WO2019166993A1 - Nanomaterial-coated fibers - Google Patents
Nanomaterial-coated fibers Download PDFInfo
- Publication number
- WO2019166993A1 WO2019166993A1 PCT/IB2019/051634 IB2019051634W WO2019166993A1 WO 2019166993 A1 WO2019166993 A1 WO 2019166993A1 IB 2019051634 W IB2019051634 W IB 2019051634W WO 2019166993 A1 WO2019166993 A1 WO 2019166993A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nanomaterial
- coated
- electrically conductive
- fiber core
- mesh
- Prior art date
Abstract
Description
Claims