WO2020015007A1 - Comfortable antibacterial fabric and processing technique therefor - Google Patents
Comfortable antibacterial fabric and processing technique therefor Download PDFInfo
- Publication number
- WO2020015007A1 WO2020015007A1 PCT/CN2018/097955 CN2018097955W WO2020015007A1 WO 2020015007 A1 WO2020015007 A1 WO 2020015007A1 CN 2018097955 W CN2018097955 W CN 2018097955W WO 2020015007 A1 WO2020015007 A1 WO 2020015007A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fiber
- warp
- polyester
- cotton
- antibacterial
- Prior art date
Abstract
Provided are a comfortable antibacterial fabric and a processing technique therefor. The fabric is made by interweaving a warp and a weft, wherein the warp is made by blending bamboo fiber, cotton fiber, polynosic fiber, and polyester fiber, and the weft is made by blending and weaving bamboo fiber, polynosic fiber, dacron and cotton fiber. The blending ratio of the bamboo fiber, cotton fiber, polynosic fiber, and polyester fiber in the warp is 2:1:1:2, and the blending ratio of the bamboo fiber, polynosic fiber, dacron and cotton fiber in the weft is 2:2:1:2. The processing technique comprises an intersecting process, a winding process, a warping process, a weaving process, and a post-finishing process. The present fabric has the effects of preventing static electricity, is soft to the touch, has a soft gloss, high strength, and high elasticity, and has anti-wrinkle, antibacterial, bacteriostatic, mite-killing, anti-odor and ultraviolet light-resistant properties.
Description
本发明专利涉及一种面料,具体涉及一种抗菌舒适型面料及其加工工艺。The invention patent relates to a fabric, in particular to an antibacterial comfortable fabric and a processing technology thereof.
随着人们生活水平的日益提高,人们对衣物的舒适度、保温性能的要求也越来越高。目前,市场上的内衣一般采用普通棉或竹类或者纤混纺面料,但人体新陈代谢产生的油脂、水分,一直在通过表皮散发湿气。棉制的面料,由于棉纤维细度较细有天然卷曲,截面有中腔,所以保暖性较好,穿着后刚开始比较舒适,但经过一段时间人体新陈代谢后会较为较粘,特别是比较容易出汗的人,人体产生的湿气更难挥发出去,尤其是冬天,人们感觉更湿冷,并且普通棉易缩、易皱,外观上不大挺括美观。纤混纺面料存在高光点的缺陷,制作成衣服后易引起皮肤干燥、摩擦静电、起毛起球、闷气或透气性差、吸水性差及洗涤时易抽丝、柔软性不如纯棉等缺陷;纤维制的面料,该面料的优点是价格便宜,保暖性透气性较好,轻巧;但是化学纤维摩擦容易产生静电,所以时间长了其内部会吸附很多灰尘和皮屑,另外,孔数越多纤维越粗糙,其贴身性就越差。As people's living standards continue to improve, people's requirements for the comfort and thermal insulation performance of clothing are becoming higher and higher. At present, the underwear on the market generally uses ordinary cotton or bamboo or fiber blended fabrics, but the fat and moisture produced by the human body's metabolism have been emitting moisture through the epidermis. Cotton fabrics, because of the fineness of cotton fibers, have natural curls, and have a cavity in the cross section, so they have better warmth and are more comfortable after wearing, but after a period of time, the human body's metabolism will be more sticky, especially easier. Sweating people, the moisture generated by the human body is more difficult to volatilize, especially in winter, people feel colder and colder, and ordinary cotton is easy to shrink, easy to wrinkle, and it is not very beautiful in appearance. Fiber-blend fabrics have defects of high light points, which can cause skin dryness, static friction, pilling, suffocation or poor air permeability, poor water absorption and easy threading when washing, and softness not as pure as cotton when made into clothing. The fabric has the advantages of cheap price, good warmth, breathability, and lightness; but the chemical fiber is easy to generate static electricity due to friction, so it will adsorb a lot of dust and dander inside over time. In addition, the more the number of holes, the more rough the fiber , The worse the fit.
发明内容Summary of the invention
发明的目的:本发明的目的在于提供一种抗菌舒适型面料及其加工工艺。Object of the invention: The object of the present invention is to provide an antibacterial comfortable fabric and its processing technology.
本发明采用的技术方案:一种抗菌舒适型面料,由经线和纬线相互编织而成,所述经线由竹纤维,棉纤维,富强纤维和聚酯纤维混纺而成,所述的纬线由竹纤维,富强纤维、涤纶和棉纤维混纺编织而成,所述的经线中竹纤维,棉纤维,富强纤维和聚酯纤维混纺混纺比例为2:1:1:2,所述的纬线中竹纤维、富强纤维、涤纶和棉纤维的混纺比例为2:2:1:2。The technical solution adopted by the present invention is an antibacterial comfortable fabric, which is woven by warp and weft, the warp is made of bamboo fiber, cotton fiber, rich and strong fiber and polyester fiber, and the weft is made of bamboo fiber , Weaving and weaving of rayon fiber, polyester and cotton fiber, the warp yarn bamboo fiber, cotton fiber, rayon fiber and polyester fiber blended blending ratio is 2: 1: 1: 2, the weft yarn bamboo fiber, The blending ratio of rich and strong fiber, polyester and cotton fiber is 2: 2: 1: 2.
进一步的,所述经线和纬线采用平纹或斜纹编织。Further, the warp and weft are woven using plain weave or twill.
一种抗菌舒适型面料加工工艺,其特征在于:具体包括如下步骤:An antibacterial comfort fabric processing technology is characterized in that it specifically includes the following steps:
a、交并工序:将竹纤维,棉纤维,富强纤维和聚酯纤维送入并纱机中进行纱线交并形成混并经线,将竹纤维,富强纤维、涤纶和棉纤维送入并纱机中进行纱线交并形成混并纬线;a. Merging process: Send bamboo fiber, cotton fiber, rich and strong fiber and polyester fiber into the yarn-spinning machine for yarn blending and form a mixed warp, and send bamboo fiber, rich and strong fiber, polyester and cotton fiber into the yarn Interlacing yarns in the machine and forming mixed wefts;
b、络筒工序:将步骤a中混并的经线及纬线送入络筒机内进行络筒,同时控制槽筒线速度为1100~1300m/min,卷绕密度为0.36~0.42g/cm
3;
b. Winding process: send the warp and weft threads mixed in step a into the winder for winding, while controlling the linear speed of the slot to 1100 to 1300 m / min, and the winding density to 0.36 to 0.42 g / cm 3 ;
c、整经工序:采用整经机对步骤b中络筒的纱线进行分条整经,控制整经机的整经速度为340~360mm/min,卷绕密度为0.6~0.8g/cm
3;
c. Warping process: The warping machine is used to warp the yarn in step b. The warping speed of the warping machine is 340-360mm / min, and the winding density is 0.6-0.8g / cm. 3 ;
d、织造工艺:采用剑杆织机进行织造,其中经纱及纬纱按照预设比例送入,其中织造速度为170~220r/min,开口时间为300~320°;d. Weaving process: Weaving with a rapier weaving machine, in which warp and weft yarns are fed in according to a preset ratio, in which the weaving speed is 170-220r / min and the opening time is 300-320 °;
e、后整理工序:将步骤d织造完的原布进行检验,然后烧去布面上的绒毛,再送入定型机中进行定型,使成布符合要求,再进行验布,包装。e. Finishing process: The original cloth woven in step d is inspected, and then the fluff on the cloth surface is burned, and then sent to the setting machine for setting, so that the finished fabric meets the requirements, and then the cloth is inspected and packed.
进一步的,所述步骤b中槽筒线速度为1250m/min,卷绕密度为0.38g/cm
3。
Further, in the step b, the linear speed of the slot cylinder is 1250 m / min, and the winding density is 0.38 g / cm 3 .
进一步的,所述步骤c中整径速度为360mm/min,卷绕密度为0.6g/cm
3。
Further, in the step c, the entire diameter speed is 360 mm / min, and the winding density is 0.6 g / cm 3 .
进一步的,所述步骤d中制造速度为210r/min,开口时间为320°。Further, in the step d, the manufacturing speed is 210 r / min, and the opening time is 320 °.
进一步的,所述步骤e中验布速度为20~25m/min。Further, the cloth inspection speed in the step e is 20-25 m / min.
有益效果:一种抗菌舒适型面料具有防止静电,手感柔软,光泽柔和,强度高、弹性高,抗褶皱,抗菌、抑菌、除螨、防臭和抗紫外线的效果。Beneficial effect: An antibacterial comfortable fabric has the effects of preventing static electricity, soft hand feeling, soft gloss, high strength, high elasticity, anti-wrinkle, antibacterial, antibacterial, anti-mite, deodorant and anti-ultraviolet effects.
下面结合具体实施例对本发明的技术内容进行详细阐述:The technical content of the present invention is described in detail below with reference to specific embodiments:
本发明所揭示的一种抗菌舒适型面料,由经线和纬线相互编织而成,所述经线由竹纤维,棉纤维,富强纤维和聚酯纤维混纺而成,所述的纬线由竹纤维,富强纤维、涤纶和棉纤维混纺编织而成,所述的经线中竹纤维,棉纤维,富强纤维和聚酯纤维混纺混纺比例为2:1:1:2,所述的纬线中竹纤维、富强纤维、涤纶和棉纤维的混纺比例为2:2:1:2。The antibacterial comfortable fabric disclosed by the present invention is woven with warp and weft threads, the warp threads are made by blending bamboo fiber, cotton fiber, rich fiber and polyester fiber, and the weft thread is made of bamboo fiber and rich Fiber, polyester and cotton fiber blended and woven, the warp yarn bamboo fiber, cotton fiber, rich and strong fiber and polyester fiber blended blending ratio is 2: 1: 1: 2, the weft medium bamboo fiber, rich and strong fiber , Polyester and cotton fiber blending ratio is 2: 2: 1: 2.
进一步的,所述经线和纬线采用平纹或斜纹编织。Further, the warp and weft are woven using plain weave or twill.
一种抗菌舒适型面料加工工艺,其特征在于:具体包括如下步骤:An antibacterial comfort fabric processing technology is characterized in that it specifically includes the following steps:
a、交并工序:将竹纤维,棉纤维,富强纤维和聚酯纤维送入并纱机中进行纱线交并形成混并经线,将竹纤维,富强纤维、涤纶和棉纤维送入并纱机中进行纱线交并形成混并纬线;a. Merging process: Send bamboo fiber, cotton fiber, rich and strong fiber and polyester fiber into the yarn-spinning machine for yarn blending and form a mixed warp, and send bamboo fiber, rich and strong fiber, polyester and cotton fiber into the yarn Interlacing yarns in the machine and forming mixed wefts;
b、络筒工序:将步骤a中混并的经线及纬线送入络筒机内进行络筒,同时控制槽筒线速度为1100~1300m/min,卷绕密度为0.36~0.42g/cm
3;
b. Winding process: send the warp and weft threads mixed in step a into the winder for winding, while controlling the linear speed of the slot to 1100 to 1300 m / min, and the winding density to 0.36 to 0.42 g / cm 3 ;
c、整经工序:采用整经机对步骤b中络筒的纱线进行分条整经,控制整经机的整经速度为340~360mm/min,卷绕密度为0.6~0.8g/cm
3;
c. Warping process: The warping machine is used to warp the yarn in step b. The warping speed of the warping machine is 340-360mm / min, and the winding density is 0.6-0.8g / cm. 3 ;
d、织造工艺:采用剑杆织机进行织造,其中经纱及纬纱按照预设比例送入,其中织造速度为170~220r/min,开口时间为300~320°;d. Weaving process: Weaving with a rapier weaving machine, in which warp and weft yarns are fed in according to a preset ratio, in which the weaving speed is 170-220r / min and the opening time is 300-320 °;
e、后整理工序:将步骤d织造完的原布进行检验,然后烧去布面上的绒毛,再送入定型机中进行定型,使成布符合要求,再进行验布,包装。e. Finishing process: The original cloth woven in step d is inspected, and then the fluff on the cloth surface is burned, and then sent to the setting machine for setting, so that the finished fabric meets the requirements, and then the cloth is inspected and packed.
本实例中,所述步骤b中槽筒线速度为1250m/min,卷绕密度为0.38g/cm
3。
In this example, in the step b, the linear speed of the slot cylinder is 1250 m / min, and the winding density is 0.38 g / cm 3 .
本实例中,所述步骤c中整径速度为360mm/min,卷绕密度为0.6g/cm
3。
In this example, in the step c, the entire diameter speed is 360 mm / min, and the winding density is 0.6 g / cm 3 .
本实例中,所述步骤d中制造速度为210r/min,开口时间为320°。In this example, the manufacturing speed in the step d is 210 r / min, and the opening time is 320 °.
本实例中,所述步骤e中验布速度为20~25m/min。In this example, the cloth inspection speed in the step e is 20 to 25 m / min.
以上所述仅是本发明的优选实施方式,应当指出:对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。The above is only a preferred embodiment of the present invention, and it should be pointed out that for those of ordinary skill in the art, without departing from the principles of the present invention, several improvements and retouches can be made. These improvements and retouches also It should be regarded as the protection scope of the present invention.
Claims (7)
- 一种抗菌舒适型面料,由经线和纬线相互编织而成,其特征在于:所述经线由竹纤维,棉纤维,富强纤维和聚酯纤维混纺而成,所述的纬线由竹纤维,富强纤维、涤纶和棉纤维混纺编织而成,所述的经线中竹纤维,棉纤维,富强纤维和聚酯纤维混纺混纺比例为2:1:1:2,所述的纬线中竹纤维、富强纤维、涤纶和棉纤维的混纺比例为2:2:1:2。An antibacterial comfortable fabric made of warp and weft threads, which is characterized in that the warp threads are made of bamboo fiber, cotton fiber, rich fiber and polyester fiber, and the weft thread is made of bamboo fiber and rich fiber Polyester and cotton fibers are blended and woven. The warp yarns are mixed with bamboo fibers, cotton fibers, rich and strong fibers, and polyester fibers in a blended ratio of 2: 1: 1: 2. The blending ratio of polyester and cotton fiber is 2: 2: 1: 2.
- 根据权利要求1所述的一种抗菌舒适型面料,其特征在于:所述经线和纬线采用平纹或斜纹编织。The antibacterial comfort type fabric according to claim 1, wherein the warp and weft threads are woven in plain or twill.
- 一种抗菌舒适型面料加工工艺,其特征在于:具体包括如下步骤:An antibacterial comfort fabric processing technology is characterized in that it specifically includes the following steps:a、交并工序:将竹纤维,棉纤维,富强纤维和聚酯纤维送入并纱机中进行纱线交并形成混并经线,将竹纤维,富强纤维、涤纶和棉纤维送入并纱机中进行纱线交并形成混并纬线;a. Merging process: Send bamboo fiber, cotton fiber, rich and strong fiber and polyester fiber into the yarn-spinning machine for yarn blending and form a mixed warp, and send bamboo fiber, rich and strong fiber, polyester and cotton fiber into the yarn Interlacing yarns in the machine and forming mixed wefts;b、络筒工序:将步骤a中混并的经线及纬线送入络筒机内进行络筒,同时控制槽筒线速度为1100~1300m/min,卷绕密度为0.36~0.42g/cm 3; b. Winding process: send the warp and weft threads mixed in step a into the winder for winding, while controlling the linear speed of the slot to 1100 to 1300 m / min, and the winding density to 0.36 to 0.42 g / cm 3 ;c、整经工序:采用整经机对步骤b中络筒的纱线进行分条整经,控制整经机的整经速度为340~360mm/min,卷绕密度为0.6~0.8g/cm 3; c. Warping process: The warping machine is used to warp the yarn in step b. The warping speed of the warping machine is 340-360mm / min, and the winding density is 0.6-0.8g / cm. 3 ;d、织造工艺:采用剑杆织机进行织造,其中经纱及纬纱按照预设比例送入,其中织造速度为170~220r/min,开口时间为300~320°;d. Weaving process: Weaving with a rapier weaving machine, in which warp and weft yarns are fed in according to a preset ratio, in which the weaving speed is 170-220r / min and the opening time is 300-320 °;e、后整理工序:将步骤d织造完的原布进行检验,然后烧去布面上的绒毛,再送入定型机中进行定型,使成布符合要求,再进行验布,包装。e. Finishing process: The original cloth woven in step d is inspected, and then the fluff on the cloth surface is burned, and then sent to the setting machine for setting, so that the finished fabric meets the requirements, and then the cloth is inspected and packed.
- 根据权利要求3所述的一种抗菌舒适型面料加工工艺,其特征在于:所述步骤b中槽筒线速度为1250m/min,卷绕密度为0.38g/cm 3。 The processing technology for an antibacterial comfort type fabric according to claim 3, characterized in that: in the step b, the linear speed of the slot cylinder is 1250 m / min, and the winding density is 0.38 g / cm 3 .
- 根据权利要求3所述的一种抗菌舒适型面料加工工艺,其特征在于:所述步骤c中整径速度为360mm/min,卷绕密度为0.6g/cm 3。 The processing technology for an antibacterial comfort type fabric according to claim 3, wherein in the step c, the diameter adjustment speed is 360 mm / min, and the winding density is 0.6 g / cm 3 .
- 根据权利要求3所述的一种抗菌舒适型面料加工工艺,其特征在于:所述步骤d中制造速度为210r/min,开口时间为320°。The process for processing an antibacterial comfort type fabric according to claim 3, wherein in the step d, the manufacturing speed is 210 r / min and the opening time is 320 °.
- 根据权利要求3所述的一种抗菌舒适型面料加工工艺,其特征在于:所述步骤e中验布速度为20~25m/min。The processing technology for an antibacterial comfort type fabric according to claim 3, wherein the fabric inspection speed in the step e is 20 to 25 m / min.