗｔ％含むアルミナ担体を調製し、その後、同様の方法で白金を担持して、０．５ｗｔ％のバナジウムと１．０ｗｔ％の白金を担持した、エッグシェル型バナジウム添加白金担持アルミナ触媒（触媒Ｎｏ．９）、２．０ｗｔ％のバナジウムと１．０ｗｔ％の白金とを担持したエッグシェル型バナジウム添加白金担持アルミナ触媒（触媒Ｎｏ．１０）を得た。
　［実施例７（触媒Ｎｏ．１１）］
　実施例１と同様の方法で、メタバナジン酸アンモニウム水溶液の濃度を変更して、第二成分としてバナジウム（Ｖ）が０．５ｗｔ％含むアルミナ担体を調製し、その後、同様の方法でジニトロジアミン白金水溶液の濃度を調整し、０．５ｗｔ％のバナジウムと０．５ｗｔ％の白金とを担持したエッグシェル型バナジウム添加白金担持アルミナ触媒（触媒Ｎｏ．１１）を得た。
　［実施例８－１０（触媒Ｎｏ．１２－１４）］
　実施例２と同様の方法で、硝酸クロム水溶液の濃度を変更して、第二成分としてクロム（Ｃｒ）が０．５ｗｔ％、２．０ｗｔ％、３．０ｗｔ％含むアルミナ担体を調製し、その後、同様の方法で白金を担持して、０．５ｗｔ％のクロムと１．０ｗｔ％の白金とを担持したエッグシェル型クロム添加白金担持アルミナ触媒（触媒Ｎｏ．１２）、２．０ｗｔ％のクロムと１．０ｗｔ％の白金とを担持したエッグシェル型クロム添加白金担持アルミナ触媒（触媒Ｎｏ．１３）、及び３．０ｗｔ％のクロムと１．０ｗｔ％の白金とを担持したエッグシェル型クロム添加白金担持アルミナ触媒（触媒Ｎｏ．１４）を得た。
　［実施例１１、１２（触媒Ｎｏ．１５、１６）］
　実施例３と同様の方法で、モリブデン酸アンモニウム水溶液の濃度を変更して、第二成分としてモリブデン（Ｍｏ）が０．５ｗｔ％、２．０ｗｔ％含むアルミナ担体を調製し、その後、同様の方法で白金を担持して、０．５ｗｔ％のモリブデンと１．０ｗｔ％の白金とを担持したエッグシェル型モリブデン添加白金担持アルミナ触媒（触媒Ｎｏ．１５）、２．０ｗｔ％のモリブデンと１．０ｗｔ％の白金とを担持したエッグシェル型モリブデン添加白金担持アルミナ触媒（触媒Ｎｏ．１６）を得た。
　（加速反応試験）
　次に、上記の比較例１～４（触媒Ｎｏ．１～４）及び実施例１～１２（触媒Ｎｏ．５～１６）を用いた反応試験を実施した。反応試験は比較的に短時間で性能の差が得られるよう加速条件で実施した。反応管断面の中心に外形１／８インチの熱電対用保護管を備えた内径１２．６ｍｍ×３００ｍｍサイズのステンレス製反応管の長さ方向の中心部に、１．３ｇの各触媒をα－アルミナビーズ１１．７ｇで希釈して充填した。触媒の上側に予熱層として外径１ｍｍの球状α－アルミナビーズを充填した。その後、触媒層温度を３８０℃に昇温して、水素気流下で１５時間の前処理還元を行った。前処理還元終了後、触媒層入口温度を４００℃、触媒層出口温度が４１０℃、圧力０．３ＭＰａに設定し、前処理還元として供給した水素ガスを止め、ヒーターで蒸発させたメチルシクロヘキサン（ＭＣＨ）ガスを２．９Ｌ／ｈ（ＬＨＳＶ：８ｈ－１）の流量で反応器に供給した。反応管の出口側には、反応器から出たガスを冷却する冷却器を設け、ステンレス製の容器に回収して、液化したトルエン（ＴＯＬ）等の液状生成物と水素ガス等の気体を気液分離した。回収された液状生成物と気体を各々ガスクロマトグラフィで組成分析を行って、反応開始から１４０時間後までのＭＣＨ転化率（％）とＴＯＬ選択率（％）とを算出した。また、反応試験後の触媒を抜き出し、触媒劣化要因であるカーボン生成量を炭素・硫黄分析装置により測定した。
　（触媒寿命試験）
　次に上記の比較例３（触媒Ｎｏ．３）及び実施例１（触媒Ｎｏ．５）を用いて次の要領で長時間の反応試験を実施した。反応管断面の中心に外形１／４インチの熱電対用保護管を備えた内径２１．２ｍｍ×８１６ｍｍサイズのステンレス製反応管の長さ方向の中心部に、各触媒８．５ｇを外径５ｍｍの球状α-アルミナビーズ１２９ｇで希釈して充填した。触媒の上側に予熱層として外径１ｍｍの球状α-アルミナビーズを充填した。触媒層温度を３８０℃に設定し、水素気流下で１５時間の条件で前処理還元を行った。前処理還元終了後、触媒層入口温度２８０℃、触媒層出口温度３８０℃、反応圧力０．５５ＭＰａに設定し、ＭＣＨガスを２．８Ｌ／ｈ（ＬＨＳＶ：２．６ｈ－１）の流量で反応器に供給した。反応管の出口側には、反応器から出たガスを冷却する冷却器を設け、ステンレス製の容器に回収して、液化したトルエン等の液状生成物と水素ガス等の気体を気液分離した。回収された液状生成物と気体を各々ガスクロマトグラフィで組成分析を行って、反応開始から１４００時間後までのＭＣＨ転化率（％）とＴＯＬ選択率（％）を算出した。
　上記の加速反応試験の結果を表１～表４、触媒寿命試験の結果を表５に示す。
Figure JPOXMLDOC01-appb-T000001
　表１から、比較例１（触媒Ｎｏ．１）の白金が担体の外郭部のみに分散担持されたエッグシェル型白金担持アルミナ触媒と、比較例２（触媒Ｎｏ．２）のエッグシェル型アルカリ添加白金担持アルミナ触媒とに比べて、比較例３（触媒Ｎｏ．３）の硫黄がアルミナ担体の全体に分散担持され、かつ白金がアルミナ担体の全体に分散担持された均一型硫黄－白金担持アルミナ触媒の方が、加速反応試験の初期及び１４０時間反応後におけるＭＣＨ転化率（９８．７％→９５．０％）及びＴＯＬ選択率が共に高い値であり、触媒の安定性、選択性に優れていることがわかる。
　このように、比較例３の均一型硫黄―白金担持アルミナ触媒は優れた触媒性能を示すが、反応試験後のカーボン生成量が２．６ｗｔ％であり、比較例２（触媒Ｎｏ．２）のエッグシェル型アルカリ添加白金担持アルミナ触媒よりも増加していることがわかる。この結果から、比較例３の触媒では触媒成分である白金が、担体上に均一に分散されることで分散性が向上し、反応に有効な多数の活性点を持つため、カーボン析出量が増加しても、依然として反応に有効な活性点を保持していることが推測される。
　同様に表１から、実施例１～４（実施例1：バナジウム、実施例２：クロム、実施例３：モリブデン、実施例４：リン）のいずれも、反応開始２０時間後のＭＣＨ転化率が比較例３と同等以上であり、１４０時間後におけるＭＣＨ転化率は比較例３以上の値を維持しており、比較例３と比べて安定性に優れた触媒であることがわかる。また、ＴＯＬ選択率も９９．９％と比較例３よりも向上し、かつ、反応試験後のカーボン生成量が０．７％～１．４％と比較例３の２．６ｗｔ％に比べて、１／３～１／２程度に低減されることがわかる。ＴＯＬ選択率の向上は数値として０．１％の違いではあるが、不純物生成量は以下の式で計算されるため、ＴＯＬ選択率が９９．８％から９９．９％に向上することで、不純物生成量が半分程度に抑制されることを意味している。
不純物生成量＝ＭＣＨ供給量×ＭＣＨ転化率／１００×（１００－ＴＯＬ選択率）／１００
　実施例１～４のエッグシェル型白金担持アルミナ触媒は、比較例４の硫黄及びナトリウムが添加されたエッグシェル型白金担持アルミナ触媒と比べてもＭＣＨ転化率及びＴＯＬ選択率において、高い値を示すことがわかる。これらから、エッグシェル型白金担持アルミナ触媒の添加剤は、アルカリ金属であるナトリウムよりも、バナジウム、クロム、モリブデン、又はリンの方がＭＣＨ転化率及びＴＯＬ選択率が向上することがわかる。
Figure JPOXMLDOC01-appb-T000002
　バナジウムの担持量の影響を評価した表２から、バナジウム担持量を２．０ｗｔ％（実施例６）程度まで増加させると、ＭＣＨ転化率の低下が生じ始めることがわかる。一方、カーボン生成量については、０．５ｗｔ％（実施例５）よりも多いバナジウムを担持していれば大きな影響はない結果となっている。
　また、表２からバナジウムと白金の重量比率を１：１に維持し、かつ白金量を０．５ｗｔ％に低減した実施例７は、２０時間後、１４０時間後のＭＣＨ転化率が比較例３（表１参照）よりも高いことがわかる。これにより、第二金属成分を添加したエッグシェル型白金担持アルミナ触媒を採用することで、反応に有効な触媒外周部の白金量を増加させ、高価な白金の担持量を低下させることが可能となることが示されている。
Figure JPOXMLDOC01-appb-T000003
　クロムの担持量の影響を評価した表３から、クロム担持量の３．０ｗｔ％程度まで増加させると、ＭＣＨ転化率の低下が生じ始めることがわかる。クロムの場合、０．５ｗｔ％の担持量ではＴＯＬ選択率が比較例３と同等程度であり、１．０ｗｔ％以上の担持が選択率向上の点では有効であることがわかる。一方、カーボン生成量については、０．５ｗｔ％よりも多いクロム担持量であれば大きな影響はない結果が示された。
Figure JPOXMLDOC01-appb-T000004
　モリブデンの担持量の影響を評価した表４から、モリブデン担持量が０．５ｗｔ％と２．０ｗｔ％とである場合は、モリブデン担持量が１．３ｗｔ％である場合に比べて、ＭＣＨ転化率が若干低く、モリブデン担持量が１．０ｗｔ％以上である場合に、最も良いＭＣＨ転化率と安定性とが示された。
　実施例１～１２の加速試験結果から、比較的ＭＣＨ転化率が高く安定に推移し、かつ、カーボン生成量の少ない実施例１（触媒Ｎｏ．５，バナジウム１．２ｗｔ％）と、比較例３について、触媒寿命試験を実施した結果を表５に示す。
Figure JPOXMLDOC01-appb-T000005
　表５より、第二成分を添加した実施例１（触媒Ｎｏ．５）のエッグシェル型白金担持アルミナ触媒は反応開始５０時間後から反応開始１２００時間後にかけてＭＣＨ転化率が０．４％しか低下しないのに対して、比較例３（触媒Ｎｏ．３）の均一型白金担持アルミナ触媒ではＭＣＨ転化率は０．８％低下しており、エッグシェル型第二成分添加白金担持アルミナ触媒は、触媒寿命が長いことが予想される。また、ＴＯＬ選択率についても、エッグシェル型第二成分添加白金担持アルミナ触媒は反応開始５０時間後から反応開始１２００時間後にかけて９９．９％を維持しており、比較例３（触媒Ｎｏ．３）の均一型白金担持アルミナ触媒に比べて高いＴＯＬ選択率を示し、不純物生成量が少ない触媒であることがわかる。合わせて、１２００時間反応試験後のカーボン生成量は比較例３の２．７％に対して、実施例１は１．１％と少なく、カーボン生成量を抑制することで触媒の安定性を高める効果が得られることが示唆される。
　本発明のエッグシェル型白金担持アルミナ触媒は、水素エネルギーキャリアとして利用されるメチルシクロヘキサン等の水素化芳香族類の脱水素反応に好適に利用でき、有機ケミカルハイドライド法水素貯蔵輸送システムの実用化に資するほか、白金担持アルミナ触媒が利用されている既存の触媒反応プロセスに広く適用できる可能性があり、産業上の利用性が非常に高い発明である。
　　１　担体
　　２　金属担持部分

Claims (9)

  1. 　エッグシェル型白金担持アルミナ触媒であって、
    　アルミナ担体と、
    　前記アルミナ担体の外郭に分散して担持された白金と、
    　バナジウム、クロム、モリブデン、及びリンの群から選ばれる１種又は２種以上の第２成分とを有するエッグシェル型白金担持アルミナ触媒。
  2. 　前記白金の含有量が白金元素として０．０５ｗｔ％以上５．０ｗｔ％以下である請求項１に記載のエッグシェル型白金担持アルミナ触媒。
  3. 　前記第２成分の含有量が、各元素として０．１ｗｔ％以上５．０ｗｔ％以下である請求項１又は請求項２に記載のエッグシェル型白金担持アルミナ触媒。
  4. 　前記アルミナ担体は、表面積が１５０ｍ２／ｇ以上、細孔容積が０．４０ｃｍ３／ｇ以上、平均細孔径が４０Å以上３００Å以下、及び全細孔容積に対して平均細孔径±３０Å以下の細孔が占める割合が６０％以上である請求項１～請求項３のいずれか１つの項に記載のエッグシェル型白金担持アルミナ触媒。
  5. 　エッグシェル型白金担持アルミナ触媒の製造方法であって、
    　アルミナ担体にバナジウム、クロム、モリブデン、及びリンからなる群から選ばれる１種又は２種以上の成分からなる化合物の水溶液を含浸させ、その後に乾燥・焼成を行うステップと、
    　焼成後の前記アルミナ担体にエッグシェル型に白金を担持させるステップと、
    　白金を担持させた前記アルミナ担体を水素雰囲気にて還元するステップとを有するエッグシェル型白金担持アルミナ触媒の製造方法。
  6. 　請求項１～請求項４のいずれか１つの項に記載された前記エッグシェル型白金担持アルミナ触媒を用いて水素化芳香族類を脱水素化することを特徴とする水素化芳香族類の脱水素方法。
  7. 　前記水素化芳香族類が、単環芳香族類の水素化物、２環芳香族類の水素化物、及び３環以上の芳香環を有する化合物の水素化物からなる群から選ばれる１種又は２種以上の混合物である請求項６に記載の水素化芳香族類の脱水素方法。
  8. 　前記水素化芳香族類が、メチルシクロヘキサン、シクロヘキサン、ジメチルシクロヘキサン、テトラリン、デカリン、メチルデカリン、ビフェニル、ジフェニルメチル、ジベンゾトリオール、テトラデカヒドロアントラセンからなる群から選ばれる１種又は２種以上の混合物である請求項４に記載の水素化芳香族類の脱水素方法。
  9. 　前記エッグシェル型白金担持アルミナ触媒と、均一型白金担持アルミナ触媒との両方を用いて行う請求項４～請求項６のいずれか１つの項に記載の水素化芳香族類の脱水素方法。
PCT/JP2020/017564 2020-04-23 2020-04-23 エッグシェル型白金担持アルミナ触媒、その製造方法、及びその使用方法 WO2021214955A1 (ja)