WO2021124668A1 - Composition adhésive - Google Patents

Composition adhésive Download PDF

Info

Publication number
WO2021124668A1
WO2021124668A1 PCT/JP2020/039263 JP2020039263W WO2021124668A1 WO 2021124668 A1 WO2021124668 A1 WO 2021124668A1 JP 2020039263 W JP2020039263 W JP 2020039263W WO 2021124668 A1 WO2021124668 A1 WO 2021124668A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive layer
adhesive composition
adhesive
styrene
film
Prior art date
Application number
PCT/JP2020/039263
Other languages
English (en)
Japanese (ja)
Inventor
航 片桐
栞 門間
Original Assignee
信越ポリマー株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 信越ポリマー株式会社 filed Critical 信越ポリマー株式会社
Priority to CN202080088929.8A priority Critical patent/CN114846104B/zh
Priority to JP2021565340A priority patent/JPWO2021124668A1/ja
Priority to TW109143611A priority patent/TWI784365B/zh
Publication of WO2021124668A1 publication Critical patent/WO2021124668A1/fr

Abstract

L'invention concerne une composition adhésive à partir de laquelle une couche adhésive ayant une excellente propriété électrique et une excellente adhérence (adhésivité) après application de chaleur et durcissement peut être formée, et avec laquelle une adhérence (adhésivité) au cours d'un processus de stratification peut être davantage améliorée, et le pelage ou le soulèvement d'une couche pendant une opération de fixation temporaire ou une opération rouleau à rouleau peuvent être empêchés.　La composition adhésive comprend : un élastomère à base de styrène contenant un groupe carboxyle ; un élastomère à base de styrène ne contenant pas de groupe carboxyle ; et une résine époxy.
PCT/JP2020/039263 2019-12-20 2020-10-19 Composition adhésive WO2021124668A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN202080088929.8A CN114846104B (zh) 2019-12-20 2020-10-19 粘接剂组合物
JP2021565340A JPWO2021124668A1 (fr) 2019-12-20 2020-10-19
TW109143611A TWI784365B (zh) 2019-12-20 2020-12-10 黏接劑組成物

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019-230539 2019-12-20
JP2019230539 2019-12-20

Publications (1)

Publication Number Publication Date
WO2021124668A1 true WO2021124668A1 (fr) 2021-06-24

Family

ID=76477210

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/039263 WO2021124668A1 (fr) 2019-12-20 2020-10-19 Composition adhésive

Country Status (4)

Country Link
JP (1) JPWO2021124668A1 (fr)
CN (1) CN114846104B (fr)
TW (1) TWI784365B (fr)
WO (1) WO2021124668A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016017473A1 (fr) * 2014-07-31 2016-02-04 東亞合成株式会社 Stratifié avec couche adhésive, plaque stratifiée cuivrée souple mettant en œuvre celui-ci, et câble plat souple
JP2016027131A (ja) * 2014-06-26 2016-02-18 住友電気工業株式会社 接着剤組成物、プリント配線板用カバーレイ、プリント配線板用ボンディングフィルム及びプリント配線板

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014147903A1 (fr) * 2013-03-22 2014-09-25 東亞合成株式会社 Composition adhésive, et film de protection et stratifié flexible revêtu de cuivre l'utilisant
JP6705456B2 (ja) * 2015-08-19 2020-06-03 東洋紡株式会社 低誘電接着剤組成物
KR20210068424A (ko) * 2018-10-02 2021-06-09 나믹스 가부시끼가이샤 수지 조성물, 기재 부착 필름, 금속/수지 적층체 및 반도체 장치

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016027131A (ja) * 2014-06-26 2016-02-18 住友電気工業株式会社 接着剤組成物、プリント配線板用カバーレイ、プリント配線板用ボンディングフィルム及びプリント配線板
WO2016017473A1 (fr) * 2014-07-31 2016-02-04 東亞合成株式会社 Stratifié avec couche adhésive, plaque stratifiée cuivrée souple mettant en œuvre celui-ci, et câble plat souple

Also Published As

Publication number Publication date
JPWO2021124668A1 (fr) 2021-06-24
TW202128929A (zh) 2021-08-01
CN114846104A (zh) 2022-08-02
CN114846104B (zh) 2024-03-08
TWI784365B (zh) 2022-11-21

Similar Documents

Publication Publication Date Title
JP6528881B2 (ja) 接着剤層付き積層体、並びに、これを用いたフレキシブル銅張積層板及びフレキシブルフラットケーブル
WO2021131268A1 (fr) Composition adhésive
JP2020164870A (ja) 接着剤組成物及びこれを用いた接着剤層付き積層体
WO2014147903A1 (fr) Composition adhésive, et film de protection et stratifié flexible revêtu de cuivre l'utilisant
JPWO2019172109A1 (ja) 接着剤組成物及びこれを用いた接着剤層付き積層体
WO2021131267A1 (fr) Composition adhésive
WO2021124668A1 (fr) Composition adhésive
WO2022045157A1 (fr) Composition adhésive
JP7287543B2 (ja) 低誘電性接着剤組成物
JP7287542B2 (ja) 低誘電性接着剤組成物
WO2022255136A1 (fr) Composition d'agent adhésif
WO2022004476A1 (fr) Composition adhésive
JP7100299B2 (ja) 低誘電性接着剤組成物
WO2022163284A1 (fr) Composition adhésive
WO2022255141A1 (fr) Composition adhésive
JP2023032287A (ja) 低誘電性接着剤組成物
JP2023132499A (ja) 接着剤組成物及び接着剤層付き積層体

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20902015

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2021565340

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20902015

Country of ref document: EP

Kind code of ref document: A1