WO2019141787A1 - Ruban adhésif en mousse détachable - Google Patents
Ruban adhésif en mousse détachable Download PDFInfo
- Publication number
- WO2019141787A1 WO2019141787A1 PCT/EP2019/051185 EP2019051185W WO2019141787A1 WO 2019141787 A1 WO2019141787 A1 WO 2019141787A1 EP 2019051185 W EP2019051185 W EP 2019051185W WO 2019141787 A1 WO2019141787 A1 WO 2019141787A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- adhesive tape
- sensitive adhesive
- pressure
- polymer foam
- foam
- Prior art date
Abstract
L'invention vise à obtenir un ruban adhésif pour le collage de porte-étiquettes de prix qui exerce une force adhésive suffisante pour résister à un rechargement du rayon avec des marchandises et du porte-étiquettes avec des étiquettes et qui peut être retiré de manière simple sans laisser de résidus lors du détachement des porte-étiquettes de prix. À cet effet, un ruban adhésif double face selon l'invention comprend deux couches de masse adhésive extérieures, contenant respectivement un ou plusieurs poly(méth)acrylates à au moins 40 % en poids au total, une mousse polymère, et une couche de renforcement, disposée entre l'une des couches de masse adhésive extérieures et la mousse polymère, et est caractérisé en ce que la densité de la mousse polymère est de 30 à 120 kg/m3. L'objet de l'invention est aussi l'utilisation d'un ruban adhésif de ce type pour le collage d'éléments descriptifs sur les systèmes de rayonnage.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102018200877.9 | 2018-01-19 | ||
DE102018200877.9A DE102018200877A1 (de) | 2018-01-19 | 2018-01-19 | Wiederablösbares Schaumklebeband |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2019141787A1 true WO2019141787A1 (fr) | 2019-07-25 |
Family
ID=65138990
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2019/051185 WO2019141787A1 (fr) | 2018-01-19 | 2019-01-17 | Ruban adhésif en mousse détachable |
Country Status (2)
Country | Link |
---|---|
DE (1) | DE102018200877A1 (fr) |
WO (1) | WO2019141787A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112694849A (zh) * | 2020-12-28 | 2021-04-23 | 苏州德佑新材料科技股份有限公司 | 用于电子产品摄像头的泡棉胶带及其制备方法 |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102021129366A1 (de) * | 2021-11-11 | 2023-05-11 | Tesa Se | Klebeband zum Anbringen und Wiederablösen von Objekten von empfindlichen Substraten |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2001056777A1 (fr) * | 2000-02-02 | 2001-08-09 | Sylvester Michael S | Ruban de mousse auto-adhesif renforce a double face |
WO2002011985A1 (fr) | 2000-08-08 | 2002-02-14 | 3M Innovative Properties Company | Pièces pour impression flexographique à prise d'air améliorée |
WO2004067661A2 (fr) | 2003-01-29 | 2004-08-12 | Tesa Ag | Bandes adhesives destinees au collage de plaques de compression et procede de fabrication |
EP2116584A1 (fr) | 2008-05-09 | 2009-11-11 | Tesa AG | Bandes adhésives destinées au collage de plaques de pression |
EP2199354A1 (fr) * | 2008-12-16 | 2010-06-23 | tesa SE | Bande adhésive, notamment pour le collage de composants optoélectroniques |
DE202015009135U1 (de) * | 2015-10-15 | 2016-11-04 | Tesa Se | Selbstklebeartikel und dessen Verwendung zur Verklebung auf gestrichener Raufasertapete |
DE102015112206A1 (de) * | 2015-07-27 | 2017-02-02 | Infiana Germany Gmbh & Co. Kg | Montageklebeband und Verwendung des Montageklebebandes für die Druckindustrie |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
PL2025506T3 (pl) * | 2007-08-13 | 2011-03-31 | Tesa Se | Taśma klejąca z nośnikiem piankowym |
-
2018
- 2018-01-19 DE DE102018200877.9A patent/DE102018200877A1/de not_active Withdrawn
-
2019
- 2019-01-17 WO PCT/EP2019/051185 patent/WO2019141787A1/fr active Application Filing
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2001056777A1 (fr) * | 2000-02-02 | 2001-08-09 | Sylvester Michael S | Ruban de mousse auto-adhesif renforce a double face |
WO2002011985A1 (fr) | 2000-08-08 | 2002-02-14 | 3M Innovative Properties Company | Pièces pour impression flexographique à prise d'air améliorée |
WO2004067661A2 (fr) | 2003-01-29 | 2004-08-12 | Tesa Ag | Bandes adhesives destinees au collage de plaques de compression et procede de fabrication |
EP2116584A1 (fr) | 2008-05-09 | 2009-11-11 | Tesa AG | Bandes adhésives destinées au collage de plaques de pression |
EP2199354A1 (fr) * | 2008-12-16 | 2010-06-23 | tesa SE | Bande adhésive, notamment pour le collage de composants optoélectroniques |
DE102015112206A1 (de) * | 2015-07-27 | 2017-02-02 | Infiana Germany Gmbh & Co. Kg | Montageklebeband und Verwendung des Montageklebebandes für die Druckindustrie |
DE202015009135U1 (de) * | 2015-10-15 | 2016-11-04 | Tesa Se | Selbstklebeartikel und dessen Verwendung zur Verklebung auf gestrichener Raufasertapete |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112694849A (zh) * | 2020-12-28 | 2021-04-23 | 苏州德佑新材料科技股份有限公司 | 用于电子产品摄像头的泡棉胶带及其制备方法 |
Also Published As
Publication number | Publication date |
---|---|
DE102018200877A1 (de) | 2019-07-25 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
DE68910056T2 (de) | Klebriggemachte Terpolymer-Klebstoffe. | |
DE602005001128T2 (de) | Acrylhaftklebstoffzusammensetzung und Haftklebeband | |
DE68924015T2 (de) | Druckempfindliche Klebebänder. | |
EP0761793A2 (fr) | Usage multiple d'un laminé adhésif | |
EP3093322A1 (fr) | Masse adhesive pour bandes contenant un polymère acrylique, des microsphères inorganiques et des microsphères expansées | |
EP2537906B1 (fr) | Procédé de mise en réseau covalente et réversible de masses de collage | |
DE102016205808A1 (de) | Haftklebmasse | |
EP2018411B1 (fr) | Ruban adhésif double face | |
WO2017042221A1 (fr) | Auto-adhésif à base d'epdm | |
EP3543307A1 (fr) | Bande adhésive en mousse libérable | |
EP3105296A1 (fr) | Ruban adhésif | |
WO2019229150A1 (fr) | Bande adhésive multicouche dotée d'un adhésif sensible à la pression modifié par une résine | |
WO2019141787A1 (fr) | Ruban adhésif en mousse détachable | |
WO2015118138A1 (fr) | Ruban adhesif | |
EP2308937B1 (fr) | Bande adhésive avec ruban laminé flexible | |
EP3228674B1 (fr) | Substance adhésive | |
DE10029553A1 (de) | Verfahren zur Herstellung vernetzbarer Acrylathaftklebemassen | |
DE10259457B4 (de) | Verfahren zum Aufbringen von Haftklebebändern auf raue und/oder unebene Oberflächen | |
EP3173452B1 (fr) | Bande adhésive et son utilisation | |
EP3538596B1 (fr) | Kit adhésif de plusieurs couches adhésives sensibles à la pression | |
WO2020120465A1 (fr) | Ruban adhésif multicouche | |
DE102020205568B4 (de) | Blockcopolymer-basierende Haftklebmasse und Verfahren zu ihrer Herstellung | |
DE102020205048A1 (de) | Polyacrylat und darauf basierende Haftklebmasse | |
DE102019204937A1 (de) | Verfahren zur Herstellung eines Poly(meth)acrylats | |
WO2018149806A1 (fr) | Procédé pour augmenter la force d'adhérence de compositions adhésives de contact |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 19701198 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 19701198 Country of ref document: EP Kind code of ref document: A1 |