WO2020136165A1 - Procédé de production d'une composition de film en polyoléfine et films ainsi préparés - Google Patents

Procédé de production d'une composition de film en polyoléfine et films ainsi préparés Download PDF

Info

Publication number
WO2020136165A1
WO2020136165A1 PCT/EP2019/086917 EP2019086917W WO2020136165A1 WO 2020136165 A1 WO2020136165 A1 WO 2020136165A1 EP 2019086917 W EP2019086917 W EP 2019086917W WO 2020136165 A1 WO2020136165 A1 WO 2020136165A1
Authority
WO
WIPO (PCT)
Prior art keywords
ethylene
copolymer
polymer mixture
polymerisation
homo
Prior art date
Application number
PCT/EP2019/086917
Other languages
English (en)
Inventor
Tuan Anh TRAN
Victor Sumerin
Jarmo Kela
Original Assignee
Borealis Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Borealis Ag filed Critical Borealis Ag
Priority to EP19828783.1A priority Critical patent/EP3902851A1/fr
Publication of WO2020136165A1 publication Critical patent/WO2020136165A1/fr

Abstract

La présente invention concerne un procédé de production d'une composition polymère d'éthylène multimodal convenant à la production de films par moulage par soufflage. Le procédé comprend : (i) une première étape de polymérisation consistant à copolymériser de l'éthylène et éventuellement un comonomère α-oléfine en présence d'un catalyseur de polymérisation Ziegler-Natta sur silice afin d'obtenir un premier homopolymère ou copolymère d'éthylène (PE1) ayant un indice de fluidité MFR2 compris entre 10 et < 150 g/10 min ; (ii) une deuxième étape de polymérisation consistant à copolymériser l'éthylène et éventuellement un comonomère α-oléfine en présence du premier homopolymère ou copolymère d'éthylène afin d'obtenir un premier mélange de polymère d'éthylène (PEM1) comportant le premier homopolymère ou copolymère d'éthylène et un deuxième homopolymère ou copolymère d'éthylène, ledit premier mélange de polymère d'éthylène ayant un indice de fluidité MFR2 compris entre 80 et 180 g/m, et le MFR2 du premier homopolymère ou copolymère d'éthylène (PE1) est inférieur à celui du premier mélange de polymère d'éthylène (PEM1) et le deuxième homopolymère ou copolymère d'éthylène (PE2) ayant un indice de fluidité MFR2 compris entre 150 et 800 g/10 min ; et et (iii) une troisième étape de polymérisation consistant à copolymériser l'éthylène et au moins un comonomère α-oléfine en présence du premier mélange de polymère d'éthylène afin d'obtenir un deuxième mélange de polymère d'éthylène (PEM2) comprenant le premier mélange de polymère d'éthylène et un troisième copolymère d'éthylène (PE3), ledit deuxième mélange de polymère d'éthylène ayant une densité comprise entre 930 et 955 kg/m3 et un indice de fluidité MFR5 compris entre 0,3 et 5 g/10 min.
PCT/EP2019/086917 2018-12-28 2019-12-23 Procédé de production d'une composition de film en polyoléfine et films ainsi préparés WO2020136165A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP19828783.1A EP3902851A1 (fr) 2018-12-28 2019-12-23 Procédé de production d'une composition de film en polyoléfine et films ainsi préparés

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP18248112.7 2018-12-28
EP18248112 2018-12-28

Publications (1)

Publication Number Publication Date
WO2020136165A1 true WO2020136165A1 (fr) 2020-07-02

Family

ID=65010453

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2019/086917 WO2020136165A1 (fr) 2018-12-28 2019-12-23 Procédé de production d'une composition de film en polyoléfine et films ainsi préparés

Country Status (2)

Country Link
EP (1) EP3902851A1 (fr)
WO (1) WO2020136165A1 (fr)

Citations (42)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3324093A (en) 1963-10-21 1967-06-06 Phillips Petroleum Co Loop reactor
US3405109A (en) 1960-10-03 1968-10-08 Phillips Petroleum Co Polymerization process
GB1272778A (en) 1968-09-26 1972-05-03 Basf Ag Removing volatile constituents from particulate olefin polymers produced by gas-phase polymerization
EP0047077A1 (fr) 1980-09-02 1982-03-10 Union Carbide Corporation Procédé de dégazage pour éliminer les monomères non polymérisés à partir de polymères d'oléfines
EP0075049A1 (fr) 1981-09-21 1983-03-30 Mitsui Petrochemical Industries, Ltd. Agitateur ayant la forme d'une ancre destiné au récipient de polymérisation en phase gazeuse
US4582816A (en) 1985-02-21 1986-04-15 Phillips Petroleum Company Catalysts, method of preparation and polymerization processes therewith
US4588790A (en) 1982-03-24 1986-05-13 Union Carbide Corporation Method for fluidized bed polymerization
US4877587A (en) 1984-08-24 1989-10-31 Union Carbide Chemicals And Plastics Company Inc. Fluidized bed polymerization reactors
EP0372239A2 (fr) 1988-11-12 1990-06-13 BASF Aktiengesellschaft Procédé de préparation de polymères d'éthylène à l'aide d'un système catalytique Ziegler à base de Vanadium avec destruction des restes catalytiques.
US4994534A (en) 1989-09-28 1991-02-19 Union Carbide Chemicals And Plastics Company Inc. Process for producing sticky polymers
EP0428054A1 (fr) 1989-11-14 1991-05-22 Neste Oy Dispositif pour introduire un mélange de catalyseurs en forme de boue dans un réacteur de polymérisation
EP0479186A2 (fr) 1990-10-01 1992-04-08 Phillips Petroleum Company Appareil et méthode de préparation de polymères d'éthylène
FI921632A (fi) 1992-04-10 1993-10-11 Neste Oy Leijupetireaktori
EP0628343A1 (fr) 1993-05-19 1994-12-14 BP Chemicals Limited Procédé et dispositif d'introduction d'une matière solide dans un réacteur
FI933073A (fi) 1993-07-05 1995-01-06 Borealis Polymers Oy Menetelmä olefiinien polymeroimiseksi leijupetipolymerointireaktorissa
US5391654A (en) 1990-12-28 1995-02-21 Neste Oy Method for homo- or copolymerizing ethene
FI935856A (fi) 1993-12-27 1995-06-28 Borealis Polymers Oy Leijupetireaktori
EP0683176A1 (fr) 1994-05-16 1995-11-22 BP Chemicals Limited Procédé de polymérisation d'oléfine en phase gazeuse
EP0688794A1 (fr) 1994-06-20 1995-12-27 Borealis Polymers Oy Procatalyseur pour la production de polymère d'éthylène, méthode pour sa préparation et utilisation
EP0691367A1 (fr) 1994-07-08 1996-01-10 Union Carbide Chemicals & Plastics Technology Corporation Feuille extrudé d'un mélange de copolymères d'éthylène
EP0699213A1 (fr) 1993-05-20 1996-03-06 BP Chemicals Limited Procede de polymerisation
WO1996019503A1 (fr) 1994-12-22 1996-06-27 Borealis Polymers Oy Procede empechant l'encrassement des reacteurs de polymerisation
WO1996032420A1 (fr) 1995-04-12 1996-10-17 Borealis Polymers Oy Procede pour prevenir l'encrassement et le depot de strates dans des reacteurs en phase gazeuse
WO1999051646A1 (fr) 1998-04-06 1999-10-14 Borealis Technology Oy Composant catalyseur de polymerisation d'olefines, sa preparation et son utilisation
WO2001055230A1 (fr) 2000-01-27 2001-08-02 Borealis Technology Oy Catalyseur
WO2002088194A1 (fr) 2001-04-25 2002-11-07 Bp Chemicals Limited Traitement aux polymeres permettant de separer des matieres volatiles
WO2003066698A1 (fr) 2002-02-04 2003-08-14 Borealis Technology Oy Film a forte resistance aux chocs
WO2004000902A1 (fr) 2002-06-24 2003-12-31 Borealis Technology Oy Procede de production d'une composition de polyethylene lineaire a faible densite
EP1415999A1 (fr) 2002-10-30 2004-05-06 Borealis Technology Oy Procédé et dispositif pour la production de polymères d' oléfines
EP1600276A1 (fr) 2004-05-24 2005-11-30 Borealis Technology Oy Extrudeuse à deux vis contra-rotatives
WO2006063771A1 (fr) 2004-12-17 2006-06-22 Borealis Technology Oy Procede de polymerisation d'olefines en presence d'un catalyseur de polymerisation d'olefines
WO2008034630A1 (fr) 2006-09-22 2008-03-27 Borealis Technology Oy Film multicouche
EP2067799A1 (fr) 2007-12-05 2009-06-10 Borealis Technology OY Polymère
EP2186833A1 (fr) 2008-11-17 2010-05-19 Borealis AG Procédé multi-niveaux pour produire du polyéthylène avec une formation de gel diminuée
EP2228394A1 (fr) 2009-02-24 2010-09-15 Borealis AG Procédé en plusieurs étapes pour la production d'un polymère de polyéthylène de faible densité
EP2246369A1 (fr) 2009-04-30 2010-11-03 Borealis AG Polyéthylène linéaire à faible densité avec une distribution de composition de comonomère uniforme ou inversée
EP2246372A1 (fr) 2009-04-30 2010-11-03 Borealis AG Procédé multi-étapes amélioré pour la production de polyéthylène multimodal linéaire de faible densité
EP2415598A1 (fr) 2010-08-06 2012-02-08 Borealis AG Film multicouche
EP2883887A1 (fr) 2013-12-13 2015-06-17 Borealis AG Procédé en plusieurs étapes de production de compositions de polyéthylène
EP2883885A1 (fr) 2013-12-13 2015-06-17 Borealis AG Procédé en plusieurs étapes de production de compositions de polyéthylène
WO2018060029A1 (fr) * 2016-09-28 2018-04-05 Borealis Ag Procédé de production d'un tuyau revêtu
WO2018095790A1 (fr) * 2016-11-25 2018-05-31 Borealis Ag Procédé de production d'une composition de film de polyoléfine, et films préparés correspondants

Patent Citations (45)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3405109A (en) 1960-10-03 1968-10-08 Phillips Petroleum Co Polymerization process
US3324093A (en) 1963-10-21 1967-06-06 Phillips Petroleum Co Loop reactor
GB1272778A (en) 1968-09-26 1972-05-03 Basf Ag Removing volatile constituents from particulate olefin polymers produced by gas-phase polymerization
EP0047077A1 (fr) 1980-09-02 1982-03-10 Union Carbide Corporation Procédé de dégazage pour éliminer les monomères non polymérisés à partir de polymères d'oléfines
EP0075049A1 (fr) 1981-09-21 1983-03-30 Mitsui Petrochemical Industries, Ltd. Agitateur ayant la forme d'une ancre destiné au récipient de polymérisation en phase gazeuse
US4588790A (en) 1982-03-24 1986-05-13 Union Carbide Corporation Method for fluidized bed polymerization
US4877587A (en) 1984-08-24 1989-10-31 Union Carbide Chemicals And Plastics Company Inc. Fluidized bed polymerization reactors
US4582816A (en) 1985-02-21 1986-04-15 Phillips Petroleum Company Catalysts, method of preparation and polymerization processes therewith
EP0372239A2 (fr) 1988-11-12 1990-06-13 BASF Aktiengesellschaft Procédé de préparation de polymères d'éthylène à l'aide d'un système catalytique Ziegler à base de Vanadium avec destruction des restes catalytiques.
US4994534A (en) 1989-09-28 1991-02-19 Union Carbide Chemicals And Plastics Company Inc. Process for producing sticky polymers
EP0428054A1 (fr) 1989-11-14 1991-05-22 Neste Oy Dispositif pour introduire un mélange de catalyseurs en forme de boue dans un réacteur de polymérisation
EP0479186A2 (fr) 1990-10-01 1992-04-08 Phillips Petroleum Company Appareil et méthode de préparation de polymères d'éthylène
US5391654A (en) 1990-12-28 1995-02-21 Neste Oy Method for homo- or copolymerizing ethene
FI921632A (fi) 1992-04-10 1993-10-11 Neste Oy Leijupetireaktori
EP0628343A1 (fr) 1993-05-19 1994-12-14 BP Chemicals Limited Procédé et dispositif d'introduction d'une matière solide dans un réacteur
EP0699213A1 (fr) 1993-05-20 1996-03-06 BP Chemicals Limited Procede de polymerisation
FI933073A (fi) 1993-07-05 1995-01-06 Borealis Polymers Oy Menetelmä olefiinien polymeroimiseksi leijupetipolymerointireaktorissa
FI935856A (fi) 1993-12-27 1995-06-28 Borealis Polymers Oy Leijupetireaktori
EP0683176A1 (fr) 1994-05-16 1995-11-22 BP Chemicals Limited Procédé de polymérisation d'oléfine en phase gazeuse
EP0688794A1 (fr) 1994-06-20 1995-12-27 Borealis Polymers Oy Procatalyseur pour la production de polymère d'éthylène, méthode pour sa préparation et utilisation
EP0691367A1 (fr) 1994-07-08 1996-01-10 Union Carbide Chemicals & Plastics Technology Corporation Feuille extrudé d'un mélange de copolymères d'éthylène
WO1996019503A1 (fr) 1994-12-22 1996-06-27 Borealis Polymers Oy Procede empechant l'encrassement des reacteurs de polymerisation
WO1996032420A1 (fr) 1995-04-12 1996-10-17 Borealis Polymers Oy Procede pour prevenir l'encrassement et le depot de strates dans des reacteurs en phase gazeuse
WO1999051646A1 (fr) 1998-04-06 1999-10-14 Borealis Technology Oy Composant catalyseur de polymerisation d'olefines, sa preparation et son utilisation
WO2001055230A1 (fr) 2000-01-27 2001-08-02 Borealis Technology Oy Catalyseur
WO2002088194A1 (fr) 2001-04-25 2002-11-07 Bp Chemicals Limited Traitement aux polymeres permettant de separer des matieres volatiles
WO2003066698A1 (fr) 2002-02-04 2003-08-14 Borealis Technology Oy Film a forte resistance aux chocs
WO2004000902A1 (fr) 2002-06-24 2003-12-31 Borealis Technology Oy Procede de production d'une composition de polyethylene lineaire a faible densite
EP1378528A1 (fr) 2002-06-24 2004-01-07 Borealis Technology Oy Procede pour la production d'une composition lldpe
EP1415999A1 (fr) 2002-10-30 2004-05-06 Borealis Technology Oy Procédé et dispositif pour la production de polymères d' oléfines
EP1600276A1 (fr) 2004-05-24 2005-11-30 Borealis Technology Oy Extrudeuse à deux vis contra-rotatives
WO2006063771A1 (fr) 2004-12-17 2006-06-22 Borealis Technology Oy Procede de polymerisation d'olefines en presence d'un catalyseur de polymerisation d'olefines
WO2008034630A1 (fr) 2006-09-22 2008-03-27 Borealis Technology Oy Film multicouche
EP2067799A1 (fr) 2007-12-05 2009-06-10 Borealis Technology OY Polymère
EP2186833A1 (fr) 2008-11-17 2010-05-19 Borealis AG Procédé multi-niveaux pour produire du polyéthylène avec une formation de gel diminuée
EP2228394A1 (fr) 2009-02-24 2010-09-15 Borealis AG Procédé en plusieurs étapes pour la production d'un polymère de polyéthylène de faible densité
EP2246369A1 (fr) 2009-04-30 2010-11-03 Borealis AG Polyéthylène linéaire à faible densité avec une distribution de composition de comonomère uniforme ou inversée
EP2246372A1 (fr) 2009-04-30 2010-11-03 Borealis AG Procédé multi-étapes amélioré pour la production de polyéthylène multimodal linéaire de faible densité
EP2415598A1 (fr) 2010-08-06 2012-02-08 Borealis AG Film multicouche
EP2883887A1 (fr) 2013-12-13 2015-06-17 Borealis AG Procédé en plusieurs étapes de production de compositions de polyéthylène
EP2883885A1 (fr) 2013-12-13 2015-06-17 Borealis AG Procédé en plusieurs étapes de production de compositions de polyéthylène
WO2015086812A1 (fr) 2013-12-13 2015-06-18 Borealis Ag Procédé en plusieurs étapes pour la production de compositions de polyéthylène
WO2018060029A1 (fr) * 2016-09-28 2018-04-05 Borealis Ag Procédé de production d'un tuyau revêtu
WO2018095790A1 (fr) * 2016-11-25 2018-05-31 Borealis Ag Procédé de production d'une composition de film de polyoléfine, et films préparés correspondants
WO2018095788A1 (fr) * 2016-11-25 2018-05-31 Borealis Ag Procédé de production d'une composition de film de polyoléfine et films ainsi préparés

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
HEINO, E.L.: "Annual Transactions of the Nordic Rheology Society", 1995, BOREALIS POLYMERS OY, article "The influence of molecular structure on some rheological properties of polyethylene"
HEINO, E.L.LEHTINEN, A.TANNER J.SEPPALA, J.: "Theor. Appl. Rheol., Proc. Int. Congr. Rheol", vol. 11th, 1992, NESTE OY, article "Rheological characterization of polyethylene fractions", pages: 360 - 362

Also Published As

Publication number Publication date
EP3902851A1 (fr) 2021-11-03

Similar Documents

Publication Publication Date Title
EP3544815B1 (fr) Procédé de production de composition de film de polyoléfine et films préparés à partir de celle-ci
US9234061B2 (en) Multimodal polymer
EP2300529B1 (fr) Compositions de polyéthylène
US20060014897A1 (en) Breathable films
US10619036B2 (en) Multimodal polyethylene copolymer
CN114144440B (zh) 单活性中心催化的多峰聚乙烯组合物
WO2013037432A1 (fr) Composition de polyéthylène à distribution large du poids moléculaire et homogénéité améliorée
KR20190049891A (ko) 코팅된 파이프의 제조 방법
WO2020136164A1 (fr) Procédé de production d&#39;une composition de film de polyoléfine et films ainsi préparés
WO2020136165A1 (fr) Procédé de production d&#39;une composition de film en polyoléfine et films ainsi préparés
WO2022258804A1 (fr) Procédé de production d&#39;un polymère d&#39;éthylène multimodal et films préparés à partir de ce dernier
EP3037471B1 (fr) Procédé de production de compositions de polyéthylène multimodal
WO2024068977A1 (fr) Composition de copolymère d&#39;éthylène multimodal et films la comprenant
RU2777964C1 (ru) Композиция полиэтилена для труб высокого давления с улучшенной гомогенностью
WO2024083689A1 (fr) Film multicouche
JP2006514124A (ja) 呼吸できるフィルム

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19828783

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2019828783

Country of ref document: EP

Effective date: 20210728