WO2019188556A1 - エネルギー貯蔵デバイス用電極及びエネルギー貯蔵デバイス - Google Patents

エネルギー貯蔵デバイス用電極及びエネルギー貯蔵デバイス Download PDF

Info

Publication number
WO2019188556A1
WO2019188556A1 PCT/JP2019/011361 JP2019011361W WO2019188556A1 WO 2019188556 A1 WO2019188556 A1 WO 2019188556A1 JP 2019011361 W JP2019011361 W JP 2019011361W WO 2019188556 A1 WO2019188556 A1 WO 2019188556A1
Authority
WO
WIPO (PCT)
Prior art keywords
electrode
energy storage
storage device
group
undercoat layer
Prior art date
Application number
PCT/JP2019/011361
Other languages
English (en)
French (fr)
Inventor
辰也 畑中
康志 境田
Original Assignee
日産化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日産化学株式会社 filed Critical 日産化学株式会社
Priority to JP2020510731A priority Critical patent/JPWO2019188556A1/ja
Priority to CN201980021550.2A priority patent/CN111902970A/zh
Priority to EP19775814.7A priority patent/EP3780158A4/en
Publication of WO2019188556A1 publication Critical patent/WO2019188556A1/ja

Abstract

集電体と、該集電体の少なくとも一方の面に形成されたカーボンナノチューブを含むアンダーコート層と、該アンダーコート層上に形成された電極合材層とを備える積層体を、１ｋＮ／ｃｍ未満のプレス圧力でプレスしてなるエネルギー貯蔵デバイス用電極を提供する。

Description

エネルギー貯蔵デバイス用電極及びエネルギー貯蔵デバイス
　本発明は、エネルギー貯蔵デバイス用電極及びエネルギー貯蔵デバイスに関する。
　近年、リチウムイオン二次電池や電気二重層キャパシタをはじめとしたエネルギー貯蔵デバイスの用途拡大に伴い、内部抵抗の低抵抗化、高エネルギー密度化、長寿命化、高速充放電特性が求められている。これらの要求に応えるための一つの方法として、電極合材層と集電体との間に導電性炭素材料を含むアンダーコート層を配置して、それらの接触界面の抵抗を下げること、及び電極合材層と集電体との間の密着力を高め、界面剥離による電池劣化を抑制することが提案されている（例えば、特許文献１、２参照）。
　一方、電池の高速充放電特性の向上には、電池の抵抗を下げることが重要である。電極のプレスをしない又は低い圧力でプレスすることで、電極合材層の空隙率が大きく保たれ、イオンの拡散抵抗の低減や、更に電解液との接触面積の低減を抑制することによる電解移動抵抗の低減が可能である。しかしながら、プレスをしない又はプレス圧力が低い場合には、電極合材層と集電体の界面抵抗が大きく、高速充放電特性が低下してしまう問題があった。また、電極合材層と集電体の密着力が低いことにより、剥離による抵抗上昇や容量劣化が生じる問題があった。
特開２０１０－１７０９６５号公報 国際公開第２０１４／０４２０８０号
　本発明は、前記事情に鑑みなされたもので、電極製造時のプレス圧力が小さくても、電極合材層と集電体との界面の抵抗を小さくでき、高速充放電特性が良好なエネルギー貯蔵デバイス用電極を提供することを目的とする。
　本発明者らは、前記目的を達成するために鋭意検討を重ねた結果、集電体と、アンダーコート層と、アンダーコート層上に形成された電極合材層とを備える電極において、アンダーコート層にカーボンナノチューブを用いることで、電極製造時のプレス圧力が小さくても、電極合材層と集電箔の界面の抵抗が小さい電極を作製できることを見出し、本発明を完成した。
　すなわち、本発明は、下記エネルギー貯蔵デバイス用電極及びエネルギー貯蔵デバイスを提供する。
１．集電体と、該集電体の少なくとも一方の面に形成されたカーボンナノチューブを含むアンダーコート層と、該アンダーコート層上に形成された電極合材層とを備える積層体を、１ｋＮ／ｃｍ未満のプレス圧力でプレスしてなるエネルギー貯蔵デバイス用電極。
２．前記プレス圧力が、０.５ｋＮ／ｃｍ以下である１のエネルギー貯蔵デバイス用電極。
３．前記プレス圧力が、０.２ｋＮ／ｃｍ以下である２のエネルギー貯蔵デバイス用電極。
４．前記プレス圧力が、０ｋＮ／ｃｍである３のエネルギー貯蔵デバイス用電極。
５．集電体と、該集電体の少なくとも一方の面に形成されたカーボンナノチューブを含むアンダーコート層と、該アンダーコート層上に形成された電極合材層とを備える電極であって、電極密度が２.１ｇ／ｃｍ3未満であるエネルギー貯蔵デバイス用電極。
６．前記電極密度が、２.０ｇ／ｃｍ3未満である５のエネルギー貯蔵デバイス用電極。
７．前記電極密度が、１.７ｇ／ｃｍ3以下である６のエネルギー貯蔵デバイス用電極。
８．前記電極密度が、１.３ｇ／ｃｍ3以下である７のエネルギー貯蔵デバイス用電極。
９．集電体の一面あたりのアンダーコート層の目付量が、１,０００ｍｇ／ｍ2以下である１～８のいずれかのエネルギー貯蔵デバイス用電極。
１０．集電体の一面あたりのアンダーコート層の目付量が、５００ｍｇ／ｍ2以下である９のエネルギー貯蔵デバイス用電極。
１１．集電体の一面あたりのアンダーコート層の目付量が、３００ｍｇ／ｍ2以下である１０のエネルギー貯蔵デバイス用電極。
１２．集電体の一面あたりのアンダーコート層の目付量が、２００ｍｇ／ｍ2以下である１１のエネルギー貯蔵デバイス用電極。
１３．前記アンダーコート層が、カーボンナノチューブ分散剤を含むものである１～１２のいずれかのエネルギー貯蔵デバイス用電極。
１４．前記カーボンナノチューブ分散剤が、側鎖にオキサゾリン基を含むビニル系ポリマー又はトリアリールアミン系高分岐ポリマーを含むものである１３のエネルギー貯蔵デバイス用電極。
１５．前記アンダーコート層が、マトリックス高分子を含むものである１～１４のいずれかのエネルギー貯蔵デバイス用電極。
１６．前記集電体が、アルミニウム箔又は銅箔である１～１５のいずれかのエネルギー貯蔵デバイス用電極。
１７．正極である１～１６のいずれかのエネルギー貯蔵デバイス用電極。
１８．負極である１～１６のいずれかのエネルギー貯蔵デバイス用電極。
１９．１～１８のいずれかのエネルギー貯蔵デバイス用電極を備えるエネルギー貯蔵デバイス。
２０．集電体上の少なくとも一方の面にカーボンナノチューブを含むアンダーコート層を形成する工程、該アンダーコート層上に電極合材層を形成する工程、及び１ｋＮ／ｃｍ未満のプレス圧力でプレスする工程を含むエネルギー貯蔵デバイス用電極の製造方法。
２１．前記プレス圧力が、０.５ｋＮ／ｃｍ以下である２０のエネルギー貯蔵デバイス用電極の製造方法。
２２．前記プレス圧力が、０.２ｋＮ／ｃｍ以下である２１のエネルギー貯蔵デバイス用電極の製造方法。
２３．前記プレス圧力が、０ｋＮ／ｃｍである２２のエネルギー貯蔵デバイス用電極の製造方法。
　本発明のエネルギー貯蔵デバイス用電極によれば、電極合材層と集電体の界面の抵抗が小さく、高速充放電特性に優れ、サイクル劣化の少ないエネルギー貯蔵デバイスを得ることができる。
本発明で好適に用いられるくびれ部を有するカーボンナノチューブの模式断面図である。
［エネルギー貯蔵デバイス用電極］
　本発明のエネルギー貯蔵デバイス用電極は、集電体と、該集電体の少なくとも一方の面に形成されたカーボンナノチューブを含むアンダーコート層と、該アンダーコート層上に形成された電極合材層とを備える積層体を、１ｋＮ／ｃｍ未満のプレス圧力でプレスしてなるものである。
［集電体］
　前記集電体は、従来、エネルギー貯蔵デバイス用電極の集電体として用いられているものを使用することができる。例えば、銅、アルミニウム、チタン、ステンレススチール、ニッケル、金、銀及びこれらの合金や、カーボン材料、金属酸化物、導電性高分子等を用いることができるが、超音波溶接等の溶接を適用して電極構造体を作製する場合、銅、アルミニウム、チタン、ステンレススチール又はこれらの合金からなる金属箔を用いることが好ましい。集電体の厚みは特に限定されないが、本発明においては、１～１００μｍが好ましい。
［アンダーコート層］
　前記アンダーコート層は、導電材としてカーボンナノチューブ（ＣＮＴ）を含む。ＣＮＴは、一般的に、アーク放電法、化学気相成長法（ＣＶＤ法）、レーザー・アブレーション法等によって作製されるが、本発明に使用されるＣＮＴはいずれの方法で得られたものでもよい。また、ＣＮＴには１枚の炭素膜（グラフェン・シート）が円筒状に巻かれた単層ＣＮＴ（ＳＷＣＮＴ）と、２枚のグラフェン・シートが同心円状に巻かれた２層ＣＮＴ（ＤＷＣＮＴ）と、複数のグラフェン・シートが同心円状に巻かれた多層ＣＮＴ（ＭＷＣＮＴ）とがあるが、本発明においては、ＳＷＣＮＴ、ＤＷＣＮＴ、ＭＷＣＮＴをそれぞれ単体で、又は複数を組み合わせて使用できる。コストの観点からは、特に直径が２ｎｍ以上ある多層ＣＮＴが好ましく、薄膜化できるという観点からは、特に直径５００ｎｍ以下の多層ＣＮＴが好ましく、直径１００ｎｍ以下の多層ＣＮＴがより好ましく、直径５０ｎｍ以下の多層ＣＮＴがより一層好ましく、直径３０ｎｍ以下の多層ＣＮＴが最も好ましい。なお、ＣＮＴの直径は、例えば、ＣＮＴを溶媒中に分散させたものを乾燥させて得た薄膜を、透過型電子顕微鏡で観察することで測定することができる。
　なお、前記方法でＳＷＣＮＴ、ＤＷＣＮＴ又はＭＷＣＮＴを作製する際には、ニッケル、鉄、コバルト、イットリウム等の触媒金属が残存することがあるため、この不純物を除去するための精製を必要とする場合がある。不純物の除去には、硝酸、硫酸等による酸処理とともに超音波処理が有効である。しかし、硝酸、硫酸等による酸処理ではＣＮＴを構成するπ共役系が破壊され、ＣＮＴ本来の特性が損なわれてしまう可能性があるため、適切な条件で精製して使用することが望ましい。
　前記ＣＮＴとしては、その分散液を塗膜にしてアンダーコート層とした際に電池抵抗を下げる効果を発揮するために、分散液中で分散しやすいものを用いることが好ましい。そのようなＣＮＴとしては、小さいエネルギーで容易に切断可能な結晶不連続部を多く有していることが好ましい。このような観点から、本発明に用いられるＣＮＴは、くびれ部を有するものが好ましい。くびれ部を有するＣＮＴとは、ＣＮＴのウォールに、平行部と平行部のチューブ外径に対して９０％以下のチューブ外径であるくびれ部とを有するものである。このくびれ部は、ＣＮＴの成長方向が変更されることで作り出される部位であるため、結晶不連続部を有しており、小さな機械的エネルギーで容易に切断できる易破断箇所となる。
　図１に平行部１とくびれ部３とを有するＣＮＴの模式断面図を示す。平行部１は、図１に示されるように、ウォールが２本の平行な直線又は２本の平行な曲線と認識できる部分である。この平行部１において、平行線の法線方向のウォールの外壁間の距離が平行部１のチューブ外径２である。一方、くびれ部３は、その両端が平行部１と連接し、平行部１に比べてウォール間の距離が近づいている部分であり、より具体的には、平行部１のチューブ外径２に対して９０％以下のチューブ外径４を持つ部分である。なお、くびれ部３のチューブ外径４は、くびれ部３において、外壁を構成するウォールが最も近い箇所の外壁間距離である。図１に示されるように、くびれ部３の多くには結晶が不連続である箇所が存在する。
　前記ＣＮＴのウォールの形状とチューブ外径は、透過型電子顕微鏡等で観察することができる。具体的には、ＣＮＴの０.５％分散液を作製し、その分散液を試料台にのせて乾燥させ、透過型電子顕微鏡で５万倍にて撮影した画像によりくびれ部を確認することができる。
　前記ＣＮＴは、ＣＮＴの０.１％分散液を作製し、その分散液を試料台にのせて乾燥させ、透過型電子顕微鏡で２万倍にて撮影した画像を１００ｎｍ四方の区画に区切り、１００ｎｍ四方の区画にＣＮＴの占める割合が１０～８０％である区画を３００区画選択した際に、１区画中にくびれ部分が少なくとも１箇所存在する区画が３００区画中に占める割合によって易破断箇所の全体に占める割合(易破断箇所の存在割合)を判断する。区画中のＣＮＴの占める面積が１０％未満の場合には、ＣＮＴの存在量が少なすぎるため測定が困難である。また、区画のＣＮＴの占める面積が８０％を超える場合には、区画に占めるＣＮＴが多くなるためＣＮＴが重なり合ってしまい、平行部分とくびれ部分を区別するのが困難であり正確な測定が困難となる。
　本発明で用いるＣＮＴにおいては、易破断箇所の存在割合が６０％以上である。易破断箇所の存在割合が６０％よりも少ない場合は、ＣＮＴが分散しにくく、分散させるために過度の機械的エネルギーを加えた時には、グラファイト綱面の結晶構造破壊につながり、ＣＮＴの特徴である電気導電性等の特性が低下する。より高い分散性を得るためには、易破断箇所の存在割合は、７０％以上であることが好ましい。
　本発明で使用可能なＣＮＴの具体例としては、国際公開第２０１６／０７６３９３号や特開２０１７－２０６４１３号公報に開示されたくびれ構造を有するＣＮＴである、ＴＣ－２０１０、ＴＣ－２０２０、ＴＣ－３２１０Ｌ、ＴＣ－１２１０ＬＮ等のＴＣシリーズ（戸田工業(株)製）、スパーグロース法ＣＮＴ（国立研究開発法人 新エネルギー・産業技術総合開発機構製）、ｅＤＩＰＳ－ＣＮＴ（国立研究開発法人 新エネルギー・産業技術総合開発機構製）、ＳＷＮＴシリーズ（(株)名城ナノカーボン製：商品名）、ＶＧＣＦシリーズ（昭和電工(株)製：商品名）、FloTubeシリーズ（CNano Technology社製：商品名）、ＡＭＣ（宇部興産(株)製：商品名）、NANOCYL NC7000シリーズ（Nanocyl S.A.社製：商品名）、Baytubes（Bayer社製：商品名）、GRAPHISTRENGTH（アルケマ社製：商品名）、ＭＷＮＴ７（保土谷化学工業(株)製：商品名）、ハイペリオンＣＮＴ（Hypeprion Catalysis International社製：商品名）等が挙げられる。
　前記アンダーコート層は、前述したＣＮＴと、溶媒とを含むＣＮＴ含有組成物（分散液）を用いて作製することが好ましい。
　溶媒としては、従来、導電性組成物の調製に用いられるものであれば特に限定されず、例えば、水；テトラヒドロフラン（ＴＨＦ）、ジエチルエーテル、１,２－ジメトキシエタン（ＤＭＥ）等のエーテル類；塩化メチレン、クロロホルム、１,２－ジクロロエタン等のハロゲン化炭化水素類；Ｎ,Ｎ－ジメチルホルムアミド（ＤＭＦ）、Ｎ,Ｎ－ジメチルアセトアミド（ＤＭＡｃ）、Ｎ－メチル－２－ピロリドン（ＮＭＰ）等のアミド類；アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン類；メタノール、エタノール、ｎ－プロパノール、イソプロパノール、ｎ－ブタノール、ｔｅｒｔ－ブタノール等のアルコール類；ｎ－ヘプタン、ｎ－ヘキサン、シクロヘキサン等の脂肪族炭化水素類；ベンゼン、トルエン、キシレン、エチルベンゼン等の芳香族炭化水素類；エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、プロピレングリコールモノメチルエーテル等のグリコールエーテル類；エチレングリコール、プロピレングリコール等のグリコール類等の有機溶媒が挙げられる。これらの溶媒は、１種単独で又は２種以上を混合して用いることができる。特に、ＣＮＴの孤立分散の割合を向上させ得るという点から、水、ＮＭＰ、ＤＭＦ、ＴＨＦ、メタノール、エタノール、ｎ－プロパノール、イソプロパノール、ｎ－ブタノール、ｔｅｒｔ－ブタノールが好ましい。また塗工性を向上させ得るという点から、メタノール、エタノール、ｎ－プロパノール、イソプロパノール、ｎ－ブタノール、ｔｅｒｔ－ブタノールを含むことが好ましい。またコストを下げ得るという点からは、水を含むことが好ましい。これらの溶媒は、孤立分散の割合を増やすこと、塗工性を上げること、コストを下げることを目的として、１種単独で又は２種以上を混合して用いることができる。水とアルコール類との混合溶媒を用いる場合、その混合割合は特に限定されないが、質量比で、水：アルコール類＝１：１～１０：１程度が好ましい。
　また、前記ＣＮＴ含有組成物は、必要に応じてマトリックス高分子を含んでもよい。マトリックス高分子としては、ポリフッ化ビニリデン（ＰＶＤＦ）、ポリテトラフルオロエチレン、テトラフルオロエチレン－ヘキサフルオロプロピレン共重合体、フッ化ビニリデン－ヘキサフルオロプロピレン共重合体（Ｐ(ＶＤＦ－ＨＦＰ)）、フッ化ビニリデン－塩化３フッ化エチレン共重合体（Ｐ(ＶＤＦ－ＣＴＦＥ)）等のフッ素系樹脂；ポリビニルピロリドン、エチレン－プロピレン－ジエン三元共重合体、ポリエチレン（ＰＥ）、ポリプロピレン（ＰＰ）、エチレン－酢酸ビニル共重合体（ＥＶＡ）、ＥＥＡ（エチレン－アクリル酸エチル共重合体）等のポリオレフィン系樹脂；ポリスチレン（ＰＳ）、ハイインパクトポリスチレン（ＨＩＰＳ）、アクリロニトリル－スチレン共重合体（ＡＳ）、アクリロニトリル－ブタジエン－スチレン共重合体（ＡＢＳ）、メタクリル酸メチル－スチレン共重合体（ＭＳ）、スチレン－ブタジエンゴム等のポリスチレン系樹脂；ポリカーボネート樹脂；塩化ビニル樹脂；ポリアミド樹脂；ポリイミド樹脂；ポリアクリル酸ナトリウム、ポリメチルメタクリレート（ＰＭＭＡ）等の(メタ)アクリル樹脂；ポリエチレンテレフタレート（ＰＥＴ）、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンナフタレート、ポリ乳酸（ＰＬＡ）、ポリ－３－ヒドロキシ酪酸、ポリカプロラクトン、ポリブチレンサクシネート、ポリエチレンサクシネート／アジペート等のポリエステル樹脂；ポリフェニレンエーテル樹脂；変性ポリフェニレンエーテル樹脂；ポリアセタール樹脂；ポリスルホン樹脂；ポリフェニレンサルファイド樹脂；ポリビニルアルコール樹脂；ポリグルコール酸；変性でんぷん；酢酸セルロース、カルボキシメチルセルロース、三酢酸セルロース；キチン、キトサン；リグニン等の熱可塑性樹脂や、ポリアニリン及びその半酸化体であるエメラルジンベース；ポリチオフェン；ポリピロール；ポリフェニレンビニレン；ポリフェニレン；ポリアセチレン等の導電性高分子、更にはエポキシ樹脂；ウレタンアクリレート；フェノール樹脂；メラミン樹脂；尿素樹脂；アルキド樹脂等の熱硬化性樹脂や光硬化性樹脂等が挙げられる。前記ＣＮＴ含有組成物においては、溶媒として水を用いることが好適であることから、マトリックス高分子としても水溶性のもの、例えば、ポリアクリル酸ナトリウム、カルボキシメチルセルロースナトリウム、水溶性セルロースエーテル、アルギン酸ナトリウム、ポリビニルアルコール、ポリスチレンスルホン酸、ポリエチレングリコール等が好ましいが、特に、ポリアクリル酸ナトリウム、カルボキシメチルセルロースナトリウム等が好適である。
　マトリックス高分子は、市販品として入手することもでき、例えば、アロンA-10H（ポリアクリル酸、東亞合成(株)製、固形分濃度２６質量％、水溶液）、アロンA-30（ポリアクリル酸アンモニウム、東亞合成(株)製、固形分濃度３２質量％、水溶液）、ポリアクリル酸ナトリウム（和光純薬工業(株)製、重合度２,７００～７,５００）、カルボキシメチルセルロースナトリウム（和光純薬工業(株)製）、アルギン酸ナトリウム（関東化学(株)製、鹿１級）、メトローズ（登録商標）ＳＨシリーズ（ヒドロキシプロピルメチルセルロース、信越化学工業(株)製）、メトローズＳＥシリーズ（ヒドロキシエチルメチルセルロース、信越化学工業(株)製）、JC-25（完全ケン化型ポリビニルアルコール、日本酢ビ・ポバール(株)製）、JM-17（中間ケン化型ポリビニルアルコール、日本酢ビ・ポバール(株)製）、JP-03（部分ケン化型ポリビニルアルコール、日本酢ビ・ポバール(株)製）、ポリスチレンスルホン酸（Aldrich社製、固形分濃度１８質量％、水溶液）等が挙げられる。
　マトリックス高分子の含有量は、特に限定されないが、組成物中に０.０００１～９９質量％程度とすることが好ましく、０.００１～９０質量％程度とすることがより好ましい。
　更に、前記ＣＮＴ含有組成物は、組成物中でのＣＮＴの分散性を高めるため、分散剤を含んでもよい。前記分散剤としては、特に限定されないが、公知のものから適宜選択することができ、例えば、カルボキシメチルセルロース（ＣＭＣ）、ポリビニルピロリドン（ＰＶＰ）、アクリル樹脂エマルジョン、水溶性アクリル系ポリマー、スチレンエマルジョン、シリコーンエマルジョン、アクリルシリコーンエマルジョン、フッ素樹脂エマルジョン、ＥＶＡエマルジョン、酢酸ビニルエマルジョン、塩化ビニルエマルジョン、ウレタン樹脂エマルジョン、国際公開第２０１４／０４２８０号記載のトリアリールアミン系高分岐ポリマー、国際公開第２０１５／０２９９４９号記載の側鎖にオキサゾリン基を有するビニル系ポリマー等が挙げられる。本発明においては、国際公開第２０１５／０２９９４９号記載の側鎖にオキサゾリン基を有するポリマーを含む分散剤や、国際公開第２０１４／０４２８０号記載のトリアリールアミン系高分岐ポリマーを含む分散剤を用いることが好ましい。
　側鎖にオキサゾリン基を有するポリマー（以下、オキサゾリンポリマーともいう。）としては、式（１）で表されるような２位に重合性炭素－炭素二重結合含有基を有するオキサゾリンモノマーをラジカル重合して得られる、オキサゾリン環の２位でポリマー主鎖又はスペーサー基に結合した繰り返し単位を有する、側鎖にオキサゾリン基を有するビニル系ポリマーが好ましい。
Figure JPOXMLDOC01-appb-C000001
　式（１）中、Ｘは、重合性炭素－炭素二重結合含有基であり、Ｒ1～Ｒ4は、それぞれ独立に、水素原子、ハロゲン原子、炭素数１～５のアルキル基、炭素数６～２０のアリール基、又は炭素数７～２０のアラルキル基である。
　オキサゾリンモノマーが有する重合性炭素－炭素二重結合含有基としては、重合性炭素－炭素二重結合を含んでいれば特に限定されないが、重合性炭素－炭素二重結合を含む鎖状炭化水素基が好ましく、例えば、ビニル基、アリル基、イソプロペニル基等の炭素数２～８のアルケニル基等が好ましい。
　ここで、ハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子が挙げられる。
　炭素数１～５のアルキル基としては、直鎖状、分岐鎖状、環状のいずれでもよく、例えば、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ｔｅｒｔ－ブチル基、ｎ－ペンチル基、シクロヘキシル基等が挙げられる。
　炭素数６～２０のアリール基の具体例としては、フェニル基、キシリル基、トリル基、ビフェニリル基、ナフチル基等が挙げられる。
　炭素数７～２０のアラルキル基の具体例としては、ベンジル基、フェニルエチル基、フェニルシクロヘキシル基等が挙げられる。
　式（１）で表される２位に重合性炭素－炭素二重結合含有基を有するオキサゾリンモノマーの具体例としては、２－ビニル－２－オキサゾリン、２－ビニル－４－メチル－２－オキサゾリン、２－ビニル－４－エチル－２－オキサゾリン、２－ビニル－４－プロピル－２－オキサゾリン、２－ビニル－４－ブチル－２－オキサゾリン、２－ビニル－５－メチル－２－オキサゾリン、２－ビニル－５－エチル－２－オキサゾリン、２－ビニル－５－プロピル－２－オキサゾリン、２－ビニル－５－ブチル－２－オキサゾリン、２－イソプロペニル－２－オキサゾリン、２－イソプロペニル－４－メチル－２－オキサゾリン、２－イソプロペニル－４－エチル－２－オキサゾリン、２－イソプロペニル－４－プロピル－２－オキサゾリン、２－イソプロペニル－４－ブチル－２－オキサゾリン、２－イソプロペニル－５－メチル－２－オキサゾリン、２－イソプロペニル－５－エチル－２－オキサゾリン、２－イソプロペニル－５－プロピル－２－オキサゾリン、２－イソプロペニル－５－ブチル－２－オキサゾリン等が挙げられるが、入手容易性等の点から、２－イソプロペニル－２－オキサゾリンが好ましい。
　また、水系溶媒を用いて組成物を調製することを考慮すると、オキサゾリンポリマーも水溶性であることが好ましい。このような水溶性のオキサゾリンポリマーは、式（１）で表されるオキサゾリンモノマーのホモポリマーでもよいが、水への溶解性をより高めるため、前記オキサゾリンモノマーと親水性官能基を有する(メタ)アクリル酸エステル系モノマーとの少なくとも２種のモノマーをラジカル重合させて得られたものであることが好ましい。
　親水性官能基を有する(メタ)アクリル系モノマーの具体例としては、(メタ)アクリル酸、アクリル酸２－ヒドロキシエチル、アクリル酸メトキシポリエチレングリコール、アクリル酸とポリエチレングリコールとのモノエステル化物、アクリル酸２－アミノエチル及びその塩、メタクリル酸２－ヒドロキシエチル、メタクリル酸メトキシポリエチレングリコール、メタクリル酸とポリエチレングリコールとのモノエステル化物、メタクリル酸２－アミノエチル及びその塩、(メタ)アクリル酸ナトリウム、(メタ)アクリル酸アンモニウム、(メタ)アクリルニトリル、(メタ)アクリルアミド、Ｎ－メチロール(メタ)アクリルアミド、Ｎ－(２－ヒドロキシエチル)(メタ)アクリルアミド、スチレンスルホン酸ナトリウム等が挙げられ、これらは、１種単独で用いても、２種以上組み合わせて用いてもよい。これらの中でも、(メタ)アクリル酸メトキシポリエチレングリコール、(メタ)アクリル酸とポリエチレングリコールとのモノエステル化物が好適である。
　また、オキサゾリンポリマーのＣＮＴ分散能に悪影響を及ぼさない範囲で、前記オキサゾリンモノマー及び親水性官能基を有する(メタ)アクリル系モノマー以外のその他のモノマーを併用することができる。その他のモノマーの具体例としては、(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸ブチル、(メタ)アクリル酸２－エチルヘキシル、(メタ)アクリル酸ステアリル、(メタ)アクリル酸パーフルオロエチル、(メタ)アクリル酸フェニル等の(メタ)アクリル酸エステルモノマー；エチレン、プロピレン、ブテン、ペンテン等のα－オレフィン系モノマー；塩化ビニル、塩化ビニリデン、フッ化ビニル等のハロオレフィン系モノマー；スチレン、α－メチルスチレン等のスチレン系モノマー；酢酸ビニル、プロピオン酸ビニル等のカルボン酸ビニルエステル系モノマー；メチルビニルエーテル、エチルビニルエーテル等のビニルエーテル系モノマー等が挙げられ、これらはそれぞれ単独で用いても、２種以上組み合わせて用いてもよい。
　本発明で用いるオキサゾリンポリマーの製造に用いられるモノマー成分において、オキサゾリンモノマーの含有率は、得られるオキサゾリンポリマーのＣＮＴ分散能をより高めるという点から、１０質量％以上が好ましく、２０質量％以上がより好ましく、３０質量％以上がより一層好ましい。なお、モノマー成分におけるオキサゾリンモノマーの含有率の上限値は１００質量％であり、この場合は、オキサゾリンモノマーのホモポリマーが得られる。一方、得られるオキサゾリンポリマーの水溶性をより高めるという点から、モノマー成分における親水性官能基を有する(メタ)アクリル系モノマーの含有率は、１０質量％以上が好ましく、２０質量％以上がより好ましく、３０質量％以上がより一層好ましい。また、モノマー成分におけるその他の単量体の含有率は、前述のとおり、得られるオキサゾリンポリマーのＣＮＴ分散能に影響を与えない範囲であり、また、その種類によって異なるため一概には決定できないが、５～９５質量％、好ましくは１０～９０質量％の範囲で適宜設定すればよい。
　オキサゾリンポリマーの平均分子量は特に限定されないが、重量平均分子量が１,０００～２,０００,０００が好ましく、２,０００～１,０００,０００がより好ましい。なお、重量平均分子量は、ゲルパーミエーションクロマトグラフィーによるポリスチレン換算値である。
　本発明で使用可能なオキサゾリンポリマーは、前記モノマーを従来公知のラジカル重合にて合成することができるが、市販品として入手することもでき、そのような市販品としては、例えば、エポクロス（登録商標）WS-300（(株)日本触媒製、固形分濃度１０質量％、水溶液）、エポクロスWS-700（(株)日本触媒製、固形分濃度２５質量％、水溶液）、エポクロスWS-500（(株)日本触媒製、固形分濃度３９質量％、水／１－メトキシ－２－プロパノール溶液）、Poly(2-ethyl-2-oxazoline)（Aldrich社製）、Poly(2-ethyl-2-oxazoline)（AlfaAesar社製）、Poly(2-ethyl-2-oxazoline)（VWR International社製）等が挙げられる。なお、溶液として市販されている場合、そのまま使用しても、目的とする溶媒に置換してから使用してもよい。
　また、下記式（２）及び（３）で表される、トリアリールアミン類とアルデヒド類及び／又はケトン類とを酸性条件下で縮合重合することで得られる高分岐ポリマーも好適に用いられる。
Figure JPOXMLDOC01-appb-C000002
　式（２）及び（３）中、Ａｒ1～Ａｒ3は、それぞれ独立に、式（４）～（８）で表されるいずれかの２価の有機基であるが、特に、式（４）で表される置換又は非置換のフェニレン基が好ましい。
Figure JPOXMLDOC01-appb-C000003
　また、式（２）及び（３）において、Ｚ1及びＺ2は、それぞれ独立に、水素原子、炭素数１～５の分岐構造を有していてもよいアルキル基、又は式（９）～（１２）で表されるいずれかの１価の有機基である（ただし、Ｚ1及びＺ2が同時に前記アルキル基となることはない。）が、Ｚ1及びＺ2としては、それぞれ独立に、水素原子、２－又は３－チエニル基、式（９）で表される基が好ましく、特に、Ｚ1及びＺ2のいずれか一方が水素原子で、他方が、水素原子、２－又は３－チエニル基、式（９）で表される基、特にＲ141がフェニル基のもの、又はＲ141がメトキシ基のものがより好ましい。なお、Ｒ141がフェニル基の場合、後述する酸性基導入法において、ポリマー製造後に酸性基を導入する方法を用いた場合、このフェニル基上に酸性基が導入される場合もある。前記炭素数１～５の分岐構造を有していてもよいアルキル基としては、前記で例示したものと同様のものが挙げられる。
Figure JPOXMLDOC01-appb-C000004
　式（３）～（８）中、Ｒ101～Ｒ138は、それぞれ独立に、水素原子、ハロゲン原子、炭素数１～５の分岐構造を有していてもよいアルキル基、炭素数１～５の分岐構造を有していてもよいアルコキシ基、又はカルボキシ基、スルホ基、リン酸基、ホスホン酸基若しくはそれらの塩である。
　ここで、ハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子が挙げられる。
　炭素数１～５の分岐構造を有していてもよいアルキル基としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ｔｅｒｔ－ブチル基、ｎ－ペンチル基等が挙げられる。
　炭素数１～５の分岐構造を有していてもよいアルコキシ基としては、メトキシ基、エトキシ基、ｎ－プロポキシ基、イソプロポキシ基、ｎ－ブトキシ基、ｓｅｃ－ブトキシ基、ｔｅｒｔ－ブトキシ基、ｎ－ペントキシ基等が挙げられる。
　カルボキシ基、スルホ基、リン酸基及びホスホン酸基の塩としては、ナトリウム、カリウム等のアルカリ金属塩；マグネシウム、カルシウム等の２族金属塩；アンモニウム塩；プロピルアミン、ジメチルアミン、トリエチルアミン、エチレンジアミン等の脂肪族アミン塩；イミダゾリン、ピペラジン、モルホリン等の脂環式アミン塩；アニリン、ジフェニルアミン等の芳香族アミン塩；ピリジニウム塩等が挙げられる。
　式（９）～（１２）において、Ｒ139～Ｒ162は、それぞれ独立に、水素原子、ハロゲン原子、炭素数１～５の分岐構造を有していてもよいアルキル基、炭素数１～５の分岐構造を有していてもよいハロアルキル基、フェニル基、－ＯＲ163、－ＣＯＲ163、－ＮＲ163Ｒ164、－ＣＯＯＲ165（これらの式中、Ｒ163及びＲ164は、それぞれ独立に、水素原子、炭素数１～５の分岐構造を有していてもよいアルキル基、炭素数１～５の分岐構造を有していてもよいハロアルキル基、又はフェニル基であり、Ｒ165は、炭素数１～５の分岐構造を有していてもよいアルキル基、炭素数１～５の分岐構造を有していてもよいハロアルキル基、又はフェニル基である。）、又はカルボキシ基、スルホ基、リン酸基、ホスホン酸基若しくはそれらの塩である。
　ここで、炭素数１～５の分岐構造を有していてもよいハロアルキル基としては、ジフルオロメチル基、トリフルオロメチル基、ブロモジフルオロメチル基、２－クロロエチル基、２－ブロモエチル基、１,１－ジフルオロエチル基、２,２,２－トリフルオロエチル基、１,１,２,２－テトラフルオロエチル基、２－クロロ－１,１,２－トリフルオロエチル基、ペンタフルオロエチル基、３－ブロモプロピル基、２,２,３,３－テトラフルオロプロピル基、１,１,２,３,３,３－ヘキサフルオロプロピル基、１,１,１,３,３,３－ヘキサフルオロプロパン－２－イル基、３－ブロモ－２－メチルプロピル基、４－ブロモブチル基、パーフルオロペンチル基等が挙げられる。
　なお、ハロゲン原子、炭素数１～５の分岐構造を有していてもよいアルキル基としては、式（３）～（８）で例示した基と同様のものが挙げられる。
　特に、集電体との密着性をより向上させることを考慮すると、前記高分岐ポリマーは、式（２）又は（３）で表される繰り返し単位の少なくとも１つの芳香環中に、カルボキシ基、スルホ基、リン酸基、ホスホン酸基、及びそれらの塩から選ばれる少なくとも１種の酸性基を有するものが好ましく、スルホ基又はその塩を有するものがより好ましい。
　前記高分岐ポリマーの製造に用いられるアルデヒド化合物としては、ホルムアルデヒド、パラホルムアルデヒド、アセトアルデヒド、プロピルアルデヒド、ブチルアルデヒド、イソブチルアルデヒド、バレルアルデヒド、カプロンアルデヒド、２－メチルブチルアルデヒド、ヘキシルアルデヒド、ウンデシルアルデヒド、７－メトキシ－３,７－ジメチルオクチルアルデヒド、シクロヘキサンカルボキシアルデヒド、３－メチル－２－ブチルアルデヒド、グリオキザール、マロンアルデヒド、スクシンアルデヒド、グルタルアルデヒド、アジピンアルデヒド等の飽和脂肪族アルデヒド類；アクロレイン、メタクロレイン等の不飽和脂肪族アルデヒド類；フルフラール、ピリジンアルデヒド、チオフェンアルデヒド等のヘテロ環式アルデヒド類；ベンズアルデヒド、トリルアルデヒド、トリフルオロメチルベンズアルデヒド、フェニルベンズアルデヒド、サリチルアルデヒド、アニスアルデヒド、アセトキシベンズアルデヒド、テレフタルアルデヒド、アセチルベンズアルデヒド、ホルミル安息香酸、ホルミル安息香酸メチル、アミノベンズアルデヒド、Ｎ,Ｎ－ジメチルアミノベンズアルデヒド、Ｎ,Ｎ－ジフェニルアミノベンズアルデヒド、ナフチルアルデヒド、アントリルアルデヒド、フェナントリルアルデヒド等の芳香族アルデヒド類；フェニルアセトアルデヒド、３－フェニルプロピオンアルデヒド等のアラルキルアルデヒド類等が挙げられるが、中でも、芳香族アルデヒド類を用いることが好ましい。
　また、前記高分岐ポリマーの製造に用いられるケトン化合物としては、アルキルアリールケトン、ジアリールケトン類であり、例えば、アセトフェノン、プロピオフェノン、ジフェニルケトン、フェニルナフチルケトン、ジナフチルケトン、フェニルトリルケトン、ジトリルケトン等が挙げられる。
　本発明に用いられる高分岐ポリマーは、下記スキーム１に示されるように、例えば、下記式（Ａ）で表されるような、前述したトリアリールアミン骨格を与え得るトリアリールアミン化合物と、例えば下記式（Ｂ）で表されるようなアルデヒド化合物及び／又はケトン化合物とを、酸触媒の存在下で縮合重合して得られる。なお、アルデヒド化合物として、例えば、テレフタルアルデヒド等のフタルアルデヒド類のような、二官能化合物（Ｃ）を用いる場合、スキーム１で示される反応が生じるだけではなく、下記スキーム２で示される反応が生じ、２つの官能基が共に縮合反応に寄与した、架橋構造を有する高分岐ポリマーが得られる場合もある。
Figure JPOXMLDOC01-appb-C000005
 （式中、Ａｒ1～Ａｒ3、及びＺ1～Ｚ2は、前記と同じ。）
Figure JPOXMLDOC01-appb-C000006
 （式中、Ａｒ1～Ａｒ3、及びＲ101～Ｒ104は、前記と同じ。）
　前記縮合重合反応では、トリアリールアミン化合物のアリール基１当量に対して、アルデヒド化合物及び／又はケトン化合物を０.１～１０当量の割合で用いることができる。
　前記酸触媒としては、例えば、硫酸、リン酸、過塩素酸等の鉱酸類；ｐ－トルエンスルホン酸、ｐ－トルエンスルホン酸一水和物等の有機スルホン酸類；ギ酸、シュウ酸等のカルボン酸類等を用いることができる。酸触媒の使用量は、その種類によって種々選択されるが、通常、トリアリールアミン類１００質量部に対して、０.００１～１０,０００質量部、好ましくは０.０１～１,０００質量部、より好ましくは０.１～１００質量部である。
　前記縮合反応は無溶媒でも行えるが、通常溶媒を用いて行われる。溶媒としては反応を阻害しないものであれば全て使用することができ、例えば、テトラヒドロフラン、１,４－ジオキサン等の環状エーテル類；Ｎ,Ｎ－ジメチルホルムアミド（ＤＭＦ）、Ｎ,Ｎ－ジメチルアセトアミド（ＤＭＡｃ）、Ｎ－メチル－２－ピロリドン（ＮＭＰ）等のアミド類；メチルイソブチルケトン、シクロヘキサノン等のケトン類；塩化メチレン、クロロホルム、１,２－ジクロロエタン、クロロベンゼン等のハロゲン化炭化水素類；ベンゼン、トルエン、キシレン等の芳香族炭化水素類等が挙げられ、特に、環状エーテル類が好ましい。これらの溶媒は、それぞれ１種単独で又は２種以上混合して用いることができる。また、使用する酸触媒が、例えば、ギ酸のような液状のものであるならば、酸触媒に溶媒としての役割を兼ねさせることもできる。
　縮合時の反応温度は、通常４０～２００℃である。反応時間は反応温度によって種々選択されるが、通常３０分間から５０時間程度である。
　高分岐ポリマーに酸性基を導入する場合、ポリマー原料である、前記トリアリールアミン化合物、アルデヒド化合物、ケトン化合物の芳香環上に予め導入し、これを用いて高分岐ポリマーを製造する方法で導入しても、得られた高分岐ポリマーを、その芳香環上に酸性基を導入可能な試薬で処理する方法で導入してもよいが、製造の簡便さを考慮すると、後者の方法を用いることが好ましい。後者の方法において、酸性基を芳香環上に導入する方法としては、特に制限はなく、酸性基の種類に応じて従来公知の各種方法から適宜選択すればよい。例えば、スルホ基を導入する場合、過剰量の硫酸を用いてスルホン化する方法等を用いることができる。
　前記高分岐ポリマーの平均分子量は特に限定されないが、重量平均分子量が１,０００～２,０００,０００が好ましく、２,０００～１,０００,０００がより好ましい。
　具体的な高分岐ポリマーとしては、下記式で表されるものが挙げられるが、これらに限定されない。
Figure JPOXMLDOC01-appb-C000007
　前記ＣＮＴ含有組成物における、ＣＮＴと分散剤との混合比率は、質量比で１,０００：１～１：１００程度とすることができる。
　分散剤の濃度は、ＣＮＴを溶媒に分散させ得る濃度であれば特に限定されないが、組成物中、０.００１～３０質量％程度とすることが好ましく、０.００２～２０質量％程度とすることがより好ましい。
　ＣＮＴの濃度は、目的とするアンダーコート層の目付量や、要求される機械的、電気的、熱的特性等において変化するものであり、また、少なくともＣＮＴの一部が孤立分散し、実用的な目付量でアンダーコート層を作製できる限り任意であるが、組成物中、０.０００１～３０質量％程度とすることが好ましく、０.００１～２０質量％程度とすることがより好ましく、０.００１～１０質量％程度とすることがより一層好ましい。
　なお、前記ＣＮＴ含有組成物は、用いる分散剤と架橋反応を起こす架橋剤や、自己架橋する架橋剤を含んでいてもよい。これらの架橋剤は、使用する溶媒に溶解することが好ましい。
　オキサゾリンポリマーの架橋剤としては、例えば、カルボキシ基、ヒドロキシ基、チオール基、アミノ基、スルフィン酸基、エポキシ基等のオキサゾリン基との反応性を有する官能基を２個以上有する化合物であれば特に限定されないが、カルボキシ基を２個以上有する化合物が好ましい。なお、薄膜形成時の加熱や、酸触媒の存在下で前記官能基が生じて架橋反応を起こす官能基、例えば、カルボン酸のナトリウム塩、カリウム塩、リチウム塩、アンモニウム塩等を有する化合物も架橋剤として用いることができる。
　オキサゾリン基と架橋反応を起こす化合物の具体例としては、酸触媒の存在下で架橋反応性を発揮する、ポリアクリル酸やそのコポリマー等の合成高分子及びカルボキシメチルセルロースやアルギン酸といった天然高分子の金属塩、加熱により架橋反応性を発揮する、前記合成高分子及び天然高分子のアンモニウム塩等が挙げられる。特に、酸触媒の存在下や加熱条件下で架橋反応性を発揮するポリアクリル酸ナトリウム、ポリアクリル酸リチウム、ポリアクリル酸アンモニウム、カルボキシメチルセルロースナトリウム、カルボキシメチルセルロースリチウム、カルボキシメチルセルロースアンモニウム等が好ましい。
　このようなオキサゾリン基と架橋反応を起こす化合物は、市販品として入手することもでき、そのような市販品としては、例えば、ポリアクリル酸ナトリウム（和光純薬工業(株)製、重合度２,７００～７,５００）、カルボキシメチルセルロースナトリウム（和光純薬工業(株)製）、アルギン酸ナトリウム（関東化学(株)製、鹿１級）、アロンA-30（ポリアクリル酸アンモニウム、東亞合成(株)製、固形分濃度３２質量％、水溶液）、DN-800H（カルボキシメチルセルロースアンモニウム、ダイセルファインケム(株)製）アルギン酸アンモニウム（(株)キミカ製）等が挙げられる。
　トリアリールアミン系高分岐ポリマーの架橋剤としては、例えば、メラミン系、置換尿素系、これらのポリマー系架橋剤等が挙げられる。これら架橋剤は、１種単独で又は２種以上を混合して用いることができる。なお、好ましくは、少なくとも２個の架橋形成置換基を有する架橋剤であり、具体的には、ＣＹＭＥＬ（登録商標）、メトキシメチル化グリコールウリル、ブトキシメチル化グリコールウリル、メチロール化グリコールウリル、メトキシメチル化メラミン、ブトキシメチル化メラミン、メチロール化メラミン、メトキシメチル化ベンゾグアナミン、ブトキシメチル化ベンゾグアナミン、メチロール化ベンゾグアナミン、メトキシメチル化尿素、ブトキシメチル化尿素、メチロール化尿素、メトキシメチル化チオ尿素、メトキシメチル化チオ尿素、メチロール化チオ尿素等の化合物、及びこれらの化合物の縮合体が挙げられる。
　自己架橋する架橋剤としては、例えば、ヒドロキシ基に対するアルデヒド基、エポキシ基、ビニル基、イソシアネート基やアルコキシ基、カルボキシ基に対するアルデヒド基、アミノ基、イソシアネート基やエポキシ基、アミノ基に対するイソシアネート基やアルデヒド基等の、互いに反応する架橋性官能基を同一分子内に有している化合物や、同じ架橋性官能基同士で反応するヒドロキシ基（脱水縮合）、メルカプト基（ジスルフィド結合）、エステル基（クライゼン縮合）、シラノール基（脱水縮合）、ビニル基、アクリル基等を有している化合物等が挙げられる。自己架橋する架橋剤の具体例としては、酸触媒の存在下で架橋反応性を発揮する多官能アクリレート、テトラアルコキシシラン、ブロックイソシアネート基を有するモノマー及びヒドロキシ基、カルボン酸、アミノ基の少なくとも１つを有するモノマーのブロックコポリマー等が挙げられる。
　このような自己架橋する架橋剤は、市販品として入手することもでき、そのような市販品としては、例えば、多官能アクリレートでは、A-9300（エトキシ化イソシアヌル酸トリアクリレート、新中村化学工業(株)製）、A-GLY-9E（Ethoxylated glycerine triacrylate（EO 9mol）、新中村化学工業(株)製）、A-TMMT（ペンタエリスリトールテトラアクリレート、新中村化学工業(株)製）等が挙げられ、テトラアルコキシシランでは、テトラメトキシシラン（東京化成工業(株)製）、テトラエトキシシラン（東横化学(株)製）等が挙げられ、ブロックイソシアネート基を有するポリマーでは、エラストロン（登録商標）シリーズE-37、H-3、H38、BAP、NEW BAP-15、C-52、F-29、W-11P、MF-9、MF-25K（第一工業製薬(株)製）等が挙げられる。
　これら架橋剤の添加量は、使用する溶媒、使用する基材、要求される粘度、要求される膜形状等により変動するが、分散剤に対し、０.００１～８０質量％、好ましくは０.０１～５０質量％、より好ましくは０.０５～４０質量％である。これら架橋剤は、自己縮合による架橋反応を起こすこともあるが、分散剤と架橋反応を起こすものであり、分散剤中に架橋性置換基が存在する場合はこれらの架橋性置換基により架橋反応が促進される。
　本発明では、架橋反応を促進するための触媒として、ｐ－トルエンスルホン酸、トリフルオロメタンスルホン酸、ピリジニウムｐ－トルエンスルホン酸、サリチル酸、スルホサリチル酸、クエン酸、安息香酸、ヒドロキシ安息香酸、ナフタレンカルボン酸等の酸性化合物、及び／又は２,４,４,６－テトラブロモシクロヘキサジエノン、ベンゾイントシレート、２－ニトロベンジルトシレート、有機スルホン酸アルキルエステル等の熱酸発生剤を添加することができる。
　触媒の添加量は、ＣＮＴ分散剤に対し、０.０００１～２０質量％、好ましくは０.０００５～１０質量％、より好ましくは０.００１～３質量％である。
　前記ＣＮＴ含有組成物の調製法は、特に限定されないが、例えば、ＣＮＴ及び溶媒、並びに必要に応じて用いられる分散剤、マトリックスポリマー及び架橋剤を任意の順序で混合して調製することができる。
　この際、混合物を分散処理することが好ましく、この処理により、ＣＮＴの分散割合をより向上させることができる。分散処理としては、機械的処理である、ボールミル、ビーズミル、ジェットミル等を用いる湿式処理や、バス型やプローブ型のソニケータを用いる超音波処理が挙げられる。これらのうち、ジェットミルを用いた湿式処理や超音波処理が好ましい。
　分散処理の時間は任意であるが、１分間から１０時間程度が好ましく、５分間から５時間程度がより好ましい。この際、必要に応じて加熱処理を施しても構わない。なお、架橋剤及び／又はマトリックス高分子を用いる場合、これらは、分散剤、ＣＮＴ及び溶媒からなる混合物を調製した後から加えてもよい。
　前記ＣＮＴ含有組成物を前記集電体の少なくとも一方の面に塗布し、これを自然又は加熱乾燥し、アンダーコート層を形成してアンダーコート箔（複合集電体）を作製することができる。
　また、アンダーコート層の厚みは、得られるデバイスの内部抵抗を低減することを考慮すると、１ｎｍ～１０μｍが好ましく、１ｎｍ～１μｍがより好ましく、１～５００ｎｍがより一層好ましい。アンダーコート層の膜厚は、例えば、アンダーコート箔から適当な大きさの試験片を切り出し、それを手で裂く等の方法により断面を露出させ、走査電子顕微鏡（ＳＥＭ）等の顕微鏡観察により、断面部分でアンダーコート層が露出した部分から求めることができる。
　集電体の一面あたりのアンダーコート層の目付量は、前記膜厚を満たす限り特に限定されないが、１,０００ｍｇ／ｍ2以下が好ましく、５００ｍｇ／ｍ2以下がより好ましく、３００ｍｇ／ｍ2以下がより一層好ましく、２００ｍｇ／ｍ2以下が更に好ましい。一方、アンダーコート層の機能を担保して優れた特性の電池を再現性よく得るため、集電体の一面あたりのアンダーコート層の目付量を好ましくは１ｍｇ／ｍ2以上、より好ましくは５ｍｇ／ｍ2以上、より一層好ましくは１０ｍｇ／ｍ2以上、更に好ましくは１５ｍｇ／ｍ2以上とする。
　本発明におけるアンダーコート層の目付量は、アンダーコート層の面積（ｍ2）に対するアンダーコート層の質量（ｍｇ）の割合であり、アンダーコート層がパターン状に形成されている場合、当該面積はアンダーコート層のみの面積であり、パターン状に形成されたアンダーコート層の間に露出する集電体の面積を含まない。
　アンダーコート層の質量は、例えば、アンダーコート箔から適当な大きさの試験片を切り出し、その質量Ｗ0を測定し、その後、アンダーコート箔からアンダーコート層を剥離し、アンダーコート層を剥離した後の質量Ｗ1を測定し、その差（Ｗ0－Ｗ1）から算出する、又は予め集電体の質量Ｗ2を測定しておき、その後、アンダーコート層を形成したアンダーコート箔の質量Ｗ3を測定し、その差（Ｗ3－Ｗ2）から算出することができる。
　アンダーコート層を剥離する方法としては、例えばアンダーコート層が溶解、又は膨潤する溶媒に、アンダーコート層を浸漬させ、布等でアンダーコート層をふき取る等の方法が挙げられる。
　目付量は、公知の方法で調整することができる。例えば、塗布によりアンダーコート層を形成する場合、アンダーコート層を形成するための塗工液（ＣＮＴ含有組成物）の固形分濃度、塗布回数、塗工機の塗工液投入口のクリアランス等を変えることで調整できる。目付量を多くしたい場合は、固形分濃度を高くしたり、塗布回数を増やしたり、クリアランスを大きくしたりする。目付量を少なくしたい場合は、固形分濃度を低くしたり、塗布回数を減らしたり、クリアランスを小さくしたりする。
　ＣＮＴ含有組成物の塗布方法としては、例えば、スピンコート法、ディップコート法、フローコート法、インクジェット法、キャスティング法、スプレーコート法、バーコート法、グラビアコート法、スリットコート法、ロールコート法、フレキソ印刷法、転写印刷法、刷毛塗り、ブレードコート法、エアーナイフコート法等が挙げられる。これらのうち、作業効率等の点から、インクジェット法、キャスティング法、ディップコート法、バーコート法、ブレードコート法、ロールコート法、グラビアコート法、フレキソ印刷法、スプレーコート法が好適である。
　加熱乾燥する場合の温度も任意であるが、５０～２００℃程度が好ましく、８０～１５０℃程度がより好ましい。
［電極合材層］
　前記電極合材層は、活物質、バインダーポリマー及び必要に応じて溶媒を含む電極スラリーを、アンダーコート層上に塗布し、自然又は加熱乾燥して形成することができる。
　前記活物質としては、従来、エネルギー貯蔵デバイス用電極に用いられている各種活物質を用いることができる。例えば、リチウム二次電池やリチウムイオン二次電池の場合、正極活物質としてリチウムイオンを吸着・離脱可能なカルコゲン化合物又はリチウムイオン含有カルコゲン化合物、ポリアニオン系化合物、硫黄単体及びその化合物等を用いることができる。
　このようなリチウムイオンを吸着離脱可能なカルコゲン化合物としては、例えばＦｅＳ2、ＴｉＳ2、ＭｏＳ2、Ｖ2Ｏ6、Ｖ6Ｏ13、ＭｎＯ2等が挙げられる。
　リチウムイオン含有カルコゲン化合物としては、例えばＬｉＣｏＯ2、ＬｉＭｎＯ2、ＬｉＭｎ2Ｏ4、ＬｉＭｏ2Ｏ4、ＬｉＶ3Ｏ8、ＬｉＮｉＯ2、ＬｉxＮｉyＭ1-yＯ2（ただし、Ｍは、Ｃｏ、Ｍｎ、Ｔｉ、Ｃｒ、Ｖ、Ａｌ、Ｓｎ、Ｐｂ、及びＺｎから選ばれる少なくとも１種以上の金属元素であり、０.０５≦ｘ≦１.１０、０.５≦ｙ≦１.０）等が挙げられる。
　ポリアニオン系化合物としては、例えばリン酸鉄リチウム（ＬｉＦｅＰＯ4）等が挙げられる。硫黄化合物としては、例えばＬｉ2Ｓ、ルベアン酸等が挙げられる。
　一方、前記負極を構成する負極活物質としては、アルカリ金属、アルカリ合金、リチウムイオンを吸蔵・放出する周期表４～１５族の元素から選ばれる少なくとも１種の単体、酸化物、硫化物、窒化物、又はリチウムイオンを可逆的に吸蔵・放出可能な炭素材料を使用することができる。
　アルカリ金属としては、Ｌｉ、Ｎａ、Ｋ等が挙げられ、アルカリ金属合金としては、例えば、Ｌｉ－Ａｌ、Ｌｉ－Ｍｇ、Ｌｉ－Ａｌ－Ｎｉ、Ｎａ－Ｈｇ、Ｎａ－Ｚｎ等が挙げられる。
　リチウムイオンを吸蔵放出する周期表４～１５族の元素から選ばれる少なくとも１種の元素の単体としては、例えば、ケイ素やスズ、アルミニウム、亜鉛、砒素等が挙げられる。同じく酸化物としては、例えば、スズケイ素酸化物（ＳｎＳｉＯ3）、リチウム酸化ビスマス（Ｌｉ3ＢｉＯ4）、リチウム酸化亜鉛（Ｌｉ2ＺｎＯ2）、リチウム酸化チタン（Ｌｉ4Ｔｉ5Ｏ12）、酸化チタン等が挙げられる。同じく硫化物としては、リチウム硫化鉄（ＬｉxＦｅＳ2（０≦ｘ≦３））、リチウム硫化銅（ＬｉxＣｕＳ（０≦ｘ≦３））等が挙げられる。同じく窒化物としては、リチウム含有遷移金属窒化物が挙げられ、具体的には、ＬｉxＭyＮ（Ｍ＝Ｃｏ、Ｎｉ、Ｃｕ、０≦ｘ≦３、０≦ｙ≦０.５）、リチウム鉄窒化物（Ｌｉ3ＦｅＮ4）等が挙げられる。
　リチウムイオンを可逆的に吸蔵・放出可能な炭素材料としては、グラファイト、カーボンブラック、コークス、ガラス状炭素、炭素繊維、カーボンナノチューブ、又はこれらの焼結体等が挙げられる。
　また、電気二重層キャパシタの場合、活物質として炭素質材料を用いることができる。この炭素質材料としては、活性炭等が挙げられ、例えば、フェノール樹脂を炭化後、賦活処理して得られた活性炭が挙げられる。
　バインダーポリマーとしては、公知の材料から適宜選択して用いることができ、例えば、ＰＶＤＦ、ポリビニルピロリドン、ポリテトラフルオロエチレン、テトラフルオロエチレン－ヘキサフルオロプロピレン共重合体、Ｐ(ＶＤＦ－ＨＦＰ)、Ｐ(ＶＤＦ－ＣＴＦＥ)、ポリビニルアルコール、ポリイミド、エチレン－プロピレン－ジエン三元共重合体、スチレン－ブタジエンゴム、ＣＭＣ、ポリアクリル酸（ＰＡＡ）、ポリアニリン等の導電性高分子等が挙げられる。
　なお、バインダーポリマーの添加量は、活物質１００質量部に対し、０.１～２０質量部、特に１～１０質量部が好ましい。
　溶媒としては、前記ＣＮＴ含有組成物で例示した溶媒が挙げられ、これらの中からバインダーの種類に応じて適宜選択すればよいが、ＰＶＤＦ等の非水溶性のバインダーの場合はＮＭＰが好適であり、ＰＡＡ等の水溶性のバインダーの場合は水が好適である。
　なお、前記電極スラリーは、導電材を含んでいてもよい。導電材としては、例えば、カーボンブラック、ケッチェンブラック、アセチレンブラック、カーボンウイスカー、炭素繊維、天然黒鉛、人造黒鉛、酸化チタン、酸化ルテニウム、アルミニウム、ニッケル等が挙げられる。
　電極スラリーの塗布方法としては、前述したＣＮＴ含有組成物と同様の方法が挙げられる。また、加熱乾燥する場合の温度も任意であるが、５０～４００℃程度が好ましく、８０～１５０℃程度がより好ましい。
　電極合材層の形成部位は、用いるデバイスのセル形態等に応じて適宜設定すればよく、アンダーコート層の表面全部でもその一部でもよいが、ラミネートセル等に使用する目的で、金属タブと電極とを超音波溶接等の溶接により接合した電極構造体として用いる場合には、溶接部を残すためアンダーコート層の表面の一部に電極スラリーを塗布して電極合材層を形成することが好ましい。特に、ラミネートセル用途では、アンダーコート層の周縁を残したそれ以外の部分に電極スラリーを塗布して電極合材層を形成することが好適である。
　前記電極合材層の厚みは、電池の容量と抵抗のバランスを考慮すると、１０～５００μｍが好ましく、１０～３００μｍがより好ましく、２０～１００μｍがより一層好ましい。
　集電体、アンダーコート層及び電極合材層を備える積層体を、１ｋＮ／ｃｍ未満のプレス圧力でプレスすることで、本発明の電極を製造することができる。プレス法は、一般に採用されている方法を用いることができるが、特に金型プレス法やロールプレス法が好ましい。また、プレス圧力は、１ｋＮ／ｃｍ未満であれば特に限定されず、例えば０.５ｋＮ／ｃｍ以下であってもよく、０.２ｋＮ／ｃｍ以下であってもよく、更にプレス圧力が０ｋＮ／ｃｍであっても（すなわち、プレスをしなくても）本発明の電極を製造することができる。
　本発明のエネルギー貯蔵デバイス用電極は、その電極密度が２.１ｇ／ｃｍ3未満であるが、２.０ｇ／ｃｍ3未満であることが好ましく、１.７ｇ／ｃｍ3以下であることがより好ましく、１.３ｇ／ｃｍ3以下であることが更に好ましい。前記電極密度の下限は、特に限定されないが、通常０.５ｇ／ｃｍ3以上であり、０.８ｇ／ｃｍ3以上であることが好ましい。
［エネルギー貯蔵デバイス］
　本発明のエネルギー貯蔵デバイスは、前述したエネルギー貯蔵デバイス用電極を備えたものであり、より具体的には、少なくとも一対の正負極と、これら各極間に介在するセパレータと、電解質とを備えて構成され、正負極の少なくとも一方が、前述したエネルギー貯蔵デバイス用電極から構成される。
　本発明のエネルギー貯蔵デバイスとしては、例えば、リチウムイオン二次電池、ハイブリッドキャパシタ、リチウム二次電池、ニッケル水素電池、鉛蓄電池等の各種エネルギー貯蔵デバイスが挙げられる。
　このエネルギー貯蔵デバイスは、電極として前述したエネルギー貯蔵デバイス用電極を用いることにその特徴があるため、その他のデバイス構成部材であるセパレータや、電解質等は、公知の材料から適宜選択して用いることができる。
　セパレータとしては、例えば、セルロース系セパレータ、ポリオレフィン系セパレータ等が挙げられる。電解質としては、液体、固体のいずれでもよく、また水系、非水系のいずれでもよいが、本発明のエネルギー貯蔵デバイス用電極は、非水系電解質を用いたデバイスに適用した場合にも実用上十分な性能を発揮させ得る。
　非水系電解質としては、電解質塩を非水系有機溶媒に溶かしてなる非水系電解液が挙げられる。電解質塩としては、４フッ化ホウ酸リチウム、６フッ化リン酸リチウム、過塩素酸リチウム、トリフルオロメタンスルホン酸リチウム等のリチウム塩；テトラメチルアンモニウムヘキサフルオロホスフェート、テトラエチルアンモニウムヘキサフルオロホスフェート、テトラプロピルアンモニウムヘキサフルオロホスフェート、メチルトリエチルアンモニウムヘキサフルオロホスフェート、テトラエチルアンモニウムテトラフルオロボレート、テトラエチルアンモニウムパークロレート等の４級アンモニウム塩、リチウムビス(トリフルオロメタンスルホニル)イミド、リチウムビス(フルオロスルホニル)イミド等のリチウムイミド等が挙げられる。
　非水系有機溶媒としては、プロピレンカーボネート、エチレンカーボネート、ブチレンカーボネート等のアルキレンカーボネート；ジメチルカーボネート、メチルエチルカーボネート、ジエチルカーボネート等のジアルキルカーボネート；アセトニトリル等のニトリル類、ジメチルホルムアミド等のアミド類等が挙げられる。
　エネルギー貯蔵デバイスの形態は特に限定されず、円筒型、扁平巻回角型、積層角型、コイン型、扁平巻回ラミネート型、積層ラミネート型等の従来公知の各種形態のセルを採用することができる。
　コイン型に適用する場合、前述した本発明のエネルギー貯蔵デバイス用電極を、所定の円盤状に打ち抜いて用いればよい。例えば、リチウムイオン二次電池は、コインセルのワッシャーとスペーサーが溶接されたフタに、所定形状に打ち抜いたリチウム箔を所定枚数設置し、その上に、電解液を含浸させた同形状のセパレータを重ね、更に上から、電極合材層を下にして本発明のエネルギー貯蔵デバイス用電極を重ね、ケースとガスケットを載せて、コインセルかしめ機で密封して作製することができる。
　積層ラミネート型に適用する場合、電極合材層がアンダーコート層表面の一部又は全面に形成された電極における、アンダーコート層が形成され、かつ、電極合材層が形成されていない部分（溶接部）で金属タブと溶接して得られた電極構造体を用いればよい。この場合、電極構造体を構成する電極は一枚でも複数枚でもよいが、一般的には、正負極とも複数枚が用いられる。正極を形成するための複数枚の電極は、負極を形成するための複数枚の電極と、一枚ずつ交互に重ねることが好ましく、その際、正極と負極の間には前述したセパレータを介在させることが好ましい。なお、アンダーコート層が形成され、かつ、電極合材層が形成されていない部分で溶接する場合、集電体の一面あたりのアンダーコート層の目付量を好ましくは１００ｍｇ／ｍ2以下、より好ましくは９０ｍｇ／ｍ2以下、より一層好ましくは５０ｍｇ／ｍ2未満とする。
　金属タブは、複数枚の電極の最も外側の電極の溶接部で溶接しても、複数枚の電極のうち、任意の隣接する２枚の電極の溶接部間に金属タブを挟んで溶接してもよい。金属タブの材質は、一般的にエネルギー貯蔵デバイスに使用されるものであれば、特に限定されず、例えば、ニッケル、アルミニウム、チタン、銅等の金属；ステンレススチール、ニッケル合金、アルミニウム合金、チタン合金、銅合金等の合金等が挙げられる。これらのうち、溶接効率を考慮すると、アルミニウム、銅及びニッケルから選ばれる少なくとも１種の金属を含んで構成されるものが好ましい。金属タブの形状は、箔状が好ましく、その厚さは０.０５～１ｍｍ程度が好ましい。
　溶接方法は、金属同士の溶接に用いられる公知の方法を用いることができ、その具体例としては、ＴＩＧ溶接、スポット溶接、レーザー溶接、超音波溶接等が挙げられるが、超音波溶接にて電極と金属タブとを接合することが好ましい。
　超音波溶接の方法としては、例えば、複数枚の電極をアンビルとホーンとの間に配置し、溶接部に金属タブを配置して超音波をかけて一括して溶接する方法や、電極同士を先に溶接し、その後、金属タブを溶接する方法等が挙げられる。
　本発明では、いずれの方法でも、金属タブと電極とが前記溶接部で溶接されるだけでなく、複数枚の電極同士も互いに超音波溶接されることになる。溶接時の圧力、周波数、出力、処理時間等は、特に限定されず、用いる材料やアンダーコート層の目付量等を考慮して適宜設定すればよい。
　以上のようにして作製した電極構造体を、ラミネートパックに収納し、前述した電解液を注入した後、ヒートシールすることでラミネートセルが得られる。
　以下、製造例、参考例、実施例及び比較例を挙げて本発明を更に詳しく説明するが、本発明は、下記実施例に限定されない。なお、使用した装置は、以下のとおりである。
・プローブ型超音波照射装置：Hielscher Ultrasonics社製、UIP1000
・ワイヤーバーコーター：(株)エスエムテー製、PM-9050MC
・ホモディスパー：プライミクス(株)製、Ｔ.Ｋ.ロボミックス（ホモディスパー２.５型（φ３２）付き）
・薄膜旋回型高速ミキサー：プライミクス(株)製、フィルミクス４０型
・自転・公転ミキサー：(株)シンキー製、あわとり練太郎（ARE-310）
・ロールプレス装置：(有)タクミ技研、SA-602
・充放電測定装置：東洋システム(株)製、TOSCAT-3100
・粘着・皮膜剥離解析装置：協和界面科学(株)製、VERSATILE PEEL ANALYZER VPA-3
［１］アンダーコート箔の製造
［製造例１］
　オキサゾリンポリマーを含む水溶液であるエポクロスWS-300（(株)日本触媒製、固形分濃度１０質量％、重量平均分子量１.２×１０5、オキサゾリン基量７.７ｍｍｏｌ／ｇ）５.０ｇと、純水３７.１５ｇと、２－プロパノール（純正化学(株)製、試薬特級）７.３５ｇとを混合し、更にそこへ導電性炭素材料であるＣＮＴ（戸田工業(株)製、TC-2010）０.５ｇを混合した。得られた混合物に対して、プローブ型超音波照射装置を用いて３０分間超音波処理を行い、均一にＣＮＴが分散した分散液を調製した。これに、ポリアクリル酸アンモニウムを含む水溶液であるアロンA-30（東亞合成(株)製、固形分濃度３１.６質量％）１.２ｇと、純水４１.３５ｇと、２－プロパノール（純正化学(株)製、試薬特級）７.４４ｇを混合して、アンダーコート組成物Ａを調製した。
　得られたアンダーコート組成物Ａを、集電体であるアルミニウム箔（厚み１５μｍ）にワイヤーバーコーター（OSP-13、ウェット膜厚１３μｍ）で均一に展開後、１５０℃で３０分乾燥してアンダーコート層を形成し、アンダーコート箔Ａを作製した。目付量を測定した結果、１５０ｍｇ／ｍ2であった。
［比較製造例１］
　ＣＮＴのかわりにデンカブラック（デンカ(株)製、カーボンブラック）を用いたこと以外は、製造例１と同様の方法でアンダーコート箔Ｃを調製した。目付量を測定した結果、１２９ｍｇ／ｍ2であった。
［２］電極及びリチウムイオン二次電池の製造
［実施例１］
　活物質としてリン酸鉄リチウム（LFP、Aleees社製）３１.８４ｇ、バインダーとしてポリフッ化ビニリデン（PVDF）のＮＭＰ溶液（１２質量％、(株)クレハ製、ＫＦポリマーＬ#1120）１３.０５ｇ、導電材としてデンカブラック１.３９ｇ及びＮＭＰ１３.７２ｇを、ホモディスパーにて８,０００ｒｐｍで１分間混合した。次いで、薄膜旋回型高速ミキサーを用いて周速２０ｍ／秒で６０秒の混合処理をし、更に自転・公転ミキサーにて２,２００ｒｐｍで３０秒脱泡することで、電極スラリー（固形分濃度５８質量％、LFP：PVDF：デンカブラック＝９１.５：４.５：４（質量比））を作製した。得られた電極スラリーを、アンダーコート箔Ａに均一（ウェット膜厚１００μｍ）に展開後、８０℃で３０分、次いで１２０℃で３０分乾燥してアンダーコート層上に電極合材層を形成し、更にロールプレス機で０.２ｋＮ／ｃｍのプレス圧力でプレスして圧着させ、電極を作製した。
　得られた電極から、直径１０ｍｍの円盤状の電極を４枚打ち抜き、電極層の質量（打ち抜いた電極の質量から電極未塗工部を直径１０ｍｍに打ち抜いたものの質量を差し引いたもの）及び電極層厚み（打ち抜いた電極の厚みから基材の厚みを引いたもの）から電極密度を算出した。電極密度は、１.６３ｇ／ｃｍ3であった。各電極を１２０℃で１５時間真空乾燥し、アルゴンで満たされたグローブボックスに移した。
　２０３２型のコインセル（宝泉(株)製）のワッシャーとスペーサーが溶接されたフタに、直径１４ｍｍに打ち抜いたリチウム箔（本荘ケミカル(株)製、厚み０.１７ｍｍ）を６枚重ねたものを設置し、その上に、電解液（キシダ化学(株)製、エチレンカーボネート：ジエチルカーボネート＝１：１（体積比）、電解質であるリチウムヘキサフルオロホスフェートを１ｍｏｌ／Ｌ含む。）を２４時間以上染み込ませた、直径１６ｍｍに打ち抜いたセパレータ（セルガード(株)製、セルガード#2400）を一枚重ねた。更に上から、活物質を塗布した面を下にして電極を重ねた。電解液を１滴滴下したのち、ケースとガスケットを載せて、コインセルかしめ機で密封した。その後２４時間静置し、試験用のリチウムイオン二次電池Ａ１を４個作製した。
［実施例２］
　ロールプレス機で圧着しなかった（プレス圧力０ｋＮ／ｃｍ）こと以外は、実施例１と同様の方法で試験用のリチウムイオン二次電池Ａ２を４個作製した。電極密度は、１.２７ｇ／ｃｍ3であった。
［参考例１］
　プレス圧力を１ｋＮ／ｃｍに変更した以外は、実施例１と同様の方法で試験用のリチウムイオン二次電池Ａ０を４個作製した。電極密度は、２.０２ｇ／ｃｍ3であった。
［比較例１］
　アンダーコート箔Ａのかわりに無垢のアルミニウム箔を用いたこと以外は、実施例１と同様の方法で試験用のリチウムイオン二次電池Ｂ１を４個作製した。電極密度は、１.６４ｇ／ｃｍ3であった。
［比較例２］
　アンダーコート箔Ａのかわりに無垢のアルミニウム箔を用いたこと以外は、実施例２と同様の方法で試験用のリチウムイオン二次電池Ｂ２を４個作製した。電極密度は、１.２６ｇ／ｃｍ3であった。
［参考例２］
　アンダーコート箔Ａのかわりに無垢のアルミニウム箔を用いたこと以外は、参考例１と同様の方法で試験用のリチウムイオン二次電池Ｂ０を４個作製した。電極密度は、２.１６ｇ／ｃｍ3であった。
［比較例３］
　アンダーコート箔Ａのかわりにアンダーコート箔Ｃを用いたこと以外は、実施例１と同様の方法で試験用のリチウムイオン二次電池Ｃ１を４個作製した。電極密度は、１.６２ｇ／ｃｍ3であった。
［比較例４］
　アンダーコート箔Ａのかわりにアンダーコート箔Ｃを用いたこと以外は、実施例２と同様の方法で試験用のリチウムイオン二次電池Ｃ２を４個作製した。電極密度は、１.２５ｇ／ｃｍ3であった。
［参考例３］
　アンダーコート箔Ａのかわりにアンダーコート箔Ｃを用いたこと以外は、参考例１と同様の方法で試験用のリチウムイオン二次電池Ｃ０を４個作製した。電極密度は、２.００ｇ／ｃｍ3であった。
［３］電池の特性評価
（１）電極の密着力の測定
　各実施例及び比較例で得られた電極を２５ｍｍ幅で切り出し、電極合材層塗工面に２０ｍｍ幅の両面テープを貼り付けてガラス基板上に固定した。これを粘着・皮膜剥離解析装置に固定して剥離角度９０°かつ剥離速度１００ｍｍ／ｍｉｎで剥離試験を行い、密着力を測定した。結果を表２に示す。
（２）レート特性評価
　アンダーコート箔が電池に及ぼす影響を評価することを目的として、充放電測定装置を用いて、以下の条件で充放電試験を行った。結果を表２に示す。
Figure JPOXMLDOC01-appb-T000008
・カットオフ電圧：４.５０Ｖ－２.００Ｖ 
・試験電池数：４個
・温度：室温
・放電電圧：ステップ２において、各放電条件時の実放電容量を１００％とし、１０％放電した時点での電圧を放電電圧とした。
・直流抵抗（ＤＣＲ）測定：４個の試験用電池につき、ステップ２において、各放電条件時の電流値と放電電圧とからＤＣＲを算出し、その平均値を求めた。
Figure JPOXMLDOC01-appb-T000009
　表２に示した結果より、本発明の電極を用いることで、電極合材層と集電体との界面の抵抗が小さく、高速充放電特性に優れ、サイクル劣化の少ないエネルギー貯蔵デバイスが得られることがわかった。
１　平行部
２　平行部のチューブ外径
３　くびれ部
４　くびれ部のチューブ外径

Claims (23)

  1. 　集電体と、該集電体の少なくとも一方の面に形成されたカーボンナノチューブを含むアンダーコート層と、該アンダーコート層上に形成された電極合材層とを備える積層体を、１ｋＮ／ｃｍ未満のプレス圧力でプレスしてなるエネルギー貯蔵デバイス用電極。
  2. 　前記プレス圧力が、０.５ｋＮ／ｃｍ以下である請求項１記載のエネルギー貯蔵デバイス用電極。
  3. 　前記プレス圧力が、０.２ｋＮ／ｃｍ以下である請求項２記載のエネルギー貯蔵デバイス用電極。
  4. 　前記プレス圧力が、０ｋＮ／ｃｍである請求項３記載のエネルギー貯蔵デバイス用電極。
  5. 　集電体と、該集電体の少なくとも一方の面に形成されたカーボンナノチューブを含むアンダーコート層と、該アンダーコート層上に形成された電極合材層とを備える電極であって、電極密度が２.１ｇ／ｃｍ3未満であるエネルギー貯蔵デバイス用電極。
  6. 　前記電極密度が、２.０ｇ／ｃｍ3未満である請求項５記載のエネルギー貯蔵デバイス用電極。
  7. 　前記電極密度が、１.７ｇ／ｃｍ3以下である請求項６記載のエネルギー貯蔵デバイス用電極。
  8. 　前記電極密度が、１.３ｇ／ｃｍ3以下である請求項７記載のエネルギー貯蔵デバイス用電極。
  9. 　集電体の一面あたりのアンダーコート層の目付量が、１,０００ｍｇ／ｍ2以下である請求項１～８のいずれか１項記載のエネルギー貯蔵デバイス用電極。
  10. 　集電体の一面あたりのアンダーコート層の目付量が、５００ｍｇ／ｍ2以下である請求項９記載のエネルギー貯蔵デバイス用電極。
  11. 　集電体の一面あたりのアンダーコート層の目付量が、３００ｍｇ／ｍ2以下である請求項１０記載のエネルギー貯蔵デバイス用電極。
  12. 　集電体の一面あたりのアンダーコート層の目付量が、２００ｍｇ／ｍ2以下である請求項１１記載のエネルギー貯蔵デバイス用電極。
  13. 　前記アンダーコート層が、カーボンナノチューブ分散剤を含むものである請求項１～１２のいずれか１項記載のエネルギー貯蔵デバイス用電極。
  14. 　前記カーボンナノチューブ分散剤が、側鎖にオキサゾリン基を含むビニル系ポリマー又はトリアリールアミン系高分岐ポリマーを含むものである請求項１３記載のエネルギー貯蔵デバイス用電極。
  15. 　前記アンダーコート層が、マトリックス高分子を含むものである請求項１～１４のいずれか１項記載のエネルギー貯蔵デバイス用電極。
  16. 　前記集電体が、アルミニウム箔又は銅箔である請求項１～１５のいずれか１項記載のエネルギー貯蔵デバイス用電極。
  17. 　正極である請求項１～１６のいずれか１項記載のエネルギー貯蔵デバイス用電極。
  18. 　負極である請求項１～１６のいずれか１項記載のエネルギー貯蔵デバイス用電極。
  19. 　請求項１～１８のいずれか１項記載のエネルギー貯蔵デバイス用電極を備えるエネルギー貯蔵デバイス。
  20. 　集電体上の少なくとも一方の面にカーボンナノチューブを含むアンダーコート層を形成する工程、該アンダーコート層上に電極合材層を形成する工程、及び１ｋＮ／ｃｍ未満のプレス圧力でプレスする工程を含むエネルギー貯蔵デバイス用電極の製造方法。
  21. 　前記プレス圧力が、０.５ｋＮ／ｃｍ以下である請求項２０記載のエネルギー貯蔵デバイス用電極の製造方法。
  22. 　前記プレス圧力が、０.２ｋＮ／ｃｍ以下である請求項２１記載のエネルギー貯蔵デバイス用電極の製造方法。
  23. 　前記プレス圧力が、０ｋＮ／ｃｍである請求項２２記載のエネルギー貯蔵デバイス用電極の製造方法。
PCT/JP2019/011361 2018-03-29 2019-03-19 エネルギー貯蔵デバイス用電極及びエネルギー貯蔵デバイス WO2019188556A1 (ja)