WO2019177228A1 - 해충 회피 성분이 포함된 필름으로 제조된 해충 회피용 거름망 - Google Patents

해충 회피 성분이 포함된 필름으로 제조된 해충 회피용 거름망 Download PDF

Info

Publication number
WO2019177228A1
WO2019177228A1 PCT/KR2018/014802 KR2018014802W WO2019177228A1 WO 2019177228 A1 WO2019177228 A1 WO 2019177228A1 KR 2018014802 W KR2018014802 W KR 2018014802W WO 2019177228 A1 WO2019177228 A1 WO 2019177228A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
film
powder
pest
antioxidant
Prior art date
Application number
PCT/KR2018/014802
Other languages
English (en)
French (fr)
Inventor
최상필
허수학
이길주
윤용철
Original Assignee
(주)테바
최상필
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)테바, 최상필 filed Critical (주)테바
Publication of WO2019177228A1 publication Critical patent/WO2019177228A1/ko

Abstract

본 발명은 해충 회피 성분이 포함된 필름으로 제조된 해충 회피용 거름망에 관한 것이다. 상세하게는, 싱크대 등에 설치되는 하수 거름망으로서, 초파리 등의 해충을 회피할 수 있도록 하는 성분을 함유하는 필름으로 제조된 거름망에 관한 것이다. 보다 상세하게는 폴리젖산(Poly Lactic Acid, PLA), 열가소성 전분(Thermaplastic starch, TPS) 또는 전분(Starch) 중 어느 하나, 폴리뷰틸렌아디파이트테레프탈레이트(Polybutylene adipate terephthalate, PBAT), 해충 회피 성분, 탈크(Talc), 제1 산화방지제 및 제2 산화방지제를 포함하는 해충 회피용 거름망을 제공하는 것으로서, 상기 해충 회피 성분은 라벤더 파우더, 녹차 파우더, 커피 파우더, 시나몬 파우더 또는 시나몬 추출액 어느 하나 이상인 것을 특징으로 하는 해충 회피용 거름망이다.

Description

해충 회피 성분이 포함된 필름으로 제조된 해충 회피용 거름망
본 발명은 해충 회피 성분이 포함된 필름으로 제조된 해충 회피용 거름망에 관한 것이다. 상세하게는, 싱크대 등에 설치되는 하수 거름망으로서, 초파리 등의 해충을 회피할 수 있도록 하는 성분을 함유하는 필름으로 제조된 거름망에 관한 것이다.
일반적으로 싱크대의 배출구에는 음식물쓰레기를 수거하기 위하여 거름망이 설치되어 있는데, 상기 거름망에는 수거된 음식물 쓰레기가 쌓여 있어 해충이 들끓게 되는 것은 필연적이다.
그런데 종래 거름망은 주로 하수관을 통해 올라오는 해충의 유입을 방지하기 위하여 기계적인 요소를 도입하는 측면으로 기술이 발전되어 왔다.
KR 20-0262197 B (2002. 1. 15.)은 “하수구트랩”에 관한 고안으로서, 특히 하수 또는 오수배관의 관로에 설치되어 배수에 따른 부구의 승강으로 배출구를 개폐하여 상기 하수 또는 오수배관을 통해 실내로 들어오는 악취와 각종 벌레의 출입을 차단하며, 착탈이 가능한 마개를 형성하여 하수구트랩 내부의 청소가 가능하도록 하여 청결한 상태를 유지할 수 있는 하수구트랩에 관한 것이다.
그러나 상기 고안은 부구의 승강으로 배출구를 개폐하여 하수관을 통해 올라오는 해충의 유입을 방지하는 것은 가능할지라도, 싱크대(개수대) 방향으로 노출된 측면으로부터 벌레가 유입되는 것을 차단하지 못하는 한계가 있는 반면, 본 발명인 해충 회피용 거름망은 해충을 회피할 수 있도록 하는 성분이 함유되어 있어 하수관으로부터 올라오는 해충뿐만 아니라 싱크대(개수대) 방향으로 노출된 측면으로부터 해충이 유입되는 것도 차단할 수 있다.
KR 10-2002-0089289 A (2002. 11. 29.) "음식물쓰레기 처리장치 및 방법"은 음식물쓰레기 처리장치 및 방법에 관한 발명으로서 더욱 상세하게는 식당이나 주방에서 음식물 조리시나 설거지를 할 때에 허드레 물과 혼합되어 발생되는 음식물 쓰레기 처리를 미생물과 수분 조정제를 사용하지 않고 투입, 분쇄, 탈수, 건조, 배출 및 폐수정화장치(침전조형)의 처리공정에 의한 기계적인 처리장치 및 방법으로 염도를 줄이고, 악취 발생 없이 간편하고, 안전하며, 위생적으로 처리되어 체류되는 음식물쓰레기로 인한 침출수 발생을 방지하여 환경을 보호하고, 악취 및 각종 해충(파리, 바퀴벌레, 세균 등)의 서식이 방지되어 청결한 환경이 유지되고, 처리된 부산물을 유기질 비료나 연료등의 원료로 재활용할 수 있도록 처리하는 음식물쓰레기 처리장치 및 방법에 관한 것이다.
그러나 상기 발명은 각종 해충(파리, 바퀴벌레, 세균 등)의 서식을 방지하기 위하여 음식물 쓰레기를 투입, 분쇄, 건조, 배출 및 폐수정화장치(침전조형)의 처리공정에 의한 기계적인 처리장치가 요구되는데 비해, 본 발명인 해충 회피용 거름망은 별도의 기계적인 처리장치가 요구되지 아니하고 거름망 그 자체 성분이 해충 회피가 되는 성분으로 매우 간결한 구성을 가지면서도 해충을 회피할 수 있도록 한다(심지어 일부는 박멸까지도 가능하다).
KR 10-2014-0121281 A (2014. 10. 15.) “음식쓰레기 자동 수거하는 싱크대 배수구”는 싱크대 배수구에 관한 발명으로, 배수구거름망에 모인 음식물쓰레기를 바로 음식물쓰레기통으로 보내는 것을 달성하기 위해 음식물 쓰레기를 수거하는 싱크대 배수구 본체는 바닥이 경사지게 되어있는 싱크대 배수구 거름망과 경사의 최하점에 연결구와, 물은 통과하고 음식물 쓰레기만 연결구로 나오도록 한 음식물 쓰레기를 수거하는 수거용기로 이루어져 있다. 이를 통해 거름망에 음식물 쓰레기가 남아있지 않음으로써 음식쓰레기의 냄새가 실내에 퍼지지 않으며 거름망에서의 해충의 번식을 막을 수 있다.
그러나 상기 발명은 경사면을 가진 거름망을 설치하여 음식물 쓰레기가 쌓이지 않고 곧바로 음식물쓰레기통으로 모이게끔 하여 거름망에 해충 번식을 방지하고 있는 반면, 본 발명은 거름망을 경사지게끔 하여 음식물쓰레기를 외부로 배출시키는 방법이 아니고 그 자체로서 해충을 회피하게끔 하는 성분이 함유되어 있어 별도의 장치가 필요없이 동일한 목적을 달성할 수 있다.
KR 10-2007-0121939 A (2007. 12. 28.) “싱크대용 음식물 쓰레기 거름망”은 거름망을 일회용으로 제작하되 거름망 자체가 음식물쓰레기에서 분해되는 재질로 제작한 것으로서 구조가 간단하여 제작이 용이하고, 음식물쓰레기 수거용기에 거름망을 통체로 폐기할 수가 있기 때문에 위생적으로 사용할 수 있는 것으로, 거름망을 일회용으로 사용함으로서 항상 깨끗한 주방의 싱크대를 유지할 수가 있으며, 악취의 방지와 벌레가 유입되는 것을 차단할 수가 있는 유용한 발명인 것이다.
그러나 상기 발명은 일회용으로 사용케 함으로써 싱크대의 위생상태를 깨끗하게 유지하여 벌레의 유입을 차단하는 것임에 반해, 본 발명은 거름망 자체의 해충 회피 성분에 의해 벌레의 유입을 차단하는 것이다.
이처럼 거름망과 관련된 선행발명은 부구를 통한 차단; 투입, 분쇄, 탈수, 건조, 배출 및 폐수정화장치를 통한 차단; 바닥이 경사지게 되어있는 싱크대 배수구 거름망과 경사의 최하점에 연결구와, 물은 통과하고 음식물 쓰레기만 연결구로 나오도록 한 음식물 쓰레기를 수거하는 수거용기; 일회용 거름망 등의 방식을 통해 벌레(해충)의 유입을 차단하였고, 본 발명과 같이 거름망 자체에 해충 회피 성분을 함유하여 벌레(해충)의 유입을 차단하는 발명은 전혀 개시된 바 없다.
상기 언급된 문제점(즉 싱크대 거름망에 축적되는 음식물쓰레기로 인해 해충이 번식하여 들끓게 되어 비위생적인 상태가 되는 것)을 방지하고자 본 발명은 별도의 기계적 장치 등을 요하지 아니하고 거름망 자체의 성분으로 해충 회피 목적을 달성할 수 있다.
본 발명의 다른 목적 및 기술적 특징은 이하의 발명을 실시하기 위한 구체적인 내용, 청구의 범위 및 도면에 의해 보다 구체적으로 제시된다.
상기 목적을 달성하기 위하여 본 발명은 폴리젖산(Poly Lactic Acid, PLA); 열가소성 전분(Thermalplastic starch, TPS) 또는 전분(Starch) 중 어느 하나; 폴리뷰틸렌아디파이트테레프탈레이드(Polybutylene adipate terephthalate, PBAT); 해충 회피 성분; 탈크(Talc); 제1 산화방지제(1st Anti-oxidant); 및 제 2 산화방지제(2nd Anti-oxidant)를 포함하는 필름으로 제조된 해충 회피용 거름망을 제공한다.
바람직하게는, 상기 해충 회피 성분은 라벤더 파우더(Lavendor Powder), 녹차 파우더(Green Tea Powder), 커피 파우더(Coffee Powder), 시나몬 파우더(Cinnamon Powder) 또는 시나몬 추출액(Cinnamon Extraction Solution) 중 어느 하나 이상인 것을 특징으로 하는 필름으로 제조된 해충 회피용 거름망을 제공한다.
또한 바람직하게는, 상기 폴리젖산은 1~10중량%; 상기 열가소성 전분 또는 전분 중 어느 하나는 1~10중량%; 상기 폴리뷰틸렌아디파이트테레프탈레이트는 50~75중량%; 상기 탈크는 10~20중량%; 상기 제1 산화방지제는 0.01~2중량%; 상기 제2 산화방지제는 0.01~2중량%; 상기 해충 회피 성분은 라벤더 파우더 0.1~10중량%, 녹차 파우더 0.05~10중량%, 커피파우더 0.05~10중량%, 시나몬 파우더 0.01~10중량% 또는 시나몬 추출액 0.1~10중량% 중 어느 하나 이상인 것;을 포함하는 것을 특징으로 필름으로 제조된 해충 회피용 거름망을 제공한다.
또한 바람직하게는, 상기 폴리젖산은 1~10중량%; 상기 열가소성 전분 또는 전분 중 어느 하나는, s 1~10중량%; 상기 폴리뷰틸렌아디파이트테레프탈레이트는 50~75중량%; 상기 탈크는 10~20중량%; 상기 제1 산화방지제는 0.01~2중량%; 상기 제2 산화방지제는 0.01~3중량%; 상기 해충 회피 성분은 라벤더 파우더 0.1~10중량%인 것;을 포함하는 것을 특징으로 하는 필름으로 제조된 해충 회피용 거름망을 제공한다.
본 발명에 따른 제1효과는, 거름망에 축적된 음식물쓰레기로 인해 유입되는 해충을 회피하여 위생적인 싱크대를 유지할 수 있다.
본 발명에 따른 제2효과는, 해충이 유입되는 원인물질인 음식물쓰레기를 처리하는 별도의 장치 또는 방법을 요하지 아니하고 거름망 그 자체로서 해충을 회피할 수 있다.
본 발명에 따른 제3효과는, 하수관으로부터 역으로 올라오는 해충뿐만 아니라 싱크대 상부에서부터 유입되는 해충도 방지할 수 있다.
도 1은 실험 방법에 관한 개요도이다.
도 2는 대조군(Con)과 라벤더 파우더(LA) 0.5중량%를 포함한 필름의 회피능 비교 실험 사진이다.
도 3은 대조군(Con)과 시나몬 파우더(CP) 0.5중량%를 포함한 필름의 회피능 비교 실험 사진이다.
도 4는 대조군(Con)과 시나몬 추출액(CS) 0.5중량%를 포함한 필름의 회피능 비교 실험 사진이다.
도 5는 라벤더 파우더(LA) 0.5중량%를 포함한 필름과 시나몬 파우더(CP) 0.5중량%를 포함한 필름의 회피능 비교 실험 사진이다.
도 6은 라벤더 파우더(LA) 0.5중량%를 포함한 필름과 시나몬 추출액(CS) 0.5중량%를 포함한 필름의 회피능 비교 실험 사진이다.
도 7은 시나몬 파우더(CP) 0.5중량%를 포함한 필름과 시나몬 추출액(CS) 0.5중량%를 포함한 필름의 회피능 비교 실험 사진이다.
도 8은 대조군과 녹차 파우더(GT) 0.5중량%를 포함한 필름의 회피능 비교 실험 사진이다.
도 9은 본 발명에 따라 구현될 수 있는 제품 도면의 예시이다.
폴리젖산(Poly Lactic Acid, PLA);
열가소성 전분(Thermalplastic starch, TPS) 또는 전분 중 어느 하나;
폴리뷰틸렌아디파이트테레프탈레이트(Polybutylene adipate terephthalate, PBAT);
해충 회피 성분;
탈크(Talc);
제1 산화방지제; 및
제 2 산화방지제를 포함하는 필름으로 제조된 해충 회피용 거름망.
명자들은 본 발명, 해충 회피 성분이 포함된 필름으로 제조된 해충 회피용 거름망을 발명하였다.
본 발명에 따른 일 실시예로, 폴리젖산; 열가소성 전분 또는 전분 중 어느 하나; 폴리뷰틸렌아디파이트테레프탈레이드; 해충 회피 성분; 탈크; 제1 산화방지제; 및 제 2 산화방지제를 포함하는 필름으로 제조된 해충 회피용 거름망을 제공한다.
바람직하게는, 상기 해충 회피 성분은 라벤더 파우더, 녹차 파우더, 커피 파우더, 시나몬 파우더 또는 시나몬 추출액 중 어느 하나 이상인 것을 특징으로 하는 필름으로 제조된 해충 회피용 거름망을 제공한다.
또한 바람직하게는, 상기 폴리젖산은 1~10중량%; 상기 열가소성 전분 또는 전분 중 어느 하나는 1~10중량%; 상기 폴리뷰틸렌아디파이트테레프탈레이트는 50~75중량%; 상기 탈크는 10~20중량%; 상기 제1 산화방지제는 0.01~2중량%; 상기 제2 산화방지제는 0.01~3중량%; 상기 해충 회피 성분은 라벤더 파우더 0.1~10중량%, 녹차 파우더 0.05~10중량%, 커피파우더 0.05~10중량%, 시나몬 파우더 0.01~10중량% 또는 시나몬 추출액 0.1~10중량% 중 어느 하나 이상인 것;을 포함하는 것을 특징으로 하는 필름으로 제조된 해충 회피용 거름망을 제공한다.
한편, 상기 해충 회피 성분으로 제시된 라벤더 파우더, 녹차 파우더, 커피 파우더, 시나몬 파우더 또는 시나몬 추출액의 해충 회피능에 대한 실험례를 제시한다.
각 해충 회피 성분에 따른 회피 성능을 알아보기 위한 실험설계는 다음과 같다.
실험 대상이 되는 해충은 초파리로 하며, 초파리는 파리목 초파리과 곤충을 총칭하는 말이다. 거의 세계 전 지역에서 발견되며 종류에 따라 사는 곳이 굉장히 다양하다. 갖춘탈바꿈을 통해 자라며 한 세대가 짧은 것이 특징이다. 모건의 돌연변이 연구로 유명한 노랑초파리는 유전학을 비롯한 다양한 생물학 분야에서 실험 재료로 이용되고 있다(단, 본 발명이 대상으로 하는 해충은 초파리에 한하지 아니한다).
가로, 세로 5cm인 필름의 중심에 초파리의 먹이를 두고, 상온(25℃)에서 2-3시간 동안 방치하되, 2번 반복 실시한다(도 1 참조).
대조군은 폴리젖산(Poly Lactic Acid, PLA); 열가소성 전분(Thermalplastic starch, TPS) 또는 전분(Starch) 중 어느 하나; 폴리뷰틸렌아디파이트테레프탈레이드(Polybutylene adipate terephthalate, PBAT); 탈크(Talc); 제1 산화방지제(1st Anti-oxidant); 및 제2 산화방지제(2nd Anti-oxidant)를 포함하는 필름이다(단, 상기 병기된 영문 명칭은, 본 명세서에서 한글을 생략한 채로 사용되더라도 동일한 것을 지칭한다).
실험군은 상기 대조군에 해충 회피 성분으로 라벤더 파우더, 녹차 파우더, 커피 파우더, 시나몬 파우더 또는 시나몬 추출액 중 어느 하나 이상을 첨가한 필름이다.
본 발명은 상기 필름으로부터 제조된 거름망이되, 편의를 위해 필름으로 실험을 실시한다.
각 해충 회피 물질에 따른 함량비 및 그 회피능 비교를 실시한다.
라벤더 파우더를 포함하는 필름
폴리젖산은 1~10중량%; 상기 열가소성 전분은 1~10중량%; 폴리뷰틸렌아디파이트테레프탈레이트는 50~75중량%; 탈크는 10~20중량%; 제1 산화방지제는 0.01~2중량%; 제2 산화방지제는 0.01~3중량%; 라벤더 파우더는 0.1~10중량%를 포함하는 필름을 제조한다.
바람직하게는 다음 표 1에 따른 성분비에 따른 필름을 제조할 수 있다.
구분 성분명 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%)
실험예 1 실험예 2 실험예 3 실험예 4 실험예 5 실험예 6 실험예 7 실험예 8
1 PLA 4.50% 5.00% 5.00% 6.50% 8.00% 8.00% 9.00% 10.00%
2 TPS 4.50% 5.00% 6.00% 6.50% 8.00% 8.00% 9.00% 10.00%
3 PBAT 72.88% 72.20% 71.20% 68.80% 65.20% 64.70% 60.60% 55.60%
4 Lavender Powder 0.10% 0.30% 0.50% 1.00% 2.00% 3.00% 5.00% 10.00%
5 Talc 18.00% 17.46% 17.20% 17.00% 16.50% 16.00% 16.00% 15.00%
6 1st Anti-Oxidant 0.01% 0.02% 0.05% 0.10% 0.15% 0.15% 0.20% 0.20%
7 2nd Anti-Oxidant 0.01% 0.02% 0.05% 0.10% 0.15% 0.15% 0.20% 0.20%
TOTLA 100.00% 100.00% 100.00% 100.00% 100.00% 100.00% 100.00% 101.00%
상기 표 1의 실험 예3의 라벤더 파우더가 0.5중량%인 필름(이하, 이 단락에서만 ‘실험군’이라고 지칭함)과 상기 대조군을 비교한 결과(도 2 참조), 양 쪽 모두 죽은 초파리는 발견되지 아니하였으나, 1회차 실험시 필름 위 생존 개체수는 상기 대조군에서 5마리, 상기 실험군에서는 2마리가 발견되었고, 필름 밖 생존 개체수는 193마리가 발견되었으며; 2회차 실험시 필름 위 생존 개체수는 상기 대조군에서 11마리, 상기 실험군에서는 4마리가 발견되었고, 필름 밖 생존 개체수는 185마리가 발견되었다. 이를 보면, 상기 대조군의 회피율은 27.3%인 반면, 상기 실험군에서는 72.7%의 회피율을 보였다. 따라서 상기 실험군이 상기 대조군에 비해 2.7배 회피성의 효과가 있음을 확인하였다.
시나몬 파우더를 포함하는 필름
폴리젖산은 1~10중량%; 열가소성 전분은 1~10중량%; 폴리뷰틸렌아디파이트테레프탈레이트는 50~75중량%; 탈크는 10~20중량%; 제1 산화방지제는 0.01~2중량%; 제2 산화방지제는 0.01~2중량%; 시나몬 파우더는 0.01~10중량%를 포함하는 필름을 제조한다.
바람직하게는 다음 표 2에 따른 성분비를 포함하는 필름을 제조할 수 있다.
구분 성분명 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%)
실험예 1 실험예 2 실험예 3 실험예 4 실험예 5 실험예 6 실험예 7 실험예 8
1 PLA 10.00% 9.00% 9.00% 7.00% 5.00% 3.00% 3.00% 2.00%
2 TPS 10.00% 9.00% 9.00% 7.00% 5.00% 3.00% 3.00% 2.00%
3 PBAT 64.79% 65.54% 66.60% 67.30% 70.00% 72.60% 67.10% 70.00%
4 Cinnamon Powder 0.01% 0.05% 0.10% 0.50% 0.30% 1.00% 5.00% 9.00%
5 Talc 15.00% 16.37% 15.20% 18.00% 19.40% 20.00% 21.50% 16.40%
6 1st Anti-Oxidant 0.10% 0.02% 0.05% 0.10% 0.15% 0.20% 0.20% 0.20%
7 2nd Anti-Oxidant 0.10% 0.02% 0.05% 0.10% 0.15% 0.20% 0.20% 0.20%
TOTLA 100.00% 100.00% 100.00% 100.00% 100.00% 100.00% 100.00% 99.80%
상기 표2의 실험 예3의 시나몬 파우더가 0.5중량%인 필름(이하, 이 단락에서만 ‘실험군’이라고 지칭함)과 상기 대조군을 비교한 결과(도 3 참조), 죽은 초파리는 1회차 실험에서 상기 실험군에서만 1마리가 발견되었고, 1회차 실험시 대조군 및 2회차 실험에서는 상기 대조군 및 상기 실험군 모두에서 발견되지 아니하였다. 1회차 실험시 필름 위 생존 개체수는 대조군에서 12마리, 실험군에서는 0마리가 발견되었고, 필름 밖 생존 개체수는 187마리가 발견되었으며; 2회차 실험시 필름 위 생존 개체수는 상기 대조군에서 17마리, 상기 실험군에서는 0마리가 발견되었고, 필름 밖 생존 개체수는 183마리가 발견되었다. 이를 보면, 상기 대조군의 회피율은 3.3%인 반면, 상기 실험군에서는 96.7%의 회피율을 보였다. 따라서 상기 실험군이 상기 대조군에 비해 29.3배 회피성의 효과가 있음을 확인하였다.
시나몬 추출액을 포함하는 필름
폴리젖산은 1~10중량%; 열가소성 전분은 1~10중량%; 폴리뷰틸렌아디파이트테레프탈레이트는 50~75중량%; 탈크는 10~20중량%; 제1 산화방지제는 0.01~2중량%; 제2 산화방지제는 0.01~2중량%; 시나몬 추출액은 0.1~10중량%를 포함하는 필름을 제조한다.
바람직하게는 다음 표3에 따른 성분비를 포함하는 필름을 제조할 수 있다.
구분 성분명 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%)
실험예 1 실험예 2 실험예 3 실험예 4 실험예 5 실험예 6 실험예 7 실험예 8
1 PLA 4.50% 5.00% 5.00% 6.50% 8.00% 8.00% 9.00% 10.00%
2 TPS 4.50% 5.00% 6.00% 6.50% 8.00% 8.00% 9.00% 10.00%
3 PBAT 72.88% 72.20% 71.20% 68.80% 65.20% 64.70% 60.60% 55.60%
4 Cinnamon Extract(solution) 0.10% 0.30% 0.50% 1.00% 2.00% 3.00% 5.00% 10.00%
5 Talc 18.00% 17.46% 17.20% 17.00% 16.50% 16.00% 16.00% 15.00%
6 1st Anti-Oxidant 0.01% 0.02% 0.05% 0.10% 0.15% 0.15% 0.20% 0.20%
7 2nd Anti-Oxidant 0.01% 0.02% 0.05% 0.10% 0.15% 0.15% 0.20% 0.20%
TOTLA 100.00% 100.00% 100.00% 100.00% 100.00% 100.00% 100.00% 101.00%
상기 표 3의 실험예 3의 시나몬 추출액이 0.5중량%인 필름(이하, 이 단락에서만 ‘실험군’이라고 지칭함)과 상기 대조군을 비교실험한 결과(도 4 참조), 죽은 초파리는 1, 2회차 실험의 상기 대조군 및 상기 실험군 모두에서 발견되지 아니하였다. 1회차 실험시 필름 위 생존 개체수는 상기 대조군에서 22마리, 상기 실험군에서는 4마리가 발견되었고, 필름 밖 생존 개체수는 174마리가 발견되었으며; 2회차 실험시 필름 위 생존 개체수는 상기 대조군에서 26마리, 상기 실험군에서는 2마리가 발견되었고, 필름 밖 생존 개체수는 172마리가 발견되었다. 이를 보면, 상기 대조군의 회피율은 11.1%인 반면, 상기 실험군에서는 88.9%의 회피율을 보였다. 따라서 상기 실험군이 상기 대조군에 비해 8배 회피성의 효과가 있음을 확인하였다.
라벤더 파우더를 포함하는 필름과 시나몬 파우더를 포함하는 필름
상기 라벤더 파우더를 0.5중량%를 포함하는 필름(이하, 이 단락에서만 ‘라벤더 파우더 필름’라 한다)과 상기 시나몬 파우더를 0.5중량%를 포함하는 필름(이하, 이 단락에서만 ‘시나몬 파우더 필름’라 한다)을 비교한다(도 5 참조). 죽은 초파리는 1, 2회차 실험에서 라벤더 파우더 필름 및 시나몬 파우더 필름 모두에서 발견되지 아니하였다. 1회차 실험시 필름 위 생존 개체수는 라벤더 파우더 필름에서 5마리, 시나몬 파우더 필름에서는 1마리가 발견되었고, 필름 밖 생존 개체수는 196마리가 발견되었으며; 2회차 실험시 필름 위 생존 개체수는 라벤더 파우더 필름에서 7마리, 시나몬 파우더 필름에서는 1마리가 발견되었고, 필름 밖 생존 개체수는 192마리가 발견되었다. 이를 보면, 라벤더 파우더 필름의 회피율은 14.3%인 반면, 시나몬 파우더 필름에서는 85.7%의 회피율을 보였다. 따라서 시나몬 파우더 필름이 라벤더 파우더 필름에 비해 5.9배 회피성의 효과가 있음을 확인하였다.
라벤더 파우더를 포함하는 필름과 시나몬 추출액을 포함하는 필름
상기 라벤더 파우더를 0.5중량%를 포함하는 필름(이하, 이 단락에서만 ‘라벤더 파우더 필름’라고 한다)과 상기 시나몬 추출액이 0.5중량%를 포함하는 필름(이하, 이 단락에서만 ‘시나몬 추출액 필름’이라고 한다)을 비교한다. 상기 라벤더 파우더 필름과 상기 시나몬 추출액 필름을 비교한 결과(도 6 참조), 죽은 초파리는 1, 2회차 모두 발견되지 아니하였다. 1회차 실험시 필름 위 생존 개체수는 라벤더 파우더 필름에서 8마리, 시나몬 추출액 필름에서는 4마리가 발견되었고, 필름 밖 생존 개체수는 188마리가 발견되었으며; 2회차 실험시 필름 위 생존 개체수는 라벤더 파우더 필름에서 11마리, 시나몬 추출액 필름에서는 5마리가 발견되었고, 필름 밖 생존 개체수는 184마리가 발견되었다. 라벤더 파우더 필름의 회피율은 32.1%인 반면, 시나몬 추출액 필름에서는 67.9%의 회피율을 보였다. 따라서 시나몬 추출액 필름이 라벤더 파우더 필름에 비해 2.1배 회피성의 효과가 있음을 확인하였다.
시나몬 파우더를 포함하는 필름과 시나몬 추출액을 포함하는 필름
상기 시나몬 파우더를 0.5중량%를 포함하는 필름(이하, 이 단락에서만 ‘시나몬 파우더 필름’이라고 한다)과 상기 시나몬 추출액을 0.5중량%를 포함하는 필름(이하, 이 단락에서만 ‘시나몬 추출액 필름’이라고 한다)을 비교한다(도 7 참조). 죽은 초파리는 1, 2회차 실험 모두에서 발견되지 아니하였다. 1회차 실험시 필름 위 생존 개체수는 상기 시나몬 파우더 필름에서 0마리, 상기 시나몬 추출액 필름에서는 18마리가 발견되었고, 필름 밖 생존 개체수는 182마리가 발견되었으며; 2회차 실험시 필름 위 생존 개체수는 상기 시나몬 파우더 필름에서 0마리, 상기 시나몬 추출액 필름에서는 16마리가 발견되었고, 필름 밖 생존 개체수는 184마리가 발견되었다. 시나몬 파우더 필름의 회피율은 100%의 회피율을 보였다. 따라서 상기 시나몬 파우더 필름이 상기 시나몬 추출액 필름에 비해 강한 회피성의 효과가 있음을 확인하였다.
녹차 파우더를 포함하는 필름
폴리젖산은 1~10중량%; 상기 열가소성 전분은 1~10중량%; 상기 폴리뷰틸렌아디파이트테레프탈레이트는 50~75중량%; 상기 탈크는 10~20중량%; 상기 제1 산화방지제는 0.01~2중량%; 상기 제2 산화방지제는 0.01~2중량%; 녹차 파우더 0.05~10중량%를 포함하는 필름을 제조한다.
바람직하게는 다음 표 4에 따른 성분비를 포함하는 필름을 제조할 수 있다.
구분 성분명 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%)
실험예 1 실험예 2 실험예 3 실험예 4 실험예 5 실험예 6 실험예 7 실험예 8
1 PLA 4.50% 5.00% 5.00% 6.50% 8.00% 8.00% 9.00% 10.00%
2 TPS 4.50% 5.00% 6.00% 6.50% 8.00% 8.00% 9.00% 10.00%
3 PBAT 72.93% 72.40% 71.40% 68.80% 65.20% 64.70% 60.60% 55.60%
4 Green TeaPowder 0.05% 0.10% 0.50% 1.00% 2.00% 3.00% 5.00% 10.00%
5 Talc 18.00% 17.46% 17.00% 17.00% 16.50% 16.00% 16.00% 14.00%
6 1st Anti-Oxidant 0.01% 0.02% 0.05% 0.10% 0.15% 0.15% 0.20% 0.20%
7 2nd Anti-Oxidant 0.01% 0.02% 0.05% 0.10% 0.15% 0.15% 0.20% 0.20%
TOTLA 100.00% 100.00% 100.00% 100.00% 100.00% 100.00% 100.00% 100.00%
상기 표 4의 실험 예3에 따라 녹차 파우더 0.5중량%를 포함하는 필름(이하, 이 단락에서만 ‘실험군’이라고 한다)과 상기 대조군을 비교실험한 결과(도 8 참조), 죽은 초파리는 1, 2회차 실험 상기 실험군 및 상기 대조군에서 모두 발견되지 아니하였다. 1회차 실험시 필름 위 생존 개체수는 상기 대조군에서 17마리, 상기 실험군에서는 3마리가 발견되었고, 필름 밖 생존 개체수는 180마리가 발견되었으며; 2회차 실험시 필름 위 생존 개체수는 상기 대조군에서 20마리, 상기 실험군에서는 6마리가 발견되었고, 필름 밖 생존 개체수는 174마리가 발견되었다. 이를 보면, 상기 대조군은 19.6%의 회피율을 보인 반면, 상기 실험군의 회피율은 80.4%의 회피율을 보였다. 따라서 상기 실험군이 대조군에 비해 4.1배의 회피성 효과가 있음을 확인하였다.
커피 파우더를 포함하는 필름
폴리젖산은 1~10중량%; 상기 열가소성 전분은 1~10중량%; 상기 폴리뷰틸렌아디파이트테레프탈레이트는 50~75중량%; 상기 탈크는 10~20중량%; 상기 제1 산화방지제는 0.01~2중량%; 상기 제2 산화방지제는 0.01~2중량%; 커피 파우더는 0.01~10중량%를 포함하는 필름을 제조한다.
바람직하게는 다음 표 5의 성분비를 포함하는 필름을 제조할 수 있다.
구분 성분명 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%) 고형분(%)
실험예 1 실험예 2 실험예 3 실험예 4 실험예 5 실험예 6 실험예 7 실험예 8
1 PLA 10.00% 9.00% 9.00% 7.00% 5.00% 3.00% 3.00% 2.00%
2 TPS 10.00% 9.00% 9.00% 7.00% 5.00% 3.00% 3.00% 2.00%
3 PBAT 64.75% 65.56% 66.20% 67.00% 68.00% 70.00% 67.10% 70.00%
4 Coffee Powder 0.05% 0.10% 0.50% 1.00% 3.00% 5.00% 7.00% 9.00%
5 Talc 15.00% 16.30% 15.20% 17.80% 18.70% 18.60% 19.50% 16.60%
6 1st Anti-Oxidant 0.10% 0.02% 0.05% 0.10% 0.15% 0.20% 0.20% 0.20%
7 2nd Anti-Oxidant 0.10% 0.02% 0.05% 0.10% 0.15% 0.20% 0.20% 0.20%
TOTLA 100.00% 100.00% 100.00% 100.00% 100.00% 100.00% 100.00% 100.00%
상기 표 5의 실험예 3에 따라 커피 파우더 0.5중량%를 포함하는 필름(이하, 이 단락에서만 ‘실험군’이라고 한다)과 상기 대조군을 비교해보면, 죽은 초파리는 1, 2회차 실험시 상기 실험군 및 상기 대조군 모두에서 발견되지 아니하였다. 1회차 실험시 필름 위 생존 개체수는 대조군에서 19마리, 상기 실험군에서는 4마리가 발견되었고, 필름 밖 생존 개체수는 177마리가 발견되었으며; 2회차 실험시 필름 위 생존 개체수는 상기 대조군에서 22마리, 상기 실험군에서는 5마리가 발견되었고, 필름 밖 생존 개체수는 173마리가 발견되었다. 이를 보면, 상기 대조군은 18.0%의 회피율을 보인 반면, 상기 실험군의 회피율은 82.0%의 회피율을 보였다. 따라서 상기 실험군이 상기 대조군에 비해 4.5배의 회피성 효과가 있음을 확인하였다.
이와 같이 본 발명, 해충 회피 성분이 포함된 필름으로 제조된 해충 회피용 거름망은 도 9에서 도시된 바와 같이 거름망 제품으로 구현될 수 있다. 구체적으로 살펴보면, 중심에 개구부가 형성되어 있는 환형지지대; 및 상기 환형지지대 전체를 감싸는 거름망을 포함하고, 상기 거름망은, 상기 환형지지대를 거름망의 내부에 집어넣을수 있도록 형성된 열림부; 상기 환형지지대를 위아래로 모두 감싸 안을 수 있도록 봉투 모양으로 형성된 거름망 앞면부와 거름망 뒷면부; 음식물쓰레기에서 나오는 수분을 배출하기 위하여 상기 거름망 앞면부와 거름망 뒷면부에 형성되는 복수개의 수분배출구; 및 상기 거름망을 상기 환형지지대에서 쉽게 분리할 수 있도록 상기 거름망의 열림부 양단에 설치되는 손잡이부;를 포함한다. 사기 거름망은 사각형의 봉투모양으로 형성되고, 상기 열림부의 양단에 형성되는 손잡이부는 사각형의 네 개의 모서리 중 서로 인접한 두 개의 모서리에 형성되며, 상기 손잡이부가 형성되지 않은 서로 인접한 두 개의 모서리에는 상기 거름망에 음식물쓰레기와 수분이 담겨져 거름망이 터지는 것을 방지하기 위한 터짐 방지부를 더 포함할 수 있으며, 상기 환형지지대는 플라스틱 또는 금속으로 형성되어, 환형지지대의 모양을 잡아주는 내부지지대 및 상기 내부지지대의 전체면을 감싸도록 하여 실리콘으로 형성되는 외부지지대를 포함할 수 있다.

Claims (4)

  1. 폴리젖산(Poly Lactic Acid, PLA);
    열가소성 전분(Thermalplastic starch, TPS) 또는 전분 중 어느 하나;
    폴리뷰틸렌아디파이트테레프탈레이트(Polybutylene adipate terephthalate, PBAT);
    해충 회피 성분;
    탈크(Talc);
    제1 산화방지제; 및
    제 2 산화방지제를 포함하는 필름으로 제조된 해충 회피용 거름망.
  2. 제1항에 있어서,
    상기 해충 회피 성분은 라벤더 파우더; 녹차 파우더; 커피 파우더; 시나몬 파우더; 또는
    시나몬 추출액 중 어느 하나 이상인 것;을 특징으로 하는 필름으로 제조된 해충 회피용 거름망.
  3. 제1항에 있어서,
    상기 폴리젖산은 1~10중량%;
    상기 열가소성 전분 또는 상기 전분은 1~11중량%;
    상기 폴리뷰틸렌아디파이트테레프탈레이트는 50~75중량%;
    상기 탈크는 10~20중량%;
    상기 제1 산화방지제는 0.01~2중량%;
    상기 제2 산화방지제는 0.01~2중량%; 및
    상기 해충 회피 성분은 녹차 파우더 0.05~10중량%, 커피파우더 0.05~10중량%, 시나몬 파우더 0.01~10중량% 또는 시나몬 추출액 0.1~10중량% 중 어느 하나 이상인 것;을 포함하는 것을 특징으로 하는 필름으로 제조된 해충 회피용 거름망.
  4. 제1항에 있어서,
    상기 폴리젖산은 1~10중량%;
    상기 열가소성 전분 또는 상기 전분 중 어느 하나는 1~11중량%;
    상기 폴리뷰틸렌아디파이트테레프탈레이트는 50~75중량%;
    상기 탈크는 10~20중량%;
    상기 제1 산화방지제는 0.01~2중량%;
    상기 제2 산화방지제는 0.01~3중량%; 및
    상기 해충 회피 성분은 라벤더 파우더 0.1~10중량%인 것;을 포함하는 것을 특징으로 하는 필름으로 제조된 해충 회피용 거름망.
PCT/KR2018/014802 2018-03-15 2018-11-28 해충 회피 성분이 포함된 필름으로 제조된 해충 회피용 거름망 WO2019177228A1 (ko)