WO2020000572A1 - Wrinkle-free fabric and processing process thereof - Google Patents

Wrinkle-free fabric and processing process thereof Download PDF

Info

Publication number
WO2020000572A1
WO2020000572A1 PCT/CN2018/097995 CN2018097995W WO2020000572A1 WO 2020000572 A1 WO2020000572 A1 WO 2020000572A1 CN 2018097995 W CN2018097995 W CN 2018097995W WO 2020000572 A1 WO2020000572 A1 WO 2020000572A1
Authority
WO
WIPO (PCT)
Prior art keywords
warp
polyester
fabric
wrinkle
speed
Prior art date
Application number
PCT/CN2018/097995
Other languages
French (fr)
Chinese (zh)
Inventor
仝进峰
Original Assignee
南通新天地纺织品印染有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 南通新天地纺织品印染有限公司 filed Critical 南通新天地纺织品印染有限公司
Publication of WO2020000572A1 publication Critical patent/WO2020000572A1/en

Abstract

A wrinkle-free fabric, woven by warps and wefts, wherein the warps are formed by blending polyester, copper ammonia fibers and polypropylene fibers, and the wefts are formed by blending and weaving copper ammonia fibers and polyester; the blending proportion of polyester to the copper ammonia fibers to the polypropylene fibers in the warps is 2: 3: 2, and the blending proportion of the copper ammonia fibers to polyester in the wefts is 1: 1. The fabric has the advantages of soft handfeeling, high air permeability, high elasticity and good moisture absorption and is free of wrinkles or pilling.

Description

一种不易起褶皱的面料及其加工工艺Fabric not easily wrinkled and processing technology thereof 技术领域Technical field
本发明专利涉及一种面料，具体涉及一种不易起褶皱的面料及其加工工艺。The invention patent relates to a fabric, in particular to a fabric which is not easy to wrinkle and its processing technology.
背景技术Background technique
随着人们生活水平的日益提高，人们对衣物的舒适度、保温性能、弹性的要求也越来越高，目前，市场上的内衣一般采用普通棉或粘胶类或者纤混纺面料，但人体新陈代谢产生的油脂、水分，一直在通过表皮散发湿气。纤混纺面料存在高光点的缺陷，制作成衣服后易引起起毛起球、闷气或透气性差、吸水性差，容易褶皱，这种面料已经不能满足人们的要求。With the improvement of people's living standards, people's requirements for clothing comfort, thermal insulation and elasticity are becoming higher and higher. At present, underwear on the market generally uses ordinary cotton or viscose or fiber blended fabrics, but the human body's metabolism The generated oil and moisture are constantly radiating moisture through the epidermis. The fiber-blend fabric has defects of high light point, and it is easy to cause pilling, suffocation or poor breathability, poor water absorption, and easy wrinkle after being made into clothes. This fabric can no longer meet people's requirements.
发明内容Summary of the invention
发明的目的：本发明的目的在于提供一种不易起褶皱的面料。Object of the invention: The object of the present invention is to provide a fabric which is not easy to wrinkle.
本发明采用的技术方案：一种不易起褶皱的面料，由经线和纬线相互编织而成，所述经线由涤纶，铜氨纤维和丙纶混纺而成，所述的纬线由铜氨纤维，涤纶混纺编织而成，所述的经线中涤纶，铜氨纤维和丙纶混纺比例为2:3:2，所述的纬线中铜氨纤维，涤纶的混纺比例为1:1。The technical solution adopted by the present invention is a fabric that is not easy to crease, and is woven with warp and weft threads, the warp threads are blended with polyester, copper ammonia fiber and polypropylene, and the weft threads are made of copper ammonia fiber and polyester blend Weaving, the ratio of polyester, copper ammonia fiber and polypropylene blend in the warp is 2: 3: 2, and the ratio of copper ammonia fiber and polyester blend in the weft is 1: 1.
所述经线和纬线采用平纹或斜纹编织。The warp and weft threads are woven in plain or twill.
一种不易起褶皱的面料加工工艺，具体包括如下步骤：A fabric processing process that is not easy to wrinkle, specifically includes the following steps:
a、交并工序：将涤纶，铜氨纤维和丙纶送入并纱机中进行纱线交并形成混并经线，将铜氨纤维，涤纶送入并纱机中进行纱线交并形成混并纬线；a. Interleaving process: Send polyester, copper ammonia fiber and polypropylene into the yarn-spinning machine for yarn interleaving and form mixed warp yarns, and send copper ammonia fiber and polyester into the yarn-spinning machine for yarn interleaving and form mixed yarn. weft;
b、络筒工序：将步骤a中混并的经线及纬线送入络筒机内进行络筒，同时控制槽筒线速度为1050～1150m/min，卷绕密度为0.32～0.38g/cm 3； b. Winding process: send the warp and weft threads mixed in step a into the winder for winding, while controlling the linear speed of the slot to 1050 ～ 1150m / min, and the winding density of 0.32 ～ 0.38g / cm 3 ;
c、整经工序：采用整经机对步骤b中络筒的纱线进行分条整经，控制整经机的整经速度为340～360mm/min，卷绕密度为0.5～0.6g/cm 3； c. Warping process: The warping machine is used to warp the yarn in step b. The warping speed of the warping machine is controlled to be 340 ～ 360mm / min, and the winding density is 0.5 ～ 0.6g / cm. 3 ;
d、织造工艺：采用剑杆织机进行织造，其中经纱及纬纱按照预设比例送入，其中织造速度为170～200r/min，开口时间为300～320°；d. Weaving process: Weaving with a rapier loom, in which warp and weft yarns are fed in according to a preset ratio, in which the weaving speed is 170-200r / min and the opening time is 300-320 °;
e、后整理工序：将步骤d织造完的原布进行检验，然后烧去布面上的绒毛，再送入定型机中进行定型，使成布符合要求，再进行验布，包装。e. Finishing process: The original cloth woven in step d is inspected, and then the fluff on the cloth surface is burned, and then sent to the setting machine for setting, so that the finished fabric meets the requirements, and then the cloth is inspected and packed.
所述步骤b中槽筒线速度为1100m/min，卷绕密度为0.37g/cm 3。 In the step b, the linear velocity of the slot cylinder is 1100 m / min, and the winding density is 0.37 g / cm 3 .
所述步骤c中整径速度为350mm/min，卷绕密度为0.55g/cm 3。 In the step c, the entire diameter speed is 350 mm / min, and the winding density is 0.55 g / cm 3 .
所述步骤d中制造速度为190r/min，开口时间为320°。In the step d, the manufacturing speed is 190 r / min, and the opening time is 320 °.
所述步骤e中验布速度为18—20m/min。The cloth inspection speed in the step e is 18-20 m / min.
有益效果：一种不易起褶皱的面料具有手感柔软，透气性高，弹性高，不易褶皱，吸湿性好，且不起球的优点。Beneficial effect: A fabric that is not easy to wrinkle has the advantages of soft touch, high air permeability, high elasticity, not easy to wrinkle, good hygroscopicity, and no ball.
具体实施方式detailed description
下面结合具体实施例对本发明的技术内容进行详细阐述：The technical content of the present invention is described in detail below with reference to specific embodiments:
本发明所揭示的一种不易起褶皱的面料，由经线和纬线相互编织而成，所述经线由涤纶，铜氨纤维和丙纶混纺而成，所述的纬线由铜氨纤维，涤纶混纺编织而成，所述的经线中涤纶，铜氨纤维和丙纶混纺比例为2:3:2，所述的纬线中铜氨纤维，涤纶的混纺比例为1:1。The fabric disclosed in the present invention which is not easy to wrinkle is woven with warp and weft. The warp is made of polyester, copper ammonia fiber and polypropylene, and the weft is made of copper ammonia fiber and polyester fiber. As a result, the blend ratio of polyester, copper ammonia fiber and polypropylene in the warp is 2: 3: 2, and the blend ratio of copper ammonia fiber and polyester in the weft is 1: 1.
其中，所述经线和纬线采用平纹或斜纹编织。Wherein, the warp and weft are woven with plain or twill.
一种不易起褶皱的面料加工工艺，具体包括如下步骤：A fabric processing process that is not easy to wrinkle, specifically includes the following steps:
a、交并工序：将涤纶，铜氨纤维和丙纶送入并纱机中进行纱线交并形成混并经线，将铜氨纤维，涤纶送入并纱机中进行纱线交并形成混并纬线；a. Merging process: send polyester, copper-fiber and polypropylene into the yarn-spinning machine for yarn blending and forming a mixed warp, and copper-fiber and polyester-fiber into the yarn-feeding machine for yarn blending and forming a blend weft;
b、络筒工序：将步骤a中混并的经线及纬线送入络筒机内进行络筒，同时控制槽筒线速度为1050～1150m/min，卷绕密度为0.32～0.38g/cm 3； b. Winding process: send the warp and weft threads mixed in step a into the winder for winding, while controlling the linear speed of the slot to 1050 ～ 1150m / min, and the winding density of 0.32 ～ 0.38g / cm 3 ;
c、整经工序：采用整经机对步骤b中络筒的纱线进行分条整经，控制整经机的整经速度为340～360mm/min，卷绕密度为0.5～0.6g/cm 3； c. Warping process: The warping machine is used to warp the yarn in step b. The warping speed of the warping machine is controlled to be 340 ～ 360mm / min, and the winding density is 0.5 ～ 0.6g / cm. 3 ;
d、织造工艺：采用剑杆织机进行织造，其中经纱及纬纱按照预设比例送入，其中织造速度为170～200r/min，开口时间为300～320°；d. Weaving process: Weaving with a rapier loom, in which warp and weft yarns are fed in according to a preset ratio, in which the weaving speed is 170-200r / min and the opening time is 300-320 °;
e、后整理工序：将步骤d织造完的原布进行检验，然后烧去布面上的绒毛，再送入定型机中进行定型，使成布符合要求，再进行验布，包装。e. Finishing process: The original cloth woven in step d is inspected, and then the fluff on the cloth surface is burned, and then sent to the setting machine for setting, so that the finished fabric meets the requirements, and then the cloth is inspected and packed.
所述步骤b中槽筒线速度为1100m/min，卷绕密度为0.37g/cm 3。 In the step b, the linear velocity of the slot cylinder is 1100 m / min, and the winding density is 0.37 g / cm 3 .
所述步骤c中整径速度为350mm/min，卷绕密度为0.55g/cm 3。 In the step c, the entire diameter speed is 350 mm / min, and the winding density is 0.55 g / cm 3 .
所述步骤d中制造速度为190r/min，开口时间为320°。In the step d, the manufacturing speed is 190 r / min, and the opening time is 320 °.
所述步骤e中验布速度为18—20m/min。The cloth inspection speed in the step e is 18-20 m / min.
以上所述仅是本发明的优选实施方式，应当指出：对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。The above is only a preferred embodiment of the present invention, and it should be pointed out that for those of ordinary skill in the art, without departing from the principles of the present invention, several improvements and retouches can be made. These improvements and retouches also It should be regarded as the protection scope of the present invention.

Claims (7)

  1. 一种不易起褶皱的面料，由经线和纬线相互编织而成，其特征在于：所述经线由涤纶，铜氨纤维和丙纶混纺而成，所述的纬线由铜氨纤维，涤纶混纺编织而成，所述的经线中涤纶，铜氨纤维和丙纶混纺比例为2:3:2，所述的纬线中铜氨纤维，涤纶的混纺比例为1:1。A crease-resistant fabric is woven with warp and weft threads, which is characterized in that the warp threads are made of polyester, copper-spandex and polypropylene blends, and the weft threads are made of copper-spandex and polyester blends The blend ratio of polyester, copper ammonia fiber and polypropylene in the warp is 2: 3: 2, and the blend ratio of copper ammonia fiber and polyester in the weft is 1: 1.
  2. 根据权利要求1所述的一种不易起褶皱的面料，其特征在于：所述经线和纬线采用平纹或斜纹编织。The wrinkle-resistant fabric according to claim 1, wherein the warp and weft threads are woven in plain or twill.
  3. 一种不易起褶皱的面料加工工艺，其特征在于：具体包括如下步骤：A fabric processing technology that is not easy to wrinkle, which is characterized in that it specifically includes the following steps:
    a、交并工序：将涤纶，铜氨纤维和丙纶送入并纱机中进行纱线交并形成混并经线，将铜氨纤维，涤纶送入并纱机中进行纱线交并形成混并纬线；a. Merging process: send polyester, copper-fiber and polypropylene into the yarn-spinning machine for yarn blending and forming a mixed warp, and copper-fiber and polyester-fiber into the yarn-feeding machine for yarn blending and forming a blend weft;
    b、络筒工序：将步骤a中混并的经线及纬线送入络筒机内进行络筒，同时控制槽筒线速度为1050～1150m/min，卷绕密度为0.32～0.38g/cm 3； b. Winding process: send the warp and weft threads mixed in step a into the winder for winding, while controlling the linear speed of the slot to 1050 ～ 1150m / min, and the winding density of 0.32 ～ 0.38g / cm 3 ;
    c、整经工序：采用整经机对步骤b中络筒的纱线进行分条整经，控制整经机的整经速度为340～360mm/min，卷绕密度为0.5～0.6g/cm 3； c. Warping process: The warping machine is used to warp the yarn in step b. The warping speed of the warping machine is controlled to be 340 ～ 360mm / min, and the winding density is 0.5 ～ 0.6g / cm. 3 ;
    d、织造工艺：采用剑杆织机进行织造，其中经纱及纬纱按照预设比例送入，其中织造速度为170～200r/min，开口时间为300～320°；d. Weaving process: Weaving with a rapier loom, in which warp and weft yarns are fed in according to a preset ratio, in which the weaving speed is 170-200r / min and the opening time is 300-320 °;
    e、后整理工序：将步骤d织造完的原布进行检验，然后烧去布面上的绒毛，再送入定型机中进行定型，使成布符合要求，再进行验布，包装。e. Finishing process: The original cloth woven in step d is inspected, and then the fluff on the cloth surface is burned, and then sent to the setting machine for setting, so that the finished fabric meets the requirements, and then the cloth is inspected and packed.
  4. 根据权利要求3所述的一种不易起褶皱的面料加工工艺，其特征在于：所述步骤b中槽筒线速度为1100m/min，卷绕密度为0.37g/cm 3。 The fabric processing process that is not easy to wrinkle according to claim 3, characterized in that: in the step b, the linear velocity of the slot cylinder is 1100 m / min, and the winding density is 0.37 g / cm 3 .
  5. 根据权利要求3所述的一种不易起褶皱的面料加工工艺，其特征在于：所述步骤c中整径速度为350mm/min，卷绕密度为0.55g/cm 3。 The fabric processing process that is not easy to wrinkle according to claim 3, characterized in that: in the step c, the diameter adjustment speed is 350 mm / min, and the winding density is 0.55 g / cm 3 .
  6. 根据权利要求3所述的一种不易起褶皱的面料加工工艺，其特征在于：所述步骤d中制造速度为190r/min，开口时间为320°。The fabric processing technology that is not easy to wrinkle according to claim 3, characterized in that in the step d, the manufacturing speed is 190r / min, and the opening time is 320 °.
  7. 根据权利要求3所述的一种不易起褶皱的面料加工工艺，其特征在于：所述步骤e中验布速度为18—20m/min。The fabric processing technology that is not easy to wrinkle according to claim 3, characterized in that the fabric inspection speed in the step e is 18-20 m / min.
PCT/CN2018/097995 2018-06-25 2018-08-01 Wrinkle-free fabric and processing process thereof WO2020000572A1 (en)