WO2020098306A1 - Acier nm500 épais résistant à l'usure et son procédé de production - Google Patents

Acier nm500 épais résistant à l'usure et son procédé de production Download PDF

Info

Publication number
WO2020098306A1
WO2020098306A1 PCT/CN2019/097829 CN2019097829W WO2020098306A1 WO 2020098306 A1 WO2020098306 A1 WO 2020098306A1 CN 2019097829 W CN2019097829 W CN 2019097829W WO 2020098306 A1 WO2020098306 A1 WO 2020098306A1
Authority
WO
WIPO (PCT)
Prior art keywords
rolling
temperature
wear
resistant steel
thickness
Prior art date
Application number
PCT/CN2019/097829
Other languages
English (en)
Chinese (zh)
Inventor
姜在伟
王升
侯中华
闫强军
张仪杰
姜辉
王思聪
Original Assignee
南京钢铁股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 南京钢铁股份有限公司 filed Critical 南京钢铁股份有限公司
Priority to AU2019381094A priority Critical patent/AU2019381094A1/en
Publication of WO2020098306A1 publication Critical patent/WO2020098306A1/fr
Priority to ZA2021/03239A priority patent/ZA202103239B/en

Abstract

Cette invention concerne un acier NM500 épais résistant à l'usure, se rapportant au domaine de la technologie métallurgique et comprenant les constituants chimiques suivants en pourcentage en masse : 0,26 % à 0,30 % de C, 0,20 % à 0,60 % de Si, 0,60 % 1,00 % de Mn, P ≤ 0,012 %, S ≤ 0,003 %, 0,60 % à 0,90 % de Cr, 0,35 % à 0,50 % de Mo, 0,40 % à 0,60 % de Ni, 0,008 % à 0 030 % de Ti, 0,015 % à 0,050 % de Nb, 0,0008 % à 0,0025 % de B, carbone équivalent ≤ 0,75 %, le reste étant du Fe et les inévitables impuretés. Le procédé de production de l'acier résistant à l'usure selon l'invention est bref, le coût est faible, et l'acier produit présente d'excellentes propriétés mécaniques, une grande épaisseur, une dureté élevée, une bonne ténacité et une formidable performance de soudage.
PCT/CN2019/097829 2018-11-12 2019-07-26 Acier nm500 épais résistant à l'usure et son procédé de production WO2020098306A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
AU2019381094A AU2019381094A1 (en) 2018-11-12 2019-07-26 Thick NM500 wear-resistant steel and production method therefor
ZA2021/03239A ZA202103239B (en) 2018-11-12 2021-05-13 Thick nm500 wear-resistant steel and production method therefor

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201811342361.9 2018-11-12
CN201811342361.9A CN109280852A (zh) 2018-11-12 2018-11-12 一种大厚度nm500耐磨钢及生产方法

Publications (1)

Publication Number Publication Date
WO2020098306A1 true WO2020098306A1 (fr) 2020-05-22

Family

ID=65175047

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2019/097829 WO2020098306A1 (fr) 2018-11-12 2019-07-26 Acier nm500 épais résistant à l'usure et son procédé de production

Country Status (4)

Country Link
CN (1) CN109280852A (fr)
AU (2) AU2019101844A4 (fr)
WO (1) WO2020098306A1 (fr)
ZA (1) ZA202103239B (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112481546A (zh) * 2020-11-26 2021-03-12 南阳汉冶特钢有限公司 一种特厚塑料模具用钢板p20的生产方法
CN115094217A (zh) * 2022-07-12 2022-09-23 南阳汉冶特钢有限公司 一种30CrMoA钢板及其生产方法
CN115369303A (zh) * 2022-08-08 2022-11-22 包头钢铁（集团）有限责任公司 一种耐磨钢nm500制备方法
CN115449695A (zh) * 2022-08-22 2022-12-09 包头钢铁（集团）有限责任公司 一种1000MPa级高强抽油杆圆钢的生产方法
CN115491475A (zh) * 2022-10-12 2022-12-20 包头钢铁（集团）有限责任公司 一种稀土微合金化低成本高硬度塑料模具钢p20的制备方法
CN116288032A (zh) * 2023-03-29 2023-06-23 武汉科技大学 一种Nb元素微合金化抗高温抗磨损块体多组分合金及其制备方法和应用

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109280852A (zh) * 2018-11-12 2019-01-29 南京钢铁股份有限公司 一种大厚度nm500耐磨钢及生产方法
CN110343952A (zh) * 2019-07-02 2019-10-18 唐山中厚板材有限公司 一种硬度不低于600hbw的耐磨钢板及其生产方法
CN110643883A (zh) * 2019-10-10 2020-01-03 南京钢铁股份有限公司 一种一钢多级用耐磨钢坯料生产方法
CN111139349A (zh) * 2020-01-13 2020-05-12 河北普阳钢铁有限公司 一种提高大厚度耐磨钢板热处理产量和质量的方法
CN111020126A (zh) * 2020-01-13 2020-04-17 河北普阳钢铁有限公司 一种nm500以上耐磨钢中板热处理方法
CN112359284A (zh) * 2020-11-04 2021-02-12 南阳汉冶特钢有限公司 一种高强度低温韧性耐磨钢板hy550nme及其生产方法
CN112553525B (zh) * 2020-11-17 2021-12-21 天津重型装备工程研究有限公司 一种中碳低合金高强钢及其制备方法
CN114164315B (zh) * 2021-11-12 2023-02-14 哈尔滨工程大学 一种60～120mm厚1000MPa级高强度高韧性易焊接纳米钢及其制备方法

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101250673A (zh) * 2008-03-31 2008-08-27 武汉钢铁(集团)公司 一种超高强度耐磨钢及其生产方法
CN101397632A (zh) * 2008-10-31 2009-04-01 郭玉宝 一种多元素低合金水淬耐磨钢
CN101638755A (zh) * 2009-08-21 2010-02-03 东北大学 高韧性超高强度耐磨钢板及其生产方法
CN104789881A (zh) * 2015-05-07 2015-07-22 湖南华菱湘潭钢铁有限公司 一种高强度高韧性耐磨钢板的生产方法
CN105200337A (zh) * 2014-06-23 2015-12-30 鞍钢股份有限公司 一种高强度耐磨钢板及其生产方法
JP2017193740A (ja) * 2016-04-19 2017-10-26 Ｊｆｅスチール株式会社 耐摩耗鋼板および耐摩耗鋼板の製造方法
CN109280852A (zh) * 2018-11-12 2019-01-29 南京钢铁股份有限公司 一种大厚度nm500耐磨钢及生产方法

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004300474A (ja) * 2003-03-28 2004-10-28 Jfe Steel Kk 耐摩耗鋼およびその製造方法
JP5966730B2 (ja) * 2012-07-30 2016-08-10 Ｊｆｅスチール株式会社 耐衝撃摩耗特性に優れた耐摩耗鋼板およびその製造方法
CN105385951B (zh) * 2015-11-12 2017-10-13 内蒙古包钢钢联股份有限公司 兼具高硬度高韧性的nm500耐磨钢板的生产方法

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101250673A (zh) * 2008-03-31 2008-08-27 武汉钢铁(集团)公司 一种超高强度耐磨钢及其生产方法
CN101397632A (zh) * 2008-10-31 2009-04-01 郭玉宝 一种多元素低合金水淬耐磨钢
CN101638755A (zh) * 2009-08-21 2010-02-03 东北大学 高韧性超高强度耐磨钢板及其生产方法
CN105200337A (zh) * 2014-06-23 2015-12-30 鞍钢股份有限公司 一种高强度耐磨钢板及其生产方法
CN104789881A (zh) * 2015-05-07 2015-07-22 湖南华菱湘潭钢铁有限公司 一种高强度高韧性耐磨钢板的生产方法
JP2017193740A (ja) * 2016-04-19 2017-10-26 Ｊｆｅスチール株式会社 耐摩耗鋼板および耐摩耗鋼板の製造方法
CN109280852A (zh) * 2018-11-12 2019-01-29 南京钢铁股份有限公司 一种大厚度nm500耐磨钢及生产方法

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112481546A (zh) * 2020-11-26 2021-03-12 南阳汉冶特钢有限公司 一种特厚塑料模具用钢板p20的生产方法
CN112481546B (zh) * 2020-11-26 2022-06-14 南阳汉冶特钢有限公司 一种特厚塑料模具用钢板p20的生产方法
CN115094217A (zh) * 2022-07-12 2022-09-23 南阳汉冶特钢有限公司 一种30CrMoA钢板及其生产方法
CN115369303A (zh) * 2022-08-08 2022-11-22 包头钢铁（集团）有限责任公司 一种耐磨钢nm500制备方法
CN115449695A (zh) * 2022-08-22 2022-12-09 包头钢铁（集团）有限责任公司 一种1000MPa级高强抽油杆圆钢的生产方法
CN115449695B (zh) * 2022-08-22 2023-09-26 包头钢铁（集团）有限责任公司 一种1000MPa级高强抽油杆圆钢的生产方法
CN115491475A (zh) * 2022-10-12 2022-12-20 包头钢铁（集团）有限责任公司 一种稀土微合金化低成本高硬度塑料模具钢p20的制备方法
CN115491475B (zh) * 2022-10-12 2023-09-26 包头钢铁（集团）有限责任公司 一种稀土微合金化低成本高硬度塑料模具钢p20的制备方法
CN116288032A (zh) * 2023-03-29 2023-06-23 武汉科技大学 一种Nb元素微合金化抗高温抗磨损块体多组分合金及其制备方法和应用
CN116288032B (zh) * 2023-03-29 2024-04-02 武汉科技大学 一种Nb元素微合金化抗高温抗磨损块体多组分合金及其制备方法和应用

Also Published As

Publication number Publication date
AU2019101844A4 (en) 2023-06-08
AU2019381094A1 (en) 2021-05-27
ZA202103239B (en) 2023-05-31
CN109280852A (zh) 2019-01-29

Similar Documents

Publication Publication Date Title
WO2020098306A1 (fr) Acier nm500 épais résistant à l'usure et son procédé de production
WO2020087961A1 (fr) Plaque d'acier résistante à l'usure, faiblement alliée, à ténacité élevée, et de 80 mm d'épaisseur, et son procédé de fabrication
CN100412223C (zh) 具有优良耐蚀性和抗疲劳性的超高强度钢及其制造方法
CN101451212B (zh) 一种高强度钢板及其制备方法
CN101613840B (zh) 强韧性匹配及高温性能优良的特厚钢板及其制造方法
WO2016095721A1 (fr) Acier à haute résistance trempé et revenu ayant une limite d'élasticité de nuance 900 mpa à 1000 mpa, et procédé pour le fabriquer
CN105483539B (zh) 一种超硬粒子增强型奥氏体耐磨钢板及其制造方法
WO2021098208A1 (fr) Acier d'épaisseur moyenne à teneur moyenne en manganèse de qualité 690 mpa ayant une résistance élevée et un faible rapport d'élasticité, et procédé de fabrication de celui-ci
WO2021036271A1 (fr) Tôle d'acier résistant à l'usure 400hb résistante à haute température et procédé de production associé
CN108728743B (zh) 低温断裂韧性良好的海洋工程用钢及其制造方法
WO2022052335A1 (fr) Plaque en acier résistante à l'usure haute ténacité à faible équivalent en carbone épaisse et son procédé de fabrication
CN101328560B (zh) 一种Ni系无缝钢管及其制造方法
CN101451220A (zh) 一种高强度耐磨钢板及其制备方法
CN107058882A (zh) 一种特厚规格耐磨钢板及其制备方法
WO2018040859A1 (fr) Procédé de production d'acier q960e ultra-haute résistance de grande épaisseur
AU2018387506A1 (en) High-grade low-alloy wear-resistant steel plate having brookfield hardness of greater than 550 HB and manufacturing method
CN102691018A (zh) 一种低压缩比超高强度海洋工程用钢板及其生产方法
CN102234743A (zh) 一种低碳马氏体钢板及其制造方法
CN102286695A (zh) 一种高塑性高韧性超高强度钢板及其生产方法
CN109182666A (zh) 一种宽薄规格nm450耐磨钢钢板及制造方法
CN102517509A (zh) Hb500级耐磨钢板及其制备方法
CN109207858B (zh) 一种低合金超高强度钢q1100e薄板的生产方法
CN114480806B (zh) 一种厚规格TiC粒子增强型马氏体耐磨钢板的制造方法
CN105112782A (zh) 一种热轧态船用低温铁素体lt-fh40钢板及其生产方法
CN108624744A (zh) 一种Q500qE桥梁钢板及其生产方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19885713

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2019381094

Country of ref document: AU

Date of ref document: 20190726

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 19885713

Country of ref document: EP

Kind code of ref document: A1